CN105568273A - Anti-corrosion liquid for anti-corrosion treatment on surface of metal die - Google Patents
Anti-corrosion liquid for anti-corrosion treatment on surface of metal die Download PDFInfo
- Publication number
- CN105568273A CN105568273A CN201511011796.1A CN201511011796A CN105568273A CN 105568273 A CN105568273 A CN 105568273A CN 201511011796 A CN201511011796 A CN 201511011796A CN 105568273 A CN105568273 A CN 105568273A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion
- metal die
- preservative solution
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of die processing, in particular to anti-corrosion liquid for anti-corrosion treatment on the surface of a metal die. The anti-corrosion liquid is prepared from 10 parts of ethyl acetate, 15 parts of diethanol amine, 10 parts of dioxane, 5 parts of dilute acetic acid, 1 part of anthocyan, 10 parts of methyl alcohol and 40 parts of water. According to the anti-corrosion liquid used in a surface anti-corrosion treatment method, the formula is designed reasonably, especially a small amount of anthocyan is added, so that the anti-corrosion treatment efficiency of the anti-corrosion liquid is obviously improved, and the anti-corrosion performance of the metal die is obviously improved.
Description
Technical field
The present invention relates to mold machining technology field, specifically relate to a kind of metal die surface anticorrosive process preservative solution.
Background technology
Metal die, when machine-shaping, needs to carry out surface anticorrosive process to it.Mainly there is complex treatment process in the process of existing metal die surface anticorrosive, processing efficiency is low, the defects such as rotproofing is of poor quality.
Summary of the invention
For the technical problem existed in prior art, the object of the present invention is to provide a kind of metal die surface anticorrosive process preservative solution, for achieving the above object, present invention employs following technical scheme:
A kind of metal die surface anticorrosive process preservative solution, is made up of 10 parts of ethyl acetate, 15 parts of diethanolamine, 10 parts of dioxane, 5 parts of dilute acetic acid, 1 part of anthocyanin, 10 parts of methyl alcohol and 40 parts of water.
Beneficial effect of the present invention shows:
1), the preservative solution that uses in surface anti-corrosion treatment method, its formulating of recipe is reasonable, particularly with the addition of a small amount of anthocyanin, can significantly improve the rotproofing efficiency of preservative solution, the antiseptic property of metal die is significantly improved.
2), the preparation method of preservative solution, by the method for progressively adding, by appropriate design order of addition(of ingredients), the solubility property between each material can not only be improved, the possibility of particle agglomeration can also be avoided, and the rotproofing efficiency of preservative solution is significantly improved.
3), surface anti-corrosion treatment method, operating procedure is simple, soaks by adding rational preservative solution, and the formula of appropriate design preservative solution and the preparation method of preservative solution, thus significantly improves anti-corrosive treatment quality and the efficiency of metal die.
Embodiment
Below with reference to embodiment, the present invention is described in detail.But; embodiment content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from the design of invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
One, the composition of preservative solution
10 parts of ethyl acetate, 15 parts of diethanolamine, 10 parts of dioxane, 5 parts of dilute acetic acid, 1 part of anthocyanin, 10 parts of methyl alcohol and 40 parts of water.
Two, the preparation method of preservative solution is:
First in container, add 10 parts of ethyl acetate, 15 parts of diethanolamine and 15 parts of water, stir 5 minutes; Then slowly add 5 parts of dilute acetic acid, limit edged stirs, and stirs 10 minutes after interpolation; Then slowly add 10 parts of dioxane and 15 parts of water, limit edged stirs, and stirs 5 minutes after interpolation; Then slowly add 1 part of anthocyanin, limit edged stirs, and stirs 5 minutes after interpolation; Finally add 10 parts of methyl alcohol and 10 parts of water fast, stir 20 minutes.
Three, metal die surface anticorrosive process preservative solution
Step 1., use that absorbent cotton is sticky to be got ethyl acetate-ethanol mixing solutions and clean metal die surface, then with dry cloth, metal die to be dried, coolly puts 1 day;
Step 2., adopt ion implantation mode to inject zirconium phosphate, silicon-dioxide, chromic acid chromium and Sodium Silicofluoride to form insoluble altogether network layers;
Step 3., metal die put into the preservative solution being heated to 55 DEG C in advance and soaks 30 minutes;
Step 4., pull rear water out and rinse until the pH value of wash-down water returns to neutrality, dry at 200 DEG C.
Claims (1)
1. a metal die surface anticorrosive process preservative solution, is characterized in that being made up of 10 parts of ethyl acetate, 15 parts of diethanolamine, 10 parts of dioxane, 5 parts of dilute acetic acid, 1 part of anthocyanin, 10 parts of methyl alcohol and 40 parts of water.