CN105505062A - JS waterproof paint and preparing method thereof - Google Patents
JS waterproof paint and preparing method thereof Download PDFInfo
- Publication number
- CN105505062A CN105505062A CN201610011481.5A CN201610011481A CN105505062A CN 105505062 A CN105505062 A CN 105505062A CN 201610011481 A CN201610011481 A CN 201610011481A CN 105505062 A CN105505062 A CN 105505062A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- powder
- emulsion
- waterproof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to JS waterproof paint and a preparing method thereof. The JS waterproof paint comprises a liquid part and a powder part. The liquid part is prepared from, by weight, 240-260 parts of acrylic acid elastic emulsion, 0-10 parts of emulsion modifier, 90-100 parts of water, 1-5 parts of defoamer and 1-5 parts of bactericide. The powder part is prepared from, by weight, 240-260 parts of ordinary Portland cement, 290-310 parts of ground calcium carbonate, 90-110 parts of quartz powder, 0-6 parts of coal ash and 1-8 parts of water reducer. The paint is environmentally friendly, stable in performance, excellent in aging resistance and long in waterproof life. Construction can be directly conducted on a moist surface free of open water by means of the paint. Meanwhile, the coating of the paint is high in flexibility, elasticity, weather resistance, air permeability and bonding strength, construction opening time is long, hydration curing time is short, and construction is convenient. The JS waterproof paint has durable performance.
Description
Technical field
The present invention relates to a kind of building coating, be specifically related to a kind of JS waterproof paint and preparation method thereof.
Background technology
Now waterproof paint commercially mainly contains two large classes: a class is polyurethanes waterproof paint, is formed by the prepolymer containing isocyanate group and mixing by a certain percentage containing poly-hydroxy or the solidifying agent of amido and the mixture of other auxiliary agents.This kind of reactive type of coating can ambient cure, and simple to operate, the strong adhesion of film, has good mechanical property and water resistance, but due to containing noxious solvent, the requirement of people to environmental protection limits its application.Another kind of is polymer cement-base waterproof coating, by suitable polymer emulsion and mineral filler compound composition two-pack water-emulsifying type waterproof coatings.The high-ductility elastomeric property of polymkeric substance and the good durability of inorganic materials can be assembled into one by this kind of coating, reach synergistic effect, compensate for the shortcoming of the two.Polymer cement-base waterproof coating is the tasteless environmentfriendly products of low toxicity, one of developing direction belonging to waterproof coating, but its snappiness is poor.
Summary of the invention
The object of the invention is to: a kind of JS waterproof paint and preparation method thereof is provided
In order to realize foregoing invention object, the invention provides following technical scheme:
A kind of JS waterproof paint, comprise feed liquid part and powder part, described feed liquid part is made up of the raw material of following weight part: acrylic elastic emulsion 240-260 part, emulsion modifying agent 0-10 part, water 90-100 part, defoamer 1-5 part, sterilant 1-5 part; Described powder part is made up of the raw material of following weight part: ordinary Portland cement 240-260 part, water-ground limestone 290-310 part, silica powder 90-110 part, flyash 0-6 part, water reducer 1-8 part.
Preferably, described JS waterproof paint, comprises feed liquid part and powder part, and described feed liquid part is made up of the raw material of following weight part: acrylic elastic emulsion 242 parts, emulsion modifying agent 8 parts, 91 parts, water, defoamer 2 parts, 2 parts, sterilant; Described powder part is made up of the raw material of following weight part: ordinary Portland cement 250 parts, water-ground limestone 300 parts, silica powder 100 parts, 3 parts, flyash, water reducer 5 parts.
Preferably, the particle diameter of described silica powder is 130-160 order, and the particle diameter of described water-ground limestone is 400-600 order.
Preferably, a kind of preparation method of JS waterproof paint, concrete steps are as follows:
(1) preparation of feed liquid part: first water is joined in Special agitating dispersion machine, open motor, speed governing is to 180-220 rev/min, emulsion modifying agent is slowly added to the water, after adding, by electric machine speed regulation to 1800-2200 rev/min, emulsion modifying agent is all dissolved into glue, acrylic elastic emulsion is slowly joined dispersion in the emulsion modifying agent aqueous solution and stir 8-12 minute, carry out normal temperature from glue connection thickening reaction, after the copolyreaction of glue connection terminates, add defoamer, sterilant dispersed with stirring 5-10 minute;
(2) preparation of powder part: by ordinary Portland cement, water-ground limestone, silica powder, flyash, water reducer, joins in the lump in enclosed high effective dry powder blender and stirs;
(3) finally powder part is joined liquid material part to stir, can use.
Beneficial effect of the present invention is: JS waterproof paint of the present invention is green material, and it is free from environmental pollution, stable performance, ageing resistance is excellent, the waterproof life-span is long; Directly can construct at the moisture substrate without open fire; Meanwhile, well, weathering resistance and good air permeability, cohesive strength is high, and the construction open hour are longer, and the hydration curing time is short, easy construction, is a kind of JS waterproof paint of consistency of performance for the snappiness of paint coatings of the present invention and elasticity.
Embodiment
Embodiment 1
A kind of JS waterproof paint, comprise feed liquid part and powder part, described feed liquid part is made up of the raw material of following weight part: acrylic elastic emulsion 240 parts, emulsion modifying agent 1 part, 90 parts, water, defoamer 1 part, 1 part, sterilant; Described powder part is made up of the raw material of following weight part: ordinary Portland cement 240 parts, water-ground limestone 290 parts, silica powder 90 parts, 1 part, flyash, water reducer 1 part.Wherein, the particle diameter of described silica powder is 130 orders, and the particle diameter of described water-ground limestone is 400 orders.
The preparation method of above-mentioned JS waterproof paint, concrete steps are as follows:
(1) preparation of feed liquid part: first water is joined in Special agitating dispersion machine, open motor, speed governing to 180 rev/min, emulsion modifying agent is slowly added to the water, after adding, by electric machine speed regulation to 1800 rev/min, emulsion modifying agent is all dissolved into glue, acrylic elastic emulsion is slowly joined in the emulsion modifying agent aqueous solution and disperse stirring 8 minutes, carry out normal temperature from glue connection thickening reaction, after the copolyreaction of glue connection terminates, add defoamer, sterilant dispersed with stirring 5 minutes;
(2) preparation of powder part: by ordinary Portland cement, water-ground limestone, silica powder, flyash, water reducer, joins in the lump in enclosed high effective dry powder blender and stirs;
(3) finally powder part is joined liquid material part to stir, can use.
Embodiment 2
A kind of JS waterproof paint, comprise feed liquid part and powder part, described feed liquid part is made up of the raw material of following weight part: acrylic elastic emulsion 242 parts, emulsion modifying agent 8 parts, 91 parts, water, defoamer 2 parts, 2 parts, sterilant; Described powder part is made up of the raw material of following weight part: ordinary Portland cement 250 parts, water-ground limestone 300 parts, silica powder 100 parts, 3 parts, flyash, water reducer 5 parts.Wherein, the particle diameter of described silica powder is 150 orders, and the particle diameter of described water-ground limestone is 500 orders.
The preparation method of above-mentioned JS waterproof paint, concrete steps are as follows:
(1) preparation of feed liquid part: first water is joined in Special agitating dispersion machine, open motor, speed governing to 200 rev/min, emulsion modifying agent is slowly added to the water, after adding, by electric machine speed regulation to 2000 rev/min, emulsion modifying agent is all dissolved into glue, acrylic elastic emulsion is slowly joined in the emulsion modifying agent aqueous solution and disperse stirring 10 minutes, carry out normal temperature from glue connection thickening reaction, after the copolyreaction of glue connection terminates, add defoamer, sterilant dispersed with stirring 8 minutes;
(2) preparation of powder part: by ordinary Portland cement, water-ground limestone, silica powder, flyash, water reducer, joins in the lump in enclosed high effective dry powder blender and stirs;
(3) finally powder part is joined liquid material part to stir, can use.
Embodiment 3
A kind of JS waterproof paint, comprise feed liquid part and powder part, described feed liquid part is made up of the raw material of following weight part: acrylic elastic emulsion 260 parts, emulsion modifying agent 10 parts, 100 parts, water, defoamer 5 parts, 5 parts, sterilant; Described powder part is made up of the raw material of following weight part: ordinary Portland cement 260 parts, water-ground limestone 310 parts, silica powder 110 parts, 6 parts, flyash, water reducer 8 parts.Wherein, the particle diameter of described silica powder is 160 orders, and the particle diameter of described water-ground limestone is 600 orders.
The preparation method of above-mentioned JS waterproof paint, concrete steps are as follows:
(1) preparation of feed liquid part: first water is joined in Special agitating dispersion machine, open motor, speed governing to 220 rev/min, emulsion modifying agent is slowly added to the water, after adding, by electric machine speed regulation to 2200 rev/min, emulsion modifying agent is all dissolved into glue, acrylic elastic emulsion is slowly joined in the emulsion modifying agent aqueous solution and disperse stirring 12 minutes, carry out normal temperature from glue connection thickening reaction, after the copolyreaction of glue connection terminates, add defoamer, sterilant dispersed with stirring 10 minutes;
(2) preparation of powder part: by ordinary Portland cement, water-ground limestone, silica powder, flyash, water reducer, joins in the lump in enclosed high effective dry powder blender and stirs;
(3) finally powder part is joined liquid material part to stir, can use.
Claims (4)
1. a JS waterproof paint, is characterized in that, comprises feed liquid part and powder part, described feed liquid part is made up of the raw material of following weight part: acrylic elastic emulsion 240-260 part, emulsion modifying agent 0-10 part, water 90-100 part, defoamer 1-5 part, sterilant 1-5 part; Described powder part is made up of the raw material of following weight part: ordinary Portland cement 240-260 part, water-ground limestone 290-310 part, silica powder 90-110 part, flyash 0-6 part, water reducer 1-8 part.
2. JS waterproof paint according to claim 1, is characterized in that, comprises feed liquid part and powder part, described feed liquid part is made up of the raw material of following weight part: acrylic elastic emulsion 242 parts, emulsion modifying agent 8 parts, 91 parts, water, defoamer 2 parts, 2 parts, sterilant; Described powder part is made up of the raw material of following weight part: ordinary Portland cement 250 parts, water-ground limestone 300 parts, silica powder 100 parts, 3 parts, flyash, water reducer 5 parts.
3. JS waterproof paint according to claim 1 and 2, is characterized in that, the particle diameter of described silica powder is 130-160 order, and the particle diameter of described water-ground limestone is 400-600 order.
4. a preparation method for JS waterproof paint, is characterized in that, concrete steps are as follows:
(1) preparation of feed liquid part: first water is joined in Special agitating dispersion machine, open motor, speed governing is to 180-220 rev/min, emulsion modifying agent is slowly added to the water, after adding, by electric machine speed regulation to 1800-2200 rev/min, emulsion modifying agent is all dissolved into glue, acrylic elastic emulsion is slowly joined dispersion in the emulsion modifying agent aqueous solution and stir 8-12 minute, carry out normal temperature from glue connection thickening reaction, after the copolyreaction of glue connection terminates, add defoamer, sterilant dispersed with stirring 5-10 minute;
(2) preparation of powder part: by ordinary Portland cement, water-ground limestone, silica powder, flyash, water reducer, joins in the lump in enclosed high effective dry powder blender and stirs;
(3) finally powder part is joined liquid material part to stir, can use.