CN105419694A - Nail adhesive, preparation method and nail painting method using nail adhesive - Google Patents
Nail adhesive, preparation method and nail painting method using nail adhesive Download PDFInfo
- Publication number
- CN105419694A CN105419694A CN201510583982.6A CN201510583982A CN105419694A CN 105419694 A CN105419694 A CN 105419694A CN 201510583982 A CN201510583982 A CN 201510583982A CN 105419694 A CN105419694 A CN 105419694A
- Authority
- CN
- China
- Prior art keywords
- nail
- sheet
- binding agent
- resin
- soluble acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a nail adhesive. The adhesive is prepared by evenly mixing and stirring a water-soluble acrylic resin and a water-based tackifying resin. The volume ratio of the water-soluble acrylic resin and the aqueous tackifying resin is 100:(10-30). The present invention also provides a method for decorating and beautifying nails. The method comprises the following steps: coating the back of a nail used for nail painting by using the nail adhesive; drying the nail coated with the nail adhesive; and adhering the nail to a nail of a user until the nail adhesive on the back of the nail is in the shape of a transparent film. The nail adhesive provided by the present invention is prepared from environmental friendly materials, and is harmless to human bodies and the environment. The nail adhesive provided by the present invention is good in adhesion, the nail coated with the nail adhesive provided by the present invention cannot drop easily after the user wears the nail, and the nail can be used repeatedly for more than 100 times.
Description
Technical field
The present invention relates to a kind of first sheet binding agent, also relate to its preparation method and apply the method that first sheet binding agent carries out manicure, belong to manicure technical field.
Background technology
Manicure is a kind of work nail being carried out to decoration, according to color and the requirement of the hand shape of guest, first shape, skin quality, clothes, carries out disinfection, cleans nail, process that fox, maintenance, modification beautify.In tradition manicure technology, in order to reach effect attractive in appearance, first need to carry out profile correction to nail, profile modification be by manicure instrument, nail is pruned, the operation such as polishing, make nail present square, square circular, ellipse, the first shape such as pointed, circular and fan-shaped; In profile makeover process, because needs are polished nail repeatedly, make the sag of protecting coating of nail surface, larger to nail damage.Secondly, need to smear nail varnish to the nail after carrying out profile modification, make it obtain beautiful outward appearance; Generally comprise linging oil, nail polish and gloss oil, also comprise and colored drawing is carried out to nail, to obtain the nail beautifying pattern admired.The nail varnish that this process is used or nail polish glue all belong to containing a large amount of organic chemical reagents, repeatedly smear human injury comparatively large, also have infringement to the skin around nail.And in order to fixing coated nail polish glue, need to carry out the reinforcing programs such as phototherapy to it, the time is long, and the nail polish glue difficulty of coating removes, and with special removal of solvents, must bring great inconvenience to daily life.And traditional manicure arbitrarily can not change pattern, along with week in nail growth cycle two to three should repair once, price is higher, larger to nail damage.
For the defect of traditional manicure technology, occurred manicure first sheet in nail salon, manicure first sheet makes different first sheet according to nail type, carries out manicure work, obtain the first sheet with nail beautifying pattern on its surface.Then at first sheet backsizing, paste on nail.Manicure first sheet can alleviate the infringement of traditional manicure to nail, and wears conveniently, can conveniently remove.Existing first sheet generally uses double faced adhesive tape or glue to paste on nail, and double faced adhesive tape adhesive power is inadequate, very easily comes off after wearing after hanging and touching, and can not Reusability; Glue pastes viscosity higher than double faced adhesive tape, but removal is inconvenient, needs to use solvent removal, can cause damage to nail surface, also has certain damage to nail surrounding skin.
Along with people are to the pursuit of U.S. and the continuous enhancing to environment protection health consciousness, existing manicure technology is can not meet people's needs.Therefore, the present invention is directed to the deficiency of existing manicure technology, invent first sheet binding agent, first sheet binding agent selecting green environment protection material of the present invention is prepared from, and to human body and environmentally friendly, and first sheet binding agent adhesive power of the present invention is good, first sheet binding agent of the present invention is applied on first sheet, wear rear difficult drop-off, can Reusability more than 100 times, can obtain providing integrate attractive in appearance, convenient, the manicure first sheet of environmental protection and health.
Summary of the invention
The present invention is directed to the deficiency of existing manicure technology, provide a kind of first sheet binding agent, first sheet binding agent selecting green environment protection material of the present invention is prepared from, to human body and environmentally friendly, this first sheet binding agent adhesive power is good, first sheet binding agent of the present invention is applied on first sheet, wears rear difficult drop-off, can Reusability more than 100 times.
One aspect of the present invention provides a kind of first sheet binding agent, comprises water soluble acrylic resin and aqueous tackifier resin;
Wherein, shared by described water soluble acrylic resin and aqueous tackifier resin, the ratio of volume is 100:10-30.
Particularly, described water soluble acrylic resin is clear emulsion.
Especially, described aqueous tackifier resin is white extremely micro-yellow emulsion, and pH value is 6-8, and viscosity is 100-400mPas.
The present invention provides a kind of preparation method of manicure binding agent on the other hand, comprising:
Water soluble acrylic resin and aqueous tackifier mixed with resin is even, i.e. obtained described first sheet binding agent;
Wherein, shared by described water soluble acrylic resin and aqueous tackifier resin, the ratio of volume is 100:10-30.
Particularly, described water soluble acrylic resin and aqueous tackifier mixed with resin evenly to be comprised:
By water soluble acrylic resin and aqueous tackifier mixed with resin, stir process is carried out to it, obtained mixture;
Carry out leaving standstill process to described mixture, eliminate bubble wherein, be i.e. obtained milky first sheet binding agent.
Especially, the time of described stir process is 30-60min.
The present invention provides the method for a kind of decoration nail simultaneously, comprising:
By first sheet adhesive coated in the first sheet back side being used for manicure;
Drying treatment is carried out to the described first sheet binding agent first sheet that is coated with;
Until the first sheet binding agent at the first sheet back side become transparent membranaceous time, described first sheet is pasted on nail;
Wherein, described first sheet binding agent comprises water soluble acrylic resin and aqueous tackifier resin;
Wherein, shared by described water soluble acrylic resin and aqueous tackifier resin, the ratio of volume is 100:10-30.
Particularly, the treatment time of described drying treatment is 22-26h.
Especially, the treatment temp of described drying treatment is 20-30 DEG C.
Particularly, be 0.1-3mm by the coating thickness of first sheet adhesive coated in the first sheet back side being used for manicure.
Water soluble acrylic resin and aqueous tackifier resin are mixed according to the ratio that volume ratio is 100:10-30, after stirring 30-60min, water soluble acrylic resin and aqueous tackifier resin generation cross-linking and curing reaction, form the alveolate milky emulsion of homogeneous band; Left standstill process for some time, after bubble is wherein eliminated, i.e. obtained first sheet binding agent.Milky first sheet binding agent is overlying on the first sheet back side for manicure, coating thickness is 0.1-3mm, afterwards to being coated with first sheet binding agent first sheet at 20-30 DEG C of drying treatment 22-26h, the first sheet binding agent at the first sheet back side is become colorless by oyster white or flaxen transparent film, first sheet can be pasted on nail.
Advantage of the present invention and beneficial effect as follows:
1, the raw water soluble acrylic resin of first sheet binding agent of the present invention and aqueous tackifier resin are all solvent with water, not containing VOC, tasteless, are green material, to human body and environmentally friendly, are applicable to life-time service.
2, first sheet binding agent adhesive power of the present invention is good, is applied on first sheet by first sheet binding agent of the present invention, wears rear difficult drop-off, can Reusability more than 100 times.
3, manicure method of the present invention by manicure adhesive coated in the first sheet back side, the film that difference has different thickness radian can be obtained according to the nail type of different crowd and radian, first sheet can be coincide, firmly paste on nail, wear time is long, difficult drop-off.
4, apply the first sheet binding agent of the present invention manicure method of carrying out to avoid traditional manicure and need polish to nail, repair and use chemical medicinal liquid to the injury of nail and human body, in turn save the manicure time, first sheet is worn and extracts easily, can Reusability, simple and convenient.
Embodiment
The present invention is set forth further below in conjunction with specific embodiment; but the present invention is not limited thereto; those skilled in the art can principle according to the present invention modify, therefore, and all various amendments of carrying out according to principle of the present invention and change and all should be understood to fall into protection scope of the present invention.
Embodiment 1
Measure 100L water soluble acrylic resin and 20L aqueous tackifier resin is placed in container, stir process 45min is carried out to it, makes water soluble acrylic resin and aqueous tackifier resin generation cross-linking and curing reaction, obtain the alveolate milky emulsion of homogeneous band; Left standstill process for some time, after bubble is wherein eliminated, obtained first sheet binding agent.
Get manicure first sheet, by milky first sheet adhesive coated in the first sheet back side being used for manicure, coating thickness is 2mm, afterwards to being coated with first sheet binding agent first sheet at 25 DEG C of drying treatment 24h, treat that the first sheet binding agent at the first sheet back side to be become colorless transparent film by oyster white, first sheet is pasted on nail, namely completes nail beautifying and decorating.
Embodiment 2
Measure 100L water soluble acrylic resin and 10L aqueous tackifier resin is placed in container, stir process 30min is carried out to it, makes water soluble acrylic resin and aqueous tackifier resin generation cross-linking and curing reaction, obtain the alveolate milky emulsion of homogeneous band; Left standstill process for some time, after bubble is wherein eliminated, obtained first sheet binding agent.
Get manicure first sheet, by milky first sheet adhesive coated in the first sheet back side being used for manicure, coating thickness is 0.1mm, afterwards to being coated with first sheet binding agent first sheet at 20 DEG C of drying treatment 26h, treat that the first sheet binding agent at the first sheet back side becomes transparent film from oyster white, first sheet is pasted on nail, namely completes nail beautifying and decorating.
Embodiment 3
Measure 100L water soluble acrylic resin and 30L aqueous tackifier resin is placed in container, stir process 60min is carried out to it, makes water soluble acrylic resin and aqueous tackifier resin generation cross-linking and curing reaction, obtain the alveolate milky emulsion of homogeneous band; Left standstill process for some time, after bubble is wherein eliminated, obtained first sheet binding agent.
Get manicure first sheet, by milky first sheet adhesive coated in the first sheet back side being used for manicure, coating thickness is 2mm, afterwards to being coated with first sheet binding agent first sheet at 30 DEG C of drying treatment 22h, treat that the first sheet binding agent at the first sheet back side becomes transparent film from oyster white, first sheet is pasted on nail, namely completes nail beautifying and decorating.
Claims (6)
1. a manicure method for decoration nail, is characterized in that, comprising:
By first sheet adhesive coated in the first sheet back side being used for manicure;
Drying treatment is carried out to the described first sheet being coated with first sheet binding agent;
Until the first sheet binding agent at the first sheet back side become transparent membranaceous time, described first sheet is pasted with on nail;
Wherein, described first sheet binding agent comprises water soluble acrylic resin and aqueous tackifier resin;
Wherein, shared by described water soluble acrylic resin and aqueous tackifier resin, the ratio of volume is 100:10-30.
2. manicure method according to claim 1, is characterized in that, the treatment time of described drying treatment is 22-26h.
3. a preparation method for first sheet binding agent, is characterized in that, comprising:
Water soluble acrylic resin and aqueous tackifier mixed with resin is even, i.e. obtained described first sheet binding agent;
Wherein, shared by described water soluble acrylic resin and aqueous tackifier resin, the ratio of volume is 100:10-30.
4. preparation method according to claim 3, is characterized in that, described evenly comprises water soluble acrylic resin and aqueous tackifier mixed with resin:
By water soluble acrylic resin and aqueous tackifier mixed with resin, stir process is carried out to it, obtained mixture;
Carry out leaving standstill process to described mixture, eliminate bubble wherein, be i.e. obtained milky first sheet binding agent.
5. preparation method according to claim 4, is characterized in that, the time of described stir process is 30-60min.
6. a first sheet binding agent, is characterized in that, comprises water soluble acrylic resin and aqueous tackifier resin;
Wherein, shared by described water soluble acrylic resin and aqueous tackifier resin, the ratio of volume is 100:10-30.