CN105647059A - PVC wood-plastic material - Google Patents
PVC wood-plastic material Download PDFInfo
- Publication number
- CN105647059A CN105647059A CN201610073541.6A CN201610073541A CN105647059A CN 105647059 A CN105647059 A CN 105647059A CN 201610073541 A CN201610073541 A CN 201610073541A CN 105647059 A CN105647059 A CN 105647059A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- plastic material
- pvc
- pvc wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A PVC wood-plastic material is prepared from, by weight, 41-49 parts of PVC powder, 13-18 parts of quick lime, 5-10 parts of chlorite schist, 8-14 parts of butylene succinate, 8-14 parts of polyethylene terephthalate, 6-13 parts of polyethylene glycol distearate, 9-12 parts of dimethyl fumarate, 22-34 parts of plant fibre, 18-23 parts of linear low density polyethylene, 3-9 parts of lychee exocarp, 3-9 parts of luffa stems, 6-10 parts of vermiculite, 25-36 parts of dried tangerine peel, 16-24 parts of methyl sorbate, 3-7 parts of rapeseed oil, 11-16 parts of acid auxiliary and 7-12 parts of viscose auxiliary. The PVC wood-plastic material is safe, environmentally friendly, capable of saving resources, quite good in processing performance, high in thermal stability, resistant to low temperature, capable of resisting low temperature of -40 DEG C, high in material adhesiveness, resistant to corrosion, capable of having certain flame retardance and good in sound insulation effect.
Description
Technical field
The present invention relates to Wood-plastic material field, be specifically related to a kind of PVC wood plastic material.
Background technology
Wood-plastic material is the class new material being in recent years surging forward both at home and abroad, the useless Plant fiber such as wood powder, rice husk, straw and plastic components and other carriers is utilized to be mixed into new wood materials, then through plastic processing, the sheet material produced or section bars such as extruding, mold pressing, injection mouldings. It is mainly used in the industries such as building materials, furniture, logistics packaging. Along with real estate, the developing rapidly of building industry, market is increasing to the demand of Wood-plastic material, and requires also more and more tighter to product quality.
Summary of the invention
The technical problem to be solved is in that to provide one to have a good processing characteristics, and Heat stability is good is low temperature resistant, can the low temperature of anti-40 DEG C, material caking property is good, corrosion-resistant, and has certain fire resistance, and soundproof effect might as well PVC wood plastic material.
The technical problem to be solved realizes by the following technical solutions:
A kind of PVC wood plastic material, is made up of the raw material of following weight portion: PVC powder 41-49 part, quick lime 13-18 part, Lapis Micae Aureus 5-10 part, poly butylene succinate 8-14 part, polyethylene terephthalate 8-14 part, Polyethylene Glycol distearyl acid fat 6-13 part, dimethyl fumarate 9-12 part, Plant fiber's 22-34 part, linear low density polyethylene 18-23 part, Exocarpium Litchi 3-9 part, Ramulus Luffae 3-9 part, Vermiculitum 6-10 part, Pericarpium Citri Reticulatae 25-36 part, sorbic acid formicester 16-24 part, Oleum Brassicae campestris 3-7 part, acid additive 11-16 part, viscosity auxiliary agent 7-12 part;
Described acid additive includes citric acid 5-12 part, sorbic acid 5-12 part, oxalic acid 2-6 part, salicylic acid 2-6 part;
Described viscosity auxiliary agent includes polyimides 8-19 part, resorcinol-formaldehyde resin 7-16 part, xylene formal dehyde resin 5-11 part.
A kind of PVC wood plastic material, described Plant fiber includes following one or more: wood powder, cotton stalk, wheat stalk, rice straw, rice husk, bagasse, reed rod, rape stalk.
The process step of the invention is as follows: various raw material pulverizing mixed, and then utilizes the wood-plastic board processing method of routine namely to obtain the PVC wood plastic material of the present invention.
The invention has the beneficial effects as follows: PVC wood plastic material safety and environmental protection of the present invention, economize on resources, there is good processing characteristics, Heat stability is good, low temperature resistant, the low temperature of anti-40 DEG C of energy, material caking property is good, corrosion-resistant, and there is certain fire resistance, and also soundproof effect might as well.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be easy to understand, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of PVC wood plastic material, is made up of the raw material of following weight portion: PVC powder 41 parts, quick lime 13 parts, Lapis Micae Aureus 5 parts, poly butylene succinate 8 parts, polyethylene terephthalate 8 parts, 6 parts of Polyethylene Glycol distearyl acid fat, dimethyl fumarate 9 parts, wood powder 22 parts, linear low density polyethylene 18 parts, Exocarpium Litchi 3 parts, Ramulus Luffae 3 parts, Vermiculitum 6 parts, Pericarpium Citri Reticulatae 25 parts, sorbic acid formicester 16 parts, Oleum Brassicae campestris 3 parts, acid additive 11 parts, viscosity auxiliary agent 7 parts;
Described acid additive includes citric acid 5 parts, sorbic acid 5 parts, oxalic acid 2 parts, salicylic acid 2 parts;
Described viscosity auxiliary agent includes polyimides 8 parts, resorcinol-formaldehyde resin 7 parts, xylene formal dehyde resin 5 parts.
Various raw material pulverizing are mixed, then utilizes the wood-plastic board processing method of routine namely to obtain the PVC wood plastic material of the present invention.
Embodiment 2
A kind of PVC wood plastic material, is made up of the raw material of following weight portion: PVC powder 45 parts, quick lime 15 parts, Lapis Micae Aureus 8 parts, poly butylene succinate 11 parts, polyethylene terephthalate 11 parts, 9 parts of Polyethylene Glycol distearyl acid fat, dimethyl fumarate 10 parts, cotton stalk and each 14 parts of wheat stalk, linear low density polyethylene 21 parts, Exocarpium Litchi 6 parts, Ramulus Luffae 6 parts, Vermiculitum 8 parts, Pericarpium Citri Reticulatae 30 parts, sorbic acid formicester 20 parts, Oleum Brassicae campestris 5 parts, acid additive 15 parts, viscosity auxiliary agent 10 parts;
Described acid additive includes citric acid 8 parts, sorbic acid 8 parts, oxalic acid 4 parts, salicylic acid 4 parts;
Described viscosity auxiliary agent includes polyimides 14 parts, resorcinol-formaldehyde resin 12 parts, xylene formal dehyde resin 8 parts.
Various raw material pulverizing are mixed, then utilizes the wood-plastic board processing method of routine namely to obtain the PVC wood plastic material of the present invention.
Embodiment 3
A kind of PVC wood plastic material, is made up of the raw material of following weight portion: PVC powder 49 parts, quick lime 18 parts, Lapis Micae Aureus 10 parts, poly butylene succinate 14 parts, polyethylene terephthalate 14 parts, 13 parts of Polyethylene Glycol distearyl acid fat, dimethyl fumarate 12 parts, bagasse 34 parts, linear low density polyethylene 23 parts, Exocarpium Litchi 9 parts, Ramulus Luffae 9 parts, Vermiculitum 10 parts, Pericarpium Citri Reticulatae 36 parts, sorbic acid formicester 24 parts, Oleum Brassicae campestris 7 parts, acid additive 16 parts, viscosity auxiliary agent 12 parts;
Described acid additive includes citric acid 12 parts, sorbic acid 12 parts, oxalic acid 6 parts, salicylic acid 6 parts;
Described viscosity auxiliary agent includes polyimides 19 parts, resorcinol-formaldehyde resin 16 parts, xylene formal dehyde resin 11 parts.
Various raw material pulverizing are mixed, then utilizes the wood-plastic board processing method of routine namely to obtain the PVC wood plastic material of the present invention.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described. Skilled person will appreciate that of the industry; the present invention is not restricted to the described embodiments; described in above-described embodiment and description is that principles of the invention is described; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements both fall within the claimed scope of the invention. Claimed scope is defined by appending claims and equivalent thereof.
Claims (2)
1. a PVC wood plastic material, it is characterized in that, it is made up of the raw material of following weight portion: PVC powder 41-49 part, quick lime 13-18 part, Lapis Micae Aureus 5-10 part, poly butylene succinate 8-14 part, polyethylene terephthalate 8-14 part, Polyethylene Glycol distearyl acid fat 6-13 part, dimethyl fumarate 9-12 part, Plant fiber's 22-34 part, linear low density polyethylene 18-23 part, Exocarpium Litchi 3-9 part, Ramulus Luffae 3-9 part, Vermiculitum 6-10 part, Pericarpium Citri Reticulatae 25-36 part, sorbic acid formicester 16-24 part, Oleum Brassicae campestris 3-7 part, acid additive 11-16 part, viscosity auxiliary agent 7-12 part,
Described acid additive includes citric acid 5-12 part, sorbic acid 5-12 part, oxalic acid 2-6 part, salicylic acid 2-6 part;
Described viscosity auxiliary agent includes polyimides 8-19 part, resorcinol-formaldehyde resin 7-16 part, xylene formal dehyde resin 5-11 part.
2. a kind of PVC wood plastic material as claimed in claim 1, it is characterised in that described Plant fiber includes following one or more: wood powder, cotton stalk, wheat stalk, rice straw, rice husk, bagasse, reed rod, rape stalk.