CN105816137A - Efficient cleaning brush and manufacturing method thereof - Google Patents
Efficient cleaning brush and manufacturing method thereof Download PDFInfo
- Publication number
- CN105816137A CN105816137A CN201610348170.8A CN201610348170A CN105816137A CN 105816137 A CN105816137 A CN 105816137A CN 201610348170 A CN201610348170 A CN 201610348170A CN 105816137 A CN105816137 A CN 105816137A
- Authority
- CN
- China
- Prior art keywords
- alloy
- nylon
- brush
- bristle
- high efficiency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an efficient cleaning brush which comprises a brush seat and polyamide and alloy brush bristles arranged on the brush seat. The polyamide and alloy brush bristles are prepared from 65-85% of a polyamide material and 15-35% of an alloy material, wherein the alloy material is one or a mixture of aluminum oxide, silicon carbide, white corundum and diamond. The invention further discloses a manufacturing method of the efficient cleaning brush. The efficient cleaning brush is ingenious and reasonable in structure design, polyamide serves as the basic material of the polyamide and alloy brush bristles, and the polyamide and alloy brush bristles are manufactured by increasing different alloy materials; the toughness, hardness and elasticity of the bristles are effectively improved, the service life of the bristles is effectively prolonged, the cleaning effect is improved, and damage to the outer surfaces of articles is not likely to occur; in addition, the overall structure is simple, easy to achieve and beneficial to wide application and popularization. The method is simple in manufacturing process and easy to implement and achieve, and the efficient cleaning brush can be quickly manufactured.
Description
Technical field
The invention belongs to cleaning brush technical field, be specifically related to a kind of high efficiency brushes being applied on the kitchen tools such as culinary art, barbecue utensil and preparation method thereof.
Background technology
The material that the most all Clean-brushes or brush are used at present is all steel wire, steel wool or pure nylon material.Using steel wire, steel wool, material is very rigid, is easily destroyed the article that need to clean, and causes the damage of outer surface, and relatively costly；And using brush or the brush of pure nylon material, material is softer, elastic poor, and non-refractory, cleaning effect is poor.
Therefore a kind of nylon material that is higher than in intensity and elasticity of research and development, lifting cleaning effect, less than brush or the brush head materials of steel in hardness, do not easily cause article external surface damage, meet user and use the high efficiency brushes of demand for needed for generation is.
Summary of the invention
For above-mentioned deficiency, one of the object of the invention is, it is provided that a kind of smart structural design, rationally, and cleaning effect is good, and does not easily cause the high efficiency brushes of article external surface damage.
Present invention aim at, it is provided that a kind of method making above-mentioned high efficiency brushes, the processing technology of the method is simple, it is easy to accomplish, can quickly produce high efficiency brushes, production efficiency is high.
For achieving the above object, technical scheme provided by the present invention is: a kind of high efficiency brushes, and it includes brush holder and the nylon alloy bristle being arranged on this brush holder, and this nylon alloy bristle uses following material to make:
Nylon material 65～85%,
Alloy material 15～35%,
Wherein said alloy material is one or more mixing in aluminium oxide, carborundum, white fused alumina, diamond.
As a modification of the present invention, described brush holder includes brush holder and is arranged on the brush of this brush holder one end, and the other end of this brush holder is provided with hook, brings convenience to use, is not take up table space.
As a modification of the present invention, the nylon alloy bristle in the centre position being positioned at the bottom surface of described brush is vertical setting, the nylon alloy bristle of bottom surface two side position being positioned at this brush is obliquely installed, the angle that this nylon alloy bristle tilts is 60～75 degree, it is more conducive to cleaning, effectively promotes cleaning effect.
As a modification of the present invention, the front end face of described brush is provided with wing, it is also possible to the anterior end face at this brush is provided with wing, to meet different cleaning use demands.
As a modification of the present invention, a diameter of the 0.1～2.5mm of described nylon alloy bristle, in this size range, the intensity of nylon alloy bristle and elasticity are preferable, be more conducive to cleaning and protection article external surface is not damaged.
As a modification of the present invention, described nylon alloy bristle linearly type or ripple type, meet different use demands.
A kind of method making above-mentioned high efficiency brushes, it comprises the following steps:
(1) preparing material: each component of raw material and mass percent thereof are as follows:
Nylon material 65～85%,
Alloy material 15～35%,
Wherein said alloy material is one or more mixing in aluminium oxide, carborundum, white fused alumina, diamond；
(2) feed intake: first alloy material is ground to form fine particulate and puts into again in mixing apparatus, then nylon material is put in mixing apparatus；
(3) stirring is merged: after waiting to feed intake, be melted into by nylon material liquid by high temperature, be sufficiently stirred for by mixing plant, make alloy material uniformly lump together with nylon material；
(4) extrusion: after having stirred, go out nylon alloy bristle by the extrusion extrusion molding of mixing plant；
(5) assemble: nylon alloy bristle is fixed on brush holder, prepare high-efficiency cleaning brushware.
The invention have the benefit that the present invention provides high efficiency brushes smart structural design, rationally, nylon alloy bristle material based on nylon, it is made by increasing different alloy materials, effectively promote the toughness of bristle, hardness, elasticity and service life, and then liter cleaning effect, and do not easily cause article external surface damage, additionally overall structure is simple, it is easily achieved, beneficially wide popularization and application；The processing technology of the method that the present invention provides is succinct, and operation is simple, it is easy to accomplish, can quickly produce high efficiency brushes.
Below in conjunction with the accompanying drawings with embodiment, the invention will be further described.
Accompanying drawing explanation
Fig. 1 is the perspective view of the present invention.
Fig. 2 is the main TV structure schematic diagram of the present invention.
Fig. 3 is the right TV structure schematic diagram of the present invention.
Detailed description of the invention
Embodiment 1: see Fig. 1 to Fig. 3, a kind of high efficiency brushes that the present embodiment provides, it includes brush holder 1 and is arranged on the nylon alloy bristle 2 on this brush holder 1, this nylon alloy bristle 2 uses following material to make: nylon material 65%, alloy material 35%, wherein said alloy material is one or more mixing in aluminium oxide, carborundum, white fused alumina, diamond.
Seeing Fig. 1, described brush holder 1 includes brush holder 11 and is arranged on the brush 12 of this brush holder 11 one end, for being not take up table space, can be provided with hook 3 at the other end of this brush holder 11, bring convenience to use.
Preferably, see Fig. 3, the nylon alloy bristle 2 in the centre position being positioned at the bottom surface of described brush 12 is vertical setting, the nylon alloy bristle 2 of bottom surface two side position being positioned at this brush 12 is obliquely installed, the angle that this nylon alloy bristle 2 tilts is 60～75 degree, is preferably 75 degree as being positioned at the angle of inclination a of the nylon alloy bristle 2 of outermost locations, and the angle of inclination b being positioned at the nylon alloy bristle 2 of relatively position is preferably 60 degree, it is more conducive to cleaning, effectively promotes cleaning effect.
Seeing Fig. 2, the front end face at described brush 12 is provided with wing 13 and is provided with wing 13 at the anterior end face of this brush 12, uses demand meeting different cleanings.
It is also preferred that the left a diameter of the 0.1 of described nylon alloy bristle 2～2.5mm, in this size range, the intensity of nylon alloy bristle 2 and elasticity are preferable, be more conducive to cleaning and protection article external surface is not damaged.Described nylon alloy bristle 2 linearly type or ripple type, meet different use demands.
The present invention provides high efficiency brushes smart structural design, rationally, nylon alloy bristle material based on nylon, is made by increasing different alloy materials, effectively promotes the toughness of bristle, hardness, elasticity and service life, and then liter cleaning effect, and do not easily cause article external surface damage.
A kind of method making above-mentioned high efficiency brushes, it comprises the following steps:
(1) preparing material: each component of raw material and mass percent thereof are as follows: nylon material 65%, alloy material 35%, wherein said alloy material is one or more mixing in aluminium oxide, carborundum, white fused alumina, diamond；
(2) feed intake: first alloy material is ground to form fine particulate and puts into again in mixing apparatus, then nylon material is put in mixing apparatus；
(3) stirring is merged: after waiting to feed intake, be melted into by nylon material liquid by high temperature, be sufficiently stirred for by mixing plant, make alloy material uniformly lump together with nylon material；
(4) extrusion: after having stirred, go out nylon alloy bristle 2 by the extrusion extrusion molding of mixing plant；
(5) assemble: nylon alloy bristle 2 is fixed on brush holder 1, prepare high-efficiency cleaning brushware.
Embodiment 2: it is substantially the same manner as Example 1, difference is the raw material components of nylon alloy bristle.Its each component and mass percent thereof are as follows: nylon material 71%, alloy material 29%.
Embodiment 3: it is substantially the same manner as Example 1, difference is the raw material components of nylon alloy bristle.Its each component and mass percent thereof are as follows: nylon material 85%, alloy material 15%.
Embodiment 4: it is substantially the same manner as Example 1, difference is the raw material components of nylon alloy bristle.Its each component and mass percent thereof are as follows: nylon material 81%, alloy material 19%.
Embodiment 5: it is substantially the same manner as Example 1, difference is the raw material components of nylon alloy bristle.Its each component and mass percent thereof are as follows: nylon material 68%, alloy material 32%.
The processing technology of the method that the present invention provides is succinct, and operation is simple, it is easy to accomplish, can quickly produce high efficiency brushes.
Above-described embodiment is only the preferable embodiment of the present invention, and the present invention can not enumerate out whole embodiments, the technical scheme of one of all employing above-described embodiments, or the equivalent variations done according to above-described embodiment, all in scope.
The announcement of book and teaching according to the above description, above-mentioned embodiment can also be changed and revise by those skilled in the art in the invention.Therefore, the invention is not limited in detailed description of the invention disclosed and described above, should also be as some modifications and changes of the present invention falling in the scope of the claims of the present invention.Although additionally, employ some specific terms in this specification, but these terms are merely for convenience of description, the present invention is not constituted any restriction.As described in the above embodiment the present invention, same or similarity method and component are used and other brush of obtaining and preparation method thereof, all in scope.
Claims (10)
1. a high efficiency brushes, it is characterised in that it includes brush holder and the nylon alloy bristle being arranged on this brush holder, this nylon alloy bristle uses following material to make:
Nylon material 65～85%,
Alloy material 15～35%,
Wherein said alloy material is one or more mixing in aluminium oxide, carborundum, white fused alumina, diamond.
High efficiency brushes the most according to claim 1, it is characterised in that described brush holder includes brush holder and is arranged on the brush of this brush holder one end, and the other end of this brush holder is provided with hook.
High efficiency brushes the most according to claim 2, it is characterized in that, the nylon alloy bristle in the centre position being positioned at the bottom surface of described brush is vertical setting, and the nylon alloy bristle of bottom surface two side position being positioned at this brush is obliquely installed, and the angle that this nylon alloy bristle tilts is 60～75 degree.
4. according to the high efficiency brushes described in Claims 2 or 3, it is characterised in that the front end face of described brush is provided with wing.
5. according to the high efficiency brushes described in Claims 2 or 3, it is characterised in that the anterior end face of described brush is provided with wing.
6. according to the high efficiency brushes described in claim 1 or 3, it is characterised in that a diameter of the 0.1～2.5mm of described nylon alloy bristle.
High efficiency brushes the most according to claim 6, it is characterised in that described nylon alloy bristle linearly type or ripple type.
8. the method making the described high efficiency brushes of one of claim 1-7, it is characterised in that it comprises the following steps:
(1) preparing material: each component of raw material and mass percent thereof are as follows:
Nylon material 65～85%,
Alloy material 15～35%,
Wherein said alloy material is one or more mixing in aluminium oxide, carborundum, white fused alumina, diamond；
(2) feed intake: first alloy material is ground to form fine particulate and puts into again in mixing apparatus, then nylon material is put in mixing apparatus；
(3) stirring is merged: after waiting to feed intake, be melted into by nylon material liquid by high temperature, be sufficiently stirred for by mixing plant, make alloy material uniformly lump together with nylon material；
(4) extrusion: after having stirred, go out nylon alloy bristle by the extrusion extrusion molding of mixing plant；
(5) assemble: nylon alloy bristle is fixed on brush holder, prepare high-efficiency cleaning brushware.
Method the most according to claim 8, it is characterised in that a diameter of the 0.1～2.5mm of described nylon alloy bristle.
Method the most according to claim 8, it is characterised in that described nylon alloy bristle linearly type or ripple type.