CN105401004A - High-strength and high-toughness aluminum alloy sheet - Google Patents
High-strength and high-toughness aluminum alloy sheet Download PDFInfo
- Publication number
- CN105401004A CN105401004A CN201510795910.8A CN201510795910A CN105401004A CN 105401004 A CN105401004 A CN 105401004A CN 201510795910 A CN201510795910 A CN 201510795910A CN 105401004 A CN105401004 A CN 105401004A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- aluminum alloy
- strength
- herb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses to a high-strength and high-toughness aluminum alloy sheet and relates to the technical field of metal material processing and production. The high-strength and high-toughness aluminum alloy sheet is characterized by being prepared from, by weight, 20 parts of aluminum powder, 5 parts of silicon oxide, 4 parts of petroleum wax, 2 parts of attapulgite, 1 part of salicylic acid, 3 parts of aramid short fibers, 3 parts of natural rubber, 4 parts of antioxidants, 0.5 part of rare earth cerium salt, 1 part of resorcinol, 2 parts of hexamethylphosphoramid, 9 parts of carbon powder, 3 parts of ferrous sulfate, 1 part of modified tree ashes, 1 part of zinc oxide, 4 parts of glycidyl acrylate, 5 parts of polyisobutylene, 1.5 parts of microcrystalline wax, 1 part of triethanolamine, 2 parts of rosin, 1 part of sodium gluconate and 9 parts of finishing agents. According to the high-strength and high-toughness aluminum alloy sheet, the method is reasonable, the proportion is reasonable, and pressure resistance and corrosion resistance are achieved.
Description
Technical field:
The present invention relates to metal material processing production technical field, be specifically related to a kind of high-intensity high-tenacity aluminum alloy plate materials.
Background technology:
Aluminium alloy is a most widely used class non-ferrous metal structured material in industry, widely applies in Aeronautics and Astronautics, automobile, machinofacture, boats and ships and chemical industry.The develop rapidly of industrial economy, increasing to the demand of Welded structural part, make the Research on Weldability of aluminium alloy also thereupon deeply.Maximum alloys applied by aluminum current alloy.
And aluminium alloy be some metals or nonmetal with aluminium by processing, the generation of the situations such as fracture, crimp is easily there is in some aluminium alloy in the process used, be because its toughness is not high, intensity is not high and cause using for a long time or high pressure uses, many troubles will be brought to production like this.
Summary of the invention:
Technical problem to be solved by this invention be to overcome existing technological deficiency provide a kind of method rationally, reasonable ratio, withstand voltage, corrosion resistant a kind of high-intensity high-tenacity aluminum alloy plate materials.
Technical problem to be solved by this invention adopts following technical scheme to realize:
A kind of high-intensity high-tenacity aluminum alloy plate materials, is characterized in that: be made up of the material of following weight part,
Aluminium powder 20 parts, silicon oxide 5 parts, petroleum wax 4 parts, attapulgite 2 parts, Whitfield's ointment 1 part, aramid fiber short fibre 3 parts, natural rubber 3 parts, 4 parts, oxidation inhibitor, cerium salt 0.5 part, Resorcinol 1 part, HMPA 2 parts, carbon dust 9 parts, 3 parts, ferrous sulfate, modification tree ash 1 part, 1 part, zinc oxide, glycidyl acrylate 4 parts, polyisobutene 5 parts, Microcrystalline Wax 1.5 parts, trolamine 1 part, rosin 2 parts, Sunmorl N 60S 1 part, finishing composition 9 parts;
Comprise the following steps,
Aluminium powder, silicon oxide, petroleum wax, attapulgite, Whitfield's ointment, aramid fiber short fibre, natural rubber, oxidation inhibitor, cerium salt, Resorcinol, HMPA to be put into the high-temperature smelting pot 45 minutes of 689 DEG C by I jointly, are fused into liquid;
Carbon dust, ferrous sulfate, modification tree ash, zinc oxide, glycidyl acrylate, polyisobutene, Microcrystalline Wax, trolamine, rosin, Sunmorl N 60S to be put into the high-temperature smelting pot 53 minutes of 578 DEG C by II jointly, become liquid;
Material after I and II heating takes out by III, leaves standstill 5 minutes respectively, then puts into whipping device and stirs 15 minutes;
The IV condensing equipment condensation of the above-mentioned material be stirred being put into-23 DEG C becomes solid-state for 44 minutes;
V just condensed material takes out and leaves standstill 9 minutes, then puts into disintegrating apparatus and is ground into particulate state;
VI by pulverize after material put into 632 DEG C high-temperature smelting pot fusing 47 minutes become liquid, and take out leave standstill 10 minutes;
Finishing composition and the material after leaving standstill are put into whipping device by VII stirs 15 minutes, then directly puts into forming mould shaping;
Described finishing composition is made up of the material of following weight part,
Herba Ixeritis Denticulatae 5 parts, Herba Senecionis Chrysanthemoidis 9 parts, Herba Syneilesis Aconitifoliae 3 parts, Root or herb of Clethra Loosestrife 7 parts, Lindley Butterflybush Herb 8 parts, purslane 8 parts, Root of Chinese Eupatorium 7 parts, Spreading Hedyotis Herb 3 parts, buzhaye 10 part, day grass roots 3 parts, Pink Plumepoppy Herb 8 parts;
Preparation method: above-mentioned material clear water is rinsed well, then be placed on ventilation, local airing that drying has sunlight 4 hours, then above-mentioned material is put into grinding plant successively and grind to form particulate state, a kind of material is put into every 2 minutes, after material has been placed completely, continue grinding 10 minutes, then take out for subsequent use.
Beneficial effect of the present invention is: the plasticity-of aluminium is inherently stronger, and in aluminium powder, with the addition of that other material a series of so just makes the toughness of aluminium, intensity has and improve greatly, and by making oxidation-resistance, the erosion resistance raising of material after a series of step processing, its intensity too increases, and with the addition of the part of Chinese medicine, more harmful material and toxin can be neutralized, and can insect be prevented.The inventive method rationally, reasonable ratio, withstand voltage, corrosion-resistant.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.
A kind of high-intensity high-tenacity aluminum alloy plate materials, is characterized in that: be made up of the material of following weight part,
Aluminium powder 20 parts, silicon oxide 5 parts, petroleum wax 4 parts, attapulgite 2 parts, Whitfield's ointment 1 part, aramid fiber short fibre 3 parts, natural rubber 3 parts, 4 parts, oxidation inhibitor, cerium salt 0.5 part, Resorcinol 1 part, HMPA 2 parts, carbon dust 9 parts, 3 parts, ferrous sulfate, modification tree ash 1 part, 1 part, zinc oxide, glycidyl acrylate 4 parts, polyisobutene 5 parts, Microcrystalline Wax 1.5 parts, trolamine 1 part, rosin 2 parts, Sunmorl N 60S 1 part, finishing composition 9 parts;
Comprise the following steps,
Aluminium powder, silicon oxide, petroleum wax, attapulgite, Whitfield's ointment, aramid fiber short fibre, natural rubber, oxidation inhibitor, cerium salt, Resorcinol, HMPA to be put into the high-temperature smelting pot 45 minutes of 689 DEG C by I jointly, are fused into liquid;
Carbon dust, ferrous sulfate, modification tree ash, zinc oxide, glycidyl acrylate, polyisobutene, Microcrystalline Wax, trolamine, rosin, Sunmorl N 60S to be put into the high-temperature smelting pot 53 minutes of 578 DEG C by II jointly, become liquid;
Material after I and II heating takes out by III, leaves standstill 5 minutes respectively, then puts into whipping device and stirs 15 minutes;
The IV condensing equipment condensation of the above-mentioned material be stirred being put into-23 DEG C becomes solid-state for 44 minutes;
V just condensed material takes out and leaves standstill 9 minutes, then puts into disintegrating apparatus and is ground into particulate state;
VI by pulverize after material put into 632 DEG C high-temperature smelting pot fusing 47 minutes become liquid, and take out leave standstill 10 minutes;
Finishing composition and the material after leaving standstill are put into whipping device by VII stirs 15 minutes, then directly puts into forming mould shaping;
Described finishing composition is made up of the material of following weight part,
Herba Ixeritis Denticulatae 5 parts, Herba Senecionis Chrysanthemoidis 9 parts, Herba Syneilesis Aconitifoliae 3 parts, Root or herb of Clethra Loosestrife 7 parts, Lindley Butterflybush Herb 8 parts, purslane 8 parts, Root of Chinese Eupatorium 7 parts, Spreading Hedyotis Herb 3 parts, buzhaye 10 part, day grass roots 3 parts, Pink Plumepoppy Herb 8 parts;
Preparation method: above-mentioned material clear water is rinsed well, then be placed on ventilation, local airing that drying has sunlight 4 hours, then above-mentioned material is put into grinding plant successively and grind to form particulate state, a kind of material is put into every 2 minutes, after material has been placed completely, continue grinding 10 minutes, then take out for subsequent use.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. a high-intensity high-tenacity aluminum alloy plate materials, is characterized in that: be made up of the material of following weight part,
Aluminium powder 20 parts, silicon oxide 5 parts, petroleum wax 4 parts, attapulgite 2 parts, Whitfield's ointment 1 part, aramid fiber short fibre 3 parts, natural rubber 3 parts, 4 parts, oxidation inhibitor, cerium salt 0.5 part, Resorcinol 1 part, HMPA 2 parts, carbon dust 9 parts, 3 parts, ferrous sulfate, modification tree ash 1 part, 1 part, zinc oxide, glycidyl acrylate 4 parts, polyisobutene 5 parts, Microcrystalline Wax 1.5 parts, trolamine 1 part, rosin 2 parts, Sunmorl N 60S 1 part, finishing composition 9 parts;
Comprise the following steps,
Aluminium powder, silicon oxide, petroleum wax, attapulgite, Whitfield's ointment, aramid fiber short fibre, natural rubber, oxidation inhibitor, cerium salt, Resorcinol, HMPA to be put into the high-temperature smelting pot 45 minutes of 689 DEG C by I jointly, are fused into liquid;
Carbon dust, ferrous sulfate, modification tree ash, zinc oxide, glycidyl acrylate, polyisobutene, Microcrystalline Wax, trolamine, rosin, Sunmorl N 60S to be put into the high-temperature smelting pot 53 minutes of 578 DEG C by II jointly, become liquid;
Material after I and II heating takes out by III, leaves standstill 5 minutes respectively, then puts into whipping device and stirs 15 minutes;
The IV condensing equipment condensation of the above-mentioned material be stirred being put into-23 DEG C becomes solid-state for 44 minutes;
V just condensed material takes out and leaves standstill 9 minutes, then puts into disintegrating apparatus and is ground into particulate state;
VI by pulverize after material put into 632 DEG C high-temperature smelting pot fusing 47 minutes become liquid, and take out leave standstill 10 minutes;
Finishing composition and the material after leaving standstill are put into whipping device by VII stirs 15 minutes, then directly puts into forming mould shaping.
2. a kind of high-intensity high-tenacity aluminum alloy plate materials according to claim 1, is characterized in that: described finishing composition is made up of the material of following weight part,
Herba Ixeritis Denticulatae 5 parts, Herba Senecionis Chrysanthemoidis 9 parts, Herba Syneilesis Aconitifoliae 3 parts, Root or herb of Clethra Loosestrife 7 parts, Lindley Butterflybush Herb 8 parts, purslane 8 parts, Root of Chinese Eupatorium 7 parts, Spreading Hedyotis Herb 3 parts, buzhaye 10 part, day grass roots 3 parts, Pink Plumepoppy Herb 8 parts;
Preparation method: above-mentioned material clear water is rinsed well, then be placed on ventilation, local airing that drying has sunlight 4 hours, then above-mentioned material is put into grinding plant successively and grind to form particulate state, a kind of material is put into every 2 minutes, after material has been placed completely, continue grinding 10 minutes, then take out for subsequent use.