CN105601260B - A kind of water purification ceramics - Google Patents

A kind of water purification ceramics Download PDF

Info

Publication number
CN105601260B
CN105601260B CN201510990055.6A CN201510990055A CN105601260B CN 105601260 B CN105601260 B CN 105601260B CN 201510990055 A CN201510990055 A CN 201510990055A CN 105601260 B CN105601260 B CN 105601260B
Authority
CN
China
Prior art keywords
parts
oxide
nano
powder
water purification
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510990055.6A
Other languages
Chinese (zh)
Other versions
CN105601260A (en
Inventor
纪轶
张思学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Zhongsheng New Environmental Protection Technology Co ltd
Original Assignee
Guangdong Zhongsheng New Environmental Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Zhongsheng New Environmental Protection Technology Co Ltd filed Critical Guangdong Zhongsheng New Environmental Protection Technology Co Ltd
Priority to CN201510990055.6A priority Critical patent/CN105601260B/en
Publication of CN105601260A publication Critical patent/CN105601260A/en
Application granted granted Critical
Publication of CN105601260B publication Critical patent/CN105601260B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of water purification ceramics, which is characterized in that its raw material composition by weight is as follows：20 30 parts of tourmaline, 20 30 parts of medical stone, 15 20 parts of attapulgite, 20 30 parts of zeolite, 10 15 parts of magnesium aluminate spinel, 15 parts of nano aluminium oxide, 25 parts of nano magnesia, 14 parts of nano-titanium dioxide, 57 parts of samarium oxide, 14 parts of silver oxide, 15 parts of copper oxide, 15 parts of iron oxide, 68 parts of nano zine oxide, 6 10 parts of graphite powder, 15 parts of stainless steel fibre, 15 parts of zirconia powder, 13 parts of silicon nitride powder.

Description

A kind of water purification ceramics
Technical field
The present invention relates to field of environment protection, and in particular to a kind of water purification ceramics.
Background technology
Water is Source of life, and the life and water resource of the mankind is closely bound up.With people for environmental protection consciousness by Step is reinforced, and the requirement for water resource quality is also continuously improved.But the water resource of high quality is limited after all, people often need Existing water resource is handled.Therefore, how to obtain a kind of environmentally protective water-purifying material is that people continue to solve Problem.
Invention content
The present invention by adjusting ceramic material raw material form, on the one hand used tourmaline, medical stone, attapulgite and Zeolite etc. is used as primary raw material, while being added to the ingredients such as nano aluminium oxide, nano magnesia, nano-titanium dioxide, both ensures Ceramic material has higher water purification function, in turn ensures that material preparation process is easy, the characteristics such as widely used.
More particularly to a kind of environmentally friendly water purification ceramic material, which is characterized in that its raw material composition by weight is as follows：Tourmaline 20-30 parts, it is 20-30 parts of medical stone, 15-20 parts of attapulgite, 20-30 parts of zeolite, 10-15 parts of magnesium aluminate spinel, nano oxidized 1-5 parts of aluminium, 2-5 parts of nano magnesia, 1-4 parts of nano-titanium dioxide, 5-7 parts of samarium oxide, 1-4 parts of silver oxide, copper oxide 1-5 Part, 1-5 parts of iron oxide, 6-8 parts of nano zine oxide, 6-10 parts of graphite powder, 1-5 parts of stainless steel fibre, 1-5 parts of zirconia powder, nitrogen 1-3 parts of SiClx powder
Environmental protection water purification ceramic material preparation process of the invention is easy：Raw material is weighed according to the rules, is carried out at ball milling after mixing Reason；Suitable quantity of water is added after ball milling, obtains slurry；By slurry shaping forming；It is then dried and firing is handled.
The present invention has the advantage that and effect：
1, the natural materials such as tourmaline, medical stone, attapulgite and zeolite are used as primary raw material, raw material sources are wide It is general, and there is release anion, radiation infrared, antibacterial, dechlorination, remove the characteristics such as noble metal.
2, by adding the raw materials such as nano aluminium oxide, nano magnesia, nano-titanium dioxide, by reasonable disposition, it contains Amount, improves the reactivity between raw material, while product can also be made to obtain under lower firing temperature (1000 DEG C or less) The characteristics such as higher intensity, on the one hand reduce production cost, even if while ensure contacted for a long time with water, will not burst Phenomena such as dissipating, cracking.
3, pottery is improved by its content of reasonable disposition by adding the raw materials such as zirconia powder, silicon nitride powder, graphite powder The characteristics such as wearability, the thermal shock resistance of porcelain.Samarium oxide, silver oxide etc. can enhance the bactericidal property and radiation far infrared of product Line characteristic.
4, by all kinds of raw material types and the appropriately selected proportioning of content, environmentally friendly water purification ceramic material of the invention can reach To following performance indicator：Anion burst size reaches 8500/cm3, 5~14 mum wavelengths far infrared irradiation rate that is averaged is up to 0.98 or more, normal temperature strength >=230MPa, thermal shock resistance (1100 DEG C of water coolings) >=10 times, Mohs' hardness >=7.
Specific implementation mode
Embodiment 1
A kind of environmental protection water purification ceramic material, it is specific to select the following raw material composition：20 parts of tourmaline, 30 parts of medical stone, bumps Stick soil 20 parts, 25 parts of zeolite, 10 parts of magnesium aluminate spinel, 5 parts of nano aluminium oxide, 2 parts of nano magnesia, 2 parts of nano-titanium dioxide, 6 parts of samarium oxide, 2 parts of silver oxide, 5 parts of copper oxide, 5 parts of iron oxide, 6 parts of nano zine oxide, 6 parts of graphite powder, stainless steel fibre 5 Part, 5 parts of zirconia powder, 2 parts of silicon nitride powder.
Embodiment 2
A kind of environmental protection water purification ceramic material, it is specific to select the following raw material composition：25 parts of tourmaline, 25 parts of medical stone, bumps Stick soil 18 parts, 25 parts of zeolite, 15 parts of magnesium aluminate spinel, 2 parts of nano aluminium oxide, 5 parts of nano magnesia, 2 parts of nano-titanium dioxide, 6 parts of samarium oxide, 2 parts of silver oxide, 5 parts of copper oxide, 5 parts of iron oxide, 7 parts of nano zine oxide, 8 parts of graphite powder, stainless steel fibre 5 Part, 5 parts of zirconia powder, 2 parts of silicon nitride powder.
The product obtained by above example can meet：Anion burst size reaches 8500/cm3, 5~14 μm Wavelength be averaged far infrared irradiation rate be up to 0.98 or more, normal temperature strength >=230MPa, thermal shock resistance (1100 DEG C of water coolings) >= 10 times, Mohs' hardness >=7.

Claims (2)

1. a kind of water purification ceramics, which is characterized in that its raw material composition by weight is as follows：20-30 parts of tourmaline, medical stone 20- 30 parts, 15-20 parts of attapulgite, 20-30 parts of zeolite, 10-15 parts of magnesium aluminate spinel, 1-5 parts of nano aluminium oxide, nano magnesia 2-5 parts, 1-4 parts of nano-titanium dioxide, 5-7 parts of samarium oxide, 1-4 parts of silver oxide, 1-5 parts of copper oxide, 1-5 parts of iron oxide, nanometer 6-8 parts of zinc oxide, 6-10 parts of graphite powder, 1-5 parts of stainless steel fibre, 1-5 parts of zirconia powder, 1-3 parts of silicon nitride powder.
2. a kind of water purification ceramics as described in claim 1, which is characterized in that its raw material composition by weight is as follows：Tourmaline 20 parts, 30 parts of medical stone, 20 parts of attapulgite, 25 parts of zeolite, 10 parts of magnesium aluminate spinel, 5 parts of nano aluminium oxide, nano magnesia 2 parts, 2 parts of nano-titanium dioxide, 6 parts of samarium oxide, 2 parts of silver oxide, 5 parts of copper oxide, 5 parts of iron oxide, 6 parts of nano zine oxide, stone 6 parts of ink powder, 5 parts of stainless steel fibre, 5 parts of zirconia powder, 2 parts of silicon nitride powder.
CN201510990055.6A 2015-12-24 2015-12-24 A kind of water purification ceramics Expired - Fee Related CN105601260B (en)