CN105525183A - High-strength cold-rolled strip steel - Google Patents
High-strength cold-rolled strip steel Download PDFInfo
- Publication number
- CN105525183A CN105525183A CN201510892637.0A CN201510892637A CN105525183A CN 105525183 A CN105525183 A CN 105525183A CN 201510892637 A CN201510892637 A CN 201510892637A CN 105525183 A CN105525183 A CN 105525183A
- Authority
- CN
- China
- Prior art keywords
- parts
- strength cold
- rolled strip
- strip steel
- cold rolled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength cold-rolled strip steel comprising the following substances in parts by mass: 22-74 parts of C, 14-37 parts of Si, 4-11 parts of Mn, 3-16 parts of P, 4-11 parts of S, 12-31 parts of Cr, 5-12 parts of Ni, 1-6 parts of Y, 2-7 parts of W, 23-37 parts of Fe, 6-9 parts of Mo, 3-8 parts of Nb, 2-7 parts of Ta, 3-10 parts of Sn, 17-29 parts of Mg, 1-6 parts of Bi and 2-4 parts of Te. In such a way, the high-strength cold-rolled strip steel disclosed by the invention can be used for improving the strength of cold-rolled strip steel, reducing the manufacturing cost and meeting various use requirements.
Description
Technical field
The present invention relates to cold rolled strip field, particularly relate to a kind of high-strength cold rolled steel strip.
Background technology
Stainless steel is common steel alloy, by metallographic structure classification, generally can be divided into: ferritic stainless steel, austenitic stainless steel, Martensite Stainless Steel and duplex stainless steel (ferritic-austenitic stainless steel).Produce the microstructure of Cr17 type ferrite stainless strip steel at present both at home and abroad based on ferrite, and add corrosion resisting property and the raising intensity that a small amount of trace alloying element titanium, niobium etc. improve steel, some steel grades also add molybdenum, because molybdenum valency goes up in recent years, add molybdenum and the cost of steel can be made to increase.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of high-strength cold rolled steel strip, can improve the intensity of cold rolled strip, reduces manufacturing cost, meets various user demand.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of high-strength cold rolled steel strip, comprise following material and form by massfraction: C22-74 part, Si14-37 part, Mn4-11 part, P3-16 part, S4-11 part, Cr12-31 part, Ni5-12 part, Y1-6 part, W2-7 part, Fe23-37 part, Mo6-9 part, Nb3-8 part, Ta2-7 part, Sn3-10 part, Mg17-29 part, Bi1-6 part and Te2-4 part.
In a preferred embodiment of the present invention, comprise following material and form by massfraction: C22 part, Si14 part, Mn4 part, P3 part, S4 part, Cr12 part, Ni5 part, Y1 part, W2 part, Fe23 part, Mo6 part, Nb3 part, Ta2 part, Sn3 part, Mg17 part, Bi1 part and Te2 part.
In a preferred embodiment of the present invention, comprise following material and form by massfraction: C74 part, Si37 part, Mn11 part, P16 part, S11 part, Cr31 part, Ni5-12 part, Y6 part, W7 part, Fe37 part, Mo9 part, Nb8 part, Ta7 part, Sn10 part, Mg29 part, Bi6 part and Te4 part.
In a preferred embodiment of the present invention, comprise following material and form by massfraction: C55 part, Si21 part, Mn7 part, P15 part, S10 part, Cr23 part, Ni8 part, Y3 part, W6 part, Fe27 part, Mo8 part, Nb7 part, Ta6 part, Sn5 part, Mg19 part, Bi4 part and Te3 part.
The invention has the beneficial effects as follows: high-strength cold rolled steel strip of the present invention, the intensity of cold rolled strip can be improved, reduce manufacturing cost, meet various user demand.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1: a kind of high-strength cold rolled steel strip, comprises following material and forms by massfraction: C22 part, Si14 part, Mn4 part, P3 part, S4 part, Cr12 part, Ni5 part, Y1 part, W2 part, Fe23 part, Mo6 part, Nb3 part, Ta2 part, Sn3 part, Mg17 part, Bi1 part and Te2 part.
Embodiment 2: a kind of high-strength cold rolled steel strip, comprises following material and forms by massfraction: C74 part, Si37 part, Mn11 part, P16 part, S11 part, Cr31 part, Ni5-12 part, Y6 part, W7 part, Fe37 part, Mo9 part, Nb8 part, Ta7 part, Sn10 part, Mg29 part, Bi6 part and Te4 part.
Embodiment 3: a kind of high-strength cold rolled steel strip, comprises following material and forms by massfraction: C55 part, Si21 part, Mn7 part, P15 part, S10 part, Cr23 part, Ni8 part, Y3 part, W6 part, Fe27 part, Mo8 part, Nb7 part, Ta6 part, Sn5 part, Mg19 part, Bi4 part and Te3 part.
Be different from prior art, high-strength cold rolled steel strip of the present invention, the intensity of cold rolled strip can be improved, reduce manufacturing cost, meet various user demand.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (4)
1. a high-strength cold rolled steel strip, it is characterized in that, comprise following material and form by massfraction: C22-74 part, Si14-37 part, Mn4-11 part, P3-16 part, S4-11 part, Cr12-31 part, Ni5-12 part, Y1-6 part, W2-7 part, Fe23-37 part, Mo6-9 part, Nb3-8 part, Ta2-7 part, Sn3-10 part, Mg17-29 part, Bi1-6 part and Te2-4 part.
2. high-strength cold rolled steel strip according to claim 1, it is characterized in that, comprise following material and form by massfraction: C22 part, Si14 part, Mn4 part, P3 part, S4 part, Cr12 part, Ni5 part, Y1 part, W2 part, Fe23 part, Mo6 part, Nb3 part, Ta2 part, Sn3 part, Mg17 part, Bi1 part and Te2 part.
3. high-strength cold rolled steel strip according to claim 1, it is characterized in that, comprise following material and form by massfraction: C74 part, Si37 part, Mn11 part, P16 part, S11 part, Cr31 part, Ni5-12 part, Y6 part, W7 part, Fe37 part, Mo9 part, Nb8 part, Ta7 part, Sn10 part, Mg29 part, Bi6 part and Te4 part.
4. high-strength cold rolled steel strip according to claim 1, it is characterized in that, comprise following material and form by massfraction: C55 part, Si21 part, Mn7 part, P15 part, S10 part, Cr23 part, Ni8 part, Y3 part, W6 part, Fe27 part, Mo8 part, Nb7 part, Ta6 part, Sn5 part, Mg19 part, Bi4 part and Te3 part.