CN105525380A - 一种抗菌阻燃的丙纶有色长丝及其制备方法 - Google Patents
一种抗菌阻燃的丙纶有色长丝及其制备方法 Download PDFInfo
- Publication number
- CN105525380A CN105525380A CN201510700832.9A CN201510700832A CN105525380A CN 105525380 A CN105525380 A CN 105525380A CN 201510700832 A CN201510700832 A CN 201510700832A CN 105525380 A CN105525380 A CN 105525380A
- Authority
- CN
- China
- Prior art keywords
- retardant
- antibacterial flame
- flame
- polypropylene fibre
- coloured yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种抗菌阻燃的丙纶有色长丝及其制备方法,涉及纺织制造技术领域,所述长丝由基本树脂92-97%、抗菌剂0.5-1%、阻燃剂0.5-2%、彩色母粒0.3-2%、载体1-3%制成,通过特殊工艺,结合无机载银粒子的加入达到99.9%的抗菌效果以及阻燃丙纶有色母粒的加入达到阻燃与颜色的需求,使两者相容,制得抗菌和阻燃兼顾的有色丙纶长丝,使得生产出的纺织面料具有良好的抗菌阻燃效果。
Description
技术领域:
本发明涉及纺织制造技术领域,具体涉及一种抗菌阻燃的丙纶有色长丝及其制备方法。
背景技术:
丙纶的特性是虹吸、快干,加上丙纶不能用水浴染色法上色,而只能用原液着色法上色,在家用纺织品领域有着环保,舒适的功能,而广受关注。丙纶的极限氧指数是18.6,属于易燃类纤维,市场上一般使用有机助剂作为抗菌剂对丙纶面料进行处理,但这只会导致该类面料更易燃。
发明内容:
本发明所要解决的技术问题在于克服现有的技术缺陷,提供一种抗菌阻燃的丙纶有色长丝及其制备方法,通过特殊工艺,结合无机载银粒子的加入达到99.9%的抗菌效果以及阻燃丙纶有色母粒的加入达到阻燃与颜色的需求,使两者相容,制得抗菌和阻燃兼顾的有色丙纶长丝,使得生产出的纺织面料具有良好的抗菌阻燃效果。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种抗菌阻燃的丙纶有色长丝,其特征在于,所述长丝由以下重量份的配方配比制成:
基本树脂92-97%、抗菌剂0.5-1%、阻燃剂0.5-2%、彩色母粒0.3-2%、载体1-3%。
所述基本树脂为纺丝级别的PP聚丙烯粒子。
所述抗菌剂为无机材料分散载银离子的粉末小颗粒,纳米银粉末由于粒径太小,容易团聚,抗菌成分将无法良好的分散,因此将无机材料做预分散处理,达到良好的抗菌效果。
所述阻燃剂为无卤氢氧化物粉末,能够大大提高丙纶的极限氧指数,阻燃效果显著而且环保。
所述彩色母粒为含喹吖二酮、酞菁的一种或两者混合成分的树脂粒子,使用此类彩色树脂粒子,便于所需颜色更好的分布在长丝中。
所述载体为聚烯烃类,所负载上述功能材料可顺利进入PP熔体中。
一种抗菌阻燃的丙纶有色长丝的制备方法,其特征在于以下步骤:
1)、将1-3%相对含量的载体、0.5-1%相对含量的抗菌剂和0.5-2%相对含量的阻燃剂,通过高速搅拌混合机搅拌混合,以300-800转/分的速度搅拌混合30分钟,制得混合料;
2)、通过双螺杆挤出机,使用100-180℃的工艺温度,将步骤1)的混合料进行拉条造粒,得到混合粒;
3)、通过另一组双螺杆挤出机,使用150-250℃的工艺温度,将0.3-2%相对含量的彩色母粒与第二步骤的混合粒搅拌混合后进行再造粒,得到二次混合粒;
4)、通过丙纶长丝纺丝设备,设定230-290℃的纺丝温度,以2000-3000米/分的速度,将90-95%相对含量的基本树脂PP粒料和步骤3)的二次混合粒以一定的比例添加进入螺杆熔融纺丝,最终制得有抗菌阻燃双重功能的丙纶有色长丝。
本发明的有益效果为,提供一种抗菌阻燃的丙纶有色长丝及其制备方法,通过特殊工艺,结合无机载银粒子的加入达到99.9%的抗菌效果以及阻燃丙纶有色母粒的加入达到阻燃与颜色的需求,使两者相容,制得抗菌和阻燃兼顾的有色丙纶长丝,使得生产出的纺织面料具有良好的抗菌阻燃效果。
附图说明:
图1为本发明纳米银与阻燃剂在纤维中的粒径分布示意图。
图2为本发明丙纶长丝纵向截面中显示抗菌粒子,阻燃粒子,颜料粒子的显微镜效果图。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种添加抗菌阻燃的丙纶有色长丝的制备方法,其特征在于以下步骤:
1)、将1-3%相对含量的载体、0.5-1%相对含量的抗菌剂和0.5-2%相对含量的阻燃剂,通过高速搅拌混合机搅拌混合,以300-800转/分的速度搅拌混合30分钟,制得混合料;
2)、通过双螺杆挤出机,使用100-180℃的工艺温度,将步骤1)的混合料进行拉条造粒,得到混合粒;
3)、通过另一组双螺杆挤出机,使用150-250℃的工艺温度,将0.3-2%相对含量的彩色母粒与第二步骤的混合粒搅拌混合后进行再造粒,得到二次混合粒;
4)、通过丙纶长丝纺丝设备,设定230-290℃的纺丝温度,以2000-3000米/分的速度,将90-95%相对含量的基本树脂PP粒料和步骤3)的二次混合粒以一定的比例添加进入螺杆熔融纺丝,最终制得有抗菌阻燃双重功能的丙纶有色长丝。
具体实施例如下:
成分(质量分数) | 实施例1 | 实施例2 | 实施例3 | 对比例 |
基本树脂 | 97% | 95% | 92% | 97% |
抗菌剂 | 0.5% | 0.7% | 1% | 3% |
阻燃剂 | 0.5% | 1% | 2% | - |
彩色母粒 | 1% | 1.3% | 2% | - |
载体 | 1% | 2% | 3% | - |
极限氧指数 | 19 | 21 | 23 | 18.6 |
丙纶的极限氧指数越高,阻燃效果越好,从上表以及图1(图中,三角形为纳米银,深灰色不规则球状为阻燃剂,通过纳米银与阻燃剂的不规则分布,达到抗菌又阻燃的效果)和图2所示可知,通过本发明配方配比以及本发明提供的方法制得抗菌阻燃的丙纶有色长丝与传统方式制得的丙纶长丝相比,极限氧指数得到大大提高,阻燃效果显著。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (7)
1.一种抗菌阻燃的丙纶有色长丝,其特征在于,所述长丝由以下重量份的配方配比制成:
基本树脂92-97%、抗菌剂0.5-1%、阻燃剂0.5-2%、彩色母粒0.3-2%、载体1-3%。
2.根据权利要求1所述的一种抗菌阻燃的丙纶有色长丝,其特征在于,所述基本树脂为纺丝级别的PP聚丙烯粒子。
3.根据权利要求1所述的一种抗菌阻燃的丙纶有色长丝,其特征在于,所述抗菌剂为无机材料分散载银离子的粉末小颗粒。
4.根据权利要求1所述的一种抗菌阻燃的丙纶有色长丝,其特征在于,所述阻燃剂为无卤氢氧化物粉末。
5.根据权利要求1所述的一种抗菌阻燃的丙纶有色长丝,其特征在于,所述彩色母粒为含喹吖二酮、酞菁的一种或两者混合成分的树脂粒子。
6.根据权利要求1所述的一种抗菌阻燃的丙纶有色长丝,其特征在于,所述载体为聚烯烃类。
7.一种抗菌阻燃的丙纶有色长丝的制备方法,其特征在于以下步骤:
1)、将1-3%相对含量的载体、0.5-1%相对含量的抗菌剂和0.5-2%相对含量的阻燃剂,通过高速搅拌混合机搅拌混合,以300-800转/分的速度搅拌混合30分钟,制得混合料;
2)、通过双螺杆挤出机,使用100-180℃的工艺温度,将步骤1)的混合料进行拉条造粒,得到混合粒;
3)、通过另一组双螺杆挤出机,使用150-250℃的工艺温度,将0.3-2%相对含量的彩色母粒与第二步骤的混合粒搅拌混合后进行再造粒,得到二次混合粒;
4)、通过丙纶长丝纺丝设备,设定230-290℃的纺丝温度,以2000-3000米/分的速度,将90-95%相对含量的基本树脂PP粒料和步骤3)的二次混合粒以一定的比例添加进入螺杆熔融纺丝,最终制得有抗菌阻燃双重功能的丙纶有色长丝。