CN105694349A - 一种塑料焊条 - Google Patents
一种塑料焊条 Download PDFInfo
- Publication number
- CN105694349A CN105694349A CN201410699217.6A CN201410699217A CN105694349A CN 105694349 A CN105694349 A CN 105694349A CN 201410699217 A CN201410699217 A CN 201410699217A CN 105694349 A CN105694349 A CN 105694349A
- Authority
- CN
- China
- Prior art keywords
- welding rod
- plastic
- plastic welding
- metal dust
- plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种焊条,尤其是涉及一种塑料焊条。该塑料焊条包括塑料和金属粉末,所述塑料质量百分含量为70%~80%,所述金属粉末质量百分含量为20%~30%。本发明在塑料焊条制备过程中加入一定比例的金属粉末,可以满足各种成分塑料制品的焊接要求,具有很大的应用前景;本塑料焊条制作简单,价格低廉,易于推广;加入脱氧剂,在焊接过程中可以减少焊缝中氧的含量,避免氧化后产生老化现象。
Description
技术领域
本发明涉及一种焊条,尤其是涉及一种塑料焊条。
背景技术
焊接作业被明确定为特种作业,因为该作业对于操作者本人、他人、周围设施的安全设施具有重大的危害,触发、引发火灾和设备烧损都是焊接作业中最容易发生的人员伤亡和财产损失事故。就电焊钳和焊接电缆而言,因为其具有移动性的使用特点,而且是在焊接作业中与操作人员接触最为频繁的带电器材,大电流从电焊钳把中流过,电焊工及有关人员随时都可能接触这些器材和相关带电物体,如更换焊条、整理焊件、挪动电缆、提放电焊钳等操作活动,操作人员都将直接或间接地接触它们,还有许多无意的或意外的碰触,由于是毫无防备的,所以也是最危险的。
塑料的主要成分是树脂。树脂这一名词最初是由动植物分泌出的脂质而得名,如松香、虫胶等,树脂是指尚未和各种添加剂混合的高聚物。树脂约占塑料总重量的40%~100%。塑料的基本性能主要决定于树脂的本性,但添加剂也起着重要作用。有些塑料基本上是由合成树脂所组成,不含或少含添加剂,如有机玻璃、聚苯乙烯等。所谓塑料,其实它是合成树脂中的一种,形状跟天然树脂中的松树脂相似,但因经过化学手段进行人工合成,而被称之为塑料。塑料可区分为热固性与热塑性二类,前者无法重新塑造使用,后者可以再重复生产。热可塑性其物理延伸率较大,一般在50%~500%。在不同延伸率下力不完全成线性变化。对于塑料研发机构或企业都有欧标仪器的塑料拉伸实验机。塑料不同性能决定了其在生活在工业中的用途,随着技术的进步,对塑料改性一直没有停止过研究。希望不远的将来,塑料通过改性后的可以有更广泛的应用,甚至可代替钢铁等材料并对环境不再污染。
塑料在生活中到处可见,已经被越来越广泛地应用于各个领域,其具有质量轻,易成型等优点,在很多地方替代钢材使用。但是塑料制品有着易断裂、漏眼、老化、损坏等缺点,修补起来相当困难,许多塑料制品在产生一点小小的问题时就会不再具备利用价值,但通过焊接修复后还是能再次利用,但一般的塑料焊接条都是简单的通过塑料作为焊条,这样虽然当时从外观上看能达到焊接修复的效果,但时间久了,断裂处还是会凸显出来,达不到“治本”的效果,且采用单纯的塑料焊条,在焊条的焊接处还是容易产生氧化、老化等现象,也无法达到原先一体化的塑料制品的使用价值。
在工程上塑料焊条要求材料的成分与被焊接材料的成分相同,但是因为现有塑料制品成分的多样性,在制造塑料制品时,往往加入其它成分,所以现有的塑料焊条,如聚乙烯焊条、聚丙烯焊条或聚氯乙烯焊条,不能满足塑料制品的焊接要求,而如果将每一种塑料制品都配备具有相同成分的塑料焊条,对塑料焊条制造企业又存在很大的市场风险,所以,研发一种能满足各种不同成分塑料制品的塑料焊条,具有很大的市场潜力和经济价值。
发明内容
本发明要解决的技术问题是:克服现有技术的缺陷,提供一种塑料焊条,能够适用于各种成分的塑料制品。
本发明目的通过下述技术方案来实现:
一种塑料焊条,其特征在于:包括塑料和金属粉末,所述塑料质量百分含量为70%~80%,所述金属粉末质量百分含量为20%~30%。
作为优选,所述金属粉末粒径为0.3mm~0.8mm。
作为优选,所述塑料为酚醛树脂、聚乙烯、聚丙烯或聚氯乙烯。
作为优选,所述金属粉末为铜粉、铁粉或铝粉。
作为优选,所述塑料焊条还包括脱氧剂。
作为优选,所述脱氧剂占总质量的1.2%~1.8%。
作为优选,所述塑料质量百分含量为75%,所述金属粉末质量百分含量为25%。
一种塑料焊条制备方法,其特征在于:首先将塑料加热到70℃~80℃,然后将金属粉末加到塑料中搅拌均匀,压缩成型后冷却到室温。
本发明的有益效果:本发明在塑料焊条制备过程中加入一定比例的金属粉末,可以满足各种成分塑料制品的焊接要求,具有很大的应用前景;本塑料焊条制作简单,价格低廉,易于推广;加入脱氧剂,在焊接过程中可以减少焊缝中氧的含量,避免氧化后产生老化现象。
具体实施方式
下列非限制性实施例用于说明本发明。
一种塑料焊条,其特征在于:包括塑料和金属粉末,所述塑料质量百分含量为70%~80%,所述金属粉末质量百分含量为20%~30%。所述金属粉末粒径为0.3mm~0.8mm;所述塑料为酚醛树脂、聚乙烯、聚丙烯或聚氯乙烯;所述金属粉末为铜粉、铁粉或铝粉;所述塑料焊条还包括脱氧剂;所述脱氧剂占总质量的1.2%~1.8%;作为优选,所述塑料质量百分含量为75%,所述金属粉末质量百分含量为25%。
一种塑料焊条制备方法,首先将塑料加热到70℃~80℃,然后将金属粉末加到塑料中搅拌均匀,压缩成型后冷却到室温。
实施例1:
取70g酚醛树脂,加热到70℃,然后加入粒径为0.3mm~0.8mm的铁粉20g,搅拌均匀,再加入1.5g脱氧剂,再搅拌均匀,压缩成型后冷却至室温。
实施例2:
取75g聚乙烯,加热到70℃,然后加入粒径为0.3mm~0.8mm的铁粉25g,搅拌均匀,压缩成型后冷却至室温。
实施例3:
取80g聚乙烯,加热到75℃,然后加入粒径为0.3mm~0.8mm的铝粉25g,搅拌均匀,压缩成型后冷却至室温。
实施例4:
取80g聚丙烯,加热到75℃,然后加入粒径为0.3mm~0.8mm的铜粉30g,搅拌均匀,压缩成型后冷却至室温。
实施例5:
取80g聚氯乙烯,加热到75℃,然后加入粒径为0.3mm~0.8mm的铜粉20g,搅拌均匀,压缩成型后冷却至室温。
实施例6:
取70g聚氯乙烯,加热到80℃,然后加入粒径为0.3mm~0.8mm的铁粉30g,搅拌均匀,再加入1.2g脱氧剂,再搅拌均匀,压缩成型后冷却至室温。
实施例7:
取75g聚氯乙烯,加热到80℃,然后加入粒径为0.3mm~0.8mm的铁粉30g,搅拌均匀,再加入1.2g脱氧剂,再搅拌均匀,压缩成型后冷却至室温。
实施例8:
取75g聚氯乙烯,加热到75℃,然后加入粒径为0.3mm~0.8mm的铁粉30g,搅拌均匀,再加入1.2g脱氧剂,再搅拌均匀,压缩成型后冷却至室温。
实施例9:
取75g聚氯乙烯,加热到75℃,然后加入粒径为0.3mm~0.8mm的铜粉20g,搅拌均匀,再加入1.2g脱氧剂,再搅拌均匀,压缩成型后冷却至室温。
实施例10:
取75g聚氯乙烯,加热到75℃,然后加入粒径为0.3mm~0.8mm的铜粉30g,搅拌均匀,再加入1.2g脱氧剂,再搅拌均匀,压缩成型后冷却至室温。
采用本发明制备的塑料焊条,能够适用于各种塑料焊接,焊接后牢固,不易脱落,美观。本塑料焊条制作简单,价格低廉,易于推广;加入脱氧剂,在焊接过程中可以减少焊缝中氧的含量,避免氧化后产生老化现象。
以上仅是本发明的较佳实施例而已,并非对本发明做任何形式上的限制,凡是依据本发明的技术实质对以上实施例所作的任何简单修改或等同变化,均仍属于本发明技术方案的范围内。
Claims (8)
1.一种塑料焊条,其特征在于:包括塑料和金属粉末,所述塑料质量百分含量为70%~80%,所述金属粉末质量百分含量为20%~30%。
2.根据权利要求1所述的塑料焊条,其特征在于:所述金属粉末粒径为0.3mm~0.8mm。
3.根据权利要求1所述的塑料焊条,其特征在于:所述塑料为酚醛树脂、聚乙烯、聚丙烯或聚氯乙烯。
4.根据权利要求1所述的塑料焊条,其特征在于:所述金属粉末为铜粉、铁粉或铝粉。
5.根据权利要求1所述的塑料焊条,其特征在于:所述塑料焊条还包括脱氧剂。
6.根据权利要求5所述的塑料焊条,其特征在于:所述脱氧剂占总质量的1.2%~1.8%。
7.根据权利要求1所述的塑料焊条,其特征在于:所述塑料质量百分含量为75%,所述金属粉末质量百分含量为25%。
8.根据权利要求1至7任一项所述的塑料焊条制备方法,其特征在于:首先将塑料加热到70℃~80℃,然后将金属粉末加到塑料中搅拌均匀,压缩成型后冷却到室温。