CN105349234A - Solid electronic lubricant and preparation method thereof - Google Patents
Solid electronic lubricant and preparation method thereof Download PDFInfo
- Publication number
- CN105349234A CN105349234A CN201510809606.4A CN201510809606A CN105349234A CN 105349234 A CN105349234 A CN 105349234A CN 201510809606 A CN201510809606 A CN 201510809606A CN 105349234 A CN105349234 A CN 105349234A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricant
- paraffin
- wilkinite
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a solid electronic lubricant and its preparation method, and belongs to the technical field of lubricating oil production. The lubricant of the invention comprises, by weight, 10-30 parts of paraffin, 20-30 parts of bentonite, 10-20 parts of iso-dodec alkane, 20-30 parts of titanium bronze, 5-10 parts of sodium dodecyl benzene sulfonate, 5-10 parts of molybdenum dioxide, 10-20 parts of lecithin, and 10-20 parts of water. The preparation method comprises the following steps: uniformly mixing the above ingredients, and carrying out high-speed homogenization at 1-3 atmospheres, at 20-40 DEG C and at the rotate speed of 1000-4000 r/min for 20-40 min, and spray-drying at 50-70 DEG C at 100-300 r to obtain a powder. After spray-dried to a powder, the solid lubricant is convenient to preserve and transport. Lubrication effect of the solid lubricant is outstanding, lubricating capacity between electrons is enhanced, abrasion is reduced to the maximum, and service life of electronic components is prolonged.
Description
Technical field
The present invention relates to a kind of lubricant and preparation method thereof, be specifically related to a kind of solid electronic lubricant and preparation method thereof, belong to lubricant production technical field.
Background technology
Electronic devices and components are integral parts of the small-sized machine of electronic component and electricity, instrument, and itself is often made up of some parts, can be general in like product; Some part of the industry such as normal finger electrical equipment, wireless, instrument, as the general name of the sub-devices such as electric capacity, transistor, hairspring, clockwork spring.Common are diode etc.
Electronic devices and components comprise: resistance, electrical condenser, potentiometer, electron tube, scatterer, electromechanical compo, junctor, semi-conductor discrete device, electro-acoustic element, Laser Devices, electron display device, photoelectric device, sensor, power supply, switch, small and special electric machine, electronic transformer, rly., printed circuit board, unicircuit, all kinds of circuit, piezoelectricity, crystal, quartz, ceramic magnet material, base material substrate used for printed circuit, electric function technique proprietary material, electronic pastes (band) goods, electron chemistry material and component etc.
The lubricant with plasticity that solid lubricant is made up of viscosifying agent and base oil, also can add various additive sometimes as required.Base oil accounts for 90% in lubricating grease, very large to the performance impact of lubricating grease.Viscosifying agent is the important component part of lubricating grease, after adding viscosifying agent, could form the lubricating grease with certain structure formation in lubricating oil.Viscosifying agent can be divided into soap base and non-soap base two class.Soap base viscosifying agent refers to various fatty acid metal soap.Fat raw material generally adopts various animal and plant grease and from the lipid acid wherein separated and various synthetic fatty acid.Forming the raw material of metallic soap is generally basic metal, the oxyhydroxide (as calcium hydroxide, sodium hydroxide and lithium hydroxide etc.) of alkaline-earth metal, carbonate-free lime and Tai-Ace S 150 etc.Non-soap base viscosifying agent mainly contains: alkyl viscosifying agent, as paraffin and ceresine; Inorganic thickening agent, as wilkinite and silica gel etc.; Organic viscosifying agent, as indanthrene blue dyestuff, phthalocyanine bronze, aryl ureas, polyureas, tetrafluoroethylene, fluorinated ethylene propylene copolymer and perfluor polyphenyl etc.; Filler, as graphite, molybdenumdisulphide and carbon black etc.Lubricating grease can be divided into 3 classes by purposes.1. antiwear lubricating grease: be mainly used in improving the Frotteurism of friction pair to slow down wearing and tearing.2. protective grease: be mainly used in the corrosion and the corrosion that prevent metallic element.3. seal lubrication agent: the joint being mainly used in sealed vacuum system, pipe fitting and screw element etc.Different by viscosifying agent, lubricating grease can be divided into again soap base grease, hydr ocarbon-based grease, inorganic base grease and organic base grease 4 class.
Chinese patent, application number: 00801663.1 lubricant disclosing a kind of balljoint, wherein fusion two kinds of varigrained spherical particles in oil or lubricant.Macrobead plays distance and keeps thing (spacer), and this spacer prevents being seated on spheric thrust bearing when balljoint is static of the ball of balljoint.Small-particle prevents oarse-grained gathering, and they maintain macrobead distance each other, thus are also distributed among balljoint.But this lubricant complex manufacturing technology is not solid state, transport is inconvenient.Therefore develop a kind of solid lubricant tool to be of great significance.
Summary of the invention
The object of this invention is to provide a kind of solid electronic lubricant, this lubricant is spray-dried make powder after, be convenient to preserve, convenient transportation, lubrication is given prominence to, and strengthens the lubricity between electronics, reduce its wearing and tearing to greatest extent, extend electrical fittings work-ing life.
In order to realize the object of foregoing invention, the technical solution adopted in the present invention
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part:
Paraffin 10-30 part, wilkinite 20-30 part, isomery dodecane hydrocarbon 10-20 part, phthalocyanine bronze 20-30 part, Sodium dodecylbenzene sulfonate 5-10 part, molybdenum dioxide 5-10 part, Yelkin TTS 10-20 part, water 10-20 part.
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part: paraffin 10-20 part, wilkinite 20-25 part, isomery dodecane hydrocarbon 10-15 part, phthalocyanine bronze 20-25 part, Sodium dodecylbenzene sulfonate 5-8 part, molybdenum dioxide 5-8 part, Yelkin TTS 10-15 part, water 10-15 part.
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part: 10 parts, paraffin, wilkinite 20 parts, isomery dodecane hydrocarbon 10 parts, phthalocyanine bronze 20 parts, Sodium dodecylbenzene sulfonate 5 parts, molybdenum dioxide 5 parts, 10 parts, Yelkin TTS, 10 parts, water.
A kind of preparation method of solid electronic lubricant is:
By paraffin, wilkinite, isomery dodecane hydrocarbon, phthalocyanine bronze, Sodium dodecylbenzene sulfonate, molybdenum dioxide, Yelkin TTS, water mixes, high speed homogenization 20-40min under 1-3 normal atmosphere, temperature 20-40 DEG C, rotating speed 1000-4000r/min condition, at 50-70 DEG C, under 100-300 turns, be spray dried to powder.
the present invention relative to the beneficial effect of prior art is:
This lubricant is spray-dried make powder after, be convenient to preserve, convenient transportation, lubrication is given prominence to, and strengthens the lubricity between electronics, reduces its wearing and tearing to greatest extent, extends electrical fittings work-ing life.
Embodiment
Be described in further details the present invention below by embodiment, these embodiments are only used for the present invention is described, do not limit the scope of the invention.
Embodiment 1
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part: 10 parts, paraffin, wilkinite 20 parts, isomery dodecane hydrocarbon 10 parts, phthalocyanine bronze 20 parts, Sodium dodecylbenzene sulfonate 5 parts, molybdenum dioxide 5 parts, 10 parts, Yelkin TTS, 10 parts, water.
Its preparation method is:
By paraffin, wilkinite, isomery dodecane hydrocarbon, phthalocyanine bronze, Sodium dodecylbenzene sulfonate, molybdenum dioxide, Yelkin TTS, water mixes, high speed homogenization 20min under 1 normal atmosphere, temperature 20 DEG C, rotating speed 1000r/min condition, at 50 DEG C, is spray dried to powder under 100 turns.
Embodiment 2
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part:
15 parts, paraffin, wilkinite 22 parts, isomery dodecane hydrocarbon 12 parts, phthalocyanine bronze 22 parts, Sodium dodecylbenzene sulfonate 6 parts, molybdenum dioxide 6 parts, 12 parts, Yelkin TTS, 12 parts, water.
Its preparation method is:
By paraffin, wilkinite, isomery dodecane hydrocarbon, phthalocyanine bronze, Sodium dodecylbenzene sulfonate, molybdenum dioxide, Yelkin TTS, water mixes, high speed homogenization 25min under 2 normal atmosphere, temperature 25 DEG C, rotating speed 2000r/min condition, at 55 DEG C, is spray dried to powder under 200 turns.
Embodiment 3
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part:
20 parts, paraffin, wilkinite 24 parts, isomery dodecane hydrocarbon 14 parts, phthalocyanine bronze 24 parts, Sodium dodecylbenzene sulfonate 7 parts, molybdenum dioxide 7 parts, 14 parts, Yelkin TTS, 14 parts, water.
Its preparation method is:
By paraffin, wilkinite, isomery dodecane hydrocarbon, phthalocyanine bronze, Sodium dodecylbenzene sulfonate, molybdenum dioxide, Yelkin TTS, water mixes, high speed homogenization 30min under 3 normal atmosphere, temperature 30 DEG C, rotating speed 3000r/min condition, at 60 DEG C, is spray dried to powder under 300 turns.
Embodiment 4
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part:
25 parts, paraffin, wilkinite 28 parts, isomery dodecane hydrocarbon 18 parts, phthalocyanine bronze 28 parts, Sodium dodecylbenzene sulfonate 9 parts, molybdenum dioxide 8 parts, 18 parts, Yelkin TTS, 18 parts, water.
Its preparation method is:
By paraffin, wilkinite, isomery dodecane hydrocarbon, phthalocyanine bronze, Sodium dodecylbenzene sulfonate, molybdenum dioxide, Yelkin TTS, water mixes, high speed homogenization 30min under 1 normal atmosphere, temperature 35 DEG C, rotating speed 3000r/min condition, at 65 DEG C, is spray dried to powder under 200 turns.
Embodiment 5
A kind of solid electronic lubricant, this lubricant is made up of the component of following weight part:
30 parts, paraffin, wilkinite 30 parts, isomery dodecane hydrocarbon 20 parts, phthalocyanine bronze 30 parts, Sodium dodecylbenzene sulfonate 10 parts, molybdenum dioxide 10 parts, 20 parts, Yelkin TTS, 20 parts, water.
Its preparation method is:
By paraffin, wilkinite, isomery dodecane hydrocarbon, phthalocyanine bronze, Sodium dodecylbenzene sulfonate, molybdenum dioxide, Yelkin TTS, water mixes, high speed homogenization 40min under 3 normal atmosphere, temperature 40 DEG C, rotating speed 4000r/min condition, at 70 DEG C, is spray dried to powder under 300 turns.
Claims (4)
1. a solid electronic lubricant, is characterized in that: this lubricant is made up of the component of following weight part:
Paraffin 10-30 part, wilkinite 20-30 part, isomery dodecane hydrocarbon 10-20 part, phthalocyanine bronze 20-30 part, Sodium dodecylbenzene sulfonate 5-10 part, molybdenum dioxide 5-10 part, Yelkin TTS 10-20 part, water 10-20 part.
2. a solid electronic lubricant, is characterized in that: this lubricant is made up of the component of following weight part:
Paraffin 10-20 part, wilkinite 20-25 part, isomery dodecane hydrocarbon 10-15 part, phthalocyanine bronze 20-25 part, Sodium dodecylbenzene sulfonate 5-8 part, molybdenum dioxide 5-8 part, Yelkin TTS 10-15 part, water 10-15 part.
3. a solid electronic lubricant, is characterized in that: this lubricant is made up of the component of following weight part:
10 parts, paraffin, wilkinite 20 parts, isomery dodecane hydrocarbon 10 parts, phthalocyanine bronze 20 parts, Sodium dodecylbenzene sulfonate 5 parts, molybdenum dioxide 5 parts, 10 parts, Yelkin TTS, 10 parts, water.
4. a preparation method for solid electronic lubricant, is characterized in that, comprises the following steps:
By paraffin, wilkinite, isomery dodecane hydrocarbon, phthalocyanine bronze, Sodium dodecylbenzene sulfonate, molybdenum dioxide, Yelkin TTS, water mixes, high speed homogenization 20-40min under 1-3 normal atmosphere, temperature 20-40 DEG C, rotating speed 1000-4000r/min condition, at 50-70 DEG C, under 100-300 turns, be spray dried to powder.