CN1055775A - Chromate composite used for passivation of zine plated layer on metal body and application thereof - Google Patents
Chromate composite used for passivation of zine plated layer on metal body and application thereof Download PDFInfo
- Publication number
- CN1055775A CN1055775A CN 91102396 CN91102396A CN1055775A CN 1055775 A CN1055775 A CN 1055775A CN 91102396 CN91102396 CN 91102396 CN 91102396 A CN91102396 A CN 91102396A CN 1055775 A CN1055775 A CN 1055775A
- Authority
- CN
- China
- Prior art keywords
- passivation
- metal body
- plated layer
- zine
- olive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention has disclosed a kind of chromate metal surface treatment solution composition and with described liquid etch-proof olive colour passivation technology has been made on the zine plated layer on metal body surface, and this liquid is containing CrO
3, NaHSO
4, NaH
2PO
4Passivating solution in, add AgNO
30.08-0.2g/l, alkyl polyoxyethylene ether 0.04-0.1g/l.The corrosion resistance of the zine plated layer on metal body tool excellence after this liquid is made Passivation Treatment, bigger passivation thickness and sticking power, beautiful, thick and heavy olive-green color and luster, simultaneously, the work-ing life and the use range that has enlarged passivation technology of passivating solution have been prolonged, thereby, can in harsh environment, use.
Description
The present invention relates to a kind of chemical conversion treatment liquid and application thereof of metal plating, more particularly, relate to olive colour Passivation Treatment chromate composite and uses thereof of a kind of zine plated layer on metal body.
For improving the Corrosion Protection of zine plated layer on metal body, up to now, people have developed the surface treatment method of multiple zine plated layer on metal body.Open clear 59-31872 number as the Japanese Patent spy, and for example United States Patent (USP) 4,749, No. 418 and 4,591, in No. 416, all disclosed relevant surface treatment method.
The spy opens in clear 59-31872 number and discloses, and will add reductive agent, contain Cr
+ 6And Cr
+ 6The chromatedsolution of reduction resultant coat on the galvanized steel, can obtain Corrosion Protection preferably, United States Patent (USP) 4,749 provides the corrosion resistance that a kind of tool improved and the chromic salt coating composition and the coating process thereof of paint adhesion for No. 418.Wherein, described acidic aqueous compositions comprises the phosphoric acid salt and the fluoro zirconate of sexavalence and tervalent chromium.Do not wash with water and through using and the said composition of oven dry can generate 10-200mg/m
2Chromium coating.United States Patent (USP) 4,591, provide for No. 416 a kind of on zinc-nickel alloy plating with the aqueous acid solution and the plating cloth method thereof of the chromic salt of required color.
Yet the zinc-plating material of opening the metal coating surface disposal methods that discloses for clear 59-31872 number through the spy still has some deficits on corrosion resistance, and its incidence through white corrosion thing after the salt-fog test still reaches about 15-25%; United States Patent (USP) 4,749, the chromic salt coating that provides for No. 418 in thickness of coating and by the corrosion resistance of salt-fog test on also defectiveness still; United States Patent (USP) 4,591, though the certain thickness of the chromic salt coating tool that provides for No. 416 and through the corrosion resistance of salt-fog test, method therefor is an electrolytic process, used is admiro by the plating material, and its required color and the present invention have bigger difference.
One of purpose of the present invention is, a kind of olive colour passivation technology chromate composite of zine plated layer on metal body is provided, and this liquid has added AgNO in common chromic salt surface treatment liquid
3And peregal (alkyl polyoxyethylene ether) can successfully improve the interior external quality of coating through using this additive, thereby improves corrosion resistance greatly.Enlarged the technology use range and prolonged passivating dip work-ing life, alleviated pollution environment.
Another purpose of the present invention is, provide a kind of zine plated layer on metal body chromic salt olive colour passivation process, zine plated layer on metal body through this art breading, its surface generates chromate conversion coating, have the beautiful olive colour gloss of paint shape, good thickness, sticking power, corrosion resistance, thereby can be used in the harsh physical environment.
The olive colour chromate composite used for passivation of zine plated layer on metal body of the present invention consists of:
CrO
310-100g/l
NaHSO
45-50g/l
NaH
2PO
45-50g/l
AgNO
30.02-2g/l
Peregal
(alkyl polyoxyethylene ether) 0.01-1g/l
The preferred content of forming:
CrO
325-35g/l
NaHSO
415-20g/l
NaH
2PO
43-4g/l
AgNO
30.08-0.2g/l
Peregal 0.04-0.1g/l
The olive colour passivation technology of zinc coating chromic salt of the present invention is following realization:
To being coated with material through quilt zinc-plated, that the clear water that flows is washed with 3% HNO
3Polishing imposes passivation with chromate composite of the present invention again after washing, distillation washing, then secondary imposes sealing treatment with chromic salt after the clear water that flows is washed, and is drying to obtain required olive colour chromate conversion coating at last.
The passivation technology condition is again:
pH 1.5-1.9
Temperature 20-28 ℃
Time 30-90 second
Sealing treatment agent of the present invention is CrO
30.5-1 grams per liter
Temperature is: 60-65 ℃.Time: 1-5 second.
Feature of the present invention particularly in additive is:
AgNO
30.02-2 grams per liter preferred ingredients content is: 0.08-0.2 grams per liter nonionic surface active agent-alkyl polyoxyethylene ether (peregal) 0.01-1 grams per liter, preferred ingredients content 0.04-0.1 grams per liter.
Among the present invention, with CrO
3And NaHS
4Basic composition as preparation of passivation solution.Wherein, CrO
3Chromium ion in the passive film component is provided.Cr
+ 6And Cr
+ 6The major ingredient of having formed passive film, and the content of their compound, ratio, structures shape the thickness of passive film, outward appearance, color and luster and corrosion resistance thereof.NaHSO
4HSO then is provided
--
4And HSO
-- 4Ion its role is to activate passivation reaction, constantly gives newborn passive film with activation potential energy, passivation reaction is continuously taken place, thereby obtain the passive film of desired thickness.
Among the present invention, add NaH
2PO
4In order to generating graminaceous primary passivation film, but its green is more shallow, and gloss is relatively poor.
With CrO
3, NaHSO
4And NaH
PO
4When making Passivation Treatment, poor because the passivating solution surface tension is big to the wetting property of zinc layer, make the generation of zinc laminar surface each several part passivation reaction and carry out the speed inequality, cause being easy to generate growing dim and stick with paste the passive film of outward appearance.Especially in the passivation of zinc-plated fastening piece or complicated part in addition, this kind phenomenon is more obvious, does not have passive film sometimes even at screw thread and recess.
Add AgNO
3With average in addition after, tensio-active agent in this additive has effects such as good infiltration, diffusion, solubilising, thereby reduced the interfacial tension between passivation reaction phase (solid phase) and (liquid phase), the sunk part of screw thread depths or complicated shape is soaked into fully, passivation reaction comprises that on whole part surface in addition the internal thread sunk part takes place rapidly.Simultaneously, the effective ion concentration of reaction interface sharply descends in the reaction process, because surface tension is little, the ion in the solution can move to the interface each several part rapidly, equably and replenish, and makes reaction be able to continuously, carry out equably.Like this, introduce these two doses after, even complicated zinc-plated part in addition also can obtain complete, uniform olive colour passive film.Its result, (1) makes original gloss relatively poor, even the passive film stuck with paste of growing dim become seemed one deck oil add like beautiful olive-green; (2) passivation film is thickened; (3) improved sticking power; (4) improved corrosion resistance.
In addition, the AgNO in the additive
3In Ag
+The current potential calibration in the redox reaction of passivation, participates in the composition of film with the form of the oxide compound of silver.Chocolate silver oxide component makes that to be that lighter grass green passive film becomes originally denseer thicker in the film.AgNO in passivating solution
3Content when reaching preferable the requirement, can obtain satisfied olive-green.Its color and luster depth, green deep or light, also can suitably regulate by the control of this agent according to the processing request of product.
Moreover, there is not the AgNO of interpolation
3With the olive colour passivating dip of peregal in use for some time, when passive film can't meet the quality requirement, be difficult to be adjusted, and often adopt the method for the new liquid of reprovision by adding the partition component again, recover the passivation quality.Add AgNO
3After the peregal agent, make the easy to adjust feasible of passivating solution.When the passive film attenuation becomes light, during downgrade, can take effect as long as suitably add these two doses.All the other components also are easy to add by rule of thumb.Like this, promptly stablize the passive film quality, need not often more renew liquid again, made things convenient for operation, alleviated environmental pollution.
Also has AgNO
3Enlarged the technology use range with the introducing of peregal.It is not only applicable to big part and hangs zinc-plated part, is applicable to smallclothes barrel plating zinc part yet.Big part hangs zinc-plated part can the single-piece passivation, and passivation is after the sealing treatment hot blast drying, or blows away water stain back and dry, its drying temperature≤65 ℃.Smallclothes barrel plating zinc part can be adorned blue passivation, floods centrifugal drying after the passivation in≤65 ℃ of sealing treatment liquid.
In sum, by at passivating solution (CrO
3And HaHSO
4) the middle additive NaH that adds
2PO
4, especially add additive A gNO
3Behind peregal, not only can improve the visual appearance of zinc coating-control effectively, regulate gloss, the color depth of the olive colour passive film of zinc coating effectively; And can improve passive film inner quality-increase thickness and thickness sense effectively; Improve film adhesion; Improve corrosion resistance; Simultaneously, reduce environmental pollution the work-ing life that has prolonged passivating solution and enlarged the use range of passivation technology.
The present invention has been used for the fastening piece of the olive colour passive surface processing of car part zinc coating and the part of multiple this technology of need is handled.It handles the standard that quality has met or exceeded 150452-1981 " chromate conversion coating on zinc coating and the zinc coating " and TLVW217 " galvanizing coating material requirements ".
Below, with reference to embodiment, further specify the present invention.
Embodiment 1
Material: the thick 2mm of 45# steel plate, galvanized layer thickness 20 μ.
Preparation of passivation solution is CrO
320g/l, NaHSO
415g/l, NaH
2SO
44g/l, AgNO
30.2g/l, peregal 0.1g/l.To do the neutral salt test through the passive film of this solution-treated, test conditions is NaCl solution (5%), pH value 6.7-7.2, and 35 ± 2 ℃ of the temperature inside the box impose continuous spraying.Then as seen, through 5 all after dates of salt-fog test, rete is still glossy, 10 all after dates, and except that color and luster was thin out, its rete was intact, no zinc layer corrosion phenomenon.(seeing Table one)
Comparative example 1
The test conditions same as embodiment 1 only do not have AgNO in the prescription
3And peregal, then behind neutral salt spray test, passive film promptly faded since the period 3, to period 5 redgreen substantially.Illustrate that this moment, passive film did not exist basically, zinc coating begins to occur corrosion phenomenon.After, corrosion is accelerated, to the 8th cycle heavy corrosion.(seeing Table one).
Embodiment 2
Preparation of passivation solution is: CrO
325g/l, NaHSO
415g/l, NaH
2PO
43g/l, AgNO
30.2g/l, the passive film of handling through this passivating solution is done the test of film adhesion.(seeing Table two)
Comparative example 2
Preparation of passivation solution is for to remove AgNO in above-mentioned prescription
3The passive film of handling through this passivating solution is done the film adhesion test.(seeing Table two)
By table two as seen, add AgNO
3The friction number of times is brought up to 14 times from 6 times.
Embodiment 3
Add peregal 0.1g/l in as the prescription of comparative example 2, the passive film of handling through this passivating solution is done the film adhesion test, it the results are shown in Table two.
Embodiment 4
In prescription, add AgNO as embodiment 3
30.2g/l, the passive film of handling through this passivating solution is done the film adhesion test, it the results are shown in table two.
By table two as seen, the interpolation of peregal is brought up to the friction number of times 20 times, and the interpolation of peregal and AgNO can further improve the friction number of times and reaches 37 times more than.
Embodiment 5
To galvanized layer thickness is 65 of 20 μ
#The car part pad that the Mn steel is done is made olive colour Passivation Treatment.Its prescription, processing condition see Table three, the result, thick and heavy, paint shape olivaceous pad.Through neutral salt spray test, qualified to press TLVW217 " galvanizing coating material requirements " standard check.
Embodiment 6
Car part one nut is made olive colour Passivation Treatment, and its material is a carbon steel, and galvanized layer thickness 15 μ adorn blue passivation behind the barrel plating zinc.
Passivation and processing condition see Table three.Passivation Treatment result gets the olive colour product of outward appearance.Its neutral salt spray test is qualified through pressing TLVW217 " galvanizing coating material requirements " standard check 240 hours.The abrasivity of its crevice corrosion performance is " 0 ".
Embodiment 7
Car part-vapor pipe hanger bracket is made Passivation Treatment.Its material is a carbon steel, zinc-plated thickness 〉=15 μ, and its passivation and operational condition see Table three.
Its passivation result gets the thick and heavy olivaceous product of outward appearance.Its neutral salt spray test is through examination, and 240 hours qualified.Its crevice corrosion performance abrasivity is " 0 ".
Embodiment 8
Car part-assembling bolt is made Passivation Treatment.Its material carbon steel, zinc-plated thickness 〉=15 μ.Its passivation and operational condition see Table three.
Outer, the interior appearance quality of product is with embodiment 5 after its passivation.
Embodiment 9
Car part-gear box support is made Passivation Treatment.Its material is a carbon steel, zinc-plated thick 〉=15 μ.Its passivation and operational condition see Table three.
Outside after its passivation, inner quality and embodiment 7 are together.
Embodiment 10
To car part-F
4The metal lining material is, external diameter is the steel ring of 20mm, and the inner ring lining is with tetrafluoroethylene and graphite linings after the copper facing.Impose olive colour passivation after the outer ring is zinc-plated.
Its passivation and operational condition see Table three.Its passivation result and embodiment's 5 is same.
Table one salt-fog test comparison sheet
| Test period | Time (hour) | Embodiment 1 | Comparative example 1 |
| Passive film corrosion situation | |||
| 1 | 24 | Be the bright olive colour white corrosion thing of not seeing | Color and luster does not become, and does not see the white corrosion thing |
| 2 | 48 | The same | Grow dim and do not see the white corrosion thing in the surface |
| 3 | 72 | Rete gloss is constant does not substantially see the white corrosion thing | Color and luster is slightly thin out does not see the white corrosion thing |
| 4 | 96 | The same | Color and luster is thin out does not see the white corrosion thing |
| 5 | 120 | Rete is still glossy does not see the white corrosion thing | The basic redgreen denier white point in surface |
| 6 | 144 | The rete tarnish is not seen the white corrosion thing | The trace white point |
| 7 | 168 | The same | White point is more |
| 8 | 190 | The same | White point is serious |
| 9 | 216 | The rete color and luster is thin out does not see the white corrosion thing | The same |
| 10 | 240 | The same | The same |
Table two film adhesion test
| Example | Preparation of passivation solution | The friction number of times |
| Comparative example 2 | CrO 3 25g/l NaHSO 4 15g/l NaH 2PO 4 3g/l | 6 |
| Embodiment 2 | CrO 3 25g/l NaHSO 4 15g/l NaH 2PO 4 3g/l AgNO 3 0.2g/l | 14 |
| Embodiment 3 | CrO 3 25g/l NaHSO 4 15g/l NaH 2PO 43g/l peregal 0.1g/l | 20 |
| Embodiment 4 | CrO 3 25g/l NaHSO 4 15g/l NaH 2PO 4 3g/l AgNO 30.2g/l peregal 0.1g/l | 37 |
Annotate: 1. adhesion test: the GB9791-88 standard
2. friction time numerical value is as the criterion for wearing up to basic dew dezincify matrix.
Claims (4)
1, the olive colour passivation of a kind of zine plated layer on metal body is with containing CrO
310-100 grams per liter, NaHSO
45-50 grams per liter, NaH
2PO
4The chromate composite of 5-50 grams per liter is characterized in that, in described chromate composite, comprises AgNO again
30.02-2 grams per liter and alkyl polyoxyethylene ether 0.01-1 grams per liter.
2, the olive colour chromate composite used for passivation of zine plated layer on metal body as claimed in claim 1 is characterized in that, described AgNO
3Be the 0.08-0.2 grams per liter.
3, the olive colour chromate composite used for passivation of zine plated layer on metal body as claimed in claim 1 is characterized in that, described alkyl polyoxyethylene ether is the 0.04-0.1 grams per liter.
4, the olive colour chromate composite used for passivation of zine plated layer on metal body as claimed in claim 1 is characterized in that, this chromate composite is used for the anticorrosive olive colour Passivation Treatment of zine plated layer on metal body.