CN105439489A - Foaming agent for mining filling - Google Patents
Foaming agent for mining filling Download PDFInfo
- Publication number
- CN105439489A CN105439489A CN201510799351.8A CN201510799351A CN105439489A CN 105439489 A CN105439489 A CN 105439489A CN 201510799351 A CN201510799351 A CN 201510799351A CN 105439489 A CN105439489 A CN 105439489A
- Authority
- CN
- China
- Prior art keywords
- filling
- whipping agent
- mining
- mining filling
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a foaming agent for mining filling, which comprises the following components in percentage by weight: 5-10% of alkylbenzene sulfonate, 10-20% of fatty alcohol ether sulfate, 2-8% of foam stabilizer and 62-83% of water. Mixing all the components at normal temperature, and stirring. The foaming agent is used for preparing a foam tailing cemented filling material with good fluidity, increases the utilization rate of ore dressing tailing, realizes the self-flow conveying of underground pipelines, reduces the water consumption, solves the problems of serious slurry sedimentation, serious segregation and the like after the filler is dehydrated, improves the strength of the filler, and improves the underground operation environment.
Description
Technical field
The invention belongs to Mine Stope packing technique field, relate to a kind of whipping agent that filling is carried out in mine worked-out section, particularly prepare a kind of whipping agent of foam tailings cemented filling material.
Background technology
Mining with stowing is a kind of mining methods of with various suitable casting resin, the worked-out section formed in underground after ore extraction being carried out to filling.The object of bashing mainly utilizes obturator to carry out underground pressure management, to control country rock avalanche and subsidence and to create safety and condition easily for actual mining, and the environment at protection exploitation scene and the eubiosis effectively.At present, domestic mine adopts down mostly to cemented filling mining method, high density fine sand pipeline self conveying consolidated fill technique.Existing filling process Problems existing in actual production process mainly contains: filling slurry poor fluidity, needs a large amount of wash-down water in course of conveying, causes pulp density on the low side, easily produces segregation in stowing operation, affects the stable of Quality of filling body; The mud amount that Tight filling overflows is about filling total amount 5 ‰-10 ‰, not only pollute stope, and mud is mixed into ore, causes ore dilution; In addition, in slurry pipeline transport process, comparatively large to the wearing and tearing of pipeline, shorten the work-ing life of filling borehole and filling pipe.
Summary of the invention
The present invention is in order to solve the deficiencies in the prior art; object is to provide a kind of for the preparation of foam mortar compaction material; utilize the lubrication of efficient dense foam; still can guarantee the mobility of compound when low water-cement ratio, realize the mining filling whipping agent of the remote self-flowing pastefill of high density.
To achieve these goals, the technical scheme that the present invention takes is: a kind of mining filling whipping agent, composed of the following components by weight percentage:
Alkylbenzene sulfonate 5 ~ 10%
Fatty alcohol ether sulphate 10 ~ 20%
Suds-stabilizing agent 2 ~ 8%
Water 62 ~ 83%.
Further, described alkylbenzene sulfonate is Sodium dodecylbenzene sulfonate.
Further, described fatty alcohol ether sulphate is polyoxyethylenated alcohol sodium sulfate.
Further, described suds-stabilizing agent is polyoxyethylene glycol.
Preferably, a kind of mining filling whipping agent, its each weight percentages of components is: Sodium dodecylbenzene sulfonate 5 ~ 10%; Polyoxyethylenated alcohol sodium sulfate 10 ~ 20%; Suds-stabilizing agent 2 ~ 8%; Water 62 ~ 83%, each weight percentages of components sum is 100%.
A kind of preparation method of above-mentioned mining filling whipping agent: at normal temperatures and pressures, by each component mixing and stirring, obtains described mining filling whipping agent.
The usage of above-mentioned mining filling whipping agent: add dilution water with whipping agent and make an expanding foam solution, then pass into pressurized air in expanding foam solution, form bubble flow, it is 1200 ~ 1700kg/m that bubble flow and sand-cement slurry mix and blend are formed wet density
3foam mortar stream, by transport pipe, filling construction is carried out to stope.
The invention has the beneficial effects as follows:
1. the present invention can solve the conspicuous contradiction between the mobility of filling slurry, water consumption and Quality of filling body preferably, improve Tight filling rate, improve Quality of filling body and placement efficiency, improve working environment at coal mines, reduce filling cost, to Sustainable development, the ground surface environment reparation of Mineral resources and prevent and reduce natural disasters significant.
2. utilize the present invention to produce the lubrication of foam, under guaranteeing that the mechanical index such as intensity, mobility meets the prerequisite of stope filling requirement, placement efficiency can improve more than 20%, setting percentage brings up to more than 95% by current less than 70%, comprehensive filling cost reduces by more than 10%, can reach improve obturator total quality, reduce filling cost, improve the multiple effects such as working environment at coal mines, to Sustainable development, the environment remediation of Mineral resources and prevent and reduce natural disasters all of great advantage.
3. whipping agent of the present invention is for the preparation of the husky cemented filling material of foam tail of good fluidity, add the utilization ratio of ore dressing tail sand, achieve the self-flowing pastefill of down-hole pipeline, decrease water consumption, slurry sedimentation after solving Dewatering of fills, the problem such as serious of emanating, improve strength of filling mass, improve working environment at coal mines.
Embodiment
Be described principle of the present invention and feature below, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment 1:
One prepares mining filling whipping agent 100Kg, and each component concentration is:
Sodium dodecylbenzene sulfonate 5Kg
Polyoxyethylenated alcohol sodium sulfate 10Kg
Polyoxyethylene glycol 2Kg
Water 83Kg
Under normal temperature, each component is mixed in proportion dissolving, stirs.
The usage of above-mentioned mining filling whipping agent: add dilution water with whipping agent and make an expanding foam solution, then pass into pressurized air in expanding foam solution, form bubble flow, it is 1330kg/m that bubble flow and sand-cement slurry mix and blend are formed wet density
3foam mortar stream, by transport pipe, filling construction is carried out to stope.
And detect the test block compression strength value of 3 days, 7 days, 28 days by unbearable sampling.Table 1 is visible, and the ultimate compression strength of 28 days reaches 2.31Mpa.
The husky cemented filling material ultimate compression strength of table 1. embodiment 1 foam tail.
Embodiment 2:
One prepares mining filling whipping agent 100Kg, and each component concentration is:
Sodium dodecylbenzene sulfonate 10Kg
Polyoxyethylenated alcohol sodium sulfate 15Kg
Polyoxyethylene glycol 5Kg
Water 70Kg
Under normal temperature, each component is mixed in proportion dissolving, stirs.
The usage of above-mentioned mining filling whipping agent: add dilution water with whipping agent and make an expanding foam solution, then pass into pressurized air in expanding foam solution, form bubble flow, it is 1330kg/m that bubble flow and sand-cement slurry mix and blend are formed wet density
3foam mortar stream, by transport pipe, filling construction is carried out to stope.
And detect the test block compression strength value of 3 days, 7 days, 28 days by unbearable sampling.Table 2 is visible, and the ultimate compression strength of 28 days reaches 2.15Mpa.
The husky cemented filling material ultimate compression strength of table 2. embodiment 2 foam tail.
Embodiment 3:
One prepares mining filling whipping agent 100Kg, and each component concentration is:
Sodium dodecylbenzene sulfonate 10Kg
Polyoxyethylenated alcohol sodium sulfate 10Kg
Polyoxyethylene glycol 8Kg
Water 72Kg
Under normal temperature, each component is mixed in proportion dissolving, stirs.
The usage of above-mentioned mining filling whipping agent: add dilution water with whipping agent and make an expanding foam solution, then pass into pressurized air in expanding foam solution, form bubble flow, it is 1330kg/m that bubble flow and sand-cement slurry mix and blend are formed wet density
3foam mortar stream, by transport pipe, filling construction is carried out to stope.
And detect the test block compression strength value of 3 days, 7 days, 28 days by unbearable sampling.Table 3 is visible, and the ultimate compression strength of 28 days reaches 2.24Mpa.
The husky cemented filling material ultimate compression strength of table 3. embodiment 3 foam tail.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (6)
1. a mining filling whipping agent, is characterized in that: composed of the following components by weight percentage:
Alkylbenzene sulfonate 5 ~ 10%
Fatty alcohol ether sulphate 10 ~ 20%
Suds-stabilizing agent 2 ~ 8%
Water 62 ~ 83%.
2. a kind of mining filling whipping agent as claimed in claim 1, is characterized in that: described alkylbenzene sulfonate is Sodium dodecylbenzene sulfonate.
3. a kind of mining filling whipping agent as claimed in claim 1, is characterized in that: described fatty alcohol ether sulphate is polyoxyethylenated alcohol sodium sulfate.
4. a kind of mining filling whipping agent as claimed in claim 1, is characterized in that: described suds-stabilizing agent is polyoxyethylene glycol.
5. the one mining filling whipping agent as described in any one of claim 1-4, is characterized in that: its each weight percentages of components is: Sodium dodecylbenzene sulfonate 5 ~ 10%; Polyoxyethylenated alcohol sodium sulfate 10 ~ 20%; Suds-stabilizing agent 2 ~ 8%; Water 62 ~ 83%, each weight percentages of components sum is 100%.
6. mining filling whipping agent as claimed in claim 5, is characterized in that: add dilution water with whipping agent and make expanding foam solution, it is 1200 ~ 1700kg/m that bubble flow and sand-cement slurry mix and blend are formed wet density
3foam mortar stream, by transport pipe, filling is carried out to stope.