CN105348979A - Fireproof compound coating - Google Patents
Fireproof compound coating Download PDFInfo
- Publication number
- CN105348979A CN105348979A CN201510912697.4A CN201510912697A CN105348979A CN 105348979 A CN105348979 A CN 105348979A CN 201510912697 A CN201510912697 A CN 201510912697A CN 105348979 A CN105348979 A CN 105348979A
- Authority
- CN
- China
- Prior art keywords
- parts
- compound coating
- modified phenolic
- fire prevention
- conductive filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof compound coating. The coating is prepared from, by weight, 100-200 parts of modified phenolic resin, 50-70 parts of acrylic resin, 15-20 parts of methyltriacetoxysilane, 23-35 parts of silicone polyurethane resin, 14-28 parts of methyl tetrahydrophthalic anhydride, 32-50 parts of conductive filler, 11-18 parts of amine-terminated polyether and 8-22 parts of polyisocyanates. The durable compound coating material which can effectively isolate external heat and has high corrosion resistance can be provided under the condition that an existing insufficient coating is compensated for.
Description
Technical field
The invention belongs to building coating Material Field, particularly relate to a kind of fire prevention compound coating.
Background technology
Chemical industry equipment, the storage tank of storage and conveying oil gas and pipeline also need to tackle importing into of external heat in the daily rot-resistant situation of reply, especially when transporting inflammable and explosive liquids and gases, need strict separation outside heat, daily usual employing aluminium powder painting anticorrosion method, because of aluminium powder good heat-transfer, when being subject to solar radiation, the temperature of equipment outer wall tends to exceed more than 60 DEG C, according to common equipment de-sign specification, for storage and the pipe-line equipment carrying oil gas, the temperature of outer wall just needs to take the cooling measures such as cold water spray more than 30 DEG C, all pipelines can not be looked after on the one hand, on the other hand the coating of pipeline outer wall and inwall is had higher requirement.
Summary of the invention
For solving the problem, the invention discloses a kind of fire prevention compound coating, when making up existing coating deficiency, providing a kind of and effectively can completely cut off the durable composite coating material that outside heat has strong non-corrosibility simultaneously.
In order to achieve the above object, the invention provides following technical scheme: a kind of fire prevention compound coating, be made up of the raw material of following parts by weight: modified phenolic resins 100-200 part, acrylic resin 50-70 part, methyl triacetoxysilane 15-20 part, organic silicon polyurethane resin 23-35 part, methyl tetrahydro phthalic anhydride 14-28 part, conductive filler material 32-50 part, Amino Terminated polyether(ATPE) 11-18 part, polyisocyanates 8-22 part.
As a preferred embodiment of the present invention, described conductive filler material comprises conductive nano mica powder, should report glass microballon, polyaniline, conductive zinc oxide.
As a preferred embodiment of the present invention, described modified phenolic resins comprises epoxide modified phenolic aldehyde.
The beneficial effect that the present invention possesses: the present invention by mixed and modified resol, acrylic resin, organic silicon polyurethane resin three kinds of materials as different coatings, in composition compound coating, modified phenolic resins is as the bottom of coating, acrylic resin is as middle level, organic silicon polyurethane resin the most effectively can completely cut off the intrusion of heat as most Top-layer Design Method, methyl triacetoxysilane, conductive filler material, Amino Terminated polyether(ATPE) can be assisted a ruler in governing a country and be carried out anticorrosion and durable use simultaneously, ensure stronger sticking power while ensureing to increase the service life.
Embodiment
Below with reference to specific embodiment, technical scheme provided by the invention is described in detail, following embodiment should be understood and be only not used in for illustration of the present invention and limit the scope of the invention.
Embodiment one: a kind of fire prevention compound coating, be made up of the raw material of following parts by weight: modified phenolic resins 100 parts, acrylic resin 50 parts, methyl triacetoxysilane 15 parts, organic silicon polyurethane resin 23 parts, methyl tetrahydro phthalic anhydride 14 parts, conductive filler material 32 parts, Amino Terminated polyether(ATPE) 11 parts, polyisocyanates 8 parts, conductive filler material comprises conductive nano mica powder, should report glass microballon, polyaniline, conductive zinc oxide, and modified phenolic resins comprises epoxide modified phenolic aldehyde.
Embodiment two: a kind of fire prevention compound coating, be made up of the raw material of following parts by weight: modified phenolic resins 100-200 part, acrylic resin 70 parts, methyl triacetoxysilane 20 parts, organic silicon polyurethane resin 35 parts, methyl tetrahydro phthalic anhydride 28 parts, conductive filler material 50 parts, Amino Terminated polyether(ATPE) 18 parts, polyisocyanates 22 parts, conductive filler material comprises conductive nano mica powder, should report glass microballon, polyaniline, conductive zinc oxide, and modified phenolic resins comprises epoxide modified phenolic aldehyde.
Embodiment three: a kind of fire prevention compound coating, be made up of the raw material of following parts by weight: modified phenolic resins 150 parts, acrylic resin 60 parts, methyl triacetoxysilane 17 parts, organic silicon polyurethane resin 29 parts, methyl tetrahydro phthalic anhydride 22 parts, conductive filler material 44 parts, Amino Terminated polyether(ATPE) 15 parts, polyisocyanates 17 parts, conductive filler material comprises conductive nano mica powder, should report glass microballon, polyaniline, conductive zinc oxide, and modified phenolic resins comprises epoxide modified phenolic aldehyde.
Technique means disclosed in the present invention program is not limited only to the technique means disclosed in above-mentioned embodiment, also comprises the technical scheme be made up of above technical characteristic arbitrary combination.It should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (3)
1. a fire prevention compound coating, it is characterized in that, be made up of the raw material of following parts by weight: modified phenolic resins 100-200 part, acrylic resin 50-70 part, methyl triacetoxysilane 15-20 part, organic silicon polyurethane resin 23-35 part, methyl tetrahydro phthalic anhydride 14-28 part, conductive filler material 32-50 part, Amino Terminated polyether(ATPE) 11-18 part, polyisocyanates 8-22 part.
2. fire prevention compound coating according to claim 1, is characterized in that: described conductive filler material comprises conductive nano mica powder, should report glass microballon, polyaniline, conductive zinc oxide.
3. fire prevention compound coating according to claim 1, is characterized in that: described modified phenolic resins comprises epoxide modified phenolic aldehyde.