CN105647067A - Engineering plastic composition with high hardness - Google Patents
Engineering plastic composition with high hardness Download PDFInfo
- Publication number
- CN105647067A CN105647067A CN201610213685.7A CN201610213685A CN105647067A CN 105647067 A CN105647067 A CN 105647067A CN 201610213685 A CN201610213685 A CN 201610213685A CN 105647067 A CN105647067 A CN 105647067A
- Authority
- CN
- China
- Prior art keywords
- parts
- engineering plastic
- plastic composition
- big
- hardness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an engineering plastic composition with high hardness. The engineering plastic composition comprises the following components in parts by weight: 100 parts of polyvinyl chloride, 4-6 parts of organic tin, 1-3 parts of epoxidized soybean oil, 0.5-0.8 part of diisooctyl phenyl phosphite, 0.3-0.7 part of triphenyl phasphine, 2-4 parts of a calcium-zinc compound stabilizer and 5-8 parts of polyethylene wax. By adopting the mode, the engineering plastic composition with high hardness, disclosed by the invention, is good in partial deformation or crack resistance when being used, is unlikely to deform, can widen the use range of engineering plastic, and thus is popular with more customers.
Description
Technical field
The present invention relates to modified plastics plastic cement field, particularly relate to the engineering plastic composition that a kind of hardness is big.
Background technology
Plastics are the macromolecular compounds of synthesis, can be described as again macromolecule or giant molecule, are also the plastics or resin that are generally commonly called as, it is possible to freely change body styles. Dividing according to operating characteristic, plastics can be divided into general-purpose plastics, engineering plastics and special plastic three types. Engineering plastics have the advantage such as low cost of manufacture, durable, waterproof, light weight, it is easy to are moulded and make difformity, are good insulating bodies. When existing engineering plastics are on using, it is not easy to the effect of opposing external force, it is easy to break.
Summary of the invention
The technical problem that present invention mainly solves is to provide the engineering plastic composition that a kind of hardness is big, uses and is not easy deformation.
For solving above-mentioned technical problem, the technical scheme that the present invention adopts is: provide the engineering plastic composition that a kind of hardness is big, including component have polrvinyl chloride, organotin, epoxy soybean oil, phosphorous acid benzene di-isooctyl, triphenyl phasphine, calcium-zinc composite stabilizing agent and Tissuemat E, the big engineering plastic composition of described hardness is with parts by weight, including component have: polrvinyl chloride 100 parts, organotin 4-6 part, epoxy soybean oil 1-3 part, phosphorous acid benzene di-isooctyl 0.5-0.8 part, triphenyl phasphine 0.3-0.7 part, calcium-zinc composite stabilizing agent 2-4 part, Tissuemat E 5-8 part.
In a preferred embodiment of the present invention, the engineering plastic composition that described hardness is big adopts extrusion blow technique to carry out.
In a preferred embodiment of the present invention, the barrel zone temperature when engineering plastic composition that described hardness is big carries out extrusion blow technique is 150-200 DEG C, is set according to workshop section.
In a preferred embodiment of the present invention, the big engineering plastic composition of described hardness with parts by weight, including component have: polrvinyl chloride 100 parts, organotin 5 parts, epoxy soybean oil 2 parts, phosphorous acid benzene di-isooctyl 0.7 part, triphenyl phasphine 0.5 part, calcium-zinc composite stabilizing agent 3 parts, Tissuemat E 6 parts.
The invention has the beneficial effects as follows: the engineering plastic composition that the hardness of the present invention is big there is local resistance to deformation or the ability broken on using, it is not easy to deform, it is possible to expand the use scope of engineering plastics, be subject to the welcome of more consumer.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments. Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art obtain under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment one:
The engineering plastic composition that a kind of hardness is big is provided, including component have polrvinyl chloride, organotin, epoxy soybean oil, phosphorous acid benzene di-isooctyl, triphenyl phasphine, calcium-zinc composite stabilizing agent and Tissuemat E, the big engineering plastic composition of described hardness with parts by weight, including component have: polrvinyl chloride 100 parts, organotin 5 parts, epoxy soybean oil 2 parts, phosphorous acid benzene di-isooctyl 0.7 part, triphenyl phasphine 0.5 part, calcium-zinc composite stabilizing agent 3 parts, Tissuemat E 6 parts. The engineering plastic composition that described hardness is big adopts extrusion blow technique to carry out. Barrel zone temperature when carrying out extrusion blow technique is 150-200 DEG C, is set according to workshop section.
Embodiment two:
The engineering plastic composition that a kind of hardness is big is provided, including component have polrvinyl chloride, organotin, epoxy soybean oil, phosphorous acid benzene di-isooctyl, triphenyl phasphine, calcium-zinc composite stabilizing agent and Tissuemat E, the big engineering plastic composition of described hardness with parts by weight, including component have: polrvinyl chloride 100 parts, organotin 4 parts, epoxy soybean oil 3 parts, phosphorous acid benzene di-isooctyl 0.5 part, triphenyl phasphine 0.7 part, calcium-zinc composite stabilizing agent 2 parts, Tissuemat E 8 parts.
Embodiment three:
The engineering plastic composition that a kind of hardness is big is provided, including component have polrvinyl chloride, organotin, epoxy soybean oil, phosphorous acid benzene di-isooctyl, triphenyl phasphine, calcium-zinc composite stabilizing agent and Tissuemat E, the big engineering plastic composition of described hardness with parts by weight, including component have: polrvinyl chloride 100 parts, organotin 6 parts, epoxy soybean oil 1 part, phosphorous acid benzene di-isooctyl 0.8 part, triphenyl phasphine 0.3 part, calcium-zinc composite stabilizing agent 4 parts, Tissuemat E 5 parts.
The invention has the beneficial effects as follows:
One, the engineering plastic composition that described hardness is big has local resistance to deformation or the ability broken on using, it is not easy to deform;
Two, the engineering plastic composition that described hardness is big can expand the use scope of engineering plastics, is subject to the welcome of more consumer.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the present invention to make or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, all in like manner include in the scope of patent protection of the present invention.
Claims (4)
1. the engineering plastic composition that a hardness is big, it is characterized in that, including component have polrvinyl chloride, organotin, epoxy soybean oil, phosphorous acid benzene di-isooctyl, triphenyl phasphine, calcium-zinc composite stabilizing agent and Tissuemat E, the big engineering plastic composition of described hardness with parts by weight, including component have: polrvinyl chloride 100 parts, organotin 4-6 part, epoxy soybean oil 1-3 part, phosphorous acid benzene di-isooctyl 0.5-0.8 part, triphenyl phasphine 0.3-0.7 part, calcium-zinc composite stabilizing agent 2-4 part, Tissuemat E 5-8 part.
2. the engineering plastic composition that hardness according to claim 1 is big, it is characterised in that the engineering plastic composition that described hardness is big adopts extrusion blow technique to carry out.
3. the engineering plastic composition that hardness according to claim 2 is big, it is characterised in that the barrel zone temperature when engineering plastic composition that described hardness is big carries out extrusion blow technique is 150-200 DEG C, is set according to workshop section.
4. the engineering plastic composition that hardness according to claim 1 is big, it is characterized in that, the big engineering plastic composition of described hardness with parts by weight, including component have: polrvinyl chloride 100 parts, organotin 5 parts, epoxy soybean oil 2 parts, phosphorous acid benzene di-isooctyl 0.7 part, triphenyl phasphine 0.5 part, calcium-zinc composite stabilizing agent 3 parts, Tissuemat E 6 parts.