CN105462455A - Special powder coating used for pumps and valves and having good stain resistance - Google Patents
Special powder coating used for pumps and valves and having good stain resistance Download PDFInfo
- Publication number
- CN105462455A CN105462455A CN201510865426.8A CN201510865426A CN105462455A CN 105462455 A CN105462455 A CN 105462455A CN 201510865426 A CN201510865426 A CN 201510865426A CN 105462455 A CN105462455 A CN 105462455A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- minute
- resin
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a special powder coating used for pumps and valves and having good stain resistance. The special powder coating is prepared from raw materials in parts by weight as follows: 44-47 parts of hydroxyl polyester resin, 7-8 parts of fluorocarbon resin, 9-11 parts of organic silicon resin, 4-5 parts of triglycidyl isocyanurate, 13-15 parts of nano-aluminium oxide, 0.8-0.9 parts of perfluorooctyltriethoxysilane, 25-30 parts of an ethanol solution with the concentration of 75wt%, 0.5-0.6 parts of a silane coupling agent kh560, 1-1.2 parts of an organosilicon leveling agent, 0.6-0.7 parts of guar gum, 4-5 parts of polyvinylidene fluoride, 3-4 parts of micron sized silica aerogel, 9-10 parts of nano titanium dioxide, 12-14 parts of calcium carbonate and a proper amount of water. A prepared coating film has the good stain resistance, and meanwhile, the coating has the good adhesion, cannot peel off, has light fastness, is stable, adopts the simple technology and has the long service life.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to the pump valve proprietary powder coatings that a kind of tool resistant is effective.
Background technology
In recent years, the application of powder coating has surmounted water-borne coatings and high solid coating etc. in coatings industry, becomes industry member and uses one of more coating variety.Powder coating process solves the problems such as inflammable, the explosive and contaminate environment existing for traditional paint coating process, and its coating possesses superior performance, the recyclable use again of raw material, and coating process is simple.Pump can be widely used in, valve housing is coated with and loads onto.Because pump valve is foundry goods or forging, therefore its surface irregularity, also certain defect is there is in currently available technology for the functional powder coating technology of valve surface process, cause coating to occur the defects such as shrinkage cavity, pinprick and serious orange peel shape, and then cause pump valve to be restricted in special dimension application such as food, biology, pharmacy, chemical industry, space flight and electronics.And most of pump valve all can be used in the factor such as the media environment impact of High water cut, Gao Hansha, deep-etching, increase the weight of the corrosion of pump valve, easier fouling on pump valve, thus cause pump valve short for work-ing life, the problem that round of visits is short, workload is large, make troubles to use, general surface intensified technique mainly contains metal plating, ceramic coating, some other coating, although slow down wearing and tearing to a certain extent, improve erosion resistance, but all there is weak point: the easy layering of metal plating causes coming off; Pottery shock resistance is poor, easy chipping phenomenon; Some polymeric coating mechanics and thermal characteristics difference etc.Thus research and development have the powder coating of the functions such as weather-proof, water-tight corrosion-proof, and possess skills the meaning promoting to improve with industry.
Summary of the invention
The object of the invention is exactly the defect in order to make up prior art, provides the pump valve proprietary powder coatings that a kind of tool resistant is effective.
The present invention is achieved by the following technical solutions:
The pump valve proprietary powder coatings that tool resistant is effective, is made up of the raw material of following weight part: hydroxy polyester resin 44-47, fluorocarbon resin 7-8, silicone resin 9-11, isocyanuric acid three-glycidyl ester 4-5, nano-aluminium oxide 13-15, perfluoro capryl triethoxyl silane 0.8-0.9, concentration are that ethanolic soln 25-30, the silane coupling agent kh5600.5-0.6 of 75wt%, organosilicon flow agent 1-1.2, guar gum 0.6-0.7, polyvinylidene difluoride (PVDF) 4-5, white rouge aerogel 3-4, nano titanium oxide 9-10, calcium carbonate 12-14, water are appropriate.
The pump valve proprietary powder coatings that described a kind of tool resistant is effective, is prepared from by following concrete steps:
(1) nano-aluminium oxide is put into the ethanolic soln that concentration is 75wt%, dispersed with stirring is even, then perfluoro capryl triethoxyl silane is added, reflux 2-2.5 hour, adds silane coupling agent kh560 after cooling, continue stirring reaction 2-3 hour, last underpressure distillation, slough the solvent in system, with the dry 60-80 minute of the temperature of 80-85 DEG C in vacuum drying oven, obtain active nano aluminium sesquioxide;
(2) calcium carbonate is added suitable quantity of water grinding 40-60 minute, filtration drying, cross 400 mesh sieves and then mix with nano titanium oxide, obtain mixed powder stand-by; To add the water of 5-7 times amount in white rouge aerogel, dispersed with stirring is even, is heated to 50-60 DEG C, adds mixed powder, stirs 30-40 minute, then spraying dry, obtain modified filler with the speed of 300 revs/min;
(3) hydroxy polyester resin, fluorocarbon resin, silicone resin, isocyanuric acid three-glycidyl ester are put into after homogenizer stirs 20-30 minute with the speed of 1000 revs/min and added active nano aluminium sesquioxide and modified filler, continue to stir discharging after 10-15 minute, compound is sent into twin screw melt extruder, continue to add all the other remaining components, melt extrude, compressing tablet, obtained fine powder through pulverizing 180 mesh sieves and get final product.
Advantage of the present invention is: the present invention adds a small amount of fluorocarbon resin Substitute For Partial hydroxy polyester resin, in the process of powder coating solidification, fluorocarbon chain section in fluorocarbon resin there occurs surface enrichment, so a small amount of fluorine just can significantly improve the hydro-oleophobicity of coating, the heat-proof water of coating, acid-proof alkaline and snappiness can be improved simultaneously; Coordinate and add through the obtained active nano aluminium sesquioxide of special process process, be easy to form chemical bonding with F-C key, make coating structure more firm, and the contact angle of coatingsurface to water sharply increases, further increase the hydrophobicity of coating, the powder coating made has anticorrosive, acid and alkali-resistance, weathering resistance, hydrophobic and lyophobic property etc. more than general powder coating excellence.
White rouge aerogel, nano titanium oxide add in the preparation of powder coating by a series of technique by the present invention, coordinate and add silicone resin, fluorocarbon resin, the coating film made is made to possess good resistance to soiling, the present invention simultaneously possesses good sticking power, obscission can not be there is, fast light stable, technique is simple, long service life.
Embodiment
The pump valve proprietary powder coatings that tool resistant is effective, is made up of the raw material of following weight part (kilogram): hydroxy polyester resin 44, fluorocarbon resin 7, silicone resin 9, isocyanuric acid three-glycidyl ester 4, nano-aluminium oxide 13, perfluoro capryl triethoxyl silane 0.8, concentration are that the ethanolic soln 25 of 75wt%, silane coupling agent kh5600.5, organosilicon flow agent 1, guar gum 0.6, polyvinylidene difluoride (PVDF) 4, white rouge aerogel 3, nano titanium oxide 9, calcium carbonate 12, water are appropriate.
The pump valve proprietary powder coatings that described a kind of tool resistant is effective, is prepared from by following concrete steps:
(1) nano-aluminium oxide is put into the ethanolic soln that concentration is 75wt%, dispersed with stirring is even, then perfluoro capryl triethoxyl silane is added, reflux 2 hours, adds silane coupling agent kh560 after cooling, continue stirring reaction 2 hours, last underpressure distillation, slough the solvent in system, with the temperature of 80 DEG C drying 60 minutes in vacuum drying oven, obtain active nano aluminium sesquioxide;
(2) calcium carbonate is added suitable quantity of water and grind 40 minutes, filtration drying, cross 400 mesh sieves and then mix with nano titanium oxide, obtain mixed powder stand-by; To add the water of 5 times amount in white rouge aerogel, dispersed with stirring is even, is heated to 50 DEG C, adds mixed powder, stir 30 minutes, then spraying dry, obtain modified filler with the speed of 300 revs/min;
(3) hydroxy polyester resin, fluorocarbon resin, silicone resin, isocyanuric acid three-glycidyl ester are put into after homogenizer stirs 20 minutes with the speed of 1000 revs/min and added active nano aluminium sesquioxide and modified filler, continue stirring discharging after 10 minutes, compound is sent into twin screw melt extruder, continue to add all the other remaining components, melt extrude, compressing tablet, obtained fine powder through pulverizing 180 mesh sieves and get final product.
Electrostatic spraying constructional method is adopted to act on the device surface such as pump, valve powder coating of the present invention, through the abundant solidification of 180 DEG C, naturally cool to room temperature, place after 24 hours, measure coating performance: paint film appearance flat smooth, surface tinted is consistent, without particle, pin hole, bubble, wrinkle; Sticking power reaches 1 grade, and resistance to neutral salt spray 2000 hours is without exception, and resistance to impact shock is greater than 60cm.
Claims (2)
1. the pump valve proprietary powder coatings that a tool resistant is effective, it is characterized in that, be made up of the raw material of following weight part: hydroxy polyester resin 44-47, fluorocarbon resin 7-8, silicone resin 9-11, isocyanuric acid three-glycidyl ester 4-5, nano-aluminium oxide 13-15, perfluoro capryl triethoxyl silane 0.8-0.9, concentration is the ethanolic soln 25-30 of 75wt%, silane coupling agent kh5600.5-0.6, organosilicon flow agent 1-1.2, guar gum 0.6-0.7, polyvinylidene difluoride (PVDF) 4-5, white rouge aerogel 3-4, nano titanium oxide 9-10, calcium carbonate 12-14, water is appropriate.
2. the pump valve proprietary powder coatings that a kind of tool resistant is effective according to claim 1, is characterized in that, is prepared from by following concrete steps:
(1) nano-aluminium oxide is put into the ethanolic soln that concentration is 75wt%, dispersed with stirring is even, then perfluoro capryl triethoxyl silane is added, reflux 2-2.5 hour, adds silane coupling agent kh560 after cooling, continue stirring reaction 2-3 hour, last underpressure distillation, slough the solvent in system, with the dry 60-80 minute of the temperature of 80-85 DEG C in vacuum drying oven, obtain active nano aluminium sesquioxide;
(2) calcium carbonate is added suitable quantity of water grinding 40-60 minute, filtration drying, cross 400 mesh sieves and then mix with nano titanium oxide, obtain mixed powder stand-by; To add the water of 5-7 times amount in white rouge aerogel, dispersed with stirring is even, is heated to 50-60 DEG C, adds mixed powder, stirs 30-40 minute, then spraying dry, obtain modified filler with the speed of 300 revs/min;
(3) hydroxy polyester resin, fluorocarbon resin, silicone resin, isocyanuric acid three-glycidyl ester are put into after homogenizer stirs 20-30 minute with the speed of 1000 revs/min and added active nano aluminium sesquioxide and modified filler, continue to stir discharging after 10-15 minute, compound is sent into twin screw melt extruder, continue to add all the other remaining components, melt extrude, compressing tablet, obtained fine powder through pulverizing 180 mesh sieves and get final product.