CN105780191A - WO3/TiO2/SiO2 composite fiber - Google Patents

WO3/TiO2/SiO2 composite fiber Download PDF

Info

Publication number
CN105780191A
CN105780191A CN201610328438.1A CN201610328438A CN105780191A CN 105780191 A CN105780191 A CN 105780191A CN 201610328438 A CN201610328438 A CN 201610328438A CN 105780191 A CN105780191 A CN 105780191A
Authority
CN
China
Prior art keywords
fiber
weight portion
composite fibre
tio
sio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610328438.1A
Other languages
Chinese (zh)
Inventor
何咸稳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIAN COUNTY BROTHERS SYNTHETIC FIBER CO Ltd
Original Assignee
HAIAN COUNTY BROTHERS SYNTHETIC FIBER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIAN COUNTY BROTHERS SYNTHETIC FIBER CO Ltd filed Critical HAIAN COUNTY BROTHERS SYNTHETIC FIBER CO Ltd
Priority to CN201610328438.1A priority Critical patent/CN105780191A/en
Publication of CN105780191A publication Critical patent/CN105780191A/en
Pending legal-status Critical Current

Abstract

The invention provides WO3/TiO2/SiO2 composite fiber. The composite fiber is prepared by an electrostatic spinning technology. The composite fiber comprises the following fibers in parts by weight: 20-30 parts of WO3 fiber, 20-30 parts of TiO2 fiber and 20-30 parts of SiO2 fiber. The composite fiber is composited by the fibers with different performances or structures, and different forms and effects can be generated by utilizing different performances of all the components.

Description

A kind of WO3/TiO2/SiO2Composite fibre
Technical field
The present invention relates to a kind of WO3/TiO2/SiO2Composite fibre, belongs to chemical fiber field.
Background technology
Along with raising and the enhancing of environmental consciousness of people's living standard, consumption market occurs in that high sensibility, Gao Gong The demand of textile can be changed.In order to solve these demands, it is necessary to traditional fiber manufacture is changed, develop high function fine Dimension, high sensibility fiber, intelligent fiber and biodegradable fiber etc., the life matter of scientific and technological content and people to improve textile Amount.The exploitation of composite fibre is then to realize that fiber height is sensibility, an important means of multifunction.It can pass through spinneret Shape design, the various ways such as Cross section Design joining choosing design and spinning fibre of polymer, it is thus achieved that various performances, style new Type textile material.
Composite fibre refers to the high polymer by two or more or the polymer of different performance of the same race, with certain side The fiber that formula is axially composited along fiber.This fibrid can integrate the advantage of various ingredients, as washed/chinlon composite fiber, It had both had chinlon wearability dye good, high-strength, easy, the advantage of moisture absorption, had again terylene good springiness, modulus is high, fabric is well-pressed Feature.
Summary of the invention
In place of it is an object of the invention to overcome the deficiencies in the prior art, it is provided that a kind of WO3/TiO2/SiO2Composite fibre.
The WO of the present invention3/TiO2/SiO2Composite fibre, is prepared from by electrostatic spinning technique, described composite fibre Following fiber: WO is included according to parts by weight3Fiber 20-30 weight portion, TiO2Fiber 20-30 weight portion, SiO2 fiber 20-30 Weight portion.
Preferably,
Described composite fibre includes following fiber: WO according to parts by weight3Fiber 25 weight portion, TiO2Fiber 25 weight portion, SiO2Fiber 25 weight portion.
The composite fibre of the present invention is by the fiber composite of different performance or structure, the property that available each component is different Matter and produce different forms and effect.
Detailed description of the invention
Embodiment 1
The WO of the present embodiment3/TiO2/SiO2Composite fibre, is prepared from by electrostatic spinning technique, and described composite fibre is pressed Following fiber: WO is included according to parts by weight3Fiber 20 weight portion, TiO2Fiber 30 weight portion, SiO2Fiber 30 weight portion.
Embodiment 2
The WO of the present embodiment3/TiO2/SiO2Composite fibre, is prepared from by electrostatic spinning technique, and described composite fibre is pressed Following fiber: WO is included according to parts by weight3Fiber 30 weight portion, TiO2Fiber 20 weight portion, SiO2Fiber 20 weight portion.
Embodiment 3
The WO of the present embodiment3/TiO2/SiO2Composite fibre, is prepared from by electrostatic spinning technique, and described composite fibre is pressed Following fiber: WO is included according to parts by weight3Fiber 25 weight portion, TiO2Fiber 25 weight portion, SiO2Fiber 25 weight portion.

Claims (2)

1. a WO3/TiO2/SiO2Composite fibre, it is characterised in that described composite fibre is prepared by electrostatic spinning technique Forming, described composite fibre includes following fiber: WO according to parts by weight3Fiber 20-30 weight portion, TiO2Fiber 20-30 weight Amount part, SiO2Fiber 20-30 weight portion.
WO the most according to claim 13/TiO2/SiO2Composite fibre, it is characterised in that described composite fibre is according to weight Amount number includes following fiber: WO3Fiber 25 weight portion, TiO2Fiber 25 weight portion, SiO2Fiber 25 weight portion.
CN201610328438.1A 2016-05-18 2016-05-18 WO3/TiO2/SiO2 composite fiber Pending CN105780191A (en)