CN105527411B - Test the method for testing of priming paint alkali burnout resistance - Google Patents
Test the method for testing of priming paint alkali burnout resistance Download PDFInfo
- Publication number
- CN105527411B CN105527411B CN201510961260.XA CN201510961260A CN105527411B CN 105527411 B CN105527411 B CN 105527411B CN 201510961260 A CN201510961260 A CN 201510961260A CN 105527411 B CN105527411 B CN 105527411B
- Authority
- CN
- China
- Prior art keywords
- metope
- panel
- test plate
- priming paint
- measured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to primer performance testing field, specifically for a kind of method of testing for testing priming paint alkali burnout resistance.The present invention is comprised the steps of:Step one:Criticize Puttying:Puttying layer is criticized, next step is carried out after the putty layer on metope or test plate (panel) is dried;Step 2:Smear sodium hydroxide:Sodium hydroxide solution is coated with, next step is carried out after the sodium hydroxide solution on metope or test plate (panel) is dried;Step 3:Smear priming paint to be measured:Priming paint to be measured is coated with metope or test plate (panel), next step is carried out after the priming paint to be measured on metope or test plate (panel) is done solid work;Step 4:Shower lacquer painting:Shower metope or test plate (panel) surface are drenched to putty layer, and next step is carried out after metope or test plate (panel) are dried;Step 5:Measurement result:The testing result of the priming paint to be measured is used as using water drenching number of times and lacquer painting breakage rate.The present invention can be applied to the metope for having completed to brush, and simulate alkali number, the alkali burnout resistance of accelerated test priming paint in actual applications that wall is appeared for a long time.
Description
Technical field
The present invention relates to primer performance testing field, specifically for a kind of method of testing for testing priming paint alkali burnout resistance.
Background technology
The alkali burnout resistance test of current priming paint is by the examination of GB/T 210-2007 standard gauges location survey, and standard law test is time-consuming
It is longer and actual test effect can not be embodied completely;Construction testing according to a conventional method, it can more preferably embody actually making for priming paint
Alkali burnout resistance effect in, but its alkali burnout resistance testing time is very long (some months or several years), while test result is also because certainly
The change of right environment difference, reappearance is low.Construction testing using effect is the actual embodiment of primer performance, thus invention one
It is extremely joyous to plant the new measure of merit that can embody priming paint actual use can greatly shorten the method for assessment testing time again
Meet.
Meanwhile, existing alkali burnout resistance test can only be confined to carry out in laboratory, not have for the metope for having completed to brush
There is the method for testing of the suitable anti-accumulation of salt in the surface soil.
The content of the invention
It is an object of the invention to:A kind of method of testing for testing priming paint alkali burnout resistance is provided, it can be applied to complete
Into the metope of brushing, alkali number, the alkali burnout resistance of accelerated test priming paint in actual applications that wall is appeared for a long time can be simulated
So as to shorten the testing time of external application priming paint alkali burnout resistance.
The present invention is achieved through the following technical solutions:A kind of method of testing for testing priming paint alkali burnout resistance, it is characterised in that:
Comprise the steps of:
Step one:Criticize Puttying:The Pi Gua 2-3 roads putty layer on metope or test plate (panel), and relief metope or test plate (panel) dry 18-
36h, next step is carried out after the putty layer on metope or test plate (panel) is dried;
Step 2:Smear sodium hydroxide:Coating quality is than hydrogen-oxygen of the scope for 3-5% in the putty layer of metope or test plate (panel)
Change sodium solution, the spreading rate scope of sodium hydroxide solution is 100-150g/ ㎡, and relief metope or test plate (panel) dry 0.5-2h, treat
Sodium hydroxide solution on metope or test plate (panel) carries out next step after drying;
Step 3:Smear priming paint to be measured:Priming paint to be measured is coated with metope or test plate (panel), the spreading rate scope of priming paint to be measured is
100-120g/ ㎡, and relief metope or test plate (panel) dry 18-24h, are carried out after the priming paint to be measured on metope or test plate (panel) is done solid work next
Individual step;
Step 4:Shower lacquer painting:The running water shower metope for being 6-7 with distilled water or pH range or test plate (panel) surface are to greasy
Sublayer drenches, and water drenching amount scope is 2-3 ㎏/㎡/secondary, and relief metope or test plate (panel) dry 0.5-1.5h, treats that metope or test plate (panel) are dry
Next step is carried out after dry;
Step 5:Measurement result:Observation metope or test plate (panel) surface are whether there is because growing dim, getting confused, the accumulation of salt in the surface soil and/or salting-out phenomenon and
The phenomenon of priming paint lacquer painting to be measured is destroyed, if there are no the phenomenon for destroying priming paint lacquer painting to be measured, repeat step four and step 5
The phenomenon of priming paint lacquer painting to be measured is destroyed until observing, water drenching number of times and the bottom to be measured of the metope or test plate (panel) is now recorded
The lacquer painting breakage rate of paint, and the testing result of the priming paint to be measured is used as using water drenching number of times and lacquer painting breakage rate;
The lacquer painting breakage rate refers to the destroyed lacquer painting area of unit area priming paint to be measured.
Its operation principle is:Priming paint lower section smear basic species with increase metope or test plate (panel) basic species content so as to
Simulate in a short period of time wall or test plate (panel) for a long time go out alkali number, reach accelerated test priming paint in actual applications anti-general
The effect of the alkaline testing time that, can effectively shorten external application priming paint alkali burnout resistance.
In order to preferably implement this programme, following prioritization scheme is also provided:
Further, if priming paint to be measured is adjustable color bottom paint, also comprised the following steps between step 3 and step 4:
Step A:It is coated with finish paint:Metope or test plate (panel) surface coating pigmented top coat after step 3 processing, and relief metope or test plate (panel) are dry
Dry 18-24h, next step is carried out after the pigmented top coat on metope or test plate (panel) is dried.
Further, the pigmented top coat is color-adjustable finish paint by 90-93 parts by weight and the mill base of 7-10 parts by weight
It is formulated.
Further, the color-adjustable finish paint is the color-adjustable finish paint that Sankeshu Paint Joint-Stock Limited Company produces
One kind in SGE100, color-adjustable finish paint SGE400, color-adjustable finish paint SB002C.
Further, the mill base is one kind in iron oxide red mill base, carbon black color paste, phthalocyanine blue mill base, dark green mill base.
Raw material used in each step of the present invention is:
Sodium hydroxide (chemistry is pure) (producer:Tianjin red rock reagent chemical plant);
Distilled water (Sankeshu Paint Joint-Stock Limited Company's preparation);
(Si Ming or Ke Laien iron oxide red mill base, carbon black color paste, phthalocyanine blue mill base dark green mill base etc. are easy to observation to mill base
Color);
Three tree external application putty (SGN700, SGN702 etc.);
Three tree external application finish paints (color-adjustable such as SGE100/SGE400/SB002C finish paint).
Instrument used in each step of the present invention is:
Roller:Several, for the various raw materials of roller coating;
Pallette knife:Several, for mixing solubilising reagent, stirring coating;
Bucket:It is several, for containing solution;
Jar:Volume is 0.5L, several, for containing solution;
Electronic balance:1, for weighing quality.
Form used in present invention record testing result:
Subordinate list 1:
Subordinate list 2:
Than before for technology, beneficial effects of the present invention are:
1. the present invention can shorten the testing time of external application priming paint alkali burnout resistance, while bottom can quickly and accurately be simulated
The test result of alkali burnout resistance is painted, can be with the quality of the objective alkali burnout resistance for contrasting different priming paint, while different time
And environmental condition has no significant effect to test result, anti-general the saltouing property of test priming paint can also be attached, resist general saline alkali.
2. the detection method of the present invention is different with existing method of testing from the method for result evaluation, it is not only able to be applied to
On the metope that open air can also be directly applied in laboratory, have a wide range of application.
Embodiment
The present invention is elaborated with reference to embodiment:
Embodiment 1:
The detection object of the present embodiment is a kind of adjustable color bottom paint, is comprised the steps of:
Step one:Criticize Puttying:Criticized on metope or test plate (panel) and scrape 2 road putty layers, and relief metope or test plate (panel) dry 18h,
Next step is carried out after the putty layer on metope or test plate (panel) is dried;
Step 2:Smear sodium hydroxide:Coating quality is more molten than for 3% sodium hydroxide in the putty layer of metope or test plate (panel)
Liquid, the spreading rate of sodium hydroxide solution is 100g/ ㎡, and relief metope or test plate (panel) dry 0.5h, treat the hydrogen on metope or test plate (panel)
Sodium hydroxide solution carries out next step after drying;
Step 3:Smear priming paint to be measured:Priming paint to be measured is coated with metope or test plate (panel), the spreading rate of priming paint to be measured is
100g/ ㎡, and relief metope or test plate (panel) dry 18h, and next step is carried out after the priming paint to be measured on metope or test plate (panel) is done solid work;
Step A:It is coated with finish paint:Metope or test plate (panel) surface coating pigmented top coat after step 3 processing, and relief metope
Or test plate (panel) dries 18h, next step is carried out after the pigmented top coat on metope or test plate (panel) is dried.
Step 4:Shower lacquer painting:It is that 6 running water shower metope or test plate (panel) surface are wet to putty layer with distilled water or pH value
Thoroughly, water drenching amount is 2 ㎏/㎡/secondary, and relief metope or test plate (panel) dry 0.5h, and next step is carried out after metope or test plate (panel) are dried
Suddenly;
Step 5:Measurement result:Observation metope or test plate (panel) surface are whether there is because growing dim, getting confused, the accumulation of salt in the surface soil and/or salting-out phenomenon and
The phenomenon of priming paint lacquer painting to be measured is destroyed, if there are no the phenomenon for destroying priming paint lacquer painting to be measured, repeat step four and step 5
The phenomenon of priming paint lacquer painting to be measured is destroyed until observing, water drenching number of times and the bottom to be measured of the metope or test plate (panel) is now recorded
The lacquer painting breakage rate of paint, and the testing result of the priming paint to be measured is used as using water drenching number of times and lacquer painting breakage rate;
The lacquer painting breakage rate refers to the destroyed lacquer painting area of unit area priming paint to be measured.
Further, the pigmented top coat is by the color-adjustable of Sankeshu Paint Joint-Stock Limited Company's production of 90 parts by weight
Finish paint SGE100 and the iron oxide red mill base of 10 parts by weight are formulated.
Embodiment 2:
The detection object of the present embodiment is a kind of adjustable color bottom paint, is comprised the steps of:
Step one:Criticize Puttying:Criticized on metope or test plate (panel) and scrape 3 road putty layers, and relief metope or test plate (panel) dry 24h,
Next step is carried out after the putty layer on metope or test plate (panel) is dried;
Step 2:Smear sodium hydroxide:Coating quality is more molten than for 4% sodium hydroxide in the putty layer of metope or test plate (panel)
Liquid, the spreading rate of sodium hydroxide solution is 125g/ ㎡, and relief metope or test plate (panel) dry 1h, treat the hydrogen-oxygen on metope or test plate (panel)
Change after sodium solution is dried and carry out next step;
Step 3:Smear priming paint to be measured:Priming paint to be measured is coated with metope or test plate (panel), the spreading rate of priming paint to be measured is
110g/ ㎡, and relief metope or test plate (panel) dry 20h, and next step is carried out after the priming paint to be measured on metope or test plate (panel) is done solid work;
Step A:It is coated with finish paint:Metope or test plate (panel) surface coating pigmented top coat after step 3 processing, and relief metope
Or test plate (panel) dries 24h, next step is carried out after the pigmented top coat on metope or test plate (panel) is dried.
Step 4:Shower lacquer painting:It is that 7 running water shower metope or test plate (panel) surface are wet to putty layer with distilled water or pH value
Thoroughly, water drenching amount is 2.5 ㎏/㎡/secondary, and relief metope or test plate (panel) dry 1h, and next step is carried out after metope or test plate (panel) are dried
Suddenly;
Step 5:Measurement result:Observation metope or test plate (panel) surface are whether there is because growing dim, getting confused, the accumulation of salt in the surface soil and/or salting-out phenomenon and
The phenomenon of priming paint lacquer painting to be measured is destroyed, if there are no the phenomenon for destroying priming paint lacquer painting to be measured, repeat step four and step 5
The phenomenon of priming paint lacquer painting to be measured is destroyed until observing, water drenching number of times and the bottom to be measured of the metope or test plate (panel) is now recorded
The lacquer painting breakage rate of paint, and the testing result of the priming paint to be measured is used as using water drenching number of times and lacquer painting breakage rate;
The lacquer painting breakage rate refers to the destroyed lacquer painting area of unit area priming paint to be measured.
Further, the pigmented top coat is by the color-adjustable of Sankeshu Paint Joint-Stock Limited Company's production of 93 parts by weight
Finish paint SGE400 and the carbon black color paste of 7 parts by weight are formulated.
Embodiment 3:
The detection object of the present embodiment is a kind of adjustable color bottom paint, is comprised the steps of:
Step one:Criticize Puttying:Criticized on metope or test plate (panel) and scrape 2 road putty layers, and relief metope or test plate (panel) dry 30h,
Next step is carried out after the putty layer on metope or test plate (panel) is dried;
Step 2:Smear sodium hydroxide:Coating quality is than the sodium hydroxide for 4.5% in the putty layer of metope or test plate (panel)
Solution, the spreading rate of sodium hydroxide solution is 140g/ ㎡, and relief metope or test plate (panel) dry 1.5h, treat on metope or test plate (panel)
Sodium hydroxide solution carries out next step after drying;
Step 3:Smear priming paint to be measured:Priming paint to be measured is coated with metope or test plate (panel), the spreading rate of priming paint to be measured is
115g/ ㎡, and relief metope or test plate (panel) dry 22h, and next step is carried out after the priming paint to be measured on metope or test plate (panel) is done solid work;
Step 4:Shower lacquer painting:It is that 6 running water shower metope or test plate (panel) surface are wet to putty layer with distilled water or pH value
Thoroughly, water drenching amount is 2.7 ㎏/㎡/secondary, and relief metope or test plate (panel) dry 1.3h, is carried out after metope or test plate (panel) are dried next
Step;
Step 5:Measurement result:Observation metope or test plate (panel) surface are whether there is because growing dim, getting confused, the accumulation of salt in the surface soil and/or salting-out phenomenon and
The phenomenon of priming paint lacquer painting to be measured is destroyed, if there are no the phenomenon for destroying priming paint lacquer painting to be measured, repeat step four and step 5
The phenomenon of priming paint lacquer painting to be measured is destroyed until observing, water drenching number of times and the bottom to be measured of the metope or test plate (panel) is now recorded
The lacquer painting breakage rate of paint, and the testing result of the priming paint to be measured is used as using water drenching number of times and lacquer painting breakage rate;
The lacquer painting breakage rate refers to the destroyed lacquer painting area of unit area priming paint to be measured.
Embodiment 4:
The detection object of the present embodiment is a kind of non-adjustable color bottom paint, is comprised the steps of:
Step one:Criticize Puttying:Criticized on metope or test plate (panel) and scrape 3 road putty layers, and relief metope or test plate (panel) dry 36h,
Next step is carried out after the putty layer on metope or test plate (panel) is dried;
Step 2:Smear sodium hydroxide:Coating quality is more molten than for 5% sodium hydroxide in the putty layer of metope or test plate (panel)
Liquid, the spreading rate of sodium hydroxide solution is 150g/ ㎡, and relief metope or test plate (panel) dry 2h, treat the hydrogen-oxygen on metope or test plate (panel)
Change after sodium solution is dried and carry out next step;
Step 3:Smear priming paint to be measured:Priming paint to be measured is coated with metope or test plate (panel), the spreading rate of priming paint to be measured is
120g/ ㎡, and relief metope or test plate (panel) dry 24h, and next step is carried out after the priming paint to be measured on metope or test plate (panel) is done solid work;
Step 4:Shower lacquer painting:It is that 7 running water shower metope or test plate (panel) surface are wet to putty layer with distilled water or pH value
Thoroughly, water drenching amount is 3 ㎏/㎡/secondary, and relief metope or test plate (panel) dry 1.5h, and next step is carried out after metope or test plate (panel) are dried
Suddenly;
Step 5:Measurement result:Observation metope or test plate (panel) surface are whether there is because growing dim, getting confused, the accumulation of salt in the surface soil and/or salting-out phenomenon and
The phenomenon of priming paint lacquer painting to be measured is destroyed, if there are no the phenomenon for destroying priming paint lacquer painting to be measured, repeat step four and step 5
The phenomenon of priming paint lacquer painting to be measured is destroyed until observing, water drenching number of times and the bottom to be measured of the metope or test plate (panel) is now recorded
The lacquer painting breakage rate of paint, and the testing result of the priming paint to be measured is used as using water drenching number of times and lacquer painting breakage rate;
The lacquer painting breakage rate refers to the destroyed lacquer painting area of unit area priming paint to be measured.
Although the present invention is illustrated and illustrated to the present invention using specific embodiment and its alternative, but it should reason
Solution, can implement without departing from the variations and modifications in the scope of the present invention.It is therefore understood that except by with
Outside the limitation of attached claim and its condition of equivalent, the present invention is not limited by all senses.
Claims (5)
1. a kind of method of testing for testing priming paint alkali burnout resistance, it is characterised in that:Comprise the steps of:
Step one:Criticize Puttying:The Pi Gua 2-3 roads putty layer on metope or test plate (panel), and relief metope or test plate (panel) dry 18-36h,
Next step is carried out after the putty layer on metope or test plate (panel) is dried;
Step 2:Smear sodium hydroxide:Coating quality is than sodium hydroxide of the scope for 3-5% in the putty layer of metope or test plate (panel)
Solution, the spreading rate scope of sodium hydroxide solution is 100-150g/ ㎡, and relief metope or test plate (panel) dry 0.5-2h, treat metope
Or carry out next step after the sodium hydroxide solution drying on test plate (panel);
Step 3:Smear priming paint to be measured:Priming paint to be measured is coated with metope or test plate (panel), the spreading rate scope of priming paint to be measured is 100-
120g/ ㎡, and relief metope or test plate (panel) dry 18-24h, and next step is carried out after the priming paint to be measured on metope or test plate (panel) is done solid work
Suddenly;
Step 4:Shower lacquer painting:The running water shower metope for being 6-7 with distilled water or pH range or test plate (panel) surface are to putty layer
Drenched, water drenching amount scope is 2-3 ㎏/㎡/secondary, and relief metope or test plate (panel) dry 0.5-1.5h, after metope or test plate (panel) are dried
Carry out next step;
Step 5:Measurement result:Observation metope or test plate (panel) surface are whether there is because growing dim, getting confused, destroyed the accumulation of salt in the surface soil and/or salting-out phenomenon
The phenomenon of priming paint lacquer painting to be measured, if there are no the phenomenon for destroying priming paint lacquer painting to be measured, repeat step four and step 5 until
It was observed that there is the phenomenon for destroying priming paint lacquer painting to be measured, the water drenching number of times and priming paint to be measured of the metope or test plate (panel) are now recorded
Lacquer painting breakage rate, and the testing result of the priming paint to be measured is used as using water drenching number of times and lacquer painting breakage rate;
The lacquer painting breakage rate refers to the destroyed lacquer painting area of unit area priming paint to be measured.
2. the method for testing of test priming paint alkali burnout resistance according to claim 1, it is characterised in that:Can if priming paint to be measured is
Toning priming paint, then also comprise the following steps between step 3 and step 4:
Step A:It is coated with finish paint:Metope or test plate (panel) surface coating pigmented top coat after step 3 processing, and relief metope or examination
Plate dries 18-24h, and next step is carried out after the pigmented top coat on metope or test plate (panel) is dried.
3. the method for testing of test priming paint alkali burnout resistance according to claim 2, it is characterised in that:The pigmented top coat is
It is formulated by the color-adjustable finish paint of 90-93 parts by weight and the mill base of 7-10 parts by weight.
4. the method for testing of test priming paint alkali burnout resistance according to claim 3, it is characterised in that:The color-adjustable finish paint
Color-adjustable finish paint SGE100, color-adjustable finish paint SGE400, the color-adjustable finish paint produced for Sankeshu Paint Joint-Stock Limited Company
One kind in SB002C.
5. the method for testing of test priming paint alkali burnout resistance according to claim 3, it is characterised in that:The mill base is iron oxide red
One kind in mill base, carbon black color paste, phthalocyanine blue mill base, dark green mill base.