CN105541190A - Anti-corrosion coating material - Google Patents
Anti-corrosion coating material Download PDFInfo
- Publication number
- CN105541190A CN105541190A CN201410585201.2A CN201410585201A CN105541190A CN 105541190 A CN105541190 A CN 105541190A CN 201410585201 A CN201410585201 A CN 201410585201A CN 105541190 A CN105541190 A CN 105541190A
- Authority
- CN
- China
- Prior art keywords
- rare earth
- cement
- earth compound
- powder
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-corrosion coating material, which is prepared from the following components by weight: 15-20 kg of silica particles, 10-15 kg of siloxane, 5-10 kg of mica powder, 10-15 kg of porcelain powder, 5-10 kg of a flame retardant agent, 5-10 kg of a rare earth compound, 5-10 kg of a catalyst, 5-10 kg of alumina, 15-20 kg of cement, and 800-100 kg of water. The preparation method specifically comprises: weighing raw materials according to a certain ratio, pouring water into a reaction kettle, heating to a temperature of 30-40 DEG C, adding the silica particles, the siloxane, the mica powder, the porcelain powder, the flame retardant agent, the rare earth compound, the catalyst, the alumina and cement, stirring, heating to a temperature of 90 DEG C, and carrying out thermal incubation for 30 min so as to obtain the finished product. According to the present invention, the anti-corrosion coating material has characteristics of no toxicity, no odor, no corrosion, no environment pollution, good sealing property, high strength, and no crack.
Description
Technical field
The present invention relates to paint field, particularly one is applicable to build high temperature resistant coating and preparation method.
Background technology
Coating forms protection to body material, but because the hot-spraying techniques of routine is due to technology itself, be difficult to form fully dense coating, the existence of coating porosity not only reduces abrasion resistant effect, to corrosion-resistant protection critical defect especially.Therefore reducing the hole of coating as much as possible or close coating porosity, is the direction that a lot of expert makes great efforts to reach the object that acid, alkali, salt and base material completely cut off.
Summary of the invention
The object of the present invention is to provide that a kind of heat-insulating property is good, thermal conductivity is low, stable performance, cheap, nonpoisonous and tasteless insulation raw material make a kind of protective system of obturator foramen micro-hole structural.
A kind of protective system, following weight configuration forms, and comprises silica dioxide granule 15-20kg, siloxanes 10-15kg, mica powder 5-10kg, porcelain powder 10-15kg, fire retardant 5-10kg, rare earth compound 5-10kg, catalyzer 5-10kg, aluminum oxide 5-10kg, cement 15-20kg, water 800-1000kg.
Preparation method of the present invention is specific as follows: first take raw material according to each component raw material, then water is poured in reactor, when being heated to 30-40 DEG C, add silica dioxide granule, siloxanes, mica powder, porcelain powder, fire retardant, rare earth compound, catalyzer, aluminum oxide, cement mixing, be warming up to 90 DEG C again, after being incubated 30 points, get product.
Advantage of the present invention is nonpoisonous and tasteless corrosion-free; pollution-free to bad border; construction cost is lower than 30-50% of benzene plate; Keep away from rain leaching Exposure to Sunlight is not frozen with cold; with body of wall and outer cover coating mortar associativity good, is greater than 30 years work-ing life and can adapts on any complex-shaped interface and be shaped with thing, and closure is good; intensity is high, flawless.
Specific embodiment
Embodiment one
A kind of protective system, following weight configuration forms, and comprises silica dioxide granule 18kg, siloxanes 13kg, mica powder 8kg, porcelain powder 13kg, fire retardant 8kg, rare earth compound 8kg, catalyzer 8kg, aluminum oxide 8kg, cement 18kg, water 900kg.
Preparation method of the present invention is specific as follows: first take raw material according to each component raw material, then water is poured in reactor, when being heated to 30-40 DEG C, add silica dioxide granule, siloxanes, mica powder, porcelain powder, fire retardant, rare earth compound, catalyzer, aluminum oxide, cement mixing, be warming up to 90 DEG C again, after being incubated 30 points, get product.
Embodiment two
Embodiment two is substantially identical with enforcement one, and its difference is that following weight is configured to silica dioxide granule 15kg, siloxanes 10kg, mica powder 5kg, porcelain powder 10kg, fire retardant 5kg, rare earth compound 5kg, catalyzer 5kg, aluminum oxide 5kg, cement 15kg, water 800kg.
Embodiment three
Embodiment three is substantially identical with enforcement one, and its difference is that following weight is configured to silica dioxide granule 20kg, siloxanes 15kg, mica powder 10kg, porcelain powder 15kg, fire retardant 10kg, rare earth compound 10kg, catalyzer 10kg, aluminum oxide 10kg, cement 20kg, water 1000kg.
Claims (2)
1. a protective system, it is characterized in that the configuration of following weight forms, comprise silica dioxide granule 15-20kg, siloxanes 10-15kg, mica powder 5-10kg, porcelain powder 10-15kg, fire retardant 5-10kg, rare earth compound 5-10kg, catalyzer 5-10kg, aluminum oxide 5-10kg, cement 15-20kg, water 800-1000kg; Preparation method of the present invention is specific as follows: first take raw material according to each component raw material, then water is poured in reactor, when being heated to 30-40 DEG C, add silica dioxide granule, siloxanes, mica powder, porcelain powder, fire retardant, rare earth compound, catalyzer, aluminum oxide, cement mixing, be warming up to 90 DEG C again, after being incubated 30 points, get product.
2. a kind of protective system according to claim 1, is characterized in that described weight is configured to silica dioxide granule 18kg, siloxanes 13kg, mica powder 8kg, porcelain powder 13kg, fire retardant 8kg, rare earth compound 8kg, catalyzer 8kg, aluminum oxide 8kg, cement 18kg, water 900kg.