CN105563583A - 一种高阻燃型木材 - Google Patents
一种高阻燃型木材 Download PDFInfo
- Publication number
- CN105563583A CN105563583A CN201510948059.8A CN201510948059A CN105563583A CN 105563583 A CN105563583 A CN 105563583A CN 201510948059 A CN201510948059 A CN 201510948059A CN 105563583 A CN105563583 A CN 105563583A
- Authority
- CN
- China
- Prior art keywords
- wood
- timber
- flame
- retardant
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高阻燃型木材,其主要通过在木材上添加了阻燃剂使得木材具有良好的阻燃性,具体步骤如下:先制备由聚磷酸钠、硼酸锌、重铬酸钾、二氯甲烷、钼酸钠、十二烷基磺酸钠组成的阻燃剂;随后将制备好的阻燃剂完全溶解到树脂液中,采用加压法将木材充分浸渍在树脂液中处理;一段时间后取出木材进行干燥。本发明工艺简单方便,经过加压浸渍处理后的木材稳定性显著提高,采用无卤环保阻燃剂,不但具有很好的阻燃抑制性能而且环保、防腐、防蛀性能好,使用安全方便,阻燃性达到难燃级别。
Description
技术领域
本发明涉及木材处理技术领域,特别是涉及一种高阻燃型木材。
背景技术
我国人工林面积居世界第一,目前已超过0.53亿公顷,主要有杨树、杉木、马尾松、松树等,这些木材普遍存在的材质软、密度低、变形大、加工性能差等弱点,在某些方面限制了他们的应用。通过木材增加密实处理可以解决上述问题;同事木材属于可燃材料,并且容易腐朽和发生变形,因此,对木材还需予以阻燃、防腐等方面的处理,这对赋予木材新功能、拓宽木材新应用领域具有重要的现实意义。
随着人们对木材质量的要求越来越高越来越全面,多功能性的木材改性技术也是木材改性发展的主要方向,不仅仅是材性的提高,同时还应该使木材具备防腐性能和阻燃等性能。目前,改性木的种类很多,虽说部分改性木具有一定的阻燃性能,但是还远不能适应阻燃使用的需求。要想真正的达到性能的要求,还需进一步的进行阻燃处理,工序繁琐,还有可能损失改性木的部分性能。一般的阻燃剂处理木材后,还容易流失,不仅达不到长久阻燃的功能,而又对环境也造成了污染。
发明内容
为了解决上述问题,本发明主要提供一种高阻燃型木材,该木材通过表面添加阻燃剂,密度增大,强度提高,具有良好的阻燃性。
本发明通过以下技术方式实现:一种高阻燃型木材,其主要是通过在木材上添加了一种阻燃剂,具体步骤如下:先制备由聚磷酸钠、硼酸锌、重铬酸钾、钼酸钠、十二烷基磺酸钠组成的阻燃剂;随后将制备好的阻燃剂完全溶解到树脂液中,采用加压法将木材充分浸渍在树脂液中处理;一段时间后取出木材进行干燥。
进一步地,所述阻燃剂的组分为:按重量百分比计,聚磷酸钠25%-35%、硼酸锌15%-25%、重铬酸钾15%-25%、二氯甲烷10%-25%、钼酸钠2%-10%、十二烷基磺酸钠1-%-2%。
进一步地,所述木材浸渍在树脂液中的浸渍时间为25-75min。
本发明的有益效果是,与现代技术相比,本发明工艺简单方便,经过加压浸渍处理后的木材稳定性显著提高,采用无卤环保阻燃剂,不但具有很好的阻燃抑制性能而且环保、防腐、防蛀性能好,使用安全方便,阻燃性达到难燃级别。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
实施例一:
一种高阻燃型木材,主要是通过在木材上添加了一种阻燃剂,具体步骤如下:先制备阻燃剂,其各组分的百分数配比如下:聚磷酸钠30%、硼酸锌25%、重铬酸钾15%、二氯甲烷20%、钼酸钠8%、十二烷基磺酸钠2%;随后将制备好的阻燃剂完全溶解到树脂液中,采用加压法将木材充分浸渍在树脂液中处理;一段时间后取出木材进行干燥,所述木材浸渍在树脂液中的浸渍时间为30min。
实施例二:
一种高阻燃型木材,主要是通过在木材上添加了一种阻燃剂,具体步骤如下:先制备阻燃剂,其各组分的百分数配比如下:聚磷酸钠35%、硼酸锌15%、重铬酸钾24%、二氯甲烷15%、钼酸钠10%、十二烷基磺酸钠1%;随后将制备好的阻燃剂完全溶解到树脂液中,采用加压法将木材充分浸渍在树脂液中处理;一段时间后取出木材进行干燥,所述木材浸渍在树脂液中的浸渍时间为75min。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种高阻燃型木材,其特征在于,主要是通过在木材上添加了一种阻燃剂,具体步骤如下:先制备由聚磷酸钠、硼酸锌、重铬酸钾、二氯甲烷、钼酸钠、十二烷基磺酸钠组成的阻燃剂;随后将制备好的阻燃剂完全溶解到树脂液中,采用加压法将木材充分浸渍在树脂液中处理;一段时间后取出木材进行干燥。
2.根据权利要求1所述的一种高阻燃型木材,其特征在于,所述阻燃剂的组分为:按重量百分比计,聚磷酸钠聚磷酸钠25%-35%、硼酸锌15%-25%、重铬酸钾15%-25%、二氯甲烷10%-25%、钼酸钠2%-10%、十二烷基磺酸钠1-%-2%。
3.根据权利要求1所述的一种高阻燃型木材,其特征在于,所述木材浸渍在树脂液中的浸渍时间为25-75min。