CN105368286A - Flame-retardation heat-insulation insulating varnish - Google Patents
Flame-retardation heat-insulation insulating varnish Download PDFInfo
- Publication number
- CN105368286A CN105368286A CN201510820851.5A CN201510820851A CN105368286A CN 105368286 A CN105368286 A CN 105368286A CN 201510820851 A CN201510820851 A CN 201510820851A CN 105368286 A CN105368286 A CN 105368286A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation
- flame
- insulating varnish
- insullac
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardation heat-insulation insulating varnish. The flame-retardation heat-insulation insulating varnish comprises the following raw materials in parts by weight: 42 parts of polyurethane resin, 17 parts of aqueous baking finish resin, 16 parts of an organosilicon cross-linking agent, 18 parts of silica, 14 parts of silicon hydroxide, 12 parts of magnesium hydroxide, 6 parts of iron oxide, 6 parts of barium sulfate, 6 parts of magnesium silicate, 3.5 parts of a lubricant, 5 parts of an anti-oxidant, 3 parts of a compatilizer, 2 parts of an organosilicon antifoaming agent and 1.5 parts of an organosilicon leveling agent. The flame-retardation heat-insulation insulating varnish has excellent characteristics of low smoke, no toxicity, no halogen, and flame retardation; the insulating property of the insulating varnish is excellent, and the insulating varnish is suitable for insulating layers of various electric wires and cables as well as material surfaces.
Description
Technical field
The present invention relates to a kind of anti-flaming thermal-insulation insullac.
Background technology
In today of high-tech fast development, the family of increasing electrical equipment turnover people, safer in order to people can be allowed to live, the anti-flaming thermal-insulation insullac needing insulation effect better is to carry out the insulation of electrical equipment.
In work on hand and life, existing insulating material manufactures by common DIN standard production, such as: Jiao of heat-resisting 90 joins polyethylene, polyvinyl chloride.Its shortcoming is: thermo-labile, not fire-resistant, does not prevent fires.
Common pvc material insulation degree 0.6 ~ 110 can not excess load, and super overcurrent is easy to puncture insulating material, causes short circuit; In naked light, easily ignited, discharged suffocative toxic gas, contaminate environment.
Therefore, need a kind of new anti-flaming thermal-insulation insullac to solve the problem.
Summary of the invention
The object of the invention is the defect for insullac in the prior art, a kind of anti-flaming thermal-insulation insullac of better effects if is provided.
For achieving the above object, anti-flaming thermal-insulation insullac of the present invention can adopt following technical scheme:
A kind of anti-flaming thermal-insulation insullac, comprises the raw material of following composition by weight: 42 parts of urethane resins, 17 parts of water-based stoving paint resins, 16 parts of organosilicon cross-linking agents, 18 parts of silicon-dioxide, 14 parts of silicon hydroxides, 12 parts of magnesium hydroxides, 6 parts of ferric oxide, 6 parts of barium sulfate, 6 parts of Magnesium Silicate q-agents, 3.5 parts of lubricants, 5 parts of oxidation inhibitor, 3 parts of compatilizers, 2 parts of silicone antifoam agents and 1.5 parts of organosilicon flow agents.
Further, described oxidation inhibitor is antioxidant 3114 or irgasfos 168.
Further, described compatilizer is ST-7 compatilizer.
Further, described lubricant is paraffin.
Inventive principle:
Insulating material selects urethane resin and water-based stoving paint resin, and the creationary combination combinationally using silicon-dioxide, silicon hydroxide, magnesium hydroxide, ferric oxide, barium sulfate and Magnesium Silicate q-agent, anti-flaming thermal-insulation insullac of the present invention is made to have outstanding insulating property, spendable temperature is higher, and material environment friendly, also can not produce toxic gas during heating, the use of talcum powder, lubricant, compatilizer and organosilicon flow agent, makes excellent insulation performance.
Beneficial effect: anti-flaming thermal-insulation insullac excellent performance of the present invention has low cigarette, nontoxic, Halogen, fire-retardant characteristic; Its excellent insulation performance, is suitable for the insulation layer of various electric wire, material surface simultaneously.
Embodiment
Below in conjunction with specific embodiment, illustrate the present invention further, these embodiments should be understood only be not used in for illustration of the present invention and limit the scope of the invention, after having read the present invention, the amendment of those skilled in the art to the various equivalent form of value of the present invention has all fallen within the application's claims limited range.
embodiment 1
Anti-flaming thermal-insulation insullac, comprises the raw material of following composition by weight: 42 parts of urethane resins, 17 parts of water-based stoving paint resins, 16 parts of organosilicon cross-linking agents, 18 parts of silicon-dioxide, 14 parts of silicon hydroxides, 12 parts of magnesium hydroxides, 6 parts of ferric oxide, 6 parts of barium sulfate, 6 parts of Magnesium Silicate q-agents, 3.5 parts of lubricants, 5 parts of oxidation inhibitor, 3 parts of compatilizers, 2 parts of silicone antifoam agents and 1.5 parts of organosilicon flow agents.Wherein, oxidation inhibitor is irgasfos 168.Compatilizer is ST-7 compatilizer.Lubricant is paraffin.
Test result:
Burning or add Thermal test: the gas testing its release, wherein and find no poisonous gas, has low cigarette, nontoxic, Halogen, fire-retardant characteristic;
Can excess load 6 times and as usual play insulating effect under voltage rating.
Inventive principle:
Insulating material selects urethane resin and water-based stoving paint resin, and the creationary combination combinationally using silicon-dioxide, silicon hydroxide, magnesium hydroxide, ferric oxide, barium sulfate and Magnesium Silicate q-agent, anti-flaming thermal-insulation insullac of the present invention is made to have outstanding insulating property, spendable temperature is higher, and material environment friendly, also can not produce toxic gas during heating, the use of talcum powder, lubricant, compatilizer and organosilicon flow agent, makes insulation layer excellent performance.
Anti-flaming thermal-insulation insullac excellent performance of the present invention has low cigarette, nontoxic, Halogen, fire-retardant characteristic; Its excellent insulation performance, is suitable for the insulation layer of various electric wire, material surface simultaneously.
Claims (4)
1. an anti-flaming thermal-insulation insullac, it is characterized in that, comprise the raw material of following composition by weight: 42 parts of urethane resins, 17 parts of water-based stoving paint resins, 16 parts of organosilicon cross-linking agents, 18 parts of silicon-dioxide, 14 parts of silicon hydroxides, 12 parts of magnesium hydroxides, 6 parts of ferric oxide, 6 parts of barium sulfate, 6 parts of Magnesium Silicate q-agents, 3.5 parts of lubricants, 5 parts of oxidation inhibitor, 3 parts of compatilizers, 2 parts of silicone antifoam agents and 1.5 parts of organosilicon flow agents.
2. anti-flaming thermal-insulation insullac as claimed in claim 1, is characterized in that: described oxidation inhibitor is irgasfos 168.
3. anti-flaming thermal-insulation insullac as claimed in claim 1, is characterized in that: described compatilizer is ST-7 compatilizer.
4. anti-flaming thermal-insulation insullac as claimed in claim 1, is characterized in that: described lubricant is paraffin.