CN105802066A - High-hardness plastic pipe fitting composition - Google Patents
High-hardness plastic pipe fitting composition Download PDFInfo
- Publication number
- CN105802066A CN105802066A CN201610213703.1A CN201610213703A CN105802066A CN 105802066 A CN105802066 A CN 105802066A CN 201610213703 A CN201610213703 A CN 201610213703A CN 105802066 A CN105802066 A CN 105802066A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic pipe
- hardness
- big
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-hardness plastic pipe fitting composition. The high-hardness plastic pipe fitting composition is prepared from components in parts by weight as follows: 100 parts of polyvinyl chloride powder, 12-16 parts of activated calcium carbonate, 6-9 parts of a calcium-zinc composite stabilizer, 30-40 parts of chlorinated polyethylene, 1-4 parts of titanium dioxide and 3-8 parts of tribasic lead. Accordingly, the high-hardness plastic pipe fitting composition can have deformation resistance and damage resistance under external force and can be used for a long time; blocking, leaking and other conditions cannot occur; selected raw materials are low in price, have wide sources and are easy to obtain.
Description
Technical field
The present invention relates to modified plastics plastic cement field, particularly relate to the plastic pipe compositions that a kind of hardness is big.
Background technology
Plastic pipe is usually with synthetic resin, and namely polyester is raw material, adds stabilizer, lubricant, plasticizer etc., forms through extrusion process in tuber with the method moulded.Plastic pipe have light weight, corrosion-resistant, appearance looks elegant, without bad smell, be easily worked, the feature such as easy construction, obtain in architectural engineering and be increasingly widely applied.Because plastic pipe has very many application in architectural engineering, it is therefore desirable to plastic pipe has extraordinary hardness, but the hardness of some plastic pipe is not met by requirement.
Summary of the invention
The technical problem that present invention mainly solves is to provide the plastic pipe compositions that a kind of hardness is big, uses and deformation is less likely to occur.
For solving above-mentioned technical problem, the technical scheme that the present invention uses is: provide the plastic pipe compositions that a kind of hardness is big, including component have polyvinyl chloride powder, activated Calcium carbonate, calcium-zinc composite stabilizing agent, chlorinated polyethylene, titanium dioxide and three salt lead, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 12-16 part, calcium-zinc composite stabilizing agent 6-9 part, chlorinated polyethylene 30-40 part, titanium dioxide 1-4 part, three salt lead 3-8 parts.
In a preferred embodiment of the present invention, the particle diameter of described polyvinyl chloride powder is 0.1-0.3 μm.
In a preferred embodiment of the present invention, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 14 parts, calcium-zinc composite stabilizing agent 7 parts, chlorinated polyethylene 35 parts, titanium dioxide 3 parts, 6 parts of three salt lead.
In a preferred embodiment of the present invention, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 12 parts, calcium-zinc composite stabilizing agent 9 parts, chlorinated polyethylene 30 parts, titanium dioxide 4 parts, 8 parts of three salt lead.
The invention has the beneficial effects as follows: the plastic pipe compositions that the hardness of the present invention is big, it is possible to external force is had the ability of resistance to deformation or damage, can use for a long time, do not have the generation of the situations such as blocking, leakage, the cost of material chosen is cheap, and wide material sources are readily obtained.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment one:
The plastic pipe compositions that a kind of hardness is big is provided, including component have polyvinyl chloride powder, activated Calcium carbonate, calcium-zinc composite stabilizing agent, chlorinated polyethylene, titanium dioxide and three salt lead, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 14 parts, calcium-zinc composite stabilizing agent 7 parts, chlorinated polyethylene 35 parts, titanium dioxide 3 parts, 6 parts of three salt lead.The particle diameter of described polyvinyl chloride powder is 0.2 μm.
Embodiment two:
The plastic pipe compositions that a kind of hardness is big is provided, including component have polyvinyl chloride powder, activated Calcium carbonate, calcium-zinc composite stabilizing agent, chlorinated polyethylene, titanium dioxide and three salt lead, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 12 parts, calcium-zinc composite stabilizing agent 9 parts, chlorinated polyethylene 30 parts, titanium dioxide 4 parts, 8 parts of three salt lead.The particle diameter of described polyvinyl chloride powder is 0.1 μm.
Embodiment three:
The plastic pipe compositions that a kind of hardness is big is provided, including component have polyvinyl chloride powder, activated Calcium carbonate, calcium-zinc composite stabilizing agent, chlorinated polyethylene, titanium dioxide and three salt lead, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 16 parts, calcium-zinc composite stabilizing agent 6 parts, chlorinated polyethylene 40 parts, titanium dioxide 1 part, 3 parts of three salt lead.The particle diameter of described polyvinyl chloride powder is 0.3 μm.
The invention has the beneficial effects as follows:
One, the plastic pipe compositions that described hardness is big can have the ability of resistance to deformation or damage to external force, can use for a long time, not have the generation of the situations such as blocking, leakage；
Two, the cost of material that the plastic pipe compositions that described hardness is big is chosen is cheap, and wide material sources are readily obtained.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, the most in like manner it is included in the scope of patent protection of the present invention.
Claims (4)
1. the plastic pipe compositions that a hardness is big, it is characterized in that, including component have polyvinyl chloride powder, activated Calcium carbonate, calcium-zinc composite stabilizing agent, chlorinated polyethylene, titanium dioxide and three salt lead, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 12-16 part, calcium-zinc composite stabilizing agent 6-9 part, chlorinated polyethylene 30-40 part, titanium dioxide 1-4 part, three salt lead 3-8 parts.
The plastic pipe compositions that hardness the most according to claim 1 is big, it is characterised in that the particle diameter of described polyvinyl chloride powder is 0.1-0.3 μm.
The plastic pipe compositions that hardness the most according to claim 1 is big, it is characterized in that, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 14 parts, calcium-zinc composite stabilizing agent 7 parts, chlorinated polyethylene 35 parts, titanium dioxide 3 parts, 6 parts of three salt lead.
The plastic pipe compositions that hardness the most according to claim 1 is big, it is characterized in that, the big plastic pipe compositions of described hardness in parts by weight, including component have: polyvinyl chloride powder 100 parts, activated Calcium carbonate 12 parts, calcium-zinc composite stabilizing agent 9 parts, chlorinated polyethylene 30 parts, titanium dioxide 4 parts, 8 parts of three salt lead.