CN105348983A - Environmental friendly water-borne coating - Google Patents
Environmental friendly water-borne coating Download PDFInfo
- Publication number
- CN105348983A CN105348983A CN201510779538.1A CN201510779538A CN105348983A CN 105348983 A CN105348983 A CN 105348983A CN 201510779538 A CN201510779538 A CN 201510779538A CN 105348983 A CN105348983 A CN 105348983A
- Authority
- CN
- China
- Prior art keywords
- water
- solution
- attapulgite
- stir
- attapulgite modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Environmental friendly water-borne coating is disclosed. The coating comprises following raw materials by weight: 100-120 parts of water-soluble epoxy resin emulsion, 10-20 parts of water, 6-7 parts of dipropylene glycol n-butyl ether, 25-35 parts of a composite filler, 0.1-0.3 part of BYK346, 1-2 parts of methylpentanol, 1-3 parts of magnesium stearate, 0.3-0.4 part of polyvinyl alcohol, 0.1-0.2 part of polyacrylamide, 0.2-0.4 part of an emulsifier 6100, 0.1-0.2 part of an organosilicone type efficient defoamer Tego901W, 0.05-0.07 part of polydimethylsiloxane, 0.1-0.2 part of propylene glycol, 0.01-0.03 part of an antiseptic DL702, 0.01-0.02 part of eucalyptus oil, 0.02-0.04 part of 1,2-benzisothiazolin-3-one and 0.4-0.5 part of a leveling agent. Raw materials of the composite filler comprise modified attapulgite, diatomite, activated carbon and kaolin.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of environment protecting water-based paint.
Background technology
Coating is a kind of novel macromolecular material, has and is evenly attached to baseplate material surface and forms the firm characteristic of film without cracking.Traditional coating uses organism as solvent, can discharge volatile organic matter, and then bring pollution to environment in processing and production process.Water-borne coatings, with water as solvent, can be saved ample resources, fire hazard when eliminating construction, to reduce topsoil.
Although water-borne coatings can reduce the pollution to air, but still there is organism in water-borne coatings, these organism are present in coating as filler and matrix, its content is about 2-12%, still can, to environment, therefore need to provide a kind of coating can removed organism, purify air.
Summary of the invention
Based on the technical problem that background technology exists, the present invention proposes a kind of environment protecting water-based paint, consumption of organic solvent of the present invention is few, and absorption, the decomposability of PARA FORMALDEHYDE PRILLS(91,95) are good.
A kind of environment protecting water-based paint that the present invention proposes, its raw material comprises by weight: water-soluble epoxy resin emulsion 100-120 part, water 10-20 part, dipropylene glycol n-butyl ether 6-7 part, compounded mix 25-35 part, BYK3460.1-0.3 part, methyl amyl alcohol 1-2 part, Magnesium Stearate 1-3 part, polyvinyl alcohol 0.3-0.4 part, polyacrylamide 0.1-0.2 part, emulsifying agent 61000.2-0.4 part, silicone based high effective antifoaming agent Tego901W0.1-0.2 part, polydimethylsiloxane 0.05-0.07 part, propylene glycol 0.1-0.2 part, sanitas DL7020.01-0.03 part, eucalyptus oil 0.01-0.02 part, BIT 0.02-0.04 part, flow agent 0.4-0.5 part,
Wherein, the raw material of compounded mix comprises: attapulgite modified, diatomite, gac, kaolin.
Preferably, attapulgite modified, diatomite, gac, kaolinic weight ratio are 1.5-2.5:1.1-1.2:1.2-1.3:1.6-1.8.
Preferably, attapulgite modified, diatomite, gac, kaolin are 300-500 order.
Preferably, its raw material comprises by weight: water-soluble epoxy resin emulsion 105-115 part, water 12-18 part, dipropylene glycol n-butyl ether 6.3-6.7 part, compounded mix 28-32 part, BYK3460.15-0.25 part, methyl amyl alcohol 1.2-1.8 part, Magnesium Stearate 1.5-2.5 part, polyvinyl alcohol 0.32-0.38 part, polyacrylamide 0.13-0.17 part, emulsifying agent 61000.25-0.35 part, silicone based high effective antifoaming agent Tego901W0.13-0.17 part, polydimethylsiloxane 0.055-0.065 part, propylene glycol 0.14-0.16 part, sanitas DL7020.015-0.025 part, eucalyptus oil 0.013-0.017 part, BIT 0.025-0.035 part, flow agent 0.42-0.48 part.
Preferably, attapulgite modified preparation method is: get silica hydrosol, heats up, and drip the ethanolic soln of γ-aminopropyl triethoxysilane, insulated and stirred obtains solution A; Butyl (tetra) titanate is added after dissolving in ethanol, be added drop-wise in aqueous hydrochloric acid, stir, regulate pH with aqueous sodium hydroxide solution, continue stirring and obtain solution B; Be added to the water by attapulgite swelling, add solution A, stir, add solution B, continue to stir, centrifugal, washing, heat up, dry, pulverize, sieving, it is attapulgite modified to obtain.
Preferably, attapulgite modified preparation method is: the silica hydrosol getting pH=8-10, be warming up to 60-70 DEG C, drip the ethanolic soln of γ-aminopropyl triethoxysilane, dropwise in 50-60min, constantly stir in dropping process, obtain solution A with the speed insulated and stirred 14-18h of 400-600r/min; Added by butyl (tetra) titanate after dissolving in ethanol, being added drop-wise to massfraction is in 3-4wt% aqueous hydrochloric acid, stirs 1-2h, regulate pH=1.5-2.5 with aqueous sodium hydroxide solution with the speed of 600-800r/min, continues to stir 30-50min and obtains solution B; Attapulgite is added to the water swelling 1-2h, adds solution A, stir 3-4h, add solution B with the speed of 800-1000r/min, continue to stir 4-5h, centrifugal, washing, is warming up to 180-200 DEG C, dry 2-3h, and pulverize, sieving, it is attapulgite modified to obtain.
Preferably, in attapulgite modified preparation method, in the preparation process of solution A, the weight ratio of silicon-dioxide, γ-aminopropyl triethoxysilane, ethanol is 10-20:2-4:10-20.
Preferably, in attapulgite modified preparation method, in the preparation process of solution B, the weight ratio of ethanol, butyl (tetra) titanate, aqueous hydrochloric acid is 220-240:180-200:500-580.
Preferably, in attapulgite modified preparation method, the weight ratio of attapulgite, solution A, solution B is 60-70:5-6:10-12.
In the preparation method of above-mentioned modification infusorial earth, in " silica hydrosol ", do not specify the consumption of water, determine its consumption according to actually operating; The effect of aqueous sodium hydroxide solution regulates pH, do not specify its concentration; In " being added to the water by diatomite swelling ", the effect of water is swelling, does not specify its consumption, determines its consumption according to concrete operations.
Above-mentioned water is deionized water.
Preparation method of the present invention is as follows: by water, water-soluble epoxy resin emulsion mixes, 7min is stirred with the speed of 600r/min, add dipropylene glycol n-butyl ether to continue to stir 6min, add BYK346, methyl amyl alcohol, Magnesium Stearate, emulsifying agent 6100, silicone based high effective antifoaming agent Tego901W, polydimethylsiloxane, propylene glycol, sanitas DL702, eucalyptus oil, BIT stirs 10min with the speed of 800r/min, add compounded mix, 25min is stirred with the speed of 1000r/min, add flow agent, 6min is stirred with the speed of 600r/min, add polyvinyl alcohol, polyacrylamide continues to stir 15min and obtains environment protecting water-based paint.
The high reactivity hydroxyl that the γ-aminopropyl triethoxysilane that the present invention selects is hydrolyzed silica sphere in the silicone hydroxyl and silica hydrosol formed afterwards combines, γ-aminopropyl triethoxysilane is grafted on silicon-dioxide, avoid the silicon-dioxide caused because high reactivity hydroxyl be combined with each other to reunite, add the dispersiveness of silica hydrosol, silica hydrosol after grafting and attapulgite dispersed, the remaining silicone hydroxyl of γ-aminopropyl triethoxysilane can with swelling after attapulgite in hydroxyl combine, thus reticulated structure is formed between silicon-dioxide and attapulgite, greatly increase the adsorptivity of silica hydrosol and attapulgite, TiO 2 sol is prepared by butyl (tetra) titanate, and and silica hydrosol, attapulgite Homogeneous phase mixing, by adsorption, titanium dioxide be uniformly distributed and be adsorbed on as the silicon-dioxide of carrier and attapulgite obtain attapulgite modified, silicon-dioxide during one side is attapulgite modified, attapulgite and reticulated structure can be a large amount of, the firmly obnoxious flavour such as formaldehyde adsorption, titanium dioxide during another aspect is attapulgite modified has photocatalytic Degradation, the organic gass such as formaldehyde can be resolved into carbonic acid gas and water, the effect of adsorption Sum decomposition cooperatively interacts, purify air, thus considerably increase absorption of the present invention, environmental-protection function, attapulgite modified, diatomite, gac, kaolin cooperatively interact and namely can be used as filler and increase mechanical property of the present invention, also can increase adsorptivity of the present invention further, consumption of organic solvent is few, reduces the present invention further to the pollution of environment, BYK346, methyl amyl alcohol, Magnesium Stearate, emulsifying agent 6100, silicone based high effective antifoaming agent Tego901W, polydimethylsiloxane, flow agent interact, can promote attapulgite modified, diatomite, gac, kaolin and water-soluble epoxy resin emulsion dispersed, increase stability of the present invention and mechanical property, sanitas DL702, eucalyptus oil, BIT can increase antisepsis and sterilization performance of the present invention and mildew resistance, dipropylene glycol n-butyl ether is film coalescence aid, increases film-forming properties of the present invention, propylene glycol is frostproofer, polyvinyl alcohol, polyacrylamide are thickening material, and above-mentioned each material cooperatively interacts, the effect that can increase physical strength of the present invention, stability, adsorptivity and purify air.
Embodiment
Below, by specific embodiment, technical scheme of the present invention is described in detail.
Embodiment 1
A kind of environment protecting water-based paint, its raw material comprises by weight: water-soluble epoxy resin emulsion 120 parts, 10 parts, water, dipropylene glycol n-butyl ether 7 parts, compounded mix 25 parts, BYK3460.3 part, methyl amyl alcohol 1 part, Magnesium Stearate 3 parts, polyvinyl alcohol 0.3 part, polyacrylamide 0.2 part, emulsifying agent 61000.2 parts, silicone based high effective antifoaming agent Tego901W0.2 part, polydimethylsiloxane 0.05 part, propylene glycol 0.2 part, sanitas DL7020.01 part, eucalyptus oil 0.02 part, BIT 0.02 part, flow agent 0.5 part;
Wherein, the raw material of compounded mix comprises: 300 orders are attapulgite modified, 500 order diatomite, 300 order gacs, 500 order kaolin, and attapulgite modified, diatomite, gac, kaolinic weight ratio are 1.5:1.2:1.2:1.8;
Attapulgite modified preparation method is: the silica hydrosol getting pH=8, be warming up to 70 DEG C, drip the ethanolic soln of γ-aminopropyl triethoxysilane, dropwise in 50min, constantly stir in dropping process, obtain solution A with the speed insulated and stirred 14h of 600r/min, wherein, the weight ratio of silicon-dioxide, γ-aminopropyl triethoxysilane, ethanol is 20:2:20; Butyl (tetra) titanate is added after dissolving in ethanol, being added drop-wise to massfraction is in 3wt% aqueous hydrochloric acid, 1h is stirred with the speed of 800r/min, pH=2.5 is regulated with aqueous sodium hydroxide solution, continue to stir 30min and obtain solution B, wherein, the weight ratio of ethanol, butyl (tetra) titanate, aqueous hydrochloric acid is 240:180:580; Attapulgite is added to the water swelling 1h, adds solution A, stir 3h with the speed of 1000r/min, add solution B, continue to stir 5h, centrifugal, washing, be warming up to 180 DEG C, dry 3h, pulverize, sieving, it is attapulgite modified to obtain, wherein, the weight ratio of attapulgite, solution A, solution B is 60:6:10.
Embodiment 2
A kind of environment protecting water-based paint, its raw material comprises by weight: water-soluble epoxy resin emulsion 100 parts, 20 parts, water, dipropylene glycol n-butyl ether 6 parts, compounded mix 35 parts, BYK3460.1 part, methyl amyl alcohol 2 parts, Magnesium Stearate 1 part, polyvinyl alcohol 0.4 part, polyacrylamide 0.1 part, emulsifying agent 61000.4 parts, silicone based high effective antifoaming agent Tego901W0.1 part, polydimethylsiloxane 0.07 part, propylene glycol 0.1 part, sanitas DL7020.03 part, eucalyptus oil 0.01 part, BIT 0.04 part, flow agent 0.4 part;
Wherein, the raw material of compounded mix comprises: 500 orders are attapulgite modified, 300 order diatomite, 500 order gacs, 300 order kaolin, and attapulgite modified, diatomite, gac, kaolinic weight ratio are 2.5:1.1:1.3:1.6;
Attapulgite modified preparation method is: the silica hydrosol getting pH=10, be warming up to 60 DEG C, drip the ethanolic soln of γ-aminopropyl triethoxysilane, dropwise in 60min, constantly stir in dropping process, obtain solution A with the speed insulated and stirred 18h of 400r/min, wherein, the weight ratio of silicon-dioxide, γ-aminopropyl triethoxysilane, ethanol is 10:4:10; Butyl (tetra) titanate is added after dissolving in ethanol, being added drop-wise to massfraction is in 4wt% aqueous hydrochloric acid, 2h is stirred with the speed of 600r/min, pH=1.5 is regulated with aqueous sodium hydroxide solution, continue to stir 50min and obtain solution B, wherein, the weight ratio of ethanol, butyl (tetra) titanate, aqueous hydrochloric acid is 220:200:500; Attapulgite is added to the water swelling 2h, adds solution A, stir 4h with the speed of 800r/min, add solution B, continue to stir 4h, centrifugal, washing, be warming up to 200 DEG C, dry 2h, pulverize, sieving, it is attapulgite modified to obtain, wherein, the weight ratio of attapulgite, solution A, solution B is 70:5:12.
Embodiment 3
A kind of environment protecting water-based paint, its raw material comprises by weight: water-soluble epoxy resin emulsion 105 parts, 18 parts, water, dipropylene glycol n-butyl ether 6.3 parts, compounded mix 32 parts, BYK3460.15 part, methyl amyl alcohol 1.8 parts, Magnesium Stearate 1.5 parts, polyvinyl alcohol 0.38 part, polyacrylamide 0.13 part, emulsifying agent 61000.35 parts, silicone based high effective antifoaming agent Tego901W0.13 part, polydimethylsiloxane 0.065 part, propylene glycol 0.14 part, sanitas DL7020.025 part, eucalyptus oil 0.013 part, BIT 0.035 part, flow agent 0.42 part;
Wherein, the raw material of compounded mix comprises: 400 orders are attapulgite modified, 325 order diatomite, 400 order gacs, 325 order kaolin, and attapulgite modified, diatomite, gac, kaolinic weight ratio are 2.3:1.12:1.27:1.65;
Attapulgite modified preparation method is: the silica hydrosol getting pH=9.5, be warming up to 62 DEG C, drip the ethanolic soln of γ-aminopropyl triethoxysilane, dropwise in 57min, constantly stir in dropping process, obtain solution A with the speed insulated and stirred 17h of 450r/min, wherein, the weight ratio of silicon-dioxide, γ-aminopropyl triethoxysilane, ethanol is 13:3.5:12; Butyl (tetra) titanate is added after dissolving in ethanol, being added drop-wise to massfraction is in 3.7wt% aqueous hydrochloric acid, 1.8h is stirred with the speed of 650r/min, pH=1.9 is regulated with aqueous sodium hydroxide solution, continue to stir 45min and obtain solution B, wherein, the weight ratio of ethanol, butyl (tetra) titanate, aqueous hydrochloric acid is 225:195:520; Attapulgite is added to the water swelling 1.7h, adds solution A, stir 3.8h with the speed of 850r/min, add solution B, continue to stir 4.3h, centrifugal, washing, be warming up to 195 DEG C, dry 2.2h, pulverize, sieving, it is attapulgite modified to obtain, wherein, the weight ratio of attapulgite, solution A, solution B is 67:5.2:11.5.
Embodiment 4
A kind of environment protecting water-based paint, its raw material comprises by weight: water-soluble epoxy resin emulsion 115 parts, 12 parts, water, dipropylene glycol n-butyl ether 6.7 parts, compounded mix 28 parts, BYK3460.25 part, methyl amyl alcohol 1.2 parts, Magnesium Stearate 2.5 parts, polyvinyl alcohol 0.32 part, polyacrylamide 0.17 part, emulsifying agent 61000.25 parts, silicone based high effective antifoaming agent Tego901W0.17 part, polydimethylsiloxane 0.055 part, propylene glycol 0.16 part, sanitas DL7020.015 part, eucalyptus oil 0.017 part, BIT 0.025 part, flow agent 0.48 part;
Wherein, the raw material of compounded mix comprises: 325 orders are attapulgite modified, 400 order diatomite, 325 order gacs, 400 order kaolin, and attapulgite modified, diatomite, gac, kaolinic weight ratio are 1.7:1.18:1.23:1.75;
Attapulgite modified preparation method is: the silica hydrosol getting pH=8.5, be warming up to 68 DEG C, drip the ethanolic soln of γ-aminopropyl triethoxysilane, dropwise in 53min, constantly stir in dropping process, obtain solution A with the speed insulated and stirred 15h of 550r/min, wherein, the weight ratio of silicon-dioxide, γ-aminopropyl triethoxysilane, ethanol is 17:2.5:18; Butyl (tetra) titanate is added after dissolving in ethanol, being added drop-wise to massfraction is in 3.3wt% aqueous hydrochloric acid, 1.2h is stirred with the speed of 750r/min, pH=2.1 is regulated with aqueous sodium hydroxide solution, continue to stir 35min and obtain solution B, wherein, the weight ratio of ethanol, butyl (tetra) titanate, aqueous hydrochloric acid is 235:185:560; Attapulgite is added to the water swelling 1.3h, adds solution A, stir 3.2h with the speed of 950r/min, add solution B, continue to stir 4.7h, centrifugal, washing, be warming up to 185 DEG C, dry 2.8h, pulverize, sieving, it is attapulgite modified to obtain, wherein, the weight ratio of attapulgite, solution A, solution B is 63:5.8:10.5.
Embodiment 5
A kind of environment protecting water-based paint, its raw material comprises by weight: water-soluble epoxy resin emulsion 110 parts, 15 parts, water, dipropylene glycol n-butyl ether 6.5 parts, compounded mix 30 parts, BYK3460.2 part, methyl amyl alcohol 1.5 parts, Magnesium Stearate 2 parts, polyvinyl alcohol 0.35 part, polyacrylamide 0.15 part, emulsifying agent 61000.3 parts, silicone based high effective antifoaming agent Tego901W0.15 part, polydimethylsiloxane 0.06 part, propylene glycol 0.15 part, sanitas DL7020.02 part, eucalyptus oil 0.015 part, BIT 0.03 part, flow agent 0.45 part;
Wherein, the raw material of compounded mix comprises: 400 orders are attapulgite modified, 400 order diatomite, 400 order gacs, 400 order kaolin, and attapulgite modified, diatomite, gac, kaolinic weight ratio are 2:1.15:1.25:1.7;
Attapulgite modified preparation method is: the silica hydrosol getting pH=9, be warming up to 65 DEG C, drip the ethanolic soln of γ-aminopropyl triethoxysilane, dropwise in 55min, constantly stir in dropping process, obtain solution A with the speed insulated and stirred 16h of 500r/min, wherein, the weight ratio of silicon-dioxide, γ-aminopropyl triethoxysilane, ethanol is 15:3:15; Butyl (tetra) titanate is added after dissolving in ethanol, being added drop-wise to massfraction is in 3.5wt% aqueous hydrochloric acid, 1.5h is stirred with the speed of 700r/min, pH=2 is regulated with aqueous sodium hydroxide solution, continue to stir 40min and obtain solution B, wherein, the weight ratio of ethanol, butyl (tetra) titanate, aqueous hydrochloric acid is 230:190:540; Attapulgite is added to the water swelling 1.5h, adds solution A, stir 3.5h with the speed of 900r/min, add solution B, continue to stir 4.5h, centrifugal, washing, be warming up to 190 DEG C, dry 2.5h, pulverize, sieving, it is attapulgite modified to obtain, wherein, the weight ratio of attapulgite, solution A, solution B is 65:5.5:11.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (9)
1. an environment protecting water-based paint, it is characterized in that, its raw material comprises by weight: water-soluble epoxy resin emulsion 100-120 part, water 10-20 part, dipropylene glycol n-butyl ether 6-7 part, compounded mix 25-35 part, BYK3460.1-0.3 part, methyl amyl alcohol 1-2 part, Magnesium Stearate 1-3 part, polyvinyl alcohol 0.3-0.4 part, polyacrylamide 0.1-0.2 part, emulsifying agent 61000.2-0.4 part, silicone based high effective antifoaming agent Tego901W0.1-0.2 part, polydimethylsiloxane 0.05-0.07 part, propylene glycol 0.1-0.2 part, sanitas DL7020.01-0.03 part, eucalyptus oil 0.01-0.02 part, BIT 0.02-0.04 part, flow agent 0.4-0.5 part,
Wherein, the raw material of compounded mix comprises: attapulgite modified, diatomite, gac, kaolin.
2. environment protecting water-based paint according to claim 1, is characterized in that, attapulgite modified, diatomite, gac, kaolinic weight ratio are 1.5-2.5:1.1-1.2:1.2-1.3:1.6-1.8.
3. environment protecting water-based paint according to claim 1 or 2, is characterized in that, attapulgite modified, diatomite, gac, kaolin are 300-500 order.
4. environment protecting water-based paint according to any one of claim 1-3, it is characterized in that, its raw material comprises by weight: water-soluble epoxy resin emulsion 105-115 part, water 12-18 part, dipropylene glycol n-butyl ether 6.3-6.7 part, compounded mix 28-32 part, BYK3460.15-0.25 part, methyl amyl alcohol 1.2-1.8 part, Magnesium Stearate 1.5-2.5 part, polyvinyl alcohol 0.32-0.38 part, polyacrylamide 0.13-0.17 part, emulsifying agent 61000.25-0.35 part, silicone based high effective antifoaming agent Tego901W0.13-0.17 part, polydimethylsiloxane 0.055-0.065 part, propylene glycol 0.14-0.16 part, sanitas DL7020.015-0.025 part, eucalyptus oil 0.013-0.017 part, BIT 0.025-0.035 part, flow agent 0.42-0.48 part.
5. environment protecting water-based paint according to any one of claim 1-4, is characterized in that, attapulgite modified preparation method is: get silica hydrosol, heats up, and drip the ethanolic soln of γ-aminopropyl triethoxysilane, insulated and stirred obtains solution A; Butyl (tetra) titanate is added after dissolving in ethanol, be added drop-wise in aqueous hydrochloric acid, stir, regulate pH with aqueous sodium hydroxide solution, continue stirring and obtain solution B; Be added to the water by attapulgite swelling, add solution A, stir, add solution B, continue to stir, centrifugal, washing, heat up, dry, pulverize, sieving, it is attapulgite modified to obtain.
6. environment protecting water-based paint according to any one of claim 1-5, it is characterized in that, attapulgite modified preparation method is: the silica hydrosol getting pH=8-10, be warming up to 60-70 DEG C, drip the ethanolic soln of γ-aminopropyl triethoxysilane, dropwise in 50-60min, constantly stir in dropping process, obtain solution A with the speed insulated and stirred 14-18h of 400-600r/min; Added by butyl (tetra) titanate after dissolving in ethanol, being added drop-wise to massfraction is in 3-4wt% aqueous hydrochloric acid, stirs 1-2h, regulate pH=1.5-2.5 with aqueous sodium hydroxide solution with the speed of 600-800r/min, continues to stir 30-50min and obtains solution B; Attapulgite is added to the water swelling 1-2h, adds solution A, stir 3-4h, add solution B with the speed of 800-1000r/min, continue to stir 4-5h, centrifugal, washing, is warming up to 180-200 DEG C, dry 2-3h, and pulverize, sieving, it is attapulgite modified to obtain.
7. environment protecting water-based paint according to any one of claim 1-6, it is characterized in that, in attapulgite modified preparation method, in the preparation process of solution A, the weight ratio of silicon-dioxide, γ-aminopropyl triethoxysilane, ethanol is 10-20:2-4:10-20.
8. environment protecting water-based paint according to any one of claim 1-7, it is characterized in that, in attapulgite modified preparation method, in the preparation process of solution B, the weight ratio of ethanol, butyl (tetra) titanate, aqueous hydrochloric acid is 220-240:180-200:500-580.
9. environment protecting water-based paint according to any one of claim 1-8, is characterized in that, in attapulgite modified preparation method, the weight ratio of attapulgite, solution A, solution B is 60-70:5-6:10-12.