CN105440855A - Intermediate layer connecting paint on plate hammer - Google Patents
Intermediate layer connecting paint on plate hammer Download PDFInfo
- Publication number
- CN105440855A CN105440855A CN201510980103.3A CN201510980103A CN105440855A CN 105440855 A CN105440855 A CN 105440855A CN 201510980103 A CN201510980103 A CN 201510980103A CN 105440855 A CN105440855 A CN 105440855A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- stirring
- total amount
- intermediate layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an intermediate layer connecting paint on a plate hammer, relating to the technical field of processing production of crusher accessories. The invention is characterized in that the intermediate layer connecting paint is prepared from the following materials in parts by weight: 4 parts of iron oxide, 4 parts of carbon powder, 3 parts of wollastonite powder, 2 parts of sodium dodecyl sulfonate, 1 part of glycerol, 1.5 parts of poly-4-methyl-1-amylene, 1.5 parts of fume silica, 3 parts of diethylene glycol butyl ether, 1 part of polyacrylamide, 3 parts of silver powder, 1.5 parts of pure acrylic emulsion, 1.5 parts of dioctyl adipate, 3 parts of activated zinc oxide, 1 part of sodium gluconate, 1 part of cobalt naphthenate and 7 parts of regulator. The intermediate layer connecting paint has the advantages of reasonable method, clear proportioning and wear resistance, and is convenient to operate.
Description
Technical field:
The present invention relates to crusher accessory processing technical field, the middle layer be specifically related on a kind of bar connects coating.
Background technology:
Stoning machine can be divided into medical stoner and mining industry stoning machine according to large class.Mining industry stoning machine principle is adapted to magnanimity mine hard rock broken, its typical grouan discharging-material size≤40mm accounts for 90%, this function process length of side less than 100 ~ 500 millimeters materials, and its ultimate compression strength reaches as high as 350 MPas, have reduction ratio large, after broken, material is the advantages such as cubic granules.Mining industry rubble machinery refers to that content that granularity in discharge is greater than three millimeters accounts for the size reduction machinery of total withdrawal rate more than 50%.
And bar is component on crusher, be used to the device pulverized, and used for a long time due to its needs, cause it easily damaged, particularly outside coating, to paint etc., easily device itself is damaged after breakage.
Summary of the invention:
Technical problem to be solved by this invention is to overcome existing technological deficiency provides the middle layer on a kind of method is reasonable, easy to operate, proportioning is clear, wear-resisting a kind of bar to connect coating.
Technical problem to be solved by this invention adopts following technical scheme to realize:
Middle layer on bar connects a coating, it is characterized in that: be made up of the material of following weight part,
Ferric oxide 4 parts, carbon dust 4 parts, wollastonite powder 3 parts, sodium laurylsulfonate 2 parts, glycerine 1 part, poly-4-methyl-1-pentene 1.5 parts, gas-phase silica 1.5 parts, butyl 3 parts, polyacrylamide 1 part, 3 parts, silver powder, pure-acrylic emulsion 1.5 parts, Octyl adipate 1.5 parts, active zinc flower 3 parts, Sunmorl N 60S 1 part, cobalt naphthenate 1 part, conditioning agent 7 parts;
Comprise following preparation process,
Ferric oxide, carbon dust, wollastonite powder, sodium laurylsulfonate, glycerine, poly-4-methyl-1-pentene, gas-phase silica, butyl, polyacrylamide are put into a disintegrating apparatus and are pulverized while stirring by I, after carrying out 20 minutes, total amount of material 1/10 deionized water in inside interpolation equipment, works on 23 minutes;
Silver powder, pure-acrylic emulsion, Octyl adipate, active zinc flower, Sunmorl N 60S, cobalt naphthenate are put into No. two disintegrating apparatus and are pulverized while stirring by II, after carrying out 20 minutes, the distilled water of total amount of material 1/13 in inside interpolation equipment, works on 20 minutes;
The boiling water putting into 100 DEG C of 1/18 of equipment total amount of material after a whipping device stirs 20 minutes put into by material after I and II stirring by III jointly, continues stirring 25 minutes;
Material after stirring and conditioning agent are put into the boiling water putting into 100 DEG C of 1/21 of equipment total amount of material after No. two whipping devices stir 15 minutes by IV jointly, continue stirring 25 minutes;
Described conditioning agent is made up of the material of following weight part,
Chinese honey locust 3 parts, radix bupleuri 4 parts, Herba Lobeliae Chinensis 5 parts, rhizome of Japanese Ginseng 6 parts, 7 parts, Root of Sixpetal Clematis, eupatorium 8 parts, radix ampelopsis 9 parts, trifoliate orange seed 10 parts, Paris polyphylla 3 parts, Perilla Stem 4 parts, Herba Selaginellae Doederleinii 5 parts, Snakegourd Root 6 parts;
Preparation method: after being cleaned by above-mentioned material clear water totally, the place being placed on ventilation is dried, and then puts into disintegrating apparatus and is conventionally ground into Powdered, for subsequent use.
Beneficial effect of the present invention is: a series of material of interpolation can make coating play the effect of protection product; life-span can be increased; make material more wear-resisting, corrosion-resistant; and the Chinese medicine added can toxin in neutralization materials; staff is ensured when in use, and it is healthy; and the cost of material is not high, and to add water be to prevent material binding to becoming block together.The inventive method is reasonable, easy to operate, proportioning is clear, wear-resisting.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.
Middle layer on bar connects a coating, it is characterized in that: be made up of the material of following weight part,
Ferric oxide 4 parts, carbon dust 4 parts, wollastonite powder 3 parts, sodium laurylsulfonate 2 parts, glycerine 1 part, poly-4-methyl-1-pentene 1.5 parts, gas-phase silica 1.5 parts, butyl 3 parts, polyacrylamide 1 part, 3 parts, silver powder, pure-acrylic emulsion 1.5 parts, Octyl adipate 1.5 parts, active zinc flower 3 parts, Sunmorl N 60S 1 part, cobalt naphthenate 1 part, conditioning agent 7 parts;
Comprise following preparation process,
Ferric oxide, carbon dust, wollastonite powder, sodium laurylsulfonate, glycerine, poly-4-methyl-1-pentene, gas-phase silica, butyl, polyacrylamide are put into a disintegrating apparatus and are pulverized while stirring by I, after carrying out 20 minutes, total amount of material 1/10 deionized water in inside interpolation equipment, works on 23 minutes;
Silver powder, pure-acrylic emulsion, Octyl adipate, active zinc flower, Sunmorl N 60S, cobalt naphthenate are put into No. two disintegrating apparatus and are pulverized while stirring by II, after carrying out 20 minutes, the distilled water of total amount of material 1/13 in inside interpolation equipment, works on 20 minutes;
The boiling water putting into 100 DEG C of 1/18 of equipment total amount of material after a whipping device stirs 20 minutes put into by material after I and II stirring by III jointly, continues stirring 25 minutes;
Material after stirring and conditioning agent are put into the boiling water putting into 100 DEG C of 1/21 of equipment total amount of material after No. two whipping devices stir 15 minutes by IV jointly, continue stirring 25 minutes;
Described conditioning agent is made up of the material of following weight part,
Chinese honey locust 3 parts, radix bupleuri 4 parts, Herba Lobeliae Chinensis 5 parts, rhizome of Japanese Ginseng 6 parts, 7 parts, Root of Sixpetal Clematis, eupatorium 8 parts, radix ampelopsis 9 parts, trifoliate orange seed 10 parts, Paris polyphylla 3 parts, Perilla Stem 4 parts, Herba Selaginellae Doederleinii 5 parts, Snakegourd Root 6 parts;
Preparation method: after being cleaned by above-mentioned material clear water totally, the place being placed on ventilation is dried, and then puts into disintegrating apparatus and is conventionally ground into Powdered, for subsequent use.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (3)
1. the middle layer on bar connects a coating, it is characterized in that: be made up of the material of following weight part,
Ferric oxide 4 parts, carbon dust 4 parts, wollastonite powder 3 parts, sodium laurylsulfonate 2 parts, glycerine 1 part, poly-4-methyl-1-pentene 1.5 parts, gas-phase silica 1.5 parts, butyl 3 parts, polyacrylamide 1 part, 3 parts, silver powder, pure-acrylic emulsion 1.5 parts, Octyl adipate 1.5 parts, active zinc flower 3 parts, Sunmorl N 60S 1 part, cobalt naphthenate 1 part, conditioning agent 7 parts.
2. the middle layer on a kind of bar according to claim 1 connects coating, it is characterized in that: comprise following preparation process,
Ferric oxide, carbon dust, wollastonite powder, sodium laurylsulfonate, glycerine, poly-4-methyl-1-pentene, gas-phase silica, butyl, polyacrylamide are put into a disintegrating apparatus and are pulverized while stirring by I, after carrying out 20 minutes, total amount of material 1/10 deionized water in inside interpolation equipment, works on 23 minutes;
Silver powder, pure-acrylic emulsion, Octyl adipate, active zinc flower, Sunmorl N 60S, cobalt naphthenate are put into No. two disintegrating apparatus and are pulverized while stirring by II, after carrying out 20 minutes, the distilled water of total amount of material 1/13 in inside interpolation equipment, works on 20 minutes;
The boiling water putting into 100 DEG C of 1/18 of equipment total amount of material after a whipping device stirs 20 minutes put into by material after I and II stirring by III jointly, continues stirring 25 minutes;
Material after stirring and conditioning agent are put into the boiling water putting into 100 DEG C of 1/21 of equipment total amount of material after No. two whipping devices stir 15 minutes by IV jointly, continue stirring 25 minutes.
3. the middle layer on a kind of bar according to claim 1 connects coating, it is characterized in that: described conditioning agent is made up of the material of following weight part,
Chinese honey locust 3 parts, radix bupleuri 4 parts, Herba Lobeliae Chinensis 5 parts, rhizome of Japanese Ginseng 6 parts, 7 parts, Root of Sixpetal Clematis, eupatorium 8 parts, radix ampelopsis 9 parts, trifoliate orange seed 10 parts, Paris polyphylla 3 parts, Perilla Stem 4 parts, Herba Selaginellae Doederleinii 5 parts, Snakegourd Root 6 parts;
Preparation method: after being cleaned by above-mentioned material clear water totally, the place being placed on ventilation is dried, and then puts into disintegrating apparatus and is conventionally ground into Powdered, for subsequent use.