CN105348649B - A kind of compound mould release membrance of PP discolorations - Google Patents
A kind of compound mould release membrance of PP discolorations Download PDFInfo
- Publication number
- CN105348649B CN105348649B CN201510966320.7A CN201510966320A CN105348649B CN 105348649 B CN105348649 B CN 105348649B CN 201510966320 A CN201510966320 A CN 201510966320A CN 105348649 B CN105348649 B CN 105348649B
- Authority
- CN
- China
- Prior art keywords
- parts
- mould release
- release membrance
- discolorations
- organo montmorillonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of compound mould release membrance of PP discolorations, including:PP;PC;PBT;PET;Poly glycol monomethyl ether;PTFE;Polymethyl methacrylate;Polyphenylene sulfide;Glass fibre;Organo montmorillonite;Polyetheretherketonefiber fiber;Temperature-sensitive is red;PVA;Lauryl alcohol;Chitosan;Antioxidant 1010;Light stabilizer 622;Nano-TiO2;PP‑g‑MAH;Thickener;Coupling agent part.The mould release membrance of the present invention has splendid water resistance, corrosion resistance, temperature tolerance, weatherability, cohesive, while heated changeable colour, also with radiating energy storage effect.
Description
Technical field
The present invention relates to a kind of mould release membrance, especially a kind of compound mould release membrance of PP discolorations.
Background technology
Mould release membrance, also known as stripping film, barrier film, seperation film, adhesive block film, fractal film, film, plastic sheeting, masking hole film, silicon
Oil film, silicone oil paper, antiadhesion barrier, skidding film, that paper of day, release liners, silliconfilm, release film, release.It is logical
In order to increase the off-type force of plastic sheeting in the case of often, plastic sheeting can be done to plasma treatment, or apply fluorine processing, or apply silicon
(silicone)Mould release is on the top layer of film material, such as PET, PE, OPP, etc.;It is allowed for a variety of organic pressures
Feel glue(Such as the pressure sensitive adhesive of hot melt adhesive, acrylic glue and rubber series)Extremely light and stable off-type force can be shown.
Have the advantages that to isolate due to mould release membrance, fill, protect, be easily peeled off, therefore be widely used in various electricity
In the fields such as son, communication, machinery.
PP, with the high grade of transparency, glossiness and coating adhesion, therefore is widely used in and prepares mould release membrance.Although PE has
Have many good qualities, still, the weatherability of PP films is poor, it is easier to occur in the presence of the external environment conditions such as light, heat, oxygen old
Change, this just have impact on it and uses scope.Simultaneously current mould release membrance, performance comparision is single, is generally used only for isolating, fills.
Therefore, for expanding economy, it is necessary to develop a kind of new compound mould release membrance of PP discolorations.
The content of the invention
Goal of the invention:It is compound release there is provided a kind of PP discolorations the invention aims to solve the deficiencies in the prior art
Film.
Technical scheme:In order to realize the above object the present invention uses following technical scheme.
A kind of compound mould release membrance of PP discolorations, including film layer, the film layer include following component by weight ratio:
PP:50-60 parts;
PC:50-60 parts;
PBT:8-10 parts;That is polybutylene terephthalate (PBT);
PET:10-12 parts;
Poly glycol monomethyl ether:15-20 parts;
PTFE:8-10 parts;
Polymethyl methacrylate:8-10 parts;
Polyphenylene sulfide:4-6 parts;
Glass fibre:4-6 parts;
Organo montmorillonite:4-6 parts;
Polyetheretherketonefiber fiber:2-4 parts;
Temperature-sensitive is red:2-3 parts;
PVA:4-6 parts;Polyvinyl alcohol
Lauryl alcohol:8-10 parts;
Chitosan:2-4 parts;
Antioxidant 1010:0.6-0.8 parts;
Light stabilizer 622:0.6-0.8 parts;
Nano-TiO2:0.8-1.2 parts;
PP-g-MAH:0.6-0.8 parts;
Thickener:0.3-0.5 parts;
Coupling agent:0.8-1 parts.
The thickener is methyl hydroxyethylcellulose.
The coupling agent is the tert-butyl peroxide silane of vinyl three.
The organo montmorillonite is the organo montmorillonite that 3- hexadecane epoxide -2- trimethyl ammonium chlorides are modified.
The preparation method of the organo montmorillonite is:It is 1 by mass ratio:1 inorganic montmorillonite and 3- hexadecane epoxides -2-
Trimethyl ammonium chloride is dissolved in the ethanol water that mass fraction is 50%, and 75 DEG C, reaction are heated to after being well mixed
1 hour, filtering, filter cake was cleaned with ethanol, was drying to obtain described organo montmorillonite.
The inorganic montmorillonites of 1g need the ethanol water that 15-20ml mass fractions are 50%.
The preparation method of the film layer material is specific as follows:Required raw material is weighed according to weight proportion, then in nitrogen
Under protection, each raw material weighed is stirred, 60-80min is stirred at room temperature, be then heated to 60-80 DEG C, stir 2h, then
Temperature reduces 40-50 DEG C, stirs 2h, is finally cooled to room temperature and can obtain required film layer material.
Beneficial effect:Compared with prior art, the present invention has following conspicuousness beneficial effect:
The mould release membrance of the present invention, based on PP and PC, it is good to be aided with compatibility between various other auxiliary agents, each component, simultaneously
Material integrally has splendid water resistance, solvent resistance, resistance to chemical reagents, corrosion resistance, weatherability, can be more harsh at some
In the environment of use, while its temperature tolerance from common PP change colour compound mould release membrance resistance to 130 DEG C or so of high temperature bring up to it is resistance to
More than 220 DEG C of high temperature, tensile strength improves 150% or so, while also having radiating energy storage effect, for isolating, filling
Cheng Zhong, waste heat absorption deposit if the apparatus overheat isolated, filled, can be got up, reach quick heat radiating effect,
Function is more diversified;And the mould release membrance of the present invention can variation with temperature and change colour, so if be isolated, setting of filling
Standby temperature is too high, intuitively can be shown from the color change of mould release membrance, with warning function;Simultaneously the present invention from
Type film is without having stronger cohesive in the case of unnecessary adhesive, it is to avoid a large amount of use adhesives and the environment that brings
Pollution;The mould release membrance of the present invention, component used in its film layer material is environment-protecting and non-poisonous, and its preparation method simply, is easily operated, condition
Gently, industrialized production is more suitable for, with promotional value.
Embodiment
Technical solution of the present invention is described in further detail and completely with reference to embodiment.
Embodiment 1
A kind of compound mould release membrance of PP discolorations, including film layer, the film layer include following component by weight ratio:
PP:50 parts;
PC:50 parts;
PBT:8 parts;
PET:10 parts;
Poly glycol monomethyl ether:15 parts;
PTFE:8 parts;
Polymethyl methacrylate:8 parts;
Polyphenylene sulfide:4 parts;
Glass fibre:4 parts;
Organo montmorillonite:4 parts;
Polyetheretherketonefiber fiber:2 parts;
Temperature-sensitive is red:2 parts;
PVA:4 parts;
Lauryl alcohol:8 parts;
Chitosan:2 parts;
Antioxidant 1010:0.6 part;
Light stabilizer 622:0.6 part;
Nano-TiO2:0.8 part;
PP-g-MAH:0.6 part;
Thickener:Methyl hydroxyethylcellulose:0.3 part;
Coupling agent:The tert-butyl peroxide silane of vinyl three:0.8 part.
Embodiment 2
A kind of compound mould release membrance of PP discolorations, including film layer, the film layer include following component by weight ratio:
PP:55 parts;
PC:55 parts;
PBT:9 parts;
PET:11 parts;
Poly glycol monomethyl ether:18 parts;
PTFE:9 parts;
Polymethyl methacrylate:9 parts;
Polyphenylene sulfide:5 parts;
Glass fibre:5 parts;
Organo montmorillonite:5 parts;
Polyetheretherketonefiber fiber:3 parts;
Temperature-sensitive is red:2.5 part;
PVA:5 parts;
Lauryl alcohol:9 parts;
Chitosan:3 parts;
Antioxidant 1010:0.7 part;
Light stabilizer 622:0.7 part;
Nano-TiO2:1 part;
PP-g-MAH:0.7 part;
Thickener:Methyl hydroxyethylcellulose:0.4 part;
Coupling agent:The tert-butyl peroxide silane of vinyl three:0.9 part.
Embodiment 3
A kind of compound mould release membrance of PP discolorations, including film layer, the film layer include following component by weight ratio:
PP:60 parts;
PC:60 parts;
PBT:10 parts;
PET:12 parts;
Poly glycol monomethyl ether:20 parts;
PTFE:10 parts;
Polymethyl methacrylate:10 parts;
Polyphenylene sulfide:6 parts;
Glass fibre:6 parts;
Organo montmorillonite:6 parts;
Polyetheretherketonefiber fiber:4 parts;
Temperature-sensitive is red:3 parts;
PVA:6 parts;
Lauryl alcohol:10 parts;
Chitosan:4 parts;
Antioxidant 1010:0.8 part;
Light stabilizer 622:0.8 part;
Nano-TiO2:1.2 part;
PP-g-MAH:0.8 part;
Thickener:Methyl hydroxyethylcellulose:0.5 part;
Coupling agent:The tert-butyl peroxide silane of vinyl three:1 part.
Organo montmorillonite in above-described embodiment, is to be prepared via a method which and obtain:
It is 1 by mass ratio:1 inorganic montmorillonite and 3- hexadecane epoxide -2- trimethyl ammonium chlorides are dissolved in matter
Fraction is measured in 50% ethanol water(The inorganic montmorillonites of 1g need the ethanol water that 15-20ml mass fractions are 50%),
75 DEG C are heated to after well mixed, is reacted 1 hour, filtering, filter cake is cleaned with ethanol, described organo montmorillonite is drying to obtain.
The film layer material of its preparation of the above embodiment of the present invention, can be first in 150 DEG C of freeze-day with constant temperature 5h, then by double
Screw extruder is granulated, and is finally molded, winds and can be prepared by required composite plastic film.
The mould release membrance of the present invention, its film layer, using PP, PC, PBT, PET, poly glycol monomethyl ether, PTFE, poly- methyl
Methyl acrylate, polyphenylene sulfide, organo montmorillonite, polyetheretherketonefiber fiber, temperature-sensitive are red, boric acid, lauryl alcohol, PVA, chitosan, anti-
Oxidant, light stabilizer, PP-g-MAH etc. are as composite parts, obtained mould release membrance, and compatibility is good between each component, while material
Expect overall cohesive(Peel strength), water resistance, mechanical property, solvent resistance, resistance to elevated temperatures, resistance to chemical reagents energy,
Fire resistance, weather resistance are superior, at the same also have radiating energy storage effect, and mould release membrance can variation with temperature and change colour,
So if be isolated, the device temperature filled it is too high, intuitively can show have from the color change of mould release membrance
Warning function, function is more diversified, and its application is more extensive.
Finally need it is pointed out here that be:It the above is only the part preferred embodiment of the present invention, it is impossible to be interpreted as to this hair
The limitation of bright protection domain, those skilled in the art according to the present invention the above make some it is nonessential improvement and
Adjustment belongs to protection scope of the present invention.
Claims (4)
1. a kind of compound mould release membrance of PP discolorations, it is characterised in that:Including film layer, the film layer is included such as by weight ratio
Lower component:
PP:50-60 parts;
PC:50-60 parts;
PBT:8-10 parts;
PET:10-12 parts;
Poly glycol monomethyl ether:15-20 parts;
PTFE:8-10 parts;
Polymethyl methacrylate:8-10 parts;
Polyphenylene sulfide:4-6 parts;
Glass fibre:4-6 parts;
Organo montmorillonite:4-6 parts;
Polyetheretherketonefiber fiber:2-4 parts;
Temperature-sensitive is red:2-3 parts;
PVA:4-6 parts;
Lauryl alcohol:8-10 parts;
Chitosan:2-4 parts;
Antioxidant 1010:0.6-0.8 parts;
Light stabilizer 622:0.6-0.8 parts;
Nano TiO 2:0.8-1.2 parts;
PP-g-MAH:0.6-0.8 parts;
Thickener:0.3-0.5 parts;
Coupling agent:0.8-1 parts;
The organo montmorillonite is the organo montmorillonite that 3- hexadecane epoxide -2- trimethyl ammonium chlorides are modified;
The preparation method of the organo montmorillonite is:It is 1 by mass ratio:1 inorganic montmorillonite and 3- hexadecane epoxide -2- hydroxyls
Hydroxypropyltrimonium chloride is dissolved in the ethanol water that mass fraction is 50%, and 75 DEG C, reaction 1 are heated to after being well mixed
Hour, filtering, filter cake is cleaned with ethanol, is drying to obtain described organo montmorillonite;
The inorganic montmorillonites of 1g need the ethanol water that 15-20ml mass fractions are 50%.
2. the compound mould release membrance of PP discolorations according to claim 1, it is characterised in that:The thickener is that dimethyl hydroxyethyl is fine
Dimension element.
3. the compound mould release membrance of PP discolorations according to claim 1, it is characterised in that:The coupling agent is the tertiary fourth of vinyl three
Base peroxy-silane.
4. the compound mould release membrance of PP discolorations according to claim 1, it is characterised in that:The preparation method of the film layer material
It is specific as follows:Required raw material is weighed according to weight proportion, then under nitrogen protection, each raw material weighed is stirred, room
Temperature stirring 60-80min, is then heated to 60-80 DEG C, stirs 2h, then temperature reduces 40-50 DEG C, stir 2h, be finally cooled to
Room temperature is that can obtain required film layer material.