CN105439265A - Acrylamide and n-butylamine containing flocculant and preparation method thereof - Google Patents
Acrylamide and n-butylamine containing flocculant and preparation method thereof Download PDFInfo
- Publication number
- CN105439265A CN105439265A CN201510821702.0A CN201510821702A CN105439265A CN 105439265 A CN105439265 A CN 105439265A CN 201510821702 A CN201510821702 A CN 201510821702A CN 105439265 A CN105439265 A CN 105439265A
- Authority
- CN
- China
- Prior art keywords
- acrylamide
- butyl amine
- butylamine
- ammonium nitrate
- ceric ammonium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an acrylamide and n-butylamine containing flocculant. The acrylamide and n-butylamine containing flocculant comprises components in percentage by weight as follows: 60%-70% of acrylamide, 20%-30% of n-butylamine and 10%-20% of ceric ammonium nitrate. Meanwhile, the invention further discloses a preparation method of the acrylamide and n-butylamine containing flocculant. By comparison with a traditional technology, molecular chains contain a certain quantity of polar functional groups, and solid particles suspended in water can be adsorbed, so that large flocculates are formed through bridging of the particles, sedimentation of the particles in a suspension liquid is effectively accelerated, filtration is promoted, and the acrylamide and n-butylamine containing flocculant can be widely applied to chemical and industrial wastewater treatment.
Description
Technical field
The invention belongs to chemical field, be specifically related to a kind of acrylamide n-Butyl Amine 99 flocculation agent and preparation method thereof.
Background technology
Flocculation agent mainly contains inorganic flocculating agent, organic polymer coargulator and microbial flocculant, is mainly used to dispose of sewage.And organic polymer coargulator is mainly used for Refinery Wastewater.Acrylamide series flocculation agent is high with its molecular weight, and flocculation bridge formation ability is strong and demonstrate the superiority in water treatment.
Flocculation process is most widely used general, the most general technique in current lot of domestic and foreign water technology, it is link indispensable in wastewater treatment, the quality of flocculating effect often determines the operation conditions of follow-up flow process, final outflow water water quality and expense, selects which kind of flocculation agent for improving effluent quality, reduces water producing cost and have very important Technological Economy to be worth.
Summary of the invention
Goal of the invention: the object of the invention is to for the deficiencies in the prior art, provides a kind of acrylamide n-Butyl Amine 99 flocculation agent.
Another object of the present invention is to the preparation method that aforesaid propylene acid amides n-Butyl Amine 99 flocculation agent is provided.
Technical scheme: in order to reach foregoing invention object, the present invention has specifically come like this: a kind of acrylamide n-Butyl Amine 99 flocculation agent, comprise the component of following weight percent: the acrylamide of 60 ~ 70%, the n-Butyl Amine 99 of 20 ~ 30% and the ceric ammonium nitrate of 10 ~ 20%.
Wherein, preferably, be made up of the component of following weight percent: the acrylamide of 65%, the n-Butyl Amine 99 of 23% and the ceric ammonium nitrate of 12%.
Prepare a method for acrylamide n-Butyl Amine 99 flocculation agent, measure each material by formula, acrylamide and n-Butyl Amine 99 are carried out polyreaction at 55 ~ 75 DEG C, continue 2 ~ 4 hours, after polyreaction, temperature is reduced to room temperature, then add ceric ammonium nitrate uniform stirring 30 ~ 40 minutes.
Beneficial effect: the present invention is compared with conventional art, owing to containing the solids suspended in a certain amount of polarity merit functional group energy planar water in molecular chain, making builds bridge between particle forms large throw out, thus the particle precipitation effectively accelerated in suspension, promote to filter, be widely used in chemical industry effluent process.
Embodiment
Embodiment 1:
Get the acrylamide that weight percent is 60%, the n-Butyl Amine 99 of 30% and the ceric ammonium nitrate of 10%, acrylamide and n-Butyl Amine 99 are carried out polyreaction at 55 ~ 75 DEG C, continue 2 ~ 4 hours, after polyreaction, temperature is reduced to room temperature, then add ceric ammonium nitrate uniform stirring 30 ~ 40 minutes.
Embodiment 2:
Get the acrylamide that weight percent is 70%, the n-Butyl Amine 99 of 20% and the ceric ammonium nitrate of 10%, acrylamide and n-Butyl Amine 99 are carried out polyreaction at 55 ~ 75 DEG C, continue 2 ~ 4 hours, after polyreaction, temperature is reduced to room temperature, then add ceric ammonium nitrate uniform stirring 30 ~ 40 minutes.
Embodiment 3:
Get the acrylamide that weight percent is 65%, the n-Butyl Amine 99 of 20% and the ceric ammonium nitrate of 15%, acrylamide and n-Butyl Amine 99 are carried out polyreaction at 55 ~ 75 DEG C, continue 2 ~ 4 hours, after polyreaction, temperature is reduced to room temperature, then add ceric ammonium nitrate uniform stirring 30 ~ 40 minutes.
Embodiment 4:
Get the acrylamide that weight percent is 60%, the n-Butyl Amine 99 of 20% and the ceric ammonium nitrate of 20%, acrylamide and n-Butyl Amine 99 are carried out polyreaction at 55 ~ 75 DEG C, continue 2 ~ 4 hours, after polyreaction, temperature is reduced to room temperature, then add ceric ammonium nitrate uniform stirring 30 ~ 40 minutes.
Embodiment 5:
Get the acrylamide that weight percent is 65%, the n-Butyl Amine 99 of 25% and the ceric ammonium nitrate of 10%, acrylamide and n-Butyl Amine 99 are carried out polyreaction at 55 ~ 75 DEG C, continue 2 ~ 4 hours, after polyreaction, temperature is reduced to room temperature, then add ceric ammonium nitrate uniform stirring 30 ~ 40 minutes.
Claims (3)
1. an acrylamide n-Butyl Amine 99 flocculation agent, is characterized in that, comprises the component of following weight percent: the acrylamide of 60 ~ 70%, the n-Butyl Amine 99 of 20 ~ 30% and the ceric ammonium nitrate of 10 ~ 20%.
2. acrylamide n-Butyl Amine 99 flocculation agent according to claim 1, is characterized in that, be made up of the component of following weight percent: the acrylamide of 65%, the n-Butyl Amine 99 of 23% and the ceric ammonium nitrate of 12%.
3. prepare the method for acrylamide n-Butyl Amine 99 flocculation agent for one kind, it is characterized in that, each material is measured by formula, acrylamide and n-Butyl Amine 99 are carried out polyreaction at 55 ~ 75 DEG C, continue 2 ~ 4 hours, after polyreaction, temperature is reduced to room temperature, then add ceric ammonium nitrate uniform stirring 30 ~ 40 minutes.