CN105615174B - A kind of parasol with charge function - Google Patents
A kind of parasol with charge function Download PDFInfo
- Publication number
- CN105615174B CN105615174B CN201610152147.1A CN201610152147A CN105615174B CN 105615174 B CN105615174 B CN 105615174B CN 201610152147 A CN201610152147 A CN 201610152147A CN 105615174 B CN105615174 B CN 105615174B
- Authority
- CN
- China
- Prior art keywords
- umbrella
- photovoltaic film
- charge function
- umbrella cover
- parasol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of parasol with charge function, belong to the technical field of parachute kit.Parasol of the present invention with charge function, including umbrella handle, scalable umbrella frame, movable umbrella stand and umbrella cover, the umbrella stand is laid in the top of the umbrella frame and the umbrella cover is arranged on the umbrella stand, and the umbrella handle is arranged on the bottom of the umbrella frame；The solar energy can be converted into the photovoltaic film of electric energy by being coated with the outer surface of the umbrella cover, be provided with transparent protective film on the photovoltaic film, the area of the photovoltaic film is at least the 1/3 of the umbrella cover area.The photovoltaic film structural mechanical property of the parasol of the present invention is good and photovoltaic performance is stable, and the environment sufficient especially suitable for outdoors sunlight can be convenient for real time chargings such as smart mobile phone and tablet personal computers.
Description
Technical field
The present invention relates to the technical field of parachute kit, it is more particularly related to a kind of sun with charge function
Umbrella.
Background technology
With internet and the booming and people's living standards continue to improve of IT technologies, smart mobile phone, flat board
The use of the handheld electric products such as computer is also increasingly popularized, but carrying due to limited battery capacity and people's use intensity
Height, can usually be run into when people travel, worked out of doors electronic product without electricity and charge difficulty the problem of, it is but outdoor past
Toward the sunlight for having abundance, especially women utilizes the parasol with charge function for sun-proof generally big city carrying parasol
The electric energy that required by electronic product is changed into using the luminous energy of sunshine is one of approach of solution outdoor electronic product charging problems,
But be generally only that solar panel is mounted on umbrella cover part surface in the prior art, the area not only effectively utilized is small
And mounting structure is unreliable is easily destroyed, it is difficult to popularization and application.
The content of the invention
In order to solve above-mentioned technical problem of the prior art, it is an object of the invention to provide one kind to have charge function
Parasol.
A kind of parasol with charge function, including umbrella handle, umbrella frame, umbrella stand and umbrella cover, the umbrella stand are laid in described
The top of the umbrella frame and umbrella cover is arranged on the umbrella stand, the umbrella handle is arranged on the bottom of the umbrella frame；Its feature
It is：Coated with the photovoltaic film that the solar energy can be converted into electric energy, the photovoltaic film on the outer surface of the umbrella cover
On be provided with transparent protective film, the area of the photovoltaic film is at least the 1/3 of the umbrella cover area；It is provided with the umbrella handle
Battery and controller.
Wherein, the area of the photovoltaic film is more preferably at least the 1/2 of the umbrella cover area, it is highly preferred that the umbrella cover
Whole outer surface on be coated with photovoltaic film.
Wherein, the umbrella frame be scalable umbrella frame, the umbrella stand be movable umbrella stand.
Wherein, 5V, 1A discharge and recharge USB interface are provided with the battery.
Wherein, the photovoltaic film is using Nitrogen trifluoride as reacting gas, using Al-Sn-Se composite target materials as negative electrode, using anti-
Sputtering method is answered to be prepared.The thickness of the photovoltaic film is 0.3 ~ 1.2 μm, preferably 0.5 ~ 1.0 μm.
Wherein, in the composite target material Se mass percent be 10.0 ~ 12.0wt%, Al mass percent be 1.0 ~
5.0wt%, surplus Sn.
Parasol of the present invention with charge function has the advantages that compared with prior art：
The photovoltaic film structural mechanical property of the parasol of the present invention is good and photovoltaic performance is stable, especially suitable for open air
Sun-drenched environment can be convenient for real time chargings such as smart mobile phone and tablet personal computers.
Brief description of the drawings
Fig. 1 is the structural representation of the parasol of the present invention with charge function.
Fig. 2 is the cross-sectional structure schematic diagram of umbrella cover of the present invention.
Embodiment
The parasol of the present invention with charge function is further elaborated below with reference to specific embodiment,
To help those skilled in the art to have more complete, accurate and deep understanding to inventive concept of the invention, technical scheme.
As shown in Figure 1-2, the parasol of the present invention with charge function, including umbrella handle 1, scalable umbrella frame 2, work
Dynamic umbrella stand 3 and umbrella cover 4, the movable umbrella stand 3 is laid in the top of the scalable umbrella frame 2 and the umbrella cover 4 is arranged on institute
State on movable umbrella stand 3, the umbrella handle 1 is arranged on the bottom of the umbrella frame 2.Being coated with the outer surface of the umbrella cover 4 to incite somebody to action
The solar energy is converted into the photovoltaic film 5 of electric energy, transparent protective film 6 is provided with the photovoltaic film 5, in order to improve photoelectricity
The power of conversion, preferably the photovoltaic film 5 be covered with the whole umbrella cover 4；Battery 7 is provided with the umbrella handle 1
With controller 8,5V, 1A discharge and recharge USB interface is provided with the battery, it is convenient to the hand such as mobile phone or tablet personal computer
Holding equipment electrically connects.In order to improve the adhesion between photovoltaic film and umbrella cover and not change the outward appearance of parasol, the present invention
The photovoltaic film has abandoned the amorphous silicon membrane of routine, and use can the direct photovoltaic of sputtering sedimentation at low temperature in umbrella cover
Film.In the present embodiment, the transparent protective film can use good weatherability transparent membrane, its can prevent vapor and
The infiltration of oxygen etc. can prevent the aging of photovoltaic film performance, ensure the stabilization of electricity conversion, so as to stabilization
Electric energy is provided.In the present invention, the controller module includes being used to control photovoltaic film by electrical power storage in battery
Solar absorption contactor.In the present invention, photovoltaic film produces DC current, direct current circulation after receiving sunshine irradiation
Crossing controller will be stored in electric energy input battery, and the electric energy of storage can be supplied to mobile phone by the battery by USB interface
Or the handheld device such as tablet personal computer charging.
Embodiment 1
In the present embodiment, the photovoltaic film is using Nitrogen trifluoride as reacting gas, using Al-Sn-Se composite target materials as the moon
Pole, it is prepared using reactive sputtering.Se mass percent is 10.0 ~ 12.0wt%, Al quality in the composite target material
Percentage is 1.0 ~ 5.0wt%, surplus Sn.The flow of reacting gas Nitrogen trifluoride is 5 ~ 20 sccm during sputtering, as preferred
Ground, in order to ensure the uniformity of doping, Ar is also provided as current-carrying gas, the flow of the current-carrying gas is 10 ~ 1000 sccm,
Preferably 50 ~ 200 sccm；The temperature of umbrella cover is 20 ~ 100 DEG C during sputtering, and the sputtering power of target is 50 ~ 200 W, and is
Ensure the uniformity of sputtering, to place the pedestal of umbrella cover can be rotated.In this embodiment, the thickness of the photovoltaic film is
0.3 ~ 1.2 μm, preferably 0.5 ~ 1.0 μm.Photovoltaic film and umbrella cover of the present invention（Nylon or terylene）Adhesion not
Less than 10 N/cm, carrier concentration is not less than 2.0 × 1020, photoelectric properties are good.Table 1 gives embodiment sample and conduct
The preparation condition of comparative sample.Table 2 shows embodiment sample and the performance parameter as comparative sample.
Table 1
Table 2
Embodiment 2
In the present embodiment, the transparent protective film is the transparent membrane of good weatherability, and it is by following resin combination
Thing is prepared；The composition includes 1.0 ~ 10.0wt% fine titanium dioxide powder, 15.0 ~ 25.0wt% polybutenyl succinic
Acid esters（Molecular weight is 2000 ~ 3000）, 1.0 ~ 1.5wt% dilauryl thiodipropionate, 0.5 ~ 1.0wt% tetraalkoxy silicon
The aminoalkyl trialkoxy silane of alkane, 0.5 ~ 1.0wt%, and the polyflon of surplus.It is described transparent using conventional
Extrusion blowing be prepared, the thickness of the film is 5 ~ 20 μm, preferably 10 ~ 20 μm.The resin combination passes through
Batch mixer is well mixed, and is processed to obtain pellet by screw extruder, and processing temperature is 250 ~ 280 DEG C, then using blowing
Film machine carries out blown film, and temperature is 220 ~ 230 DEG C.Table 3 gives embodiment sample and the raw material as comparative sample forms
（Thickness is 10 μm.Table 4 shows embodiment sample and the performance parameter as comparative sample.
The wt% of table 3, surplus are polytetrafluoroethylene (PTFE)
Table 4
For the ordinary skill in the art, present invention specific implementation is not subject to the restrictions described above, as long as
The improvement of the various unsubstantialities of inventive concept and technical scheme of the present invention progress is employed, or it is not improved by the present invention's
Design and technical scheme directly apply to other occasions, within protection scope of the present invention.
Claims (6)
1. a kind of parasol with charge function, including umbrella handle, umbrella frame, umbrella stand and umbrella cover, the umbrella stand are laid in the umbrella
The top of the bone and umbrella cover is arranged on the umbrella stand, the umbrella handle is arranged on the bottom of the umbrella frame；Its feature exists
In：The solar energy can be converted into the photovoltaic film of electric energy by being coated with the outer surface of the umbrella cover, on the photovoltaic film
Transparent protective film is provided with, the area of the photovoltaic film is at least the 1/3 of the umbrella cover area；Storage is provided with the umbrella handle
Battery and controller, 5V, 1A discharge and recharge USB interface are provided with the battery；The umbrella cover is nylon or terylene, is placed
The pedestal of umbrella cover can rotate, and the temperature of umbrella cover is 80 ~ 100 DEG C during sputter, and the photovoltaic film is using Nitrogen trifluoride as reaction gas
Body, using Al-Sn-Se composite target materials as negative electrode, it is prepared using reactive sputtering；And Se quality in the composite target material
Percentage is 10.0 ~ 12.0wt%, Al mass percent is 1.0 ~ 5.0wt%, surplus Sn；The transparent protective film is by following
Resin combination is prepared, and the composition includes 1.0 ~ 10.0wt% fine titanium dioxide powder, 15.0 ~ 25.0wt% poly- fourth
Alkenyl succinate acid esters, 1.0 ~ 1.5wt% dilauryl thiodipropionate, 0.5 ~ 1.0wt% tetraalkoxysilane, 0.5 ~ 1.0wt%
Aminoalkyl trialkoxy silane, and the polyflon of surplus.
2. the parasol according to claim 1 with charge function, it is characterised in that：The area of the photovoltaic film is extremely
It is the 1/2 of the umbrella cover area less.
3. the parasol according to claim 1 with charge function, it is characterised in that：The whole outer surface of the umbrella cover
On be coated with photovoltaic film.
4. the parasol according to claim 1 with charge function, it is characterised in that：The umbrella frame is Telescopic umbrella
Bone, the umbrella stand are movable umbrella stand.
5. the parasol according to claim 1 with charge function, it is characterised in that：The thickness of the photovoltaic film is
0.3~1.2 μm。
6. the parasol according to claim 1 with charge function, it is characterised in that：The thickness of the film is 5 ~ 20
μm。