CN105503022A - 一种适用于建筑材料的负离子复合粉料 - Google Patents
一种适用于建筑材料的负离子复合粉料 Download PDFInfo
- Publication number
- CN105503022A CN105503022A CN201511032622.3A CN201511032622A CN105503022A CN 105503022 A CN105503022 A CN 105503022A CN 201511032622 A CN201511032622 A CN 201511032622A CN 105503022 A CN105503022 A CN 105503022A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- negative ion
- composite powder
- ion composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明披露了一种适用于建筑材料的负离子复合粉料，其由按质量份数计的下述组份制得：锆石粉30-80份；黑电气石粉10-30份；六偏磷酸钠1-8份；氧化锌1-5份；稀土0-30份；沸石粉1-30份；水性丙烯酸1-8份；独居石粉1-8份。本发明提供的技术方案制作工艺简单，原材料价格低廉，负离子板具有持久性、高效性、环保性，制得的负离子板能够高效稳定的释放负离子2200～4000个/s·cm2，能够净化空气、消除室内异味和有害气体，是一种环保型负离子添加剂。
Description
技术领域
本发明涉及一种复合粉料，具体涉及一种适用于建筑材料的负离子复合粉料。
背景技术
居住环境对身体健康的影响不断受到人们的关注，人们追求室内装饰装修豪华、美观的同时，也关注着室内污染影响人体健康，建筑用材的环保性，以及对人体健康产生的影响。因此，各种有益于健康的新型建筑功能性材料应运而生。
负离子材料作为一种具有环保、健康等多功能的新型材料代表之一，被广泛的应用于纺织品、陶瓷、建筑材料等领域。自1902年Aschkinass和Caspan肯定空气负离子具有生物意义，1903年苏联学者发表了利用空气负离子消除病菌的论文以来，科研人员相继开展了大量实验研究，进一步肯定了空气负离子的价值。
城市房间里的负氧离子浓度是每立方厘米100个，楼宇办公室里的浓度甚至低到每立方厘米40～50个，而世界卫生组织划定的标准，清新空气的负氧离子含量为每立方厘米空气中不低于1000～1500个，所以在这样环境工作往往容易诱发头痛失眠等不适。很多都市白领工作一天之后感到头昏脑胀，就和空气不够“营养”有一定关系。而森林和瀑布地区、高山海边和公园里的“大气维生素”含量很丰富，分别能达每立方厘米10000～20000个、5000～10000个和400～1000个。负氧离子能促进人体新陈代谢、预防流感、增强机体抗病能力。
CN103805134A中国专利公开了一种新型负离子添加剂，所得产品的缺点是产生的负离子浓度不高、功效持久性差。
本发明提供了一种适用于建筑材料的负离子复合粉料，这种负离子复合粉料具有持久、高效性，并且制作工艺简单、原材料价格低廉，适合大规模生产。
发明内容
本发明提供一种适用于建筑材料的负离子复合粉料，能够高效稳定的释放负离子，能够净化空气、消除室内异味和各种有害气体，是一种新型高效稳定负离子添加剂。
本发明目的是采用以下技术方案实现的：
一种负离子复合粉料，按照质量份数计，所述复合粉料由下述组份制得：锆石粉30-80份；黑电气石粉10-30份；六偏磷酸钠1-8份；氧化锌1-5份；稀土0-30份；沸石粉1-30份；水性丙烯酸1-8份；独居石粉1-8份；聚纤维素醚1-3份。
一种负离子复合粉料的第一优选方案，按照质量份数计，所述复合粉料由下述组份制得：锆石粉40-60份；黑电气石粉15-25份；六偏磷酸钠3-6份；氧化锌2-4份；稀土5-20份；沸石粉5-20份；水性丙烯酸3-5份；独居石粉2-6份；聚纤维素醚2-3份。
一种负离子复合粉料的第二优选方案，按照质量份数计，所述复合粉料由下述组份制得：锆石粉50份；黑电气石粉15份；六偏磷酸钠4份；氧化锌3份；稀土16份；沸石粉15份；水性丙烯酸4份；独居石粉5份；聚纤维素醚2份。
一种负离子复合粉料的第三优选方案，所述锆石粉和黑电气石粉经水性丙烯酸预处理。
一种负离子复合粉料的第四优选方案，所述锆石粉粒径为10～30μm，所述黑电气石粉粒径为15-40μm。
一种负离子复合粉料的第五优选方案，所述预处理包括：将所述锆石粉和黑电气石粉混合，然后与水性丙烯酸混合配置水溶液，在60～90℃下水浴1小时，过滤，干燥，打散。
一种负离子复合粉料的第六优选方案，所述复合粉料通过干粉混合机混合均匀得到。
与最接近的现有技术相比，本发明提供的技术方案具有以下优异效果：
(1)本发明提供的负离子复合粉料，并且制作工艺简单、原材料价格低廉，适合大规模生产；
(2)本发明提供的负离子复合粉料具有持久性、高效性、环保性；
(3)本发明提供的负离子复合粉料制备的负离子板能够高效稳定的释放负离子2000～3800个/s·cm2，能够净化空气、消除室内异味和各种有害气体。
具体实施方式
下面将结合实施例，对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施案例1：
称取粒径为30μm的锆石粉30份，粒径为40μm的黑电气石粉10份，水性丙烯酸1份，加入适量的水在60℃下水浴0.5小时，过滤，干燥，打散，称取六偏磷酸钠1份、氧化锌1份、稀土30份、沸石粉30份、独居石粉8份，聚纤维素醚1份，通过干粉混合机混合均匀，即可以得到负氧离子复合粉料。
实施案例2：
称取粒径为20μm的锆石粉80份，粒径为25μm的黑电气石粉30份，水性丙烯酸8份，加入适量的水在90℃下水浴1小时，过滤，干燥，打散，称取六偏磷酸钠8份、氧化锌5份、沸石粉1份、独居石粉1份，聚纤维素醚3份，通过干粉混合机混合均匀，即可以得到负氧离子复合粉料。
实施案例3：
称取粒径为10μm的锆石粉40份，粒径为15μm的黑电气石粉20份，水性丙烯酸3份，加入适量的水在90℃下水浴1小时，过滤，干燥，打散，称取六偏磷酸钠3份、氧化锌2份、稀土5份、沸石粉5份、独居石粉2份，聚纤维素醚2份，通过干粉混合机混合均匀，即可以得到负氧离子复合粉料。
实施案例4：
称取粒径为20μm的锆石粉60份，粒径为25μm的黑电气石粉15份，水性丙烯酸5份，加入适量的水在90℃下水浴1小时，过滤，干燥，打散，称取六偏磷酸钠6份、氧化锌4份、稀土20份、沸石粉20份、独居石粉6份，聚纤维素醚2份，通过干粉混合机混合均匀，即可以得到负氧离子复合粉料。
实施案例5：
称取粒径为10μm的锆石粉50份，粒径为20μm的黑电气石粉25份，水性丙烯酸4份，加入适量的水在90℃下水浴1小时，过滤，干燥，打散，称取六偏磷酸钠4份、氧化锌3份、稀土16份、沸石粉15份、独居石粉5份，聚纤维素醚2份，通过干粉混合机混合均匀，即可以得到负氧离子复合粉料。
实施案例6：
称取粒径为10μm的锆石粉40份，粒径为15μm的黑电气石粉20份，水性丙烯酸3份，加入适量的水在90℃下水浴1小时，过滤，干燥，打散，称取六偏磷酸钠3份、氧化锌2份、稀土5份、辉沸石粉5份、独居石粉6份，聚纤维素醚2份，通过干粉混合机混合均匀，即可以得到负氧离子复合粉料。
以上述各实施例中所得负氧离子复合粉料为原料，制得负离子板，按《JCT2040-2010负离子功能建筑室内装饰材料》标准，进行的空气负离子诱生量测试，结果列于下表：其中以现有技术CN103805134A公开的组份制得的负离子复合粉料作为对照组，以检测地未添加负离子粉的负离子量作为本底。
表1负离子板释放负离子的量
以上实施例仅用以说明本发明的技术方案而非对其限制，所属领域的普通技术人员应当理解，参照上述实施例可以对本发明的具体实施方式进行修改或者等同替换，这些未脱离本发明精神和范围的任何修改或者等同替换均在申请待批的权利要求保护范围之内。
Claims (7)
1.一种负离子复合粉料，其特征在于，按照质量份数计，所述复合粉料由下述组份制得：锆石粉30-80份；黑电气石粉10-30份；六偏磷酸钠1-8份；氧化锌1-5份；稀土0-30份；沸石粉1-30份；水性丙烯酸1-8份；独居石粉1-8份；聚纤维素醚1-3份。
2.根据权利要求1所述的一种负离子复合粉料，其特征在于，按照质量份数计，所述复合粉料由下述组份制得：锆石粉40-60份；黑电气石粉15-25份；六偏磷酸钠3-6份；氧化锌2-4份；稀土5-20份；沸石粉5-20份；水性丙烯酸3-5份；独居石粉2-6份；聚纤维素醚2-3份。
3.根据权利要求1所述的一种负离子复合粉料，其特征在于，按照质量份数计，所述复合粉料由下述组份制得：锆石粉50份；黑电气石粉20份；六偏磷酸钠4份；氧化锌3份；稀土16份；沸石粉15份；水性丙烯酸4份；独居石粉5份；聚纤维素醚2份。
4.根据权利要求1-3任一所述的一种负离子复合粉料，其特征在于，所述锆石粉和黑电气石粉经水性丙烯酸预处理。
5.根据权利要求1-3任一所述的一种负离子复合粉料，其特征在于，所述锆石粉粒径为10～30μm，所述黑电气石粉粒径为15-40μm。
6.根据权利要求4所述的一种负离子复合粉料，其特征在于，所述预处理包括：将所述锆石粉和黑电气石粉混合，然后与水性丙烯酸混合配置水溶液，在60～90℃下水浴1小时，过滤，干燥，打散。
7.根据权利要求1所述的一种负离子复合粉料，其特征在于，所述复合粉料通过干粉混合机混合均匀得到。