CN105499943A - Titanium pipe for heat exchange equipment - Google Patents
Titanium pipe for heat exchange equipment Download PDFInfo
- Publication number
- CN105499943A CN105499943A CN201510980204.0A CN201510980204A CN105499943A CN 105499943 A CN105499943 A CN 105499943A CN 201510980204 A CN201510980204 A CN 201510980204A CN 105499943 A CN105499943 A CN 105499943A
- Authority
- CN
- China
- Prior art keywords
- heat
- stock
- titanium alloy
- raw material
- grinding machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a titanium pipe for heat exchange equipment. The titanium pipe is prepared through the steps of: 1) material selection; 2) blank manufacturing; 3) surface treatment; and 4) heat treatment. The titanium pipe for the heat exchange equipment is excellent in corrosion resistance, heat resistance, cold resistance and oxidation resistance, and is long in service life.
Description
Technical field
The present invention relates to heat-exchange apparatus titanium pipe.
Background technology
Corrosion-resistant, heat-resisting, cold-resistant, the antioxygenic property of existing heat-exchange apparatus titanium pipe have to be supplied.
Summary of the invention
The object of the present invention is to provide a kind of heat-exchange apparatus titanium pipe, it is corrosion-resistant, heat-resisting, cold-resistant, antioxygenic property is good, long service life.
For achieving the above object, technical scheme of the present invention is a kind of heat-exchange apparatus titanium pipe of design, prepares as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:1~2%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
Preferably, heat-exchange apparatus titanium pipe, prepare as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:1%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
Preferably, heat-exchange apparatus titanium pipe, prepare as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:2%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
Advantage of the present invention and beneficial effect are: provide a kind of heat-exchange apparatus titanium pipe, it is corrosion-resistant, heat-resisting, cold-resistant, antioxygenic property is good, long service life.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of heat-exchange apparatus titanium pipe, prepare as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:1~2%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
Embodiment 2
Heat-exchange apparatus titanium pipe, prepare as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:1%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
Embodiment 3
Heat-exchange apparatus titanium pipe, prepare as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:2%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. heat-exchange apparatus titanium pipe, is characterized in that, prepares as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:1~2%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
2. heat-exchange apparatus titanium pipe according to claim 1, is characterized in that, prepares as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:1%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.
3. heat-exchange apparatus titanium pipe according to claim 1, is characterized in that, prepares as follows:
1) select materials: select titanium alloy to be raw material, by weight percentage, the composition of this titanium alloy is:
C:2%,
Te:0.9%,
Se:0.7%,
Pd:0.3%,
W:0.7%,
Ce:0.5%,
Surplus is Ti and inevitable impurity;
2) stock manufacture: the method adopting melting, forging, lathe process, makes tubular blank by above-mentioned titanium alloy raw material;
3) surface treatment: adopt grinding machine to roughly grind described stock, has roughly ground rear employing clear water and has been removed by surface finish sand grains, and then adopted grinding machine to refine described stock;
4) heat treatment: the stock after dipping is put into electric furnace and heat-treats.