CN105586473B - A kind of continuous solution hardening device of Cu Cr Zr alloy bar materials or wire rod - Google Patents
A kind of continuous solution hardening device of Cu Cr Zr alloy bar materials or wire rod Download PDFInfo
- Publication number
- CN105586473B CN105586473B CN201610074956.5A CN201610074956A CN105586473B CN 105586473 B CN105586473 B CN 105586473B CN 201610074956 A CN201610074956 A CN 201610074956A CN 105586473 B CN105586473 B CN 105586473B
- Authority
- CN
- China
- Prior art keywords
- induction heating
- wire rod
- alloy bar
- bar materials
- solution hardening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of high-strength highly-conductive Cu Cr Zr alloy bar materials or the continuous solution hardening device and its technique of wire rod, belong to metal material processing technology of preparing field.Continuous solution hardening device is made up of drive system, temperature-controlling system, induction heating system, quenching cooling system and gas protection system.Induction heating system uses " Frequency Induction Heating+high-frequency induction heating " two-part mode of heating, is advantageous to prevent Cu Cr Zr alloy bar materials or wire rod from entering the decline of temperature during quenching area, improves quenching cooling effect.Using the continuous solution hardening device and PROCESS FOR TREATMENT Cu Cr Zr alloy bar materials or wire rod of the present invention, automaticity is high, and production efficiency is high, is particularly advantageous to the uniformity and uniformity for ensureing alloy bar material or wire rod quenching quality.
Description
Technical field
The present invention relates to a kind of continuous heat technology of high property copper alloy, belongs to metal material processing technology of preparing neck
Domain, in particular, provide a kind of continuous solution hardening devices and methods therefor of high-strength highly-conductive Cu-Cr-Zr alloy bar materials or wire rod.
Background technology
Cu-Cr-Zr alloys have high intensity and excellent conduction, heat conductivility, and anti-softening temperature is high, anti-wear performance
It is good, it is the critical material of high ferro power network contact line etc., especially speed per hour connects more than 350 km/h, 1000 more than A current-carrying capacity high ferros
Touch the optimal selection of wire material.
The typical production process about Cu-Cr-Zr alloyed contact lines is vacuum casting-hot extrusion both at home and abroad at present(Heat
Forging, hot rolling)- solution hardening processing-cold drawing-Ageing Treatment-cold drawing [ meter Xu Jun etc., a kind of chrome zirconium copper alloy and
It is prepared and processing method, Chinese invention patent, CN 10171876 A, 2010-06-02].This method technique is more ripe, fits
Technical scale production is closed, but resistance furnace is dissolved and Ageing Treatment, uniformity, the uniformity of product quality control due to using
Difficulty is big, especially in production over-long specification(Such as 2 ~ 3 more than km)Problem is more prominent during contact line product.Develop Cu-Cr-Zr
The continuous solution hardening handling process of alloy bar material or wire rod is the effective measures to solve the above problems.
Sensing heating continuous heat processing method is widely used in ferrous materials(Thin steel strip and wire rod etc.)With copper and copper alloy
The intermediate annealing of tubing and finished products are [for example, Zhao Hongjin etc., influence of the online induction annealing to TP2 copper pipe mechanical properties, warm
Processing technology, 2011,40 (4):136-138.].Continuous annealing has uniform in quality and uniformity is good, thermal treatment rate
It hurry up, the advantages that production efficiency is high.However, because Cu-Cr-Zr alloy solid solutions temperature is high(More than 900 DEG C), time length, blank is easy
Oxidation, quenching cooling velocity require high, and traditional continuous induction annealing device and process are dfficult to apply to Cu-Cr-Zr alloy bars
The solution hardening processing of material or wire rod.
The content of the invention
The problem of existing for existing Cu-Cr-Zr alloy bar materials or wire rod solution hardening heat treatment, the invention provides one
Continuous the solution hardening processing unit and technique of kind Cu-Cr-Zr alloy bar materials or wire rod, be advantageous to improve high-performance Cu-Cr-Zr
The quality of alloy bar material or wire rod.
The technical scheme is that:A kind of continuous solution hardening device of Cu-Cr-Zr alloy bar materials or wire rod, it is described
Quenching unit includes drive system, temperature-controlling system, induction heating system, quenching cooling system and gas protection system.
Further, the drive system is used to control Cu-Cr-Zr alloy bar materials or wire rod in continuous solution hardening process
In steadily move;
The temperature-controlling system connects induction heating system, controls induction heating system to be added simultaneously for collecting temperature
Heat;
The induction heating system is placed in the Cu-Cr-Zr alloy bar materials or wire rod the week side of boss, the induction heating system bag
Include intermediate frequency induction heating device and high-frequency induction heating apparatus;
The quenching cooling system is placed in the induction heating system end;
The gas protection system is used to provide inert gas shielding environment during continuous solution hardening.
Further, the intermediate frequency induction heating device is connected with the high-frequency induction heating apparatus, the Medium frequency induction
Heater is placed in Cu-Cr-Zr alloy bar materials or the opposite side of wire rod feed direction, the high-frequency induction heating apparatus are placed in
The side of feed direction;
The intermediate frequency induction heating device by frequency 1-10 kHz, rated power 30-200 kW medium frequency induction power supply with
Induction coil forms, and the high-frequency induction heating apparatus by frequency is 30-80 kHz, the power supply that rated power is 30-150 kW
Formed with induction coil, Frequency Induction Heating section length is 0.5-50m, and high-frequency induction heating section length is 30-1000mm.
Further, the drive system includes push rolls and carry-over pinch rolls, and the roll surface of the push rolls and carry-over pinch rolls is carved with
Groove;
The Cu-Cr-Zr alloy bar materials or gauge or diameter of wire are 6-10mm;The delivery speed of the drive system is 20-
10000mm/min。
Further, the temperature-controlling system include temperature thermocouple, Non-contacting Infrared Thermometer, temperature indicating device and
PLC temperature control modules;
It is 100-1200 DEG C that the control system, which controls the scope of temperature,.
Further, the quenching cooling system includes spraying cooling mode and direct Water cooling mode;
When the quenching cooling system is cooled down, water-carrying capacity 50-800L/h, and water-carrying capacity and Cu-Cr-Zr alloys
Radius squared, delivery speed and alloy temperature are directly proportional.
Further, the gas protection system includes quartz glass tube and inert gas is blown into device.
A kind of continuous solution hardening method of Cu-Cr-Zr alloy bar materials or wire rod, filled using above-mentioned continuous solution hardening
Put, it is characterised in that comprise the following steps:
(1)By a diameter of 6-100 mm, wt% containing 0.1-1.6 Cr, 0.02-0.20 wt% Zr, impurity<0.2wt%'s
Cu-Cr-Zr alloy bar materials or wire rod are placed on push rolls arrival end, and argon gas is passed through into gas protection system;
(2)Start temperature-controlling system and drive system, delivery speed is set as 20 ~ 10000 mm/min, heating in medium frequency area and
High-frequency heating area temperature is set as 900 ~ 1070 DEG C;
(3)The delivery speed of Cu-Cr-Zr alloy bar materials or wire rod is controlled, makes its any heating position in heating in medium frequency area
Holdup time be 5 ~ 30 min;
(4)Cu-Cr-Zr alloy bar materials or wire rod are completed by being sprayed water or being worn water quenching behind high-frequency induction heating area
Continuous solution hardening.
The invention has the advantages that:
1)Using the continuous solution hardening mode of sensing heating, automaticity is high, and production efficiency is high, is particularly advantageous to ensure
The uniformity and uniformity of Cu-Cr-Zr alloy bar materials or wire rod quenching quality;
2)Continuous solution hardening device uses " Frequency Induction Heating+high-frequency induction heating " two-part mode of heating, favorably
The decline of temperature, it is cold to improve quenching during preventing Cu-Cr-Zr alloy bar materials or wire rod from intermediate frequency induction zone into quenching area
But effect;
3)Continuous solution hardening device uses inert gas(Argon gas)Protection, effectively prevent Cu-Cr-Zr alloy bar materials or
Wire rod heating, the oxidation of insulating process.
Brief description of the drawings
Fig. 1 is the continuous solution hardening schematic device of a kind of Cu-Cr-Zr alloy bar materials proposed by the present invention or wire rod.
Embodiment
Technical scheme is described further with reference to the accompanying drawings and examples.
The continuous solution hardening device of Cu-Cr-Zr alloy bar materials or wire rod is by drive system, temperature-controlling system, sensing heating
System, quenching cooling system and gas protection system composition.
The drive system is made up of push rolls 1 and carry-over pinch rolls 5, for controlling Cu-Cr-Zr alloy bar materials or wire rod even
Steadily moved during continuous solution hardening, it is characterized in that groove is carved with roll surface position, be adapted to the mm bars of diameter 6 ~ 100 or wire rod
Clamping, delivery speed adjustable range is 20 ~ 10000 mm/min;
The temperature-controlling system is controlled by common temperature thermocouple or Non-contacting Infrared Thermometer and temperature display record, PLC
Warm module(6 and 7)Deng composition, for the temperature control during Cu-Cr-Zr alloy bar materials or the continuous solution hardening of wire rod, temperature
It is 100 ~ 1200 DEG C to spend scope;
The induction heating system is made up of intermediate frequency induction heating device 2 and high-frequency induction heating apparatus 3, and Medium frequency induction adds
Thermal is made up of the kHz of frequency 1 ~ 10, the kW of rated power 30 ~ 200 medium frequency induction power supply and induction coil, and high-frequency induction adds
Thermal is made up of the power supply and induction coil that frequency is 30 ~ 80 kHz, rated power is 30 ~ 150 kW, Frequency Induction Heating
Section length is 0.5 ~ 50 m, and high-frequency induction heating section length is 30 ~ 1000 mm.
The quenching cooling system 4 to Cu-Cr-Zr alloy bar materials or wire rod force cold using cool water shower device
But, water-carrying capacity is 50 ~ 800 L/h;The quenching cooling system 4 can also use direct Water cooling mode.
The gas protection system is by quartz glass tube and inert gas(Such as argon gas)Device for blowing forms, to prevent Cu-
The oxidation of Cr-Zr alloy bar materials or wire rod during solid solution.
Embodiment 1:The solution hardening of the mm Cu-1.2%Cr-0.16%Zr alloy bar materials of diameter 30
The continuous solution hardening device basic parameter for implementing the Cu-Cr-Zr alloy bar materials of this is:Temperature-controlling system is using non-
Contact infrared radiation thermometer and PLC temperature control modules;Intermediate frequency induction heating device is by the kHz of frequency 3, the kW of rated power 45 intermediate frequency
Induction power supply and induction coil form, high-frequency induction heating apparatus by frequency is 50 kHz, rated power is 45 kW power supply with
Induction coil forms, and Frequency Induction Heating section length is 2 m, and high-frequency induction heating section length is 50 mm;Using cool water shower
Device carries out pressure cooling to bar, and water-carrying capacity is 80 L/h;Cu-Cr-Zr alloy bar material solution treatment process is protected using argon gas
Shield.
The technique for implementing this is:
(1)By a diameter of 30 mm, containing 1.2 wt% Cr, 0.16 wt% Zr, impurity<0.2 wt% Cu-Cr-Zr alloys
Bar is placed in the drive system of arrival end, and argon gas is passed through into gas protection system;
(2)Start temperature-controlling system and drive system, delivery speed are set as 100 mm/min, heating in medium frequency area and high frequency add
Hot zone temperature is set as 960 DEG C;
(3)The delivery speed of Cu-Cr-Zr alloy bar materials is controlled, makes delay of its any heating position in heating in medium frequency area
Time is 20 min;
(4)Cu-Cr-Zr alloy bar materials or wire rod behind high-frequency induction heating area by carrying out jet hardening.
The uniformity and uniformity of solid solution state Cu-Cr-Zr alloy structure performances prepared by the technique are better than using resistance
Stove handles sample, and the technique can realize the continuous solution hardening processing of Cu-Cr-Zr alloys, substantially increase production efficiency.
Embodiment 2:The solution hardening of the mm Cu-1.0%Cr-0.08%Zr alloy bar materials of diameter 50
The continuous solution hardening device basic parameter for implementing the Cu-Cr-Zr alloy bar materials of this is:Temperature-controlling system is using non-
Contact infrared radiation thermometer and PLC temperature control modules;Intermediate frequency induction heating device is by the kHz of frequency 3, the kW of rated power 45 intermediate frequency
Induction power supply and induction coil form, high-frequency induction heating apparatus by frequency is 50 kHz, rated power is 45 kW power supply with
Induction coil forms, and Frequency Induction Heating section length is 2.4 m, and high-frequency induction heating section length is 80 mm;Sprayed using cooling water
It is 100 L/h that shower device carries out forced cooling water flow to bar;Cu-Cr-Zr alloy bar materials heat treatment overall process uses argon gas
Protection.
The technique for implementing this is:
(1)By a diameter of 50 mm, containing 1.0 wt% Cr, 0.08 wt% Zr, impurity<0.2 wt% Cu-Cr-Zr alloys
Bar is placed in the drive system of arrival end, and argon gas is passed through into gas protection system;
(2)Start temperature-controlling system and drive system, delivery speed are set as 80 mm/min, heating in medium frequency area and high frequency add
Hot zone temperature is set as 980 DEG C;
(3)The delivery speed of Cu-Cr-Zr alloy bar materials or wire rod is controlled, makes its any heating position in heating in medium frequency area
Holdup time be 30 min;
(4)Cu-Cr-Zr alloy bar materials or wire rod behind high-frequency induction heating area by carrying out jet hardening.
The uniformity and uniformity of solid solution state Cu-Cr-Zr alloy structure performances prepared by the technique are better than using resistance
Stove handles sample, and the technique can realize the continuous solution hardening processing of Cu-Cr-Zr alloys, substantially increase production efficiency.
Embodiment 3:The solution hardening of the mm Cu-0.6%Cr-0.04%Zr alloy wires of diameter 10
The continuous solution hardening device basic parameter for implementing the Cu-Cr-Zr alloy bar materials of this is:Temperature-controlling system is using non-
Contact infrared radiation thermometer and PLC temperature control modules;Intermediate frequency induction heating device is by the kHz of frequency 3, the kW of rated power 45 intermediate frequency
Induction power supply and induction coil form, high-frequency induction heating apparatus by frequency is 50 kHz, rated power is 45 kW power supply with
Induction coil forms, and Frequency Induction Heating section length is 1.5 m, and high-frequency induction heating section length is 30 mm;Sprayed using cooling water
It is 60 L/h that shower device carries out forced cooling water flow to bar;Cu-Cr-Zr alloy bar materials are heat-treated overall process and protected using argon gas
Shield.
The technique for implementing this is:
(1)By a diameter of 10 mm, containing 0.6 wt% Cr, 0.04 wt% Zr, impurity<0.2 wt% Cu-Cr-Zr alloys
Bar is placed in the drive system of arrival end, and argon gas is passed through into gas protection system;
(2)Start temperature-controlling system and drive system, delivery speed are set as 100 mm/min, heating in medium frequency area and high frequency add
Hot zone temperature is set as 950 DEG C;
(3)The delivery speed of Cu-Cr-Zr alloy bar materials or wire rod is controlled, makes its any heating position in the stagnant of heating zone
It is 15 min to stay the time;
(4)Cu-Cr-Zr alloy bar materials or wire rod behind high-frequency induction heating area by carrying out jet hardening.
The uniformity and uniformity of solid solution state Cu-Cr-Zr alloy structure performances prepared by the technique are better than using resistance
Stove handles sample, and the technique can realize the continuous solution hardening processing of Cu-Cr-Zr alloys, substantially increase production efficiency.
Claims (7)
- A kind of 1. continuous solution hardening device of Cu-Cr-Zr alloy bar materials or wire rod, it is characterised in that the quenching unit bag Include drive system, temperature-controlling system, induction heating system, quenching cooling system and gas protection system;The drive system includes push rolls and carry-over pinch rolls, for controlling Cu-Cr-Zr alloy bar materials or wire rod to be quenched in continuous solid solution Steadily moved during fire;The temperature-controlling system connects induction heating system, controls induction heating system to be heated simultaneously for collecting temperature;The induction heating system is placed in the Cu-Cr-Zr alloy bar materials or wire rod the week side of boss, during the induction heating system includes Frequency induction heating apparatus and high-frequency induction heating apparatus;The quenching cooling system is placed in the induction heating system end;The gas protection system is used to provide inert gas shielding environment during continuous solution hardening.
- 2. the continuous solution hardening device of a kind of Cu-Cr-Zr alloy bar materials according to claim 1 or wire rod, its feature It is, the intermediate frequency induction heating device is connected with the high-frequency induction heating apparatus, and the intermediate frequency induction heating device is by frequency Rate 1-10kHz, rated power 30-200kW medium frequency induction power supply and induction coil form, the high-frequency induction heating apparatus by Power supply and the induction coil composition that frequency is 30-80kHz, rated power is 30-150kW, Frequency Induction Heating section length are 0.5-50m, high-frequency induction heating section length are 30-1000mm.
- 3. the continuous solution hardening device of a kind of Cu-Cr-Zr alloy bar materials according to claim 1 or wire rod, its feature It is, the roll surface of the push rolls and carry-over pinch rolls is carved with groove;The Cu-Cr-Zr alloy bar materials or gauge or diameter of wire are 6- 100mm;The delivery speed of the drive system is 20-10000mm/min.
- 4. the continuous solution hardening device of a kind of Cu-Cr-Zr alloy bar materials according to claim 1 or wire rod, its feature It is, the temperature-controlling system includes temperature thermocouple, Non-contacting Infrared Thermometer, temperature indicating device and PLC temperature control modules;It is 100-1200 DEG C that the control system, which controls the scope of temperature,.
- 5. the continuous solution hardening device of a kind of Cu-Cr-Zr alloy bar materials according to claim 1 or wire rod, its feature It is, the quenching cooling system includes spraying cooling mode and direct Water cooling mode;When the quenching cooling system is cooled down, water-carrying capacity 50-800L/h, and water-carrying capacity and Cu-Cr-Zr alloy radiuses Square, delivery speed and alloy temperature it is directly proportional.
- 6. the continuous solution hardening device of a kind of Cu-Cr-Zr alloy bar materials according to claim 1 or wire rod, its feature It is, the gas protection system includes quartz glass tube and inert gas is blown into device.
- 7. a kind of continuous solution hardening method of Cu-Cr-Zr alloy bar materials or wire rod, using one of the claims 1-6 institutes The continuous solution hardening device stated, it is characterised in that comprise the following steps:(1) by a diameter of 6-100mm, containing 0.1-1.6wt%Cr, 0.02-0.20wt%Zr, impurity < 0.2wt% Cu-Cr- Zr alloy bar materials or wire rod are placed on push rolls arrival end, and argon gas is passed through into gas protection system;(2) start temperature-controlling system and drive system, delivery speed are set as 20~10000mm/min, heating in medium frequency area and high frequency Heating Zone Temperature is set as 900~1070 DEG C;(3) delivery speed of Cu-Cr-Zr alloy bar materials or wire rod is controlled, makes its any heating position in the stagnant of heating in medium frequency area It is 5~30min to stay the time;(4) Cu-Cr-Zr alloy bar materials or wire rod are completed continuous by being sprayed water or being worn water quenching behind high-frequency induction heating area Solution hardening.