CN105734972A - Efficient antibacterial self-cleaning finishing agent - Google Patents
Efficient antibacterial self-cleaning finishing agent Download PDFInfo
- Publication number
- CN105734972A CN105734972A CN201610097970.7A CN201610097970A CN105734972A CN 105734972 A CN105734972 A CN 105734972A CN 201610097970 A CN201610097970 A CN 201610097970A CN 105734972 A CN105734972 A CN 105734972A
- Authority
- CN
- China
- Prior art keywords
- base fabric
- finishing agent
- working solution
- self
- cleaning finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to an efficient antibacterial self-cleaning finishing agent. The efficient antibacterial self-cleaning finishing agent comprises a finishing working solution A and a finishing working solution B. The working solution A is prepared from, by weight, polyacrylate, polyvinyl alcohol, ethyl silicate, polybutylene terephthalate, epoxy flax seed oil, polyethylene wax powder, distearoyl isopropoxy aluminate, bauxite powder and soybean oil. The efficient antibacterial self-cleaning finishing agent overcomes the defects of the prior art, is high in adaptability and capable of saving energy and protecting the environment, and can be used for self-cleaning finishing of shirt collars.
Description
Technical field
The invention belongs to clean fabric finishing field, particularly relate to a kind of high-efficiency antimicrobial self-cleaning finishing agent.
Background technology
As weaving big country, textile industry occupies critical role in Chinese national economy, along with the rising of the fast development of textile industry and people's living standard, the requirement of textile is no longer confined to single comfortable function, but tends to direction multi-level, multi-functional and develop.There is substantial amounts of fibre gap and micropore in garment material, received substantial amounts of people's body surface secretions simultaneously, become microorganism attachment, breeding and the good place propagated, not only growing of microorganism causes that degradation situation under mildew, abnormal flavour, fibre strength occurs in web surface, also result in human body and pruritus, anaphylaxis or other dermatosis occur, people's life is brought inconvenience, and even harm people are healthy.Current automatically cleaning clothing especially hospital's Sanitary criteria demand is big, and is gradually increased in the clothing market share.Although after self-cleaning finishing, fabric has the performances such as antibacterial, mildew-resistant, deodorant, but its endurance issues is serious;It addition, need before textile finishing fabric fibre carries out acutely chemistry pre-treatment, strengthen the adhesion of finishing agent and fabric fibre, cause increasing environmental pollution, and the suitability of fabric types is not high.
Summary of the invention
The technical problem to be solved is to overcome deficiency of the prior art to provide a kind of suitability strong, the high-efficiency antimicrobial self-cleaning finishing agent of energy-conserving and environment-protective, and utilizes it to carry out vest neckline self-cleaning finishing.
To achieve these goals, the present invention adopts the following technical scheme that a kind of high-efficiency antimicrobial self-cleaning finishing agent, including housekeeping liquid A and B,
Described working solution A is with parts by weight, composed of the following components:
Polyacrylate 40-60
Polyvinyl alcohol 33-36
Silester 3-5
Polybutylene terephthalate (PBT) 20-24
Epoxidized linseed oil 3-5
Polyethylene wax powder 12-15
Isopropyl distearyl acyloxy Aluminate 2-3
Bauxite powder 40-45
Soybean oil 3-5;
Described working solution B is with parts by weight, composed of the following components:
Fluorocarbon polymer 20-30
Modified cyanurotriamide resin 15-18
Polyox-yethylene-polyoxypropylene block copolymer 12-16
Sodium chlorite 3-7
Polyacrylamide 2-8
Fatty alcohol sulfate single ethanol ammonium salt 0.5-3
Nano titanic oxide sol 14-28
Di-n-octyl sebacate 10-20
Methylaminopropyl trimethyl silane 2-5
Ethanol 30-50
Deionized water 80-100;
The using method of finishing agent is as follows:
(1) arranging base fabric, first pad working solution A, pressure is 2.5~3kg/cm2, liquid carrying rate is 60~70%, by base fabric constant temperature 0.5~2 hour between 115~120 DEG C after drying, then bakes 15-60s at 170 DEG C;
(2) base fabric is padded working solution B, pressure 6~8kg/cm again2, liquid carrying rate 80-90%, after drying, base fabric constant temperature between 100~105 DEG C is dried for 1 hour, then at 160 DEG C, bake about 45-50s.
Further, first arrangement base fabric being carried out pretreatment before carrying out self-cleaning finishing, described pretreatment fluid is grouped into by the one-tenth of following weight percents:
Beta-schardinger dextrin-5-20%
Polyvinyl alcohol 1-10%
Dispersant 1-5%
Water 65-93%.
Further, described base fabric is cellulose fibre base fabric, synthetic fibers base fabric, blending base fabric.
Beneficial effects of the present invention
The present invention high-efficiency antimicrobial self-cleaning finishing agent obtained for working solution A and B by special composition, in two steps fabric is arranged, particular polymeric objects system is introduced fabric face, and by specific baking, polymer brute force is bonded to fabric face, there is the advantages such as good endurance, high-efficiency antimicrobial, automatically cleaning.
The high-efficiency antimicrobial self-cleaning finishing agent suitability of the present invention is strong, can for any fabric fibre, and fabric fibre needs not move through violent chemical pre-treatment, it is to avoid environment is damaged.
It is little that the technology using the high-efficiency antimicrobial self-cleaning finishing agent process fabric obtained for working solution A and B of special composition has energy consumption, the advantages such as finishing agent is good in the tack of fabric face, durability is strong, the features such as it is superior that the fabric after process has permeability, and wrinkle resistance is good.
Detailed description of the invention
By the examples below, technical scheme is described in further detail.
Embodiment one:
A kind of high-efficiency antimicrobial self-cleaning finishing agent, including housekeeping liquid A and B,
Described working solution A is with parts by weight, composed of the following components:
Polyacrylate 40
Polyvinyl alcohol 33
Silester 3
Polybutylene terephthalate (PBT) 20
Epoxidized linseed oil 3
Polyethylene wax powder 12
Isopropyl distearyl acyloxy Aluminate 2
Bauxite powder 40
Soybean oil 3;
Described working solution B is with parts by weight, composed of the following components:
Fluorocarbon polymer 20
Modified cyanurotriamide resin 15
Polyox-yethylene-polyoxypropylene block copolymer 12
Sodium chlorite 3
Polyacrylamide 2
Fatty alcohol sulfate single ethanol ammonium salt 0.5
Nano titanic oxide sol 14
Di-n-octyl sebacate 10
Methylaminopropyl trimethyl silane 2
Ethanol 30
Deionized water 80;
The using method of finishing agent is as follows:
(1) arranging base fabric, base fabric is cellulose fibre base fabric, first pads working solution A, and pressure is 2.5kg/cm2, liquid carrying rate is 60%, by base fabric constant temperature 0.5 hour between 115 DEG C after drying, then bakes 15s at 170 DEG C;
(2) base fabric is padded working solution B, pressure 6kg/cm again2, liquid carrying rate 80%, after drying, base fabric constant temperature between 100 DEG C is dried for 1 hour, then at 160 DEG C, bake about 45s.
Further, first arrangement base fabric being carried out pretreatment before carrying out self-cleaning finishing, described pretreatment fluid is grouped into by the one-tenth of following weight percents:
Beta-schardinger dextrin-5%
Polyvinyl alcohol 1%
Dispersant 1%
Water 93%.
Embodiment two:
A kind of high-efficiency antimicrobial self-cleaning finishing agent, including housekeeping liquid A and B,
Described working solution A is with parts by weight, composed of the following components:
Polyacrylate 60
Polyvinyl alcohol 36
Silester 5
Polybutylene terephthalate (PBT) 24
Epoxidized linseed oil 5
Polyethylene wax powder 15
Isopropyl distearyl acyloxy Aluminate 3
Bauxite powder 45
Soybean oil 5;
Described working solution B is with parts by weight, composed of the following components:
Fluorocarbon polymer 30
Modified cyanurotriamide resin 18
Polyox-yethylene-polyoxypropylene block copolymer 16
Sodium chlorite 7
Polyacrylamide 8
Fatty alcohol sulfate single ethanol ammonium salt 3
Nano titanic oxide sol 28
Di-n-octyl sebacate 20
Methylaminopropyl trimethyl silane 5
Ethanol 50
Deionized water 100;
The using method of finishing agent is as follows:
(1) arranging base fabric, base fabric is cellulose fibre base fabric, synthetic fibers base fabric, blending base fabric, first pads working solution A, and pressure is 3kg/cm2, liquid carrying rate is 70%, by base fabric constant temperature 02 hour between 120 DEG C after drying, then bakes 60s at 170 DEG C;
(2) base fabric is padded working solution B, pressure 8kg/cm again2, liquid carrying rate 90%, after drying, base fabric constant temperature between 105 DEG C is dried for 1 hour, then at 160 DEG C, bake about 50s.
First arrangement base fabric being carried out pretreatment before carrying out self-cleaning finishing, described pretreatment fluid is grouped into by the one-tenth of following weight percents:
Beta-schardinger dextrin-20%
Polyvinyl alcohol 10%
Dispersant 5%
Water 65%.
The above; it is only the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope that disclosed herein; the change can expected without creative work or replacement, all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with claims protection defined.
Claims (3)
1. a high-efficiency antimicrobial self-cleaning finishing agent, it is characterised in that: include housekeeping liquid A and B,
Described working solution A is with parts by weight, composed of the following components:
Polyacrylate 40-60
Polyvinyl alcohol 33-36
Silester 3-5
Polybutylene terephthalate (PBT) 20-24
Epoxidized linseed oil 3-5
Polyethylene wax powder 12-15
Isopropyl distearyl acyloxy Aluminate 2-3
Bauxite powder 40-45
Soybean oil 3-5;
Described working solution B is with parts by weight, composed of the following components:
Fluorocarbon polymer 20-30
Modified cyanurotriamide resin 15-18
Polyox-yethylene-polyoxypropylene block copolymer 12-16
Sodium chlorite 3-7
Polyacrylamide 2-8
Fatty alcohol sulfate single ethanol ammonium salt 0.5-3
Nano titanic oxide sol 14-28
Di-n-octyl sebacate 10-20
Methylaminopropyl trimethyl silane 2-5
Ethanol 30-50
Deionized water is about 80-100;
The using method of finishing agent is as follows:
(1) arranging base fabric, first pad working solution A, pressure is 2.5~3kg/cm2, liquid carrying rate is 60~70%, by base fabric constant temperature 0.5~2 hour between 115~120 DEG C after drying, then bakes 15-60s at 170 DEG C;
(2) base fabric is padded working solution B, pressure 6~8kg/cm again2, liquid carrying rate 80-90%, after drying, base fabric constant temperature between 100~105 DEG C is dried for 1 hour, then at 160 DEG C, bake about 45-50s.
2. high-efficiency antimicrobial self-cleaning finishing agent according to claim 1, it is characterised in that: first arrangement base fabric being carried out pretreatment before carrying out self-cleaning finishing, described pretreatment fluid is grouped into by the one-tenth of following weight percents:
Beta-schardinger dextrin-5-20%
Polyvinyl alcohol 1-10%
Dispersant 1-5%
Water 65%-93%.
3. the high-efficiency antimicrobial self-cleaning finishing agent according to claim 1 and 2, it is characterised in that: described base fabric is cellulose fibre base fabric, synthetic fibers base fabric or blending base fabric.