CN105440289A - Method for improving stability of organosilicone pressure-sensitive adhesive - Google Patents
Method for improving stability of organosilicone pressure-sensitive adhesive Download PDFInfo
- Publication number
- CN105440289A CN105440289A CN201511022451.6A CN201511022451A CN105440289A CN 105440289 A CN105440289 A CN 105440289A CN 201511022451 A CN201511022451 A CN 201511022451A CN 105440289 A CN105440289 A CN 105440289A
- Authority
- CN
- China
- Prior art keywords
- pressure sensitive
- silicone pressure
- sensitive gluing
- agent
- gluing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for improving stability of an organosilicone pressure-sensitive adhesive. The method comprises steps as follows: step 1), removal of water and hydroxyl: a water and hydroxyl removal agent containing alpha-functional group siloxane compounds is added to a reaction system; step 2), thorough inactivation of a catalyst: inactivation is performed in the following two ways: a) when primary amine or secondary amine is used as a condensation polymerization catalyst, the adhesive reaction system is kept at the temperature of about 70 DEG C at the nitrogen reaction atmosphere, primary amine or secondary amine and aldehydes, ketones or low-level carboxylic acid react to generate Schiff base, generated unstable Schiff base reacts with diethyl malonate, and Schiff base becomes beta-amino acid without catalytic activity; b), when secondary amine or tertiary amine is used as a condensation polymerization catalyst, acidic compounds which can react with secondary amine or tertiary amine to generate a stable compound are added to the reaction system; step 3), residual acidic compounds are neutralized; step 4), residual small molecular substances are removed in the vacuum state.
Description
Technical field
The present invention relates to sizing agent technical field, be specifically related to a kind of method improveing silicone pressure sensitive gluing agent stability.
Background technology
The agent of silicone pressure sensitive gluing is generally by hydroxy-end capped organopolysiloxane linear polymeric under the effect of catalyzer, and carries out polycondensation and a kind of high performance pressure sensitive material formed with the MQ silicone resin of hydroxyl.Because the reason of structure, the agent of silicone pressure sensitive gluing has excellent resistance to high/low temperature performance, excellent dielectric properties and ageing-resistant performance, have simultaneously surface free energy low, note can be glued live the features such as difficult sticky note thing surface, thus apply very extensive.The preparation technology of silicone pressure sensitive gluing agent is quite complicated, silicone pressure sensitive gluing of the prior art agent, Chang Yinwei raw material sources is not extensively, Research foundation is poor, manufacture the reasons such as equipment and production technology fall behind, and very easily causes that the heat resistance of product is poor, coating rear stripping performance, initial cohesiveness, holds the instability such as viscosity energy.
The agent of silicone pressure sensitive gluing is formed by the polysiloxane of hydroxyl end-blocking and the polycondensation of MQ resin by silicone hydroxyl under the effect of catalyzer of hydroxyl structure, because organic chemical reactions is a kind of balanced reaction, silicone pressure sensitive gluing agent structure also will remain the hydroxyl of certain level, this hydroxyl nature is more active, at high temperature these silicone hydroxyl will generate water by polycondensation, thus bubble etc. is bad to cause pressure-sensitive adhesive agent goods to occur, cause crosslinked sizing agent structural damage and form cull, glue-line be full of cracks etc. are bad, thus reduce the applied at elevated temperature performance of sizing agent goods.So effectively reduce the level of silicone hydroxyl residual in silicone pressure sensitive gluing agent molecule, the heat resistance of silicone pressure sensitive gluing agent effectively can be improved.
When preparing the agent of silicone pressure sensitive gluing, in polycondensation phase, along with the carrying out of polycondensation, the water of generation enters organic phase by constantly producing; The retention of these moisture content also also has a great impact the performance of silicone pressure sensitive gluing agent; Removal process time prepared by the agent of silicone industry in foreign countries pressure-sensitive adhesive takes away by constantly passing into dry nitrogen in reaction unit the moisture content produced in reaction system, the water content in reaction system is made to remain on lower level, domestic, be that the device by being similar to dean stark trap (Dean-Starktrap) and so on dewaters, but water removal effect is poor, can only except desolventizing saturated after free-water, in solvent also containing part dissolved water.Moisture content residual in system is by under the effect of catalyzer that remains at sizing agent, the sizing agent molecular moiety of polycondensation is hydrolyzed, again be decomposed into poly organic silicon siloxanes and silicone resin and otherness move out to adhesive article surface, cause the instability of sizing agent goods viscosity.
The raw material preparing the agent of silicone pressure sensitive gluing all contains oh group, so it is just of crucial importance that these oh groups can be impelled to carry out choosing of the catalyzer of polycondensation.Conventional catalyzer has acids, bases, strong acid weak base salt, strong base weak acid salt, organic amine, some metallic salt such as organo-tin compound etc.In these catalyzer, selectable catalyst requirement catalytic activity is high, consumption is few, be easily distributed in raw materials and easily deactivation.Sulfuric acid in an acidic catalyst, hydrochloric acid etc. are acid strong, excellent catalytic effect, but compare and be difficult to evenly spread in organic phase, and subsequent disposal is very difficult, and equipment corrosion is also more serious; Although the organic monoacids such as acetic acid are easily distributed in reaction system, catalytic effect is poor, and usage quantity is also higher; In basic catalyst conventional as alkali metal hydroxide, quaternary ammonium hydroxide etc. because be difficult to be distributed in reaction system, require that usage quantity is large, this will cause the generation of the side reactions such as the degraded of silica gel link; Strong acid weak base salt or strong base weak acid salt catalyzer are also strong polar materials, are also difficult to be distributed in reaction system.The metallic compound such as organotin, organic titanium easily disperses, but reaction terminates easily to remain in sizing agent reaction system afterwards, and this will cause sizing agent to carry out to reversed reaction direction, causes the adhesive property of adhesive article to occur instability.Organic amine catalyzer has suitable catalytic activity, is also easy to be distributed in reaction system, can add acid and be neutralized after having reacted, so amine substance is widely used as the polycondensation catalyst of silicone pressure sensitive gluing agent.
Therefore to solve the stability problem of silicone pressure sensitive gluing agent, just must start with from the following aspects:
(1) moisture content residual in the agent of silicone pressure sensitive gluing is reduced;
(2) level of silicone hydroxyl residual in silicone pressure sensitive gluing agent molecule is reduced;
(3) thorough inactivation treatment is carried out to polycondensation catalyst residual in organosilicon sizing agent.
But, due to the restriction of the reason such as state of the art and equipment, domestic silicone pressure sensitive gluing agent is in fact also difficult to the requirement simultaneously accomplishing this three aspect, and the inactivation treatment especially for amines catalyst is also only carry out neutralizing treatment by adding the materials such as acetic acid.The agent of this silicone pressure sensitive gluing is in coating drying process, again amine will be decomposed into by the amine salt that acid neutralizes, these amine substances are by together with the moisture content that in tackiness agent, residual or outside is brought on a small quantity, be silicon rubber and silicone resin by the organosilicon sizing agent decomposed of polycondensation at leisure, silicon rubber or silicone resin will change the structural adhesive layer of adhesive article at leisure because of the difference of rate of migration, thus cause the instability of organic silicone adhesive goods use properties, main manifestations is that heat resistance is poor, easy cull, the use propertieies such as viscosity can slowly change along with the change of time and even cannot meet service requirements.
Summary of the invention
For overcoming the deficiencies in the prior art, the silicone pressure sensitive gluing agent of the high stability that the object of the present invention is to provide a kind of making processes simple, with low cost, while being intended to the heat resistance of raising silicone pressure sensitive gluing agent, along the preparation technology holding the agent of silicone pressure sensitive gluing, the essential property of sizing agent itself also can not be changed.
For achieving the above object, the present invention is achieved through the following technical solutions:
Improve a method for silicone pressure sensitive gluing agent stability, comprise the following steps:
Step 1) dewater and remove hydroxyl: in silicone pressure sensitive gluing agent preparation process, after polycondensation step completes, in reaction system, add the hydroxyl agent that dewaters containing alpha-functional group siloxane compound with the residual hydroxyl removing in reaction system residual moisture content and reduce in sizing agent molecular structure;
Step 2) the thorough deactivation of catalyzer: completing steps 1) after, the inactivation treatment of catalyzer can be carried out, be divided into following two kinds of situations:
A) in silicone pressure sensitive gluing agent preparation process, when using primary amine or secondary amine for polycondensation catalyst, under nitrogen reaction atmosphere, keep sizing agent reaction system at about 70 DEG C, primary amine or secondary amine and aldehydes or ketone, low-grade carboxylic acid are reacted generation Schiff's base, and then the Schiff's base of the instability generated and diethyl malonate are reacted, make Schiff's base become the beta-amino acids of catalytically inactive;
B) in silicone pressure sensitive gluing agent preparation process, when using secondary amine or tertiary amine as polycondensation catalyst, can react with secondary amine or tertiary amine the acidic substance forming stable compound by adding in reaction system;
Step 3) in and remaining acid material: in step 2) after the agent of silicone pressure sensitive gluing in add alkaline matter containing sodium alkoxide to neutralize acidic substance remaining in sizing agent;
Step 4) the remaining small-molecule substance of vacuum removal: to step 3) after the agent of silicone pressure sensitive gluing carry out vacuum-treat to remove wherein residual small molecules.
Preferably, the method for described improvement silicone pressure sensitive gluing agent stability, wherein, the chemical general formula of described alpha-functional group siloxanes is X-CH
2-SiR
2-OR ', in formula, X-is [CH3-(CH
2) m]
2-N-(m be more than or equal to 1 positive integer), NH
2(CH
2) nNH-(and n be more than or equal to 2 positive integer), C
6h
5one in-NH-, HS-, CH2=C (Me)-COO-; R is the one in H, Me, Et; R ' is the one in Me, Et, Vi.
Preferably, the method for described improvement silicone pressure sensitive gluing agent stability, wherein, described chemical general formula is X-CH
2-SiR
2the alpha-functional group siloxane compound of-OR ' is alpha-amino group siloxane compound, and X-is [CH
3-(CH
2) m]
2-N-(m be more than or equal to 1 positive integer), NH
2(CH
2) nNH-(and n be more than or equal to 2 positive integer) in one; R is Me; R ' is the one in Me, Et.
Preferably, the method for described improvement silicone pressure sensitive gluing agent stability, wherein, described acidic substance contain HCl.
Preferably, the method for described improvement silicone pressure sensitive gluing agent stability, wherein, described acidic substance are the diethyl ether solution containing HCl.
Preferably, the method for described improvement silicone pressure sensitive gluing agent stability, wherein, described in the hydroxyl agent addition that dewaters be 0.05% ~ 2.5% of described silicone pressure sensitive gluing agent dry weight.
Preferably, the method of described improvement silicone pressure sensitive gluing agent stability, wherein, described step 2) in, when catalyzer be primary amine or secondary amine time, the addition of described aldehydes or ketone, low-grade carboxylic acid and diethyl malonate is respectively 0.5% ~ 2.5% of described silicone pressure sensitive gluing agent dry weight.0.0% ~ 0.5% and 0.5% ~ 2.5%; When catalyzer be secondary amine or tertiary amine time, the addition of HCl is 0.1% ~ 1.5% of described silicone pressure sensitive gluing agent dry weight.
Preferably, the method for described improvement silicone pressure sensitive gluing agent stability, wherein, the addition of described sodium alkoxide is 0.05% ~ 1.5% of described silicone pressure sensitive gluing agent dry weight.
Preferably; the method of described improvement silicone pressure sensitive gluing agent stability; wherein; the method is used for improve the agent of finished product silicone pressure sensitive gluing; also be included in step 1) front pre-treatment; be placed in reactor by the agent of finished product silicone pressure sensitive gluing, under logical nitrogen protection and whipped state, temperature of reaction be reduced to 40 DEG C ~ 45 DEG C, next with described step 1)-step 4).
The invention has the beneficial effects as follows: the present invention is by reducing the residual moisture content in the level of the hydroxyl in sizing agent molecule and sizing agent, to dewater and remove residual hydroxy groups to merge into same step and complete, simplify flow process, heat resistance and the shelf characteric of stable sizing agent can be reached; By carrying out thorough inactivation treatment to amines catalyst residual in sizing agent, thus suppress sizing agent to occur to the reversed reaction in raw material direction, to reach the adhering performance of stable sizing agent, carry out again removing small molecules with remaining acidic substance in sizing agent in carrying out after deactivation, this ensure that stability and the usability of sizing agent.The present invention both can carry out the disposal of stability of sizing agent in silicone pressure sensitive gluing agent preparation process, also can carry out aftertreatment to finished product sizing agent, and treatment process is simple, with low cost simultaneously, and the sizing agent use properties after process is good.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail, can implement according to this with reference to specification sheets word to make those skilled in the art.
Embodiment 1
Step 1) polycondensation
The dimethylbenzene of 100Kg toluene and 200Kg is put in reactor, add the diethylamine of 500g, and the viscosity that then adds 300Kg of stirring is the hydroxyl-terminated injecting two methyl siloxane of about 6500mPa.s and the nM/nQ of 200Kg be 0.75 Mn be about 5000g/mol, Mw is about the MQ resin of the hydroxy radical content about 3% of 18000g/mol, continue to stir 30min under logical nitrogen protection, then be warming up to about 135 DEG C and keep reflux stabilizes to react about 210min, the water produced in reaction process is constantly discharged by dean stark trap (Dean-Starktrap) or U-shaped pipe water trap,
Step 2) dewater and remove residual hydroxy groups
Temperature in reactor is reduced to about 45 DEG C, in whipped state downhill reaction still, adds the NH of 6Kg
2(CH
2)
6nHCH
2-Si (CH
3)
2-OCH
2cH
3, more than stirring reaction 90min, is then warming up to about 70 DEG C, starts to carry out deactivation to polycondensation catalyst;
Step 3) catalyst deactivation process
Under nitrogen reaction atmosphere, keep sizing agent reaction system at about 70 DEG C, in whipped state downhill reaction still, add the positive propionic aldehyde of 8Kg and the acetic acid of 1.0kg, after continuing stirring reaction 90min, add the diethyl malonate of 10Kg, continue stirring reaction 90min;
Step 4) in and remaining acidic substance in sizing agent: step 3) complete after, the temperature of reactor is reduced to less than 50 DEG C, then the toluene dispersion liquid of 5% sodium tert-butoxide is progressively added, until it is neutral that sampling detects sizing agent system, continue to stir more than 30min until be uniformly dispersed;
Step 5) remove small molecules: step 4) complete after, temperature of reaction kettle is risen to 110 DEG C or more, then reaction mass is removed under the vacuum condition being not less than-0.09MPa the small-molecule substance in sizing agent reaction system, the vacuum removal time is not less than 90min;
Step 6) cool and regulate the solids content of sizing agent about 60%.
The preparation of control sample silicone pressure sensitive gluing agent A: the preparation of control sample A is identical with above-described embodiment 1, difference is, eliminate the residual hydroxy groups in the residual water-content removed in sizing agent, removal silicone pressure sensitive gluing agent molecule, eliminate the inactivation treatment of catalyzer, to simulate the basic quality of domestic silicone pressure sensitive gluing agent in general sense;
Silicone pressure sensitive gluing agent prepared by embodiment 1 and control sample silicone pressure sensitive gluing agent A respectively with the BPO sulfuration of sizing agent dry weight 3.5%, with above the thick BOPET film being coated on 0.025mm of the dry glue of 0.015mm, the use properties of testing example 1 and control sample A, the results are shown in Table 1.
The use properties of table 1 embodiment 1 and control sample A compares
Visible, the silicone pressure sensitive gluing agent of embodiment 1 meets the effect of stay in grade, and actual use properties is reliable and stable.
Embodiment 2
Step 1) polycondensation
The dimethylbenzene of 100Kg toluene and 200Kg is put in reactor, add the triethylamine of 500g, and the viscosity that then adds 200Kg of stirring is the hydroxyl-terminated injecting two methyl siloxane of about 7000mPa.s and the nM/nQ of 300Kg be 0.80 Mn be about 5000g/mol, Mw is about the MQ resin of the hydroxy radical content about 3% of 18000g/mol, continue to stir 30min under logical nitrogen protection, then be warming up to about 135 DEG C and keep reflux stabilizes to react about 210min, the water produced in reaction process is constantly discharged by dean stark trap (Dean-Starktrap) or U-shaped pipe water trap,
Step 2) dewater hydroxyl
Temperature in maintenance reactor, at 40 DEG C ~ 45 DEG C, adds (the CH of 6.5Kg in whipped state downhill reaction still
3cH
2)
2n-CH
2-Si (CH
3)
2-OCH
2cH
3, stir more than 90min, be then warming up to about 70 DEG C, start to carry out deactivation to polycondensation catalyst;
Step 3) catalyst deactivation process
Under nitrogen reaction atmosphere, keep sizing agent reaction system at about 70 DEG C, in whipped state downhill reaction still, add the 5%HCl diethyl ether solution containing the pure HCl of 3.5Kg, continue stirring reaction 60min;
Step 4) in and remaining acidic substance in sizing agent: step 3) complete after, the temperature of reactor is reduced to less than 50 DEG C, then the toluene dispersion liquid containing 5% sodium ethylate is progressively added, until it is that neutral continuation stirs more than 30min until be uniformly dispersed that sampling detects sizing agent system;
Step 5) remove small molecules: step 4) complete after, temperature of reaction kettle is risen to 110 DEG C or more, then reaction mass is removed under the vacuum condition being not less than-0.09MPa the small-molecule substance in sizing agent reaction system, the vacuum removal time is not less than 90min;
Step 6) cool and regulate the solids content of sizing agent about 60%.
The preparation of control sample silicone pressure sensitive gluing agent B: the preparation of control sample B is identical with above-described embodiment 2, difference is, eliminate the residual hydroxy groups removed in silicone pressure sensitive gluing agent molecule, the inactivation treatment eliminating catalyzer and the residual water-content removed in sizing agent, to simulate the basic quality of domestic silicone pressure sensitive gluing agent in general sense;
Silicone pressure sensitive gluing agent prepared by embodiment 2 and control sample silicone pressure sensitive gluing agent B respectively with the BPO sulfuration of sizing agent dry weight 3.5%, with above the thick BOPET film being coated on 0.036mm of the dry glue of 0.010mm, the use properties of testing example 2 and control sample B, the results are shown in Table 2.
The use properties of table 2 embodiment 2 and control sample B compares
Visible, the silicone pressure sensitive gluing agent of embodiment 2 meets the effect of stay in grade, and actual use properties is reliable and stable.
Embodiment 3 (improving the stability of finished product silicone pressure sensitive gluing agent)
Step 1) dewater hydroxyl
Certain finished product silicone pressure sensitive gluing agent domestic of 1000Kg is placed in reactor, in whipped state downhill reaction still, adds the CH of 10.0Kg
3(CH
2)
3n-CH
2-Si (CH
3)
2-OCH
3, be then warming up to about 40 DEG C and continue to stir more than 90min;
Step 2) catalyst deactivation process
Under nitrogen reaction atmosphere, keep sizing agent reaction system at about 70 DEG C, add in whipped state downhill reaction still containing the pure HCl of 5.0Kg 5% HCl diethyl ether solution, continue stirring reaction 90min;
Step 3) in and remaining acidic substance in sizing agent: step 2) complete after, the temperature of reactor is reduced to less than 50 DEG C, then the toluene dispersion liquid containing 5% sodium isopropylate is progressively added, until it is neutral that sampling detects sizing agent system, continue to stir more than 30min until be uniformly dispersed;
Step 4) remove small molecules: step 3) complete after, temperature of reaction kettle is risen to 110 DEG C or more, then reaction mass is removed under the vacuum condition being not less than-0.09MPa the small-molecule substance in sizing agent reaction system, the vacuum removal time is not less than 90min;
Step 5) cool and regulate the solids content of sizing agent about 60%.
The preparation of control sample silicone pressure sensitive gluing agent C: control sample C directly selects the commercially available finished product of certain money domestic silicone pressure sensitive gluing agent, to simulate the basic quality of domestic silicone pressure sensitive gluing agent in general sense;
Silicone pressure sensitive gluing agent prepared by embodiment 3 and control sample silicone pressure sensitive gluing agent C respectively with the BPO sulfuration of sizing agent dry weight 3.5%, with above the thick BOPET film being coated on 0.050mm of the glue of 0.030mm, the use properties of testing example 3 and control sample C, the results are shown in Table 3.
The use properties of table 3 embodiment 3 and control sample C compares
Visible, the silicone pressure sensitive gluing agent of embodiment 3 meets the effect of stay in grade, and actual use properties is reliable and stable.
Although embodiment of the present invention are open as above, but it is not restricted to listed in specification sheets and embodiment utilization, it can be applied to various applicable the field of the invention completely, for those skilled in the art, can easily realize other amendment, therefore do not deviating under the universal that claim and equivalency range limit, the present invention is not limited to specific details and shown here embodiment.
Claims (9)
1. improve a method for silicone pressure sensitive gluing agent stability, it is characterized in that, comprise the following steps:
Step 1) dewaters and removes hydroxyl: in silicone pressure sensitive gluing agent preparation process, after polycondensation step completes, in reaction system, add the hydroxyl agent that dewaters containing alpha-functional group siloxane compound with the residual hydroxyl removing in reaction system residual moisture content and reduce in sizing agent molecular structure;
Step 2) the thorough deactivation of catalyzer: completing steps 1) after, the inactivation treatment of catalyzer can be carried out, be divided into following two kinds of situations:
A) in silicone pressure sensitive gluing agent preparation process, when using primary amine or secondary amine for polycondensation catalyst, under nitrogen reaction atmosphere, keep sizing agent reaction system at about 70 DEG C, primary amine or secondary amine and aldehydes or ketone, low-grade carboxylic acid are reacted generation Schiff's base, and then the Schiff's base of the instability generated and diethyl malonate are reacted, make Schiff's base become the beta-amino acids of catalytically inactive;
B) in silicone pressure sensitive gluing agent preparation process, when using secondary amine or tertiary amine as polycondensation catalyst, can react with secondary amine or tertiary amine the acidic substance forming stable compound by adding in reaction system;
In step 3) and remaining acid material: in step 2) after the agent of silicone pressure sensitive gluing in add alkaline matter containing sodium alkoxide to neutralize acidic substance remaining in sizing agent;
The remaining small-molecule substance of step 4) vacuum removal: vacuum-treat is carried out to remove wherein residual small molecules to the silicone pressure sensitive gluing agent after step 3).
2. the method for improvement silicone pressure sensitive gluing agent stability according to claim 1, it is characterized in that, the chemical general formula of described alpha-functional group siloxanes is X-CH
2-SiR
2-OR ', in formula, X-is [CH3-(CH
2) m]
2-N-(m be more than or equal to 1 positive integer), NH
2(CH
2) nNH-(n be more than or equal to 2 positive integer), C
6h
5one in-NH-, HS-, CH2=C (Me)-COO-; R is the one in H, Me, Et; R ' is the one in Me, Et, Vi.
3. the method for improvement silicone pressure sensitive gluing agent stability according to claim 2, it is characterized in that, described chemical general formula is X-CH
2-SiR
2the alpha-functional group siloxane compound of-OR ' is alpha-amino group siloxane compound, and X-is [CH
3-(CH
2) m]
2-N-(m be more than or equal to 1 positive integer), NH
2(CH
2) nNH-(n be more than or equal to 2 positive integer) in one; R is Me; R ' is the one in Me, Et.
4. the method for improvement silicone pressure sensitive gluing agent stability according to claim 1, it is characterized in that, described acidic substance contain HCl.
5. the method for improvement silicone pressure sensitive gluing agent stability according to claim 1, it is characterized in that, described acidic substance are the diethyl ether solution containing HCl.
6. the method for improvement silicone pressure sensitive gluing agent stability according to claim 1, is characterized in that, described in the hydroxyl agent addition that dewaters be 0.05% ~ 2.5% of described silicone pressure sensitive gluing agent dry weight.
7. the method for improvement silicone pressure sensitive gluing agent stability according to claim 1, it is characterized in that, described step 2) in, when catalyzer be primary amine or secondary amine time, the addition of described aldehydes or ketone, low-grade carboxylic acid and diethyl malonate is respectively 0.5% ~ 2.5%, 0.0% ~ 0.5% and 0.5% ~ 2.5% of described silicone pressure sensitive gluing agent dry weight; When catalyzer be secondary amine or tertiary amine time, the addition of HCl is 0.1% ~ 1.5% of described silicone pressure sensitive gluing agent dry weight.
8. the method for improvement silicone pressure sensitive gluing agent stability according to claim 1, is characterized in that, the addition of described sodium alkoxide is 0.05% ~ 1.5% of described silicone pressure sensitive gluing agent dry weight.
9. the method for improvement silicone pressure sensitive gluing agent stability according to claim 1; it is characterized in that; the method is used for improve the agent of finished product silicone pressure sensitive gluing; also be included in the pre-treatment before step 1); reactor is placed in by the agent of finished product silicone pressure sensitive gluing; under logical nitrogen protection and whipped state, temperature of reaction is reduced to 40 DEG C ~ 45 DEG C, next with described step 1)-step 4).