CN105803309B - Ball grinding machine lining board - Google Patents
Ball grinding machine lining board Download PDFInfo
- Publication number
- CN105803309B CN105803309B CN201610170639.3A CN201610170639A CN105803309B CN 105803309 B CN105803309 B CN 105803309B CN 201610170639 A CN201610170639 A CN 201610170639A CN 105803309 B CN105803309 B CN 105803309B
- Authority
- CN
- China
- Prior art keywords
- grinding machine
- ball grinding
- lining board
- machine lining
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of ball grinding machine lining board, include the chemical composition of following percentage by weight:C0.45~0.55%, Si0.8~1.2%, Mn0.8~1.2%, Cr1.7~2.0%, Ni0.30~0.50%, Mo0.20~0.50%, RE0.03~0.06%, Al0.02~0.05%, P≤0.025%, S≤0.025%, remaining is Fe.Present invention also offers the preparation method of ball grinding machine lining board.Alloying element and rare earth element proportion optimizing are added in molten steel by the present invention, and carry out LF stove refinings, improve Molten Steel Cleanliness, refined crystalline strengthening effect is played to liner plate, obtained tempered martensite is while wearability is improved, liner plate service life length, also improve impact flexibility and intensity, reduce the frequency that factory changes liner plate, reduce labor intensity, raw material of the present invention is easy to get, preparation method is simple, using ordinary scrap steel etc. as raw materials for production, recycle, be effectively saved the energy.
Description
Technical field
The present invention relates to plant equipment Material Field, specifically a kind of lining sheet for ball mill.
Background technology
Ball mill is the key equipment for crushing mineral aggregate, and it is widely used among industrial and mining enterprises.Ball mill is mainly logical
Between overground Jie and its with cylinder contact zone caused by extruding and mill stripping power material is ground, therefore ball grinding machine lining board is rushed
Hit, wear larger, ball grinding machine lining board occurs obvious fracture, worn out phenomenon, it is necessary to constantly be changed in use.One
As time used about 6-8 months or so of ball grinding machine lining board, it is expired then need progress lining plate replacing, with 5.03 × 8.5 meters
Exemplified by overflow type large-size ball mill, for liner plate weight at 83.5 tons or so, changing a liner plate needs substantial amounts of manpower and materials.Cause
This, extends the cycle for changing liner plate, reduces the consuming cost of liner plate, and then the service life for improving liner plate is one and important ground
Study carefully problem.
The content of the invention
The purpose of the present invention is to solve the deficiency of above-mentioned technical problem, there is provided a kind of high intensity, high tenacity, high abrasion
Ball grinding machine lining board and preparation method thereof.
The present invention is that technical scheme is used by solving above-mentioned technical problem:Ball grinding machine lining board includes following weight percent
The chemical composition of ratio:C0.45~0.55%, Si0.8~1.2%, Mn0.8~1.2%, Cr1.7~2.0%, Ni0.30~
0.50%, Mo0.20~0.50%, RE0.03~0.06%, Al0.02~0.05%, P≤0.025%, S≤0.025%, its
Remaining is Fe.
The preparation method of ball grinding machine lining board of the present invention comprises the steps of:
Step 1: dispensing:It is raw material according to the ball mill using steel scrap, ferrosilicon, ferromanganese, ferrochrome, ferronickel, molybdenum-iron, alloy
The proportioning of liner plate carries out dispensing;
Step 2: melting:By the raw material prepared in step 1 insert electric arc furnaces carry out melting, smelting temperature be 1600~
1640℃ ;
Step 3: allotment:Row element check analysis is entered to the molten steel in step 2, member is carried out to molten steel according to assay
The secondary proportioning of element;
Step 4: refining:Examine qualified molten steel to be placed in LF refining furnace element in step 3 to be refined, when molten steel temperature
Degree reach 1580~1600 DEG C, chemical composition reached target proportioning when, start buggy ladle to LF refining furnace feed silk station fortune
OK, carry out feeding silk, soft blow, thermometric sampling, input coverture operation;
Step 5: cast:Molten steel in qualified step four is come out of the stove, carries out rare earth Dy ions with stream when coming out of the stove, so
After pour into casting ladle and poured into a mould, pouring temperature is 1520~1540 DEG C;
Step 6: finishing:Die sinking obtains ball grinding machine lining board blank after being cooled to room temperature, and finishing processing is carried out to it;
Step 7: annealing:Ball grinding machine lining board after step 6 is handled is placed in annealing furnace and heated, temperature liter
To 840~860 DEG C, 4~6 hours are incubated, cools to room temperature with the furnace;
Step 8: Quenching Treatment:Ball grinding machine lining board after step 7 is handled is placed in glowing furnace and heated, temperature liter
To 860~920 DEG C, 3~4 hours are incubated, water quenching or oil quenching are cooled to room temperature;
Step 9: temper:Ball grinding machine lining board after step 8 is handled is placed in tempering furnace and heated, is being tempered
240~260 DEG C of tempering insulations 4~6 hours in stove, coming out of the stove is air-cooled to room temperature and obtains liner plate finished product.
Preferably, annealing is incubated 4 hours for 860 DEG C in step 7, furnace cooling.
Preferably, Quenching Treatment can be incubated 3~4 hours for 860 DEG C in step 8, water quenching cooling to room temperature.
Preferably, Quenching Treatment can also be incubated 3~4 hours for 880 DEG C in step 8, and oil quenching is cooled to room temperature.
Preferably, Quenching Treatment can also be incubated 4 hours for 920 DEG C in step 8, and oil quenching is cooled to room temperature.
Preferably, the holding temperature of temper is 250 DEG C in step 9.
The beneficial effects of the invention are as follows:Alloying element and rare earth element proportion optimizing are added in molten steel by the present invention, and
LF stove refinings are carried out, improve Molten Steel Cleanliness, refined crystalline strengthening effect is played to liner plate, obtained tempered martensite is carrying
While high-wearing feature, impact flexibility and intensity are also improved, extends the service life of liner plate, reduces enterprise and changes liner plate
Frequency, reduce labor intensity;Reach liner plate gross thickness without fracture, worn out phenomenon, thinnest part after the liner plate use of the present invention
1/3, thin and thick is more uniform after military service, and liner plate active time is more than 1 year, and anti-wear performance is good, and using effect is preferable;This hair
Bright preparation method is simple, using ordinary scrap steel etc. as raw material, recycles, is effectively saved the energy, molten steel is gone bad
Processing, alterant is set to form largely scattered made non-spontaneous nucleation in molten metal, so as to obtain tiny casting
Crystal grain, improve tissue, increase the toughness and intensity of liner plate, improve service life.
Embodiment
Embodiment 1
Ball grinding machine lining board, include the chemical composition of following percentage by weight:C0.54%, Si0.82%, Mn0.93%,
Cr1.89%, Ni0.48%, Mo0.46%, RE0.032%, Al0.03%, P0.023%, S0.021%, remaining is Fe.
The preparation method of ball grinding machine lining board of the present invention comprises the steps of:
Step 1: dispensing:It is raw material according to the ball mill using steel scrap, ferrosilicon, ferromanganese, ferrochrome, ferronickel, molybdenum-iron, alloy
The proportioning of liner plate carries out dispensing;
Step 2: melting:The raw material prepared in step 1 is inserted into electric arc furnaces and carries out melting, smelting temperature is 1630 DEG C;
Step 3: allotment:Row element check analysis is entered to the molten steel in step 2, member is carried out to molten steel according to assay
The secondary proportioning of element;
Step 4: refining:Examine qualified molten steel to be placed in LF refining furnace element in step 3 to be refined, as needed
Add a small amount of alloy and be particularly oxidizable alloy and be finely adjusted, when liquid steel temperature and chemical composition have reached desired value, open
Dynamic buggy ladle feeds the operation of silk station to LF refining furnace, carries out feeding silk, soft blow, thermometric sampling, input coverture operation, addition is few
Amount alloy, which is adjusted, can accurately control liquid steel temperature and component content, it is easy to accomplish narrower composition range, improve product
Stability;
Step 5: cast:Molten steel in qualified step four is come out of the stove, carries out rare earth Dy ions with stream when coming out of the stove, so
After pour into casting ladle and poured into a mould, pouring temperature is 1540 DEG C;
Step 6: finishing:Die sinking obtains ball grinding machine lining board blank after being cooled to room temperature, and finishing processing is carried out to it;
Step 7: annealing:Ball grinding machine lining board after step 6 is handled is placed in annealing furnace and annealed, temperature liter
To 840 DEG C, 6 hours are incubated, cools to room temperature with the furnace;
Step 8: Quenching Treatment:Ball grinding machine lining board after step 7 is handled is placed in glowing furnace and quenched, temperature liter
To 860 DEG C, 3.5 hours are incubated, water quenching cooling to room temperature;
Step 9: temper:Ball grinding machine lining board after step 8 is handled is placed in tempering furnace and is tempered, is being tempered
260 DEG C of tempering insulations 4 hours in stove, coming out of the stove is air-cooled to room temperature and obtains liner plate finished product.
Liner plate made from the present embodiment has good toughness plasticity.
Embodiment 2
Ball grinding machine lining board, include the chemical composition of following percentage by weight:C0.50%, Si0.97%, Mn1.12%,
Cr1.81%, Ni0.39%, Mo0.35%, RE0.046%, Al0.034%, P0.024%, S0.021%, remaining is Fe.
The preparation method of ball grinding machine lining board of the present invention comprises the steps of:
Step 1: dispensing:It is raw material according to the ball mill using steel scrap, ferrosilicon, ferromanganese, ferrochrome, ferronickel, molybdenum-iron, alloy
The proportioning of liner plate carries out dispensing;
Step 2: melting:The raw material prepared in step 1 is inserted into electric arc furnaces and carries out melting, smelting temperature is 1640 DEG C;
Step 3: allotment:Row element check analysis is entered to the molten steel in step 2, member is carried out to molten steel according to assay
The secondary proportioning of element;
Step 4: refining:Examine qualified molten steel to be placed in LF refining furnace element in step 3 to be refined, as needed
Add a small amount of alloy and be particularly oxidizable alloy and be finely adjusted, when liquid steel temperature and chemical composition have reached desired value, open
Dynamic buggy ladle feeds the operation of silk station to LF refining furnace, carries out feeding silk, soft blow, thermometric sampling, input coverture operation, addition is few
Amount alloy, which is adjusted, can accurately control liquid steel temperature and component content, it is easy to accomplish narrower composition range, improve product
Stability;
Step 5: cast:Molten steel in qualified step four is come out of the stove, carries out rare earth Dy ions with stream when coming out of the stove, so
After pour into casting ladle and poured into a mould, pouring temperature is 1530 DEG C;
Step 6: finishing:Die sinking obtains ball grinding machine lining board blank after being cooled to room temperature, and finishing processing is carried out to it;
Step 7: annealing:Ball grinding machine lining board after step 6 is handled is placed in annealing furnace and annealed, temperature liter
To 850 DEG C, 5 hours are incubated, cools to room temperature with the furnace;
Step 8: Quenching Treatment:Ball grinding machine lining board after step 7 is handled is placed in glowing furnace and quenched, temperature liter
To 880 DEG C, 3.5 hours are incubated, oil quenching is cooled to room temperature;
Step 9: temper:Ball grinding machine lining board after step 8 is handled is placed in tempering furnace and is tempered, is being tempered
240 DEG C of tempering insulations 6 hours in stove, coming out of the stove is air-cooled to room temperature and obtains liner plate finished product.
Liner plate made from the present embodiment has good comprehensive mechanical property.
Embodiment 3
Ball grinding machine lining board, include the chemical composition of following percentage by weight:C0.46%, Si0.82%, Mn1.15%,
Cr1.95%, Ni0.45%, Mo0.32%, RE0.037%, Al0.036%, P0.02%, S0.021%, remaining is Fe.
The preparation method of ball grinding machine lining board of the present invention comprises the steps of:
Step 1: dispensing:It is raw material according to the ball mill using steel scrap, ferrosilicon, ferromanganese, ferrochrome, ferronickel, molybdenum-iron, alloy
The proportioning of liner plate carries out dispensing;
Step 2: melting:The raw material prepared in step 1 is inserted into electric arc furnaces and carries out melting, smelting temperature is 1620 DEG C;
Step 3: allotment:Row element check analysis is entered to the molten steel in step 2, member is carried out to molten steel according to assay
The secondary proportioning of element;
Step 4: refining:Examine qualified molten steel to be placed in LF refining furnace element in step 3 to be refined, as needed
Add a small amount of alloy and be particularly oxidizable alloy and be finely adjusted, when liquid steel temperature and chemical composition have reached desired value, open
Dynamic buggy ladle feeds the operation of silk station to LF refining furnace, carries out feeding silk, soft blow, thermometric sampling, input coverture operation, addition is few
Amount alloy, which is adjusted, can accurately control liquid steel temperature and component content, it is easy to accomplish narrower composition range, improve product
Stability;
Step 5: cast:Molten steel in qualified step four is come out of the stove, carries out rare earth Dy ions with stream when coming out of the stove, so
After pour into casting ladle and poured into a mould, pouring temperature is 1540 DEG C;
Step 6: finishing:Die sinking obtains ball grinding machine lining board blank after being cooled to room temperature, and finishing processing is carried out to it;
Step 7: annealing:Ball grinding machine lining board after step 6 is handled is placed in annealing furnace and annealed, temperature liter
To 860 DEG C, 4 hours are incubated, cools to room temperature with the furnace;
Step 8: Quenching Treatment:Ball grinding machine lining board after step 7 is handled is placed in glowing furnace and quenched, temperature liter
To 920 DEG C, 4 hours are incubated, oil quenching is cooled to room temperature;
Step 9: temper:Ball grinding machine lining board after step 8 is handled is placed in tempering furnace and is tempered, is being tempered
250 DEG C of tempering insulations 4 hours in stove, coming out of the stove is air-cooled to room temperature and obtains liner plate finished product.
Liner plate made from the present embodiment has higher intensity and hardness.
Alloying element and rare earth element proportion optimizing are added in molten steel by the present invention, and carry out LF stove refinings, are improved
Molten Steel Cleanliness, refined crystalline strengthening effect is played to liner plate, and obtained tempered martensite also carries while wearability is improved
High impact flexibility and intensity, extend the service life of liner plate, reduce the frequency that enterprise changes liner plate, it is strong to reduce work
Degree.
It is right if making dry sample according to the preparation method of the present invention in order to further illustrate the performance of the liner plate of the present invention
Sample carries out mechanical property and quenching degree detection.Such as following table:
Table 1
Table 1
Table 2
Table 3
Test block sample | + 250 DEG C of tempering of 860 DEG C of water quenchings | + 250 DEG C of tempering of 840 DEG C of water quenchings |
Tensile strength MPa | > 1707 | > 1592 |
Impact flexibility(J/cm2) | 37 | 43 |
It is 56-58HRC that the hardenability test result of sample, which can be seen that specimen surface hardness, from table 1, and centre hardness is
54-56HRC, material quenching degree of the present invention are excellent.From Table 2, it can be seen that the table of 860 DEG C of oil quenching experiments of liner plate sample of the present invention
Surface hardness 55-58HRC, the case hardness 52-55.5HRC of 830 DEG C of water quenching experiments, illustrates to obtain using the Quenching Treatment of the present invention
Liner plate sample hardenability it is preferable, and rear lining plate flawless of quenching.As can be seen from Table 3, the tensile strength of material of the present invention
More than 1707Mpa can be reached, and have preferable impact flexibility.
It is quenching degree experiment below:Quenching degree is determined with the end quenching hardenability test of standard.Experimental sample is through 860 DEG C
Annealing, 840 DEG C of austenitizings carry out end quenching experiment, and end water quenching curve is shown in Fig. 2-1.Experiment quenching degree uses φ
50 × 100mm, 100 × 150mm of φ, 150 × 150mm of φ, tri- kinds of turriform samples, sample are poured into a mould in 5 tons of electric arc furnace smeltings,
Sample is heat-treated with castings production, and dissection sample hardness is shown in Fig. 2-2.As seen from the figure, inside and outside the hardness of sample uniformly,
Quenching degree > 150mm.
Fig. 2-1 ends water quenching curve map 2-2 turriforms dissect sample hardness
Described above is only the preferred embodiment of the present invention, for those skilled in the art,
On the premise of not departing from the technology of the present invention principle, some changes or replacement can also be made, these also should be regarded as the guarantor of the present invention
Protect scope.
Claims (6)
1. ball grinding machine lining board, it is characterised in that:Include the chemical composition of following percentage by weight:C0.5~0.54%, Si0.82
~0.97%, Mn0.8~1.2%, Cr1.7~2.0%, Ni0.30~0.50%, Mo0.39~0.50%, RE0.03~
0.06%, Al0.02~0.05%, P≤0.025%, S≤0.025%, remaining is Fe;
The preparation method of described ball grinding machine lining board, is comprised the steps of:
Step 1: dispensing:It is raw material according to the ball grinding machine lining board using steel scrap, ferrosilicon, ferromanganese, ferrochrome, ferronickel, molybdenum-iron, alloy
Proportioning carry out dispensing;
Step 2: melting:The raw material prepared in step 1 is inserted into electric arc furnaces and carries out melting, smelting temperature is 1600~1640 DEG C
;
Step 3: allotment:Row element check analysis is entered to the molten steel in step 2, row element is entered to molten steel according to assay
Secondary proportioning;
Step 4: refining:Examine qualified molten steel to be placed in LF refining furnace element in step 3 to be refined, when liquid steel temperature reaches
When having reached target proportioning to 1580~1600 DEG C, chemical composition, start buggy ladle and feed the operation of silk station to LF refining furnace, enter
Row feeds silk, soft blow, thermometric sampling, input coverture operation;
Step 5: cast:Molten steel in qualified step four is come out of the stove, rare earth Dy ions is carried out with stream when coming out of the stove, then falls
Enter casting ladle to be poured into a mould, pouring temperature is 1520~1540 DEG C;
Step 6: finishing:Die sinking obtains ball grinding machine lining board blank after being cooled to room temperature, and finishing processing is carried out to it;
Step 7: annealing:Ball grinding machine lining board after step 6 is handled is placed in annealing furnace and heated, temperature rises to
840~860 DEG C, 4~6 hours are incubated, cools to room temperature with the furnace;
Step 8: Quenching Treatment:Ball grinding machine lining board after step 7 is handled is placed in glowing furnace and heated, temperature rises to
860~920 DEG C, 3~4 hours are incubated, water quenching or oil quenching are cooled to room temperature;
Step 9: temper:Ball grinding machine lining board after step 8 is handled is placed in tempering furnace and heated, in tempering furnace
240~260 DEG C of tempering insulations 4~6 hours, coming out of the stove is air-cooled to room temperature and obtains liner plate finished product.
2. ball grinding machine lining board as claimed in claim 1, it is characterised in that:Annealing is small for 860 DEG C of insulations 4 in step 7
When, furnace cooling.
3. ball grinding machine lining board as claimed in claim 1, it is characterised in that:Quenching Treatment can be 860 DEG C of insulations 3 in step 8
~4 hours, water quenching cooling to room temperature.
4. ball grinding machine lining board as claimed in claim 1, it is characterised in that:Quenching Treatment can also be 880 DEG C of guarantors in step 8
Temperature 3~4 hours, oil quenching is cooled to room temperature.
5. ball grinding machine lining board as claimed in claim 1, it is characterised in that:Quenching Treatment can also be 920 DEG C of guarantors in step 8
Temperature 4 hours, oil quenching is cooled to room temperature.
6. ball grinding machine lining board as claimed in claim 1, it is characterised in that:The holding temperature of temper is 250 in step 9
℃。