CN105505317A - Suspending agent for grinding - Google Patents
Suspending agent for grinding Download PDFInfo
- Publication number
- CN105505317A CN105505317A CN201511013022.2A CN201511013022A CN105505317A CN 105505317 A CN105505317 A CN 105505317A CN 201511013022 A CN201511013022 A CN 201511013022A CN 105505317 A CN105505317 A CN 105505317A
- Authority
- CN
- China
- Prior art keywords
- parts
- grinding
- suspending agent
- kaolin
- triethylamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a suspending agent for grinding. The suspending agent is prepared from the following raw materials in parts by weight: 3 to 6 parts of trisodium orthophosphate, 4 to 7 parts of polyethylene, 6 to 10 parts of sorbitol, 3.2 to 6 parts of grinding particles, 4 to 8 parts of nonylphenol polyoxyethylene ether, 6 to 8 parts of boric acid ester, 4 to 9 parts of surface active agent, 5 to 8 parts of kaolin, 6 to 12 parts of calcium stearate, 6 to 11 parts of Melamine cyanurate, 1.5 to 6 parts of solvent oil, 6 to 10 parts of methyl benzoate, 3.2 to 6.8 parts of nano calcium sulfate, 8 to 14 parts of hollow glass beads and 2 to 4 parts of triethylamine. The suspending agent for grinding disclosed by the invention has the beneficial effects that the grinding effect can be improved, good lubricity is achieved, and the damage to metal is small.
Description
Technical field
The present invention relates to a kind of grinding suspension agent.
Background technology
When suspension is applied to suspension grinding operation, its lubrication shows as the strong mechanical friction that can reduce between abrasive material, makes this friction be converted to internal friction between lubrication molecule, thus improves cutting speed, reduce frictional heat simultaneously; Its perviousness shows as viscosity and the wettability of suspension.Grinding suspension, uniform microemulsion provides splendid lubricity, is mainly used in requiring that the aspect such as grinding, boring, stretch process of lubricity and the high non-ferrous metal such as Wimet, stainless steel, high carbon steel, aluminium alloy, copper alloy, steel alloy of extreme pressure property and ferrous material is suitable for.Now commercially occurred various suspension, Performance comparision is single, well can not meet user demand, awaits further raising.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of grinding suspension agent, can improve the effect of grinding, and have good oilness, little to the infringement of metal.
For solving prior art problem, technical scheme provided by the invention is, a kind of grinding suspension agent, and it is made up of the raw material of following parts by weight:
Tertiary sodium phosphate 3-6 part, polyethylene 4-7 part, sorbyl alcohol 6-10 part, polishing particles 3.2-6 part, polyoxyethylene nonylphenol ether 4-8 part, boric acid ester 6-8 part, tensio-active agent 4-9 part, kaolin 5-8 part, calcium stearate 6-12 part, melamine cyanurate salt 6-11 part, solvent oil 1.5-6 part, methyl benzoate 6-10 part, nanometer calcium sulfate 3.2-6.8 part, hollow glass micropearl 8-14 part, triethylamine 2-4 part.
Optimize, a kind of grinding suspension agent, it is made up of the raw material of following parts by weight:
Tertiary sodium phosphate 4.5 parts, polyethylene 5.5 parts, sorbyl alcohol 8 parts, polishing particles 4.5 parts, polyoxyethylene nonylphenol ether 6 parts, boric acid ester 7 parts, 6.5 parts, tensio-active agent, kaolin 6.5 parts, calcium stearate 9 parts, melamine cyanurate salt 8.5 parts, solvent oil 4 parts, methyl benzoate 8 parts, nanometer calcium sulfate 4.9 parts, hollow glass micropearl 11 parts, triethylamine 3 parts.
The invention has the beneficial effects as follows: grinding suspension agent of the present invention, the effect of grinding can be improved, and there is good oilness, little to the infringement of metal.
Embodiment
embodiment 1
A kind of grinding suspension agent, it is made up of the raw material of following parts by weight:
Tertiary sodium phosphate 3 parts, polyethylene 4 parts, sorbyl alcohol 6 parts, polishing particles 3.2 parts, polyoxyethylene nonylphenol ether 4 parts, boric acid ester 6 parts, 4 parts, tensio-active agent, kaolin 5 parts, calcium stearate 6 parts, melamine cyanurate salt 6 parts, solvent oil 1.5 parts, methyl benzoate 6 parts, nanometer calcium sulfate 3.2 parts, hollow glass micropearl 8 parts, triethylamine 2 parts.
embodiment 2
A kind of grinding suspension agent, it is made up of the raw material of following parts by weight:
Tertiary sodium phosphate 6 parts, polyethylene 7 parts, sorbyl alcohol 10 parts, polishing particles 6 parts, polyoxyethylene nonylphenol ether 8 parts, boric acid ester 8 parts, 9 parts, tensio-active agent, kaolin 8 parts, calcium stearate 12 parts, melamine cyanurate salt 11 parts, solvent oil 6 parts, methyl benzoate 10 parts, nanometer calcium sulfate 6.8 parts, hollow glass micropearl 14 parts, triethylamine 4 parts.
embodiment 3
A kind of grinding suspension agent, it is made up of the raw material of following parts by weight:
Tertiary sodium phosphate 4.5 parts, polyethylene 5.5 parts, sorbyl alcohol 8 parts, polishing particles 4.5 parts, polyoxyethylene nonylphenol ether 6 parts, boric acid ester 7 parts, 6.5 parts, tensio-active agent, kaolin 6.5 parts, calcium stearate 9 parts, melamine cyanurate salt 8.5 parts, solvent oil 4 parts, methyl benzoate 8 parts, nanometer calcium sulfate 4.9 parts, hollow glass micropearl 11 parts, triethylamine 3 parts.
Claims (2)
1. a grinding suspension agent, is characterized in that: it is made up of the raw material of following parts by weight:
Tertiary sodium phosphate 3-6 part, polyethylene 4-7 part, sorbyl alcohol 6-10 part, polishing particles 3.2-6 part, polyoxyethylene nonylphenol ether 4-8 part, boric acid ester 6-8 part, tensio-active agent 4-9 part, kaolin 5-8 part, calcium stearate 6-12 part, melamine cyanurate salt 6-11 part, solvent oil 1.5-6 part, methyl benzoate 6-10 part, nanometer calcium sulfate 3.2-6.8 part, hollow glass micropearl 8-14 part, triethylamine 2-4 part.
2. grinding suspension agent according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight:
Tertiary sodium phosphate 4.5 parts, polyethylene 5.5 parts, sorbyl alcohol 8 parts, polishing particles 4.5 parts, polyoxyethylene nonylphenol ether 6 parts, boric acid ester 7 parts, 6.5 parts, tensio-active agent, kaolin 6.5 parts, calcium stearate 9 parts, melamine cyanurate salt 8.5 parts, solvent oil 4 parts, methyl benzoate 8 parts, nanometer calcium sulfate 4.9 parts, hollow glass micropearl 11 parts, triethylamine 3 parts.