CN105470502A - Positive lead plaster containing superconducting material additive for lead storage battery - Google Patents
Positive lead plaster containing superconducting material additive for lead storage battery Download PDFInfo
- Publication number
- CN105470502A CN105470502A CN201510821135.9A CN201510821135A CN105470502A CN 105470502 A CN105470502 A CN 105470502A CN 201510821135 A CN201510821135 A CN 201510821135A CN 105470502 A CN105470502 A CN 105470502A
- Authority
- CN
- China
- Prior art keywords
- lead
- parts
- superconductor
- positive
- lead plaster
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a positive lead plaster containing a superconducting material additive for a lead storage battery. The positive lead plaster comprises the following components in parts by weight: 80-83 parts of lead powder, 10-15 parts of water, 4-10 parts of sulfuric acid, 0.1-0.5 part of a superconducting material and 0.1-0.2 part of a staple fiber. According to the positive lead plaster containing the superconducting material additive for the lead storage battery disclosed by the invention, with the superconducting material as the additive of the positive lead plaster for the lead storage battery, the superconducting material can be well fused with active materials of the lead plaster; the conductivity and the microstructure of a positive plate can be effectively improved; deposition of mass sulfate in a discharge process is hindered; the charge acceptance of the battery is improved; and the positive lead plaster can be widely applicable to various lead-acid storage battery products.
Description
Technical field
The invention belongs to chemical power source associated materials field, be specifically related to a kind of formula of positive lead paste that can be used for lead accumulator.
Background technology
Lead accumulator is widely used in each fields such as power, energy storage, electric power, communication, broad categories.The basic composition participating in electrochemical reaction in lead accumulator is anode diachylon, cathode lead plaster and electrolyte.Anode diachylon is the important component part determining cell integrated capacity and performance.When preparing anode diachylon, generally can add the conductive materials such as expanded graphite to improve the conductivity of lead plaster, improve the utilance of active material.But the corrosion-resistant of battery, stability is low, and self discharge is comparatively large, therefore causes the useful life of battery shorter.The cryogenic property of storage battery is poor simultaneously.
Therefore, be necessary to seek novel suitable additive to improve conductivity and the microstructure of positive plate.Superconductor is due to the physics and chemistry character of its uniqueness, and range of application constantly expands.The present invention is intended to select suitable superconductor additive to improve the performance of anode lead plaster and battery product.
Therefore, need a kind of formula of positive lead paste that can be used for lead accumulator to solve the problem.
Summary of the invention
Goal of the invention: the problem that the present invention is directed to prior art, provides a kind of positive electode of lead battery lead plaster containing superconductor additive.
Summary of the invention: for solving the problems of the technologies described above, the technical scheme that the positive electode of lead battery lead plaster containing superconductor additive of the present invention adopts is:
A kind of positive electode of lead battery lead plaster containing superconductor additive, comprise lead powder, water, sulfuric acid, superconductor and short fiber, the composition by weight of each component is 80 ~ 83 parts, lead powder, 10 ~ 15 parts, water, 4 ~ 10 parts, sulfuric acid, superconductor 0.1 ~ 0.5 part and 0.1 ~ 0.2 part, short fiber.
Further, described superconductor is the mixture of one or more in niobium three germanium, niobium three aluminium and niobium three tin.
Further, the mixture of niobium three germanium of described superconductor to be weight ratio be 1:2:2, niobium three aluminium and niobium three tin.Adopt the superconductor of this weight ratio, through test, the electric conductivity of positive plate is best, and battery charge acceptance is stronger, and in electric discharge engineering the slow 3-4 of deposition rate prior art of large volume sulfate is doubly.
Beneficial effect: the positive electode of lead battery lead plaster containing superconductor additive of the present invention take superconductor as the additive of positive electode of lead battery lead plaster, superconductor itself can merge well with lead plaster active material, effectively can improve conductivity and the microstructure of positive plate, hinder the deposition of large volume sulfate in discharge process, improve the charge acceptance of battery, various lead acid accumulator product can be widely used in.
Embodiment
Below in conjunction with embodiment, the present invention is further described.Below be only better embodiment of the present invention; protection scope of the present invention is not limited with above-mentioned execution mode; in every case those of ordinary skill in the art modify or change according to the equivalence that disclosed content is done, and all should include in the protection range recorded in claims.
Positive electode of lead battery lead plaster containing superconductor additive of the present invention, comprise lead powder, water, sulfuric acid, superconductor and short fiber, the composition by weight of each component is 80 ~ 83 parts, lead powder, 10 ~ 15 parts, water, 4 ~ 10 parts, sulfuric acid, superconductor 0.1 ~ 0.5 part and 0.1 ~ 0.2 part, short fiber.Preferably, superconductor is the mixture of one or more in niobium three germanium, niobium three aluminium and niobium three tin.The mixture of niobium three germanium of superconductor to be weight ratio be 1:2:2, niobium three aluminium and niobium three tin.Adopt the superconductor of this weight ratio, through test, the electric conductivity of positive plate is best, and battery charge acceptance is stronger, and in electric discharge engineering the slow 3-4 of deposition rate prior art of large volume sulfate is doubly.
The invention also discloses a kind of preparation method of the lead accumulator cathode lead plaster containing superconductor additive, comprise the following steps:
1), each component is weighed according to claim 1 composition by weight;
2), by lead powder, superconductor and short fiber mix, obtain mixed material for subsequent use; The water of 50%-60% and sulfuric acid are mixed, obtains mixed solution for subsequent use;
3), in 30 minutes, while be uniformly mixed material limit to add mixed solution, add remaining water again after solution to be mixed adds completely, stir the positive electode of lead battery lead plaster namely obtained containing superconductor additive.
The preparation method of the positive electode of lead battery lead plaster containing superconductor additive of the present invention is simple and convenient, and step is reasonable in design, comparatively fast can obtain the positive electode of lead battery lead plaster containing superconductor additive.Take superconductor as the additive of positive electode of lead battery lead plaster, superconductor itself can merge well with lead plaster active material, effectively can improve conductivity and the microstructure of positive plate, hinder the deposition of large volume sulfate in discharge process, improve the charge acceptance of battery, various lead acid accumulator product can be widely used in.
Referring to specific embodiment, do a detailed introduction to of the present invention:
embodiment one:
First, by 80 parts, lead powder, 10 parts, water, 9.8 parts, sulfuric acid, niobium three germanium (Nb
3ge) 0.1 part, powder, the composition by weight that short fiber is 0.1 part weighs each component.
Secondly, by lead powder and niobium three germanium (Nb
3ge) superconductor, short fiber fully mix for subsequent use; The water of 5 parts and sulfuric acid are mixed into homogeneous mixed solution.
Finally, add mixed solution on 30min inner edge stir solids mixed material limit, after solution to be mixed adds completely, add the water of 5 parts again, stir and obtain adding the positive electode of lead battery lead plaster of superconductor.This lead plaster can carry out the subsequent production operation of battery by the mode of mechanical or artificial coated plate.
Through test, the electric conductivity of positive plate is better, and battery charge acceptance hinge structure improves 1-2 doubly, and in electric discharge engineering the slow 2-3 of deposition rate prior art of large volume sulfate is doubly.
embodiment two:
First, by 83 parts, lead powder, 10 parts, water, 6.3 parts, sulfuric acid, niobium three aluminium (Ne
3al) 0.5 part, powder, the composition by weight that short fiber is 0.2 part weighs each component.
Secondly, lead powder is fully mixed for subsequent use with niobium three aluminium superconductor, short fiber; The water of 6 parts and sulfuric acid are mixed into homogeneous mixed solution.
Finally, add mixed solution on 30min inner edge stir solids mixed material limit, after solution to be mixed adds completely, add the water of 4 parts again, stir and obtain adding the positive electode of lead battery lead plaster of superconductor.This lead plaster can carry out the subsequent production operation of battery by the mode of mechanical or artificial coated plate.
Through test, the electric conductivity of positive plate is better, and battery charge acceptance hinge structure improves 1-2 doubly, and in electric discharge engineering the slow 2-3 of deposition rate prior art of large volume sulfate is doubly.
embodiment three:
First, by 80 parts, lead powder, 10 parts, water, 9.8 parts, sulfuric acid, niobium three germanium (Nb
3ge) 0.05 part, powder, niobium three aluminium (Ne
3al) 0.05 part, powder, the composition by weight that short fiber is 0.1 part weighs each component.
Secondly, by lead powder and niobium three germanium (Nb
3ge), niobium three aluminium (Ne
3al) solid material such as superconductor, short fiber fully mixes for subsequent use; The water of 5 parts and sulfuric acid are mixed into homogeneous mixed solution.
Finally, add mixed solution on 30min inner edge stir solids mixed material limit, after solution to be mixed adds completely, add the water of 5 parts again, stir and obtain adding the positive electode of lead battery lead plaster of superconductor.This lead plaster can carry out the subsequent production operation of battery by the mode of mechanical or artificial coated plate.
Through test, the electric conductivity of positive plate is better, and battery charge acceptance hinge structure improves 1-2 doubly, and in electric discharge engineering the slow 2-3 of deposition rate prior art of large volume sulfate is doubly.
embodiment four:
First, by 80 parts, lead powder, 12 parts, water, 7.3 parts, sulfuric acid, niobium three germanium (Nb
3ge) 0.1 part, powder, niobium three aluminium (Ne
3al) 0.2 part, powder, niobium three tin (Nb
3sn) 0.2 part, powder, the composition by weight that short fiber is 0.2 part weighs each component.
Secondly, by lead powder and niobium three germanium (Nb
3ge), niobium three aluminium (Ne
3al), niobium three tin (Nb
3sn) superconductor short fiber fully mixes for subsequent use; The water of 6 parts and sulfuric acid are mixed into homogeneous mixed solution.
Finally, add mixed solution on 30min inner edge stir solids mixed material limit, after solution to be mixed adds completely, add the water of 6 parts again, stir and obtain adding the positive electode of lead battery lead plaster of superconductor.This lead plaster can carry out the subsequent production operation of battery by the mode of mechanical or artificial coated plate.
Through test, the electric conductivity of positive plate is best, and battery charge acceptance hinge structure improves 2-3 doubly, and in electric discharge engineering the slow 4-5 of deposition rate prior art of large volume sulfate is doubly.
Claims (3)
1. the positive electode of lead battery lead plaster containing superconductor additive, it is characterized in that: comprise lead powder, water, sulfuric acid, superconductor and short fiber, the composition by weight of each component is 80 ~ 83 parts, lead powder, 10 ~ 15 parts, water, 4 ~ 10 parts, sulfuric acid, superconductor 0.1 ~ 0.5 part and 0.1 ~ 0.2 part, short fiber.
2. the positive electode of lead battery lead plaster containing superconductor additive as claimed in claim 1, is characterized in that: described superconductor is the mixture of one or more in niobium three germanium, niobium three aluminium and niobium three tin.
3. the positive electode of lead battery lead plaster containing superconductor additive as claimed in claim 1, is characterized in that: the mixture of niobium three germanium of described superconductor to be weight ratio be 1:2:2, niobium three aluminium and niobium three tin.