CN105505214A - Corrosion-resistant weather-resistant plant wood oil - Google Patents
Corrosion-resistant weather-resistant plant wood oil Download PDFInfo
- Publication number
- CN105505214A CN105505214A CN201610028931.1A CN201610028931A CN105505214A CN 105505214 A CN105505214 A CN 105505214A CN 201610028931 A CN201610028931 A CN 201610028931A CN 105505214 A CN105505214 A CN 105505214A
- Authority
- CN
- China
- Prior art keywords
- oil
- plant wood
- wood oil
- weight part
- weather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a corrosion-resistant weather-resistant plant wood oil, which is free of benzene, toluene, dimethylbenzene and other organic solvents and heavy metal toxic or harmful substances and has the advantages of high drying rate and excellent properties. The corrosion-resistant weather-resistant plant wood oil mainly comprises the following components in parts by weight: A) 40-60 parts of vegetable oil resin, B) 30-50 parts of diluting solvent, and C) 0.5-3 parts of drying agent. The plant wood oil can be used in various home decoration paints and especially various paints for wood furniture.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of anticorrosion weather-proof plant wood oil.
Background technology
At present, usual employing is that base material processing synthetic resins paints as woodenware with petrochemical complex, nitro, amino, polyester, alkyd etc. are had containing conventional in this chemosynthesis paint, cannot avoid using Chemical Solvents benzene,toluene,xylene, acetone etc., formaldehyde is harmful in more than 5 years, and containing poisonous and hazardous heavy metal, as: mercury, lead, chromium, cadmium, arsenic, selenium or antimony etc.Light then injure respiratory tract, heavy then cause the disease such as septicemia, cancer.In order to eliminate and reduce indoor pollution health hazard, national governments have launched respectively the content of objectionable impurities in a series of policy restriction and specification interior paint coating.Although these measures limit and decrease the murder by poisoning of objectionable impurities to air or human body to a certain extent.But in the long run/term, these standards are only minimum emission standards, use the paint of this chemosynthesis still poisoning of accumulating over a long period the health of people.The work material conformed that natural phant wood oil is produced according to natural original appearance, not containing poisonous and harmful substances such as organic solvent, heavy metal, formaldehyde or isocyanic ester.Paint film and deposit Shi Douhui produce toxic substance at production, treated oil, can not produce harm with during human contact, can have natural fragrance on the contrary, to the living space of people's happiness, be a kind of real environment protection oil paint.Meanwhile, natural paint is all good than chemical paint performance in most of, and such as weathering resistance, long service life, scrubbing resistance, adhesivity, anti-electrostatic, anti-be full of cracks, intensity and hardness are all very outstanding.But plant wood oil rate of drying is slow, affects production efficiency.
Summary of the invention
The object of this invention is to provide one not containing organic solvent and heavy metallic poison materials such as benzene,toluene,xylenes, rate of drying is fast, the anticorrosion weather-proof plant wood oil of excellent performance.
Anticorrosion weather-proof plant wood oil of the present invention, mainly comprises the component of following weight part: A) 40-60 weight part plant oil resin; B) 30-50 weight part diluting solvent; C) 0.5-3 weight part siccative.In anticorrosion weather-proof plant wood oil of the present invention, described plant oil resin is the various greases deriving from plant, concrete example can be, oleum lini, soya-bean oil, Viscotrol C, tung oil, Canola oil, orange oil, Chinese parasol tree oil, pine tar, loquat oil or plam oil in one or more.Consider the weathering resistance as paint, the impact of the aspect of performances such as intensity hardness, be preferably one or more in oleum lini, tung oil, pine tar or plam oil, more preferably tung oil.Consider environmental requirement, described diluting solvent is the solvent oil of Porous deproteinized bone, and concrete example, as D40 aliphatic hydrocarbon Porous deproteinized bone solvent oil, is preferably the Porous deproteinized bone solvent oil of extracting from Vegetable oil lipoprotein, as 70# solvent oil, thus the environment protecting plant paint of complete Nantural non-toxic evil can be reached.In the present invention, described siccative is specifically as follows metal oxide, metal-salt, aliphatic group acid metal compound, consider the drying efficiency to plant paint, particularly to the drying efficiency of tung oil, be preferably aliphatic group acid metal compound, the preferred carbonatoms of described aliphatic group is 10-20; Described aliphatic group acid metal compound can be saturated fatty alkyl acid metal compound, as metallic stearic compound, also can be unsaturated aliphatic hydrocarbyl moiety acid metal compound, as ricinolic acid metallic compound, be preferably unsaturated aliphatic hydrocarbyl moiety acid metal compound.Metal in described aliphatic group acid metal compound can be cobalt, manganese, zinc, calcium, iron, zirconium, cerium or rare earth.In order to improve the hardness of described anticorrosion weather-proof plant wood oil further, the stearic acid also containing 0.1-1 weight part in anticorrosion weather-proof plant wood oil of the present invention.Anticorrosion weather-proof plant wood oil of the present invention, the plants essential oil of 5-15 weight part can also be added further, by adding plants essential oil, the perviousness after the japanning of described plant wood oil and preservative property can be improved on the one hand, on the other hand, the fragrance that plants essential oil distributes can purify air, eliminate human body mental fatigue, alleviate stress, make people energetic, described plants essential oil refers to the distinctive aromatoising substance of extraction plant, can concrete example as tea tree oil, eucalyptus oil, lemon oil, Oleum lavandula angustifolia, Syzygium aromaticum stem oil, spearmint oil, Oleum Cinnamomi, thyme oil, lemongrass oil, ucuhuba oil, wintergreen oil, bay-oil, or pine needle wet goods.When not affecting its performance, in anticorrosion weather-proof plant wood oil of the present invention, various filler can also be added, pigment or other auxiliary agent.
The preparation technology of anticorrosion weather-proof plant wood oil of the present invention does not limit, following technique can be adopted to be prepared by above-mentioned composition and proportioning, first plant oil resin is added in heating kettle, be heated to 200-250 DEG C and stir 2-5 hour, then be cooled to 80-100 DEG C and add diluting solvent, siccative and other auxiliary agent stir, and reduce temperature to room temperature.
Anticorrosion weather-proof plant wood oil of the present invention, not containing containing organic solvent and the heavy metallic poison materials such as benzene,toluene,xylene, rate of drying is fast, excellent performance, can apply in various house ornamentation paint, the particularly paint of various wood furniture.
Embodiment
For a better understanding of the present invention, be described further below in conjunction with the anticorrosion weather-proof plant wood oil of specific embodiment to invention:
Embodiment 1
The tung oil of 50 weight parts is heated to 230 DEG C, stirs 4 hours, then reduce temperature to 90 DEG C, add the D40 solvent oil of 40 weight parts, the Zinic stearas of 1 weight part, the stearic acid of 0.2 weight part, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 4 hours.
Embodiment 2
The tung oil of 50 weight parts is heated to 230 DEG C, stirs 4 hours, then reduce temperature to 90 DEG C, add the D40 solvent oil of 40 weight parts, the ricinolic acid manganese of 1 weight part, the stearic acid of 0.2 weight part, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 1.5 hours.
Embodiment 3
The oleum lini of 50 weight parts is heated to 230 DEG C, stirs 4 hours, then reduce temperature to 90 DEG C, add the D40 solvent oil of 40 weight parts, the ricinolic acid manganese of 1 weight part, the stearic acid of 0.2 weight part, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 4.5 hours.
Embodiment 4
The tung oil of 50 weight parts is heated to 230 DEG C, stirs 4 hours, then reduce temperature to 90 DEG C, add the D40 solvent oil of 40 weight parts, the manganese stearate of 1 weight part, the stearic acid of 0.2 weight part, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 4 hours.
Embodiment 5
The tung oil of 60 weight parts is heated to 220 DEG C, stirs 5 hours, then reduce temperature to 90 DEG C, add the 70# solvent oil of 40 weight parts, the ricinolic acid manganese of 1.2 weight parts, the stearic acid of 0.2 weight part, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 1 hour.
Embodiment 6
The tung oil of 60 weight parts is heated to 220 DEG C, stirs 5 hours, then reduce temperature to 90 DEG C, add the 70# solvent oil of 40 weight parts, the manganese stearate of 1.2 weight parts, the stearic acid of 0.2 weight part, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 4 hours.
Embodiment 7
The tung oil of 60 weight parts is heated to 220 DEG C, stirs 5 hours, then reduce temperature to 90 DEG C, add the 70# solvent oil of 40 weight parts, 10 weight part Oleum lavandula angustifolias, the ricinolic acid manganese of 1.2 weight parts, the stearic acid of 0.2 weight part, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 1.5 hours.
Comparative example
The tung oil of 60 weight parts is heated to 220 DEG C, stirs 5 hours, then reduce temperature to 90 DEG C, add the 70# solvent oil of 40 weight parts, the stearic acid of 10.2 weight parts, stirs, and is reduced to room temperature.Carried out brushing rear drying by the above-mentioned paint prepared, its time of drying is 22 hours.
Claims (9)
1. an anticorrosion weather-proof plant wood oil, is characterized in that described plant wood oil mainly comprises the component of following weight part: A) 40-60 weight part plant oil resin; B) 30-50 weight part diluting solvent; C) 0.5-3 weight part siccative.
2. anticorrosion weather-proof plant wood oil according to claim 1, is characterized in that, described plant oil resin be oleum lini, soya-bean oil, Viscotrol C, tung oil, Canola oil, orange oil, Chinese parasol tree oil, pine tar, loquat oil or plam oil in one or more.
3. anticorrosion weather-proof plant wood oil according to claim 2, it is characterized in that, described plant oil resin is tung oil.
4. anticorrosion weather-proof plant wood oil according to claim 1, it is characterized in that, described siccative is aliphatic group acid metal compound.
5. anticorrosion weather-proof plant wood oil according to claim 4, it is characterized in that, described aliphatic group acid metal compound is unsaturated alkyl acid metal compound.
6. anticorrosion weather-proof plant wood oil according to claim 4, it is characterized in that, the metal in described aliphatic group acid metal compound is cobalt, manganese, zinc, calcium, iron, zirconium, cerium or rare earth.
7. anticorrosion weather-proof plant wood oil according to claim 1, it is characterized in that, described diluting solvent is Porous deproteinized bone solvent oil.
8. anticorrosion weather-proof plant wood oil according to claim 1, is characterized in that, the stearic acid also containing 0.1-1 weight part in described plant wood oil.
9. anticorrosion weather-proof plant wood oil according to claim 1, is characterized in that, the plants essential oil also containing 5-15 weight part in described plant wood oil.