CN105482285A - PVC floor - Google Patents
PVC floor Download PDFInfo
- Publication number
- CN105482285A CN105482285A CN201410464830.XA CN201410464830A CN105482285A CN 105482285 A CN105482285 A CN 105482285A CN 201410464830 A CN201410464830 A CN 201410464830A CN 105482285 A CN105482285 A CN 105482285A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- pvc floor
- calcium
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a PVC floor. The PVC floor comprises the following raw materials, by weight: 98-105 parts of PVC, 440-455 parts of stone powder, 28-32 parts of a plasticizer, 2.3-2.7 parts of a calcium-zinc composite stabilizing agent, and 0.1-0.3 part of carbon black. The plasticizer is a mixture of dioctyl terephthalate and non-phthalic acid, wherein the ratio of dioctyl terephthalate and non-phthalic acid, by weight part, is 1:1. According to the optimum embodiment, the PVC floor comprises the following raw materials, by weight: 100 parts of PVC, 450 parts of stone powder, 15 parts of dioctyl terephthalate, 15 parts of non-phthalic acid, 2.5 parts of the calcium-zinc composite stabilizing agent, and 0.2 part of carbon black. The PVC floor is simple and reasonable in formula. The floor prepared through the formula is safe, non-toxic, and eco-friendly, has a good plasticizing effect, and has a certain anti-microbial anti-mildew effect.
Description
Technical field
The invention belongs to floor processing technique field, relate to the PVC floor that a type material is made specifically.
Background technology
PVC floor is popular a kind of Novel light body floor decorative material in the world today, also referred to as " light body ground material ", a kind of product very popular in Japan and Korea S that are American-European and Asia, abroad fashionable, Chinese market is entered from the beginning of the eighties, so far big and medium-sized cities at home have obtained general accreditation, use widely, such as family, hospital, school, office building, factory, public place, supermarket, business, the various place such as stadiums, need to add softening agent in the process that PVC floor makes, the general softening agent used is DOP on the market at present, i.e. dioctyl phthalate (DOP), the product of such plasticizer production is used to there is carcinogenic risk.
Summary of the invention
In order to solve the problem, PVC floor prepared by the novel softening agent that the invention provides a kind of asepsis environment-protecting.
In order to achieve the above object, the present invention is achieved by the following technical solutions:
The present invention is a kind of PVC floor, and the raw material that described PVC floor comprises following weight part is made: PVC:98-105 part, stone flour: 440-455 part, softening agent: 28-32 part, calcium-zinc composite stabilizing agent: 2.3-2.7 part, carbon black: 0.1-0.3 part;
Described softening agent is dioctyl terephthalate and the benzoic mixture of non-neighboring, wherein, and dioctyl phthalate weight part: the benzoic weight part of non-neighboring is 1:1.
Further improvement of the present invention is: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 15 parts, non-o-benzoic acid: 15 parts, calcium-zinc composite stabilizing agent: 2.5 parts, carbon black: 0.2 part.
Further improvement of the present invention is: the raw material that described PVC floor comprises following weight part is made: PVC:98 part, stone flour: 455 parts, dioctyl phthalate: 14 parts, non-o-benzoic acid: 14 parts, calcium-zinc composite stabilizing agent: 2.3 parts, carbon black: 0.3 part.
Further improvement of the present invention is: the raw material that described PVC floor comprises following weight part is made: PVC:105 part, stone flour: 440 parts, dioctyl phthalate: 16 parts, non-o-benzoic acid: 16 parts, calcium-zinc composite stabilizing agent: 2.7 parts, carbon black 0.1 part.
Further improvement of the present invention is: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 14.5 parts, non-o-benzoic acid: 14.5 parts, calcium-zinc composite stabilizing agent: 2.45 parts, carbon black 0.25 part.
Further improvement of the present invention is: the raw material that described PVC floor comprises following weight part is made: PVC:101 part, stone flour: 450 parts, dioctyl phthalate: 15.5 parts, non-o-benzoic acid: 15.5 parts, calcium-zinc composite stabilizing agent: 2.55 parts, carbon black 0.21 part.
Further improvement of the present invention is: the raw material that described PVC floor comprises following weight part is made: PVC:99 part, stone flour: 448 parts, dioctyl phthalate: 14.8 parts, non-o-benzoic acid: 14.8 parts, calcium-zinc composite stabilizing agent: 2.45 parts, carbon black 0.19 part.
Further improvement of the present invention is: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 16 parts, non-o-benzoic acid: 16 parts, calcium-zinc composite stabilizing agent: 2.5 parts, carbon black 0.2 part.
The invention has the beneficial effects as follows: softening agent of the present invention adopts non-o-benzoic acid to support with mixing of DOTP, non-o-benzoic acid is carrying out the product of a class higher molecular weight of chlorination reaction generation after carrying out transesterification reaction by natural fats and oils and alcohol, and dioctyl phthalate and DOTP environment-protecting asepsis, heat-stable time is long, such softening agent is made up of natural fats and oils, there is fire-resistant, asepsis environment-protecting a little, not containing poisonous metal and adjacent benzene class material, good with PVC intermiscibility, plasticization effect is excellent, PVC floor obtained under this formula has good planeness, it is qualified that antimildew and antibacterial detects, the finished product only a little residual alcohol taste of processing.
The present invention fills a prescription simply, rationally, safe, nontoxic by the floor of this formula preparation, environmental protection, plasticization effect is good, has certain antibacterial anti-mildew effect.
Embodiment
In order to deepen the understanding of the present invention, be described in further detail the present invention below in conjunction with embodiment, this embodiment, only for explaining the present invention, not forming protection scope of the present invention and limiting.
As shown in the Examples, the present invention is a kind of PVC floor, and the raw material that described PVC floor comprises following weight part is made: PVC:98-105 part, stone flour: 440-455 part, softening agent: 28-32 part, calcium-zinc composite stabilizing agent: 2.3-2.7 part, carbon black: 0.1-0.3 part;
Described softening agent is dioctyl terephthalate and the benzoic mixture of non-neighboring, wherein, and dioctyl phthalate weight part: the benzoic weight part of non-neighboring is 1:1.
Stone flour adds to inside PVC and increases opaqueness, improve paper snappiness, calcium-zinc composite stabilizing agent keeps the stable of product, prevent its decompose, aging, softening agent of the present invention have employed natural non-o-benzoic acid agent dioctyl phthalate and mixes, and this softening agent well can mix with PVC, makes this product without poisonous metal and adjacent benzene class material, the product safety of preparation is nontoxic, and planeness is good.
Embodiment one
A kind of PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 15 parts, non-o-benzoic acid: 15 parts, calcium-zinc composite stabilizing agent: 2.5 parts, carbon black: 0.2 part.
Embodiment two
A kind of PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:98 part, stone flour: 455 parts, dioctyl phthalate: 14 parts, non-o-benzoic acid: 14 parts, calcium-zinc composite stabilizing agent: 2.3 parts, carbon black: 0.3 part.
Embodiment three
A kind of PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:105 part, stone flour: 440 parts, dioctyl phthalate: 16 parts, non-o-benzoic acid: 16 parts, calcium-zinc composite stabilizing agent: 2.7 parts, carbon black 0.1 part.
Embodiment four
A kind of PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 14.5 parts, non-o-benzoic acid: 14.5 parts, calcium-zinc composite stabilizing agent: 2.45 parts, carbon black 0.25 part.
Embodiment five
A kind of PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:101 part, stone flour: 450 parts, dioctyl phthalate: 15.5 parts, non-o-benzoic acid: 15.5 parts, calcium-zinc composite stabilizing agent: 2.55 parts, carbon black 0.21 part.
Embodiment six
A kind of PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:99 part, stone flour: 448 parts, dioctyl phthalate: 14.8 parts, non-o-benzoic acid: 14.8 parts, calcium-zinc composite stabilizing agent: 2.45 parts, carbon black 0.19 part.
Embodiment seven
A kind of PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 16 parts, non-o-benzoic acid: 16 parts, calcium-zinc composite stabilizing agent: 2.5 parts, carbon black 0.2 part.
Claims (8)
1. a PVC floor, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:98-105 part, stone flour: 440-455 part, softening agent: 28-32 part, calcium-zinc composite stabilizing agent: 2.3-2.7 part, carbon black: 0.1-0.3 part;
Described softening agent is dioctyl terephthalate and the benzoic mixture of non-neighboring, wherein, and dioctyl phthalate weight part: the benzoic weight part of non-neighboring is 1:1.
2. a kind of PVC floor according to claim 1, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 15 parts, non-o-benzoic acid: 15 parts, calcium-zinc composite stabilizing agent: 2.5 parts, carbon black: 0.2 part.
3. a kind of PVC floor according to claim 1, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:98 part, stone flour: 455 parts, dioctyl phthalate: 14 parts, non-o-benzoic acid: 14 parts, calcium-zinc composite stabilizing agent: 2.3 parts, carbon black: 0.3 part.
4. a kind of PVC floor according to claim 1, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:105 part, stone flour: 440 parts, dioctyl phthalate: 16 parts, non-o-benzoic acid: 16 parts, calcium-zinc composite stabilizing agent: 2.7 parts, carbon black 0.1 part.
5. a kind of PVC floor according to claim 1, it is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 14.5 parts, non-o-benzoic acid: 14.5 parts, calcium-zinc composite stabilizing agent: 2.45 parts, carbon black 0.25 part.
6. a kind of PVC floor according to claim 1, it is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:101 part, stone flour: 450 parts, dioctyl phthalate: 15.5 parts, non-o-benzoic acid: 15.5 parts, calcium-zinc composite stabilizing agent: 2.55 parts, carbon black 0.21 part.
7. a kind of PVC floor according to claim 1, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:99 part, stone flour: 448 parts, dioctyl phthalate: 14.8 parts, non-o-benzoic acid: 14.8 parts, calcium-zinc composite stabilizing agent: 2.45 parts, carbon black 0.19 part.
8. a kind of PVC floor according to claim 1, is characterized in that: the raw material that described PVC floor comprises following weight part is made: PVC:100 part, stone flour: 450 parts, dioctyl phthalate: 16 parts, non-o-benzoic acid: 16 parts, calcium-zinc composite stabilizing agent: 2.5 parts, carbon black 0.2 part.