CN105733737B - The copper ashes compound additive and preparation method of reduction domestic coke ignition temperature and application - Google Patents
The copper ashes compound additive and preparation method of reduction domestic coke ignition temperature and application Download PDFInfo
- Publication number
- CN105733737B CN105733737B CN201610103001.8A CN201610103001A CN105733737B CN 105733737 B CN105733737 B CN 105733737B CN 201610103001 A CN201610103001 A CN 201610103001A CN 105733737 B CN105733737 B CN 105733737B
- Authority
- CN
- China
- Prior art keywords
- copper ashes
- compound additive
- coal
- ignition temperature
- domestic coke
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
It is a kind of reduce domestic coke ignition temperature copper ashes compound additive parts by weight group become 20~70 parts of copper ashes, 30~80 parts of lime stone.Raw material sources of the present invention enrich extensively, it is cheap, ignition temperature cooling effect is significant, oxysulfide and 70% or more nitrogen oxides emission reduction, 96% or more flue dust emission reduction, to surrounding city life in the countryside coal is solved, improve rural area and city environmental quality, reduces haze weather and be of great immediate significance.
Description
Technical field
The present invention relates to a kind of copper ashes compound additives and preparation method and application for reducing domestic coke ignition temperature.
Background technique
Coal burning be China at present so that from now on for quite a long time obtain the energy major way, a large amount of coals it is direct
Dust, sulfur dioxide, nitrogen oxides of burning and exhausting etc. cause serious harm to ecological environment, especially atmospheric environment,
Cause China's air environmental pollution serious, haze weather takes place frequently.Based on pollution that caused by coal burning status, country has successively put into effect a series of
Law and regulation, and take strong punitive measures.Although the implementation of these regulations plays the aggravation of pollution that caused by coal burning degree
It is acted on to certain containment, but still poor remote apart from environmental objective to be achieved.
In fact, rural household fire coal environmental pollution can not be ignored.According to initial estimate, northern country 1 ton of height of every burning
Volatilize raw coal, it will the carbon dioxide (carbon emission coefficient 0.67) of discharge 2.5 tons or more, 150 kilograms or more other stain object
(oxidation of coal rate 0.85).Civilian scattered burning coal consumption in 2014 is 1.6 hundred million tons, accounts for the 3.8% of national coal consumption, only with sulfur dioxide
For discharge, power plant of China annual emissions are 2,000,000 tons, and it is the 1.6 of power plant emission total amount that civilian scattered burning, which is then up to 3,200,000 tons,
Times.In addition, a series of problems, such as smoke contamination of civilian scattered burning coal, nitrogen oxides pollution, cinder pollution, is to ecological environment
It destroys even more inestimable.However, being influenced by factors such as region, economy, culture, solve very difficult.To from root
The pollution that caused by coal burning of rural area and samll cities and towns is solved the problems, such as in sheet, provides high-quality, low price for these areas, clean alternative fuel is to work as
It is engaged in anxious.
Domestic coke is and to be aided with a small amount of coking coal, sulphur-fixing agent, carburant, combustion adjuvant etc. based on bunker coal (thermal coal),
Using existing coke-oven plant's production equipment, pass through cleaning solid fuel obtained by high-temperature retorting.With blocking good, moderate strength, low
Volatilization, low emission sulphur and the advantages that be not easy slagging, are not necessarily to desulfurization equipment, tail gas can meet national emission standard;And easy point
Fire, continuous fiery ability is strong, heating rate is fast, firing duration is long, is the various ideal fuel of domestic life stove.
Coke is used as domestic fuel, it is necessary to solve the problems, such as coke ignition temperature height, ignition difficulties.Currently, metallurgical coke
Fiery temperature is 600 DEG C or so, and bituminous coal and anthracitic ignition temperature are respectively 350 DEG C and 500 DEG C.Therefore, it is necessary to by helping
The introducing for firing agent, is down to 400 DEG C or so for ignition temperature, to meet civilian furnace igniting requirement.
Patent about combustion-supporting agent for fuel coal is existing very much, and if CN90105106.3 discloses a kind of combustion-supporting agent for fuel coal, it contains
There are three kinds of boron mud, lime stone, bauxite, white clay, manganese slag, iron oxide, canebreak and sodium carbonate, sodium nitrate, sodium chloride sodium
At least one of salt, the combustion adjuvant can obviously improve combustion position, improve stove fire temperature;CN97105154.2 discloses a kind of suitable
For the combustion-supporting agent for fuel coal of a variety of coals, mine tailings, manganese dioxide, production potassium bichromate are selected by boron mud, Calcium Carbide Ash, lime stone, iron
Waste residue, produce sodium dichromate waste residue, bauxite, sodium hydroxide, sodium carbonate, sodium nitrate, sodium oxide molybdena and canebreak press one
Combustion adjuvant and coal, are mixed in a certain ratio uniformly when use by certainty ratio composition;CN201310417513.8 discloses one
Energy-efficient combustion-supporting agent for fuel coal of kind and preparation method thereof, formula is made of zinc oxide and manganese dioxide, and burning of coal can be improved
Activity and ignition performance, flame temperature.These combustion adjuvants are the products for coal-fired exploitation, mostly using the skill for helping oxygen to burn
Art principle, is directly added into fire coal, promotes coal full combustion, plays the role of combustion-supporting, energization, economizes on coal.Since domestic coke needs
To pass through the special process of high-temperature retorting, most of component in combustion-supporting agent for fuel coal can fail because of pyrolytic;Therefore, civilian
Coke is not available prior art combustion-supporting agent for fuel coal.It is retrieved, the additive for reducing domestic coke ignition temperature has not been reported.
Summary of the invention
The object of the present invention is to provide a kind of compound additions of copper ashes of the reduction domestic coke ignition temperature of good cooling effect
Agent and its preparation method and application.
There are significant differences for the combustion adjuvant of the present invention and existing literature report, are mainly manifested in: 1) reducing ignition temperature
Mechanism is different.Traditional combustion-supporting agent for fuel coal itself is combustibles, because its ignition temperature is low, is ignited coal by spontaneous combustion, therefore, addition helps
Absolute prohibition high-temperature process after combustion agent, otherwise will lose combustion-supporting effect;The combustion-supporting catalytic action derived from composite oxides of the present invention.
First under high-temperature retorting reducing condition, coke surface and internal formation carbon defects are acted on by the catalytic gasification of auxiliary agent, at
For the firing point of oxidizing fire;In addition, composite assistant under high temperature reducing atmospheres, will form a small amount of microcrystalline, oxygen pole is met
Easy firing heat release forms localized hyperthermia's point, thus the coke that ignites.2) it is different that the stage is added.Traditional combustion-supporting agent for fuel coal is mostly in moulded coal system
Standby preceding addition, then through mixing, bonding, cold moudling;Or directly enter furnace burning after mixing with scattered coal.This patent auxiliary agent is in destructive distillation
It is added when coal blending, is mixed, made firm by ramming, high-temperature retorting becomes civilian clean coke.
Copper ashes is the waste residue of generation during copper metallurgy, and using blast furnace copper metallurgy discharge is blast furnace copper ashes, weight hundred
Dividing than chemical component is SiO231-39%, FeO 33-42%, Fe2O33-10, CaO 6-19%, MgO 0.8-7.0%,
Al2O34-12%, S 0.2-0.45%, Cu 0.35-2.4%;Use the waste residue of converter process copper metallurgy discharge for converter copper ashes,
Weight percent chemical component is SiO216-28%, FeO 48-65%, Fe2O312-29, CaO 1-2%, MgO 0-2%,
Al2O35-10%, S 1.5-7.0%, Cu 1.1-2.9%.
The ignition temperature that the present invention for the first time compounds copper ashes with calcium carbonate for reducing domestic coke.
To achieve the goals above, the technical solution used in the present invention is as follows:
It is a kind of reduce domestic coke ignition temperature copper ashes compound additive, parts by weight group become 20~70 parts of copper ashes,
30~80 parts of lime stone.
Preparation method of the present invention, includes the following steps:
By after drying copper ashes, raw limestone is respectively through rough and torn, thin broken to granularity≤3mm;
(2) the additive raw material being crushed is weighed respectively, and is mixed, and is stirred evenly;
(3) the mixture stirred evenly makes raw material granularity≤150 mesh (0.1mm) through dry grinding;Then 260~300
It calcines 1~2 hour, is cooled to room temperature, as copper ashes compound additive under the conditions of DEG C.
The application of copper ashes compound additive of the present invention, includes the following steps:
By copper ashes compound additive: mixed coal weight ratio is 0.4~8.0:100, and copper ashes compound additive is added to and is matched
It closes in coal, air is completely cut off in gas retort and is heated to 900~1100 DEG C, continuous heating 16~for 24 hours, then red heat furnace charge is come out of the stove
Room temperature is down to by quenching process, then screened to get arriving the domestic coke containing copper ashes compound additive.
The quality index of the mixed coal are as follows: FCd>=50%, Vadf>=25%, Ad≤ 25%, Std< 1.5%.
It is described screening be will drop to room temperature furnace charge screening be 25-80mm granularity.
The prior art of the present invention is compared, and direct bring and the advantages of necessarily leading to are as follows with good effect:
In the methods of the invention, used copper ashes compound additive, raw material sources enrich extensively, cheap, directly
It connects and is added in mixed coal, the domestic coke containing copper ashes compound additive is made by high-temperature retorting, ignition temperature can be from
550~630 DEG C are reduced to 395~410 DEG C, and decline temperature amplitude is up to 155~220 DEG C, significant effect.
In the methods of the invention, the domestic coke of production, compared with direct burning coal, oxysulfide subtracts with nitrogen oxides
70% or more row, 96% or more flue dust emission reduction improve rural area and urban environment matter to surrounding city life in the countryside coal is solved
Amount reduces haze weather and is of great immediate significance.
Specific embodiment
A specific embodiment of the invention is made below and being further explained.
Embodiment 1
(1) by blast furnace copper ashes (the chemical component SiO after drying231.0wt%, FeO 42.0wt%, Fe2O3
3.0wt%, CaO 13.0wt%, MgO 5.0wt%, Al2O35.45wt%, S 0.2wt%, Cu 0.35wt%), lime stone
Additive raw material is respectively through rough and torn, thin broken to granularity≤3mm;
(2) blast furnace copper ashes 70kg, the lime stone 30kg being crushed successively are weighed respectively, and is mixed, and stirring is equal
It is even;
(3) the mixture stirred evenly makes raw material granularity≤150 mesh (0.1mm) through dry grinding;Then in 260 DEG C of conditions
Lower calcining 2 hours, is cooled to room temperature, as copper ashes compound additive;
As-fired coal material by the jet coal of 20wt%, the meager coal of 15wt%, 1/3 coking coal of 30wt%, 20wt% rich coal
Coking coal cooperation with 15wt% forms mixed coal;The quality index of its mixed coal are as follows: Vadf30.0%, Ad13.5%,
FCd60.6%, St,d0.67%;Adhesive index=74, fineness (≤3mm)=73.6%;
(5) press copper ashes compound additive: mixed coal weight ratio is 0.4:100, and the copper ashes compound additive made is added to
In mixed coal, completely cuts off air in gas retort and be heated to 1100 DEG C, continuous heating 16h, through putting out after then red heat furnace charge is come out of the stove
Burnt process is down to room temperature, then screened, obtains the domestic coke containing copper ashes compound additive that granularity is 25-80mm.In north
The NS18-2 type 150m of Jing Chuanzi stove Co., Ltd production2Burnt progress combustion test civilian to gained, is surveyed in civilian reverberatory furnace
Its pollutant effulent is tried, compared with direct fire coal, oxysulfide emission reduction 72%, nitrogen oxides emission reduction 70%, flue dust emission reduction 96%.
Comparative example: not adding any additive in mixed coal, in gas retort completely cut off air be heated to 1100 DEG C, persistently plus
Hot 16h is down to room temperature through quenching process after then red heat furnace charge is come out of the stove, then screened, and gained coke is as control coke.
Civilian to gained burnt respectively and control carries out burning point test experiments with coke in JDRD-5A type determination of ignition point instrument, reality
Test that the results are shown in Table 1.
Table 1 adds compound additive and compares with the burning point for being not added with compound additive coke
Test group | Burning point DEG C | Decline temperature DEG C |
Control coke | 550 | - |
Add the civilian coke of compound additive | 395 | 155 |
Embodiment 2
(1) by converter copper ashes (the chemical component SiO after drying216.0wt%, FeO 57.8wt%, Fe2O3
12.0wt%, CaO 1.1wt%, MgO 0.53wt%, Al2O310.0wt%, S 1.51wt%, Cu 1.06wt%), lime
Stone additive raw material is respectively through rough and torn, thin broken to granularity≤3mm;
(2) converter copper ashes 57.5kg, the lime stone 42.5kg being crushed successively are weighed respectively, and is mixed, and are stirred
Uniformly;
(3) the mixture stirred evenly makes raw material granularity≤150 mesh (0.1mm) through dry grinding;Then in 270 DEG C of conditions
Lower calcining 1.8 hours, is packed, as copper ashes compound additive after being cooled to room temperature;
(4) as-fired coal not gluing by the weakly caking coal of 30wt%, the jet coal of 40wt%, the gas rich coal of 20wt% and 10wt%
Coal cooperation forms mixed coal;Its quality index (wt%): Vadf35.0%, Ad13.5%, FCd56.2%, St,d0.84%, bonding
Index G=40, fineness (≤3mm)=86.5%;
(5) press copper ashes compound additive: mixed coal weight ratio is 2.3:100, and the copper ashes compound additive made is added to
In mixed coal, completely cuts off air in gas retort and be heated to 1050 DEG C, continuous heating 18h, through putting out after then red heat furnace charge is come out of the stove
Burnt process is down to room temperature, then screened, obtains the domestic coke containing copper ashes compound additive that granularity is 25-80mm.In north
The NS18-2 type 150m of Jing Chuanzi stove Co., Ltd production2Burnt progress combustion test civilian to gained, is surveyed in civilian reverberatory furnace
Its pollutant effulent is tried, compared with direct fire coal, oxysulfide emission reduction 74%, nitrogen oxides emission reduction 71%, flue dust emission reduction
96.5%.
Comparative example: not adding any additive in mixed coal, in gas retort completely cut off air be heated to 1050 DEG C, persistently plus
Hot 18h is down to room temperature through quenching process after then red heat furnace charge is come out of the stove, then screened, and gained granularity is the coke of 25-80mm
As control coke.
Civilian to gained burnt respectively and control carries out burning point test experiments with coke in JDRD-5A type determination of ignition point instrument, reality
Test that the results are shown in Table 2.
Table 2 adds compound additive and compares with the burning point for being not added with compound additive coke
Test group | Burning point DEG C | Decline temperature DEG C |
Control coke | 570 | - |
Add the civilian coke of compound additive | 399 | 171 |
Embodiment 3
(1) by blast furnace copper ashes (the chemical component SiO after drying235.0wt%, FeO 36.0wt%, Fe2O3
6.5wt%, CaO 17.0wt%, MgO 0.8wt%, Al2O34.08wt%, S 0.21wt%, Cu 0.41wt%), lime stone
Additive raw material is respectively through rough and torn, thin broken to granularity≤3mm;
(2) blast furnace copper ashes 45kg, the lime stone 55kg being crushed successively are weighed respectively, and is mixed, and stirring is equal
It is even;
(3) the mixture stirred evenly makes raw material granularity≤150 mesh (0.1mm) through dry grinding;Then in 280 DEG C of conditions
Lower calcining 1.5 hours, is packed, as copper ashes compound additive after being cooled to room temperature;
As-fired coal material by the jet coal of 20wt%, the meager coal of 15wt%, 1/3 coking coal of 30wt%, 20wt% rich coal
Coking coal cooperation with 15wt% forms mixed coal;The quality index of its mixed coal are as follows: Vadf30.0%, Ad13.5%,
FCd60.6%, St,d0.67%;Adhesive index=74, fineness (≤3mm)=73.6%;
(5) press copper ashes compound additive: mixed coal weight ratio is 4.2:100, and the copper ashes compound additive made is added to
In mixed coal, completely cuts off air in gas retort and be heated to 1000 DEG C, continuous heating 20h, through putting out after then red heat furnace charge is come out of the stove
Burnt process is down to room temperature, then screened, obtains the domestic coke containing copper ashes compound additive that granularity is 25-80mm.In north
The NS18-2 type 150m of Jing Chuanzi stove Co., Ltd production2Burnt progress combustion test civilian to gained, is surveyed in civilian reverberatory furnace
Its pollutant effulent is tried, compared with direct fire coal, oxysulfide emission reduction 76%, nitrogen oxides emission reduction 72%, flue dust emission reduction 97%;
Comparative example: not adding any additive in mixed coal, in gas retort completely cut off air be heated to 1000 DEG C, persistently plus
Hot 20h is down to room temperature through quenching process after then red heat furnace charge is come out of the stove, then screened, and gained granularity is the coke of 25-80mm
As control coke.
Civilian to gained burnt respectively and control carries out burning point test experiments with coke in JDRD-5A type determination of ignition point instrument, reality
Test that the results are shown in Table 3.
Table 3 adds compound additive and compares with the burning point for being not added with compound additive coke
Test group | Burning point DEG C | Decline temperature DEG C |
Control coke | 590 | - |
Add the civilian coke of compound additive | 403 | 187 |
Embodiment 4
(1) by converter copper ashes (the chemical component SiO after drying224.0wt%, FeO 43.73wt%, Fe2O3
22.0wt%, CaO 1.42wt%, MgO 0.78wt%, Al2O35.0wt%, S 1.6wt%, Cu 1.47wt%), lime stone
Additive raw material is respectively through rough and torn, thin broken to granularity≤3mm;
(2) converter copper ashes 32.5kg, the lime stone 67.5kg being crushed successively are weighed respectively, and is mixed, and are stirred
Uniformly;
(3) the mixture stirred evenly makes raw material granularity≤150 mesh (0.1mm) through dry grinding;Then in 290 DEG C of conditions
Lower calcining 1.3 hours, is packed, as copper ashes compound additive after being cooled to room temperature;
(4) as-fired coal not gluing by the weakly caking coal of 30wt%, the jet coal of 40wt%, the gas rich coal of 20wt% and 10wt%
Coal cooperation forms mixed coal;Its quality index (wt%): Vadf35.0%, Ad13.5%, FCd56.2%, St,d0.84%, bonding
Index G=40, fineness (≤3mm)=86.5%;
(5) press copper ashes compound additive: mixed coal weight ratio is 6.1:100, and the copper ashes compound additive made is added to
In mixed coal, completely cuts off air in gas retort and be heated to 950 DEG C, continuous heating 22h, through quenching after then red heat furnace charge is come out of the stove
Process is down to room temperature, then screened, obtains the domestic coke containing copper ashes compound additive that granularity is 25-80mm.In Beijing
The NS18-2 type 150m of Chuan Zi stove Co., Ltd production2Burnt progress combustion test civilian to gained, test in civilian reverberatory furnace
Its pollutant effulent, compared with direct fire coal, oxysulfide emission reduction 77%, nitrogen oxides emission reduction 73%, flue dust emission reduction 97.5%.
Comparative example: not adding any additive in mixed coal, in gas retort completely cut off air be heated to 950 DEG C, persistently plus
Hot 22h is down to room temperature through quenching process after then red heat furnace charge is come out of the stove, then screened, and gained granularity is the coke of 25-80mm
As control coke.
Civilian to gained burnt respectively and control carries out burning point test experiments with coke in JDRD-5A type determination of ignition point instrument, reality
Test that the results are shown in Table 4.
Table 4 adds compound additive and compares with the burning point for being not added with compound additive coke
Test group | Burning point DEG C | Decline temperature DEG C |
Control coke | 610 | - |
Add the civilian coke of compound additive | 407 | 203 |
Embodiment 5
(1) by blast furnace copper ashes (the chemical component SiO after drying239.0wt%, FeO 33.0wt%, Fe2O3
10.0wt%, CaO 6.0wt%, MgO 7.0wt%, Al2O34.39wt%, S 0.23wt%, Cu 0.38wt%), lime stone
Additive raw material is respectively through rough and torn, thin broken to granularity≤3mm;
(2) blast furnace copper ashes 20kg, the lime stone 80kg being crushed successively are weighed respectively, and is mixed, and stirring is equal
It is even;
(3) the mixture stirred evenly makes raw material granularity≤150 mesh (0.1mm) through dry grinding;Then in 300 DEG C of conditions
Lower calcining 1 hour, is packed, as copper ashes compound additive after being cooled to room temperature;
As-fired coal material by the jet coal of 20wt%, the meager coal of 15wt%, 1/3 coking coal of 30wt%, 20wt% rich coal
Coking coal cooperation with 15wt% forms mixed coal;The quality index of its mixed coal are as follows: Vadf30.0%, Ad13.5%,
FCd60.6%, St,d0.67%;Adhesive index=74, fineness (≤3mm)=73.6%;
(5) press copper ashes compound additive: mixed coal weight ratio is 8.0:100, and the copper ashes compound additive made is added to
In mixed coal, completely cut off air in gas retort and be heated to 900 DEG C, continuous heating for 24 hours, through quenching after then red heat furnace charge is come out of the stove
Process is down to room temperature, then screened, obtains the domestic coke containing copper ashes compound additive that granularity is 25-80mm.In Beijing
The NS18-2 type 150m of Chuan Zi stove Co., Ltd production2Burnt progress combustion test civilian to gained, test in civilian reverberatory furnace
Its pollutant effulent, compared with direct fire coal, oxysulfide emission reduction 78%, nitrogen oxides emission reduction 74%, flue dust emission reduction 98%;
Comparative example: not adding any additive in mixed coal, in gas retort completely cut off air be heated to 900 DEG C, persistently plus
Heat for 24 hours, is down to room temperature through quenching process after then red heat furnace charge is come out of the stove, then screened, and gained granularity is the coke of 25-80mm
As control coke.
Civilian to gained burnt respectively and control carries out burning point test experiments with coke in JDRD-5A type determination of ignition point instrument, reality
Test that the results are shown in Table 5.
Table 5 adds compound additive and compares with the burning point for being not added with compound additive coke
Test group | Burning point DEG C | Decline temperature DEG C |
Control coke | 630 | - |
Add the civilian coke of compound additive | 410 | 220 |
After can be seen that addition copper ashes compound additive by Examples 1 to 5 experimental result, civilian coke is significantly reduced
The burning point of charcoal ensure that a kind of application of the domestic coke as fuel so that domestic coke is easier to catch fire.
Claims (6)
1. a kind of application for the copper ashes compound additive for reducing domestic coke ignition temperature, it is characterised in that include the following steps:
By copper ashes compound additive: mixed coal weight ratio is 0.4~8.0:100, and copper ashes compound additive is added to mixed coal
In, completely cut off air in gas retort and is heated to 900~1100 DEG C, continuous heating 16~for 24 hours, it is passed through after then red heat furnace charge is come out of the stove
Quenching process is down to room temperature, then screened to get arriving the domestic coke containing copper ashes compound additive;
The parts by weight group of the copper ashes compound additive for reducing domestic coke ignition temperature becomes 20~70 parts of copper ashes, lime stone
30~80 parts;
The quality index of the mixed coal are as follows: FCd>=50%, Vadf>=25%, Ad≤ 25%, Std< 1.5%.
2. a kind of application of copper ashes compound additive for reducing domestic coke ignition temperature as described in claim 1, feature
It is that the copper ashes is blast furnace copper ashes or converter copper ashes.
3. a kind of application of copper ashes compound additive for reducing domestic coke ignition temperature as claimed in claim 2, feature
The weight percent chemical component for being the blast furnace copper ashes is SiO231-39%, FeO 33-42%, Fe2O33-10,
CaO 6-19%, MgO 0.8-7.0%, Al2O34-12%, S 0.2-0.45%, Cu 0.35-2.4%.
4. a kind of application of copper ashes compound additive for reducing domestic coke ignition temperature as claimed in claim 2, feature
The weight percent chemical component for being the converter copper ashes is SiO216-28%, FeO 48-65%, Fe2O312-29, CaO
1-2%, MgO 0-2%, Al2O35-10%, S 1.5-7.0%, Cu 1.1-2.9%.
5. a kind of application of copper ashes compound additive for reducing domestic coke ignition temperature as described in claim 1, feature
Be sieve be will drop to room temperature furnace charge screening be 25-80mm granularity.
6. special such as a kind of application for the copper ashes compound additive for reducing domestic coke ignition temperature of any one of claim 1-5
Sign is the preparation method of the copper ashes compound additive for reducing domestic coke ignition temperature, includes the following steps:
By after drying copper ashes, raw limestone is respectively through rough and torn, thin broken to granularity≤3mm;
(2) the additive raw material being crushed is weighed respectively, and is mixed, and is stirred evenly;
(3) the mixture stirred evenly makes raw material granularity≤0.1mm through dry grinding, then calcines under the conditions of 260~300 DEG C
It 1~2 hour, is cooled to room temperature, as copper ashes compound additive.