CN105345022A - Purification method for silver nanowire - Google Patents
Purification method for silver nanowire Download PDFInfo
- Publication number
- CN105345022A CN105345022A CN201510690210.2A CN201510690210A CN105345022A CN 105345022 A CN105345022 A CN 105345022A CN 201510690210 A CN201510690210 A CN 201510690210A CN 105345022 A CN105345022 A CN 105345022A
- Authority
- CN
- China
- Prior art keywords
- nano silver
- silver wire
- purification
- silver nanowire
- wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a purification method for a silver nanowire. The purification method is characterized by comprising the steps that firstly, the silver nanowire is dispersed in a polyvinyl pyrrolidone (PVP) aqueous solution to obtain silver nanowire dispersion liquid, another kind of solvents is added to agglomerate the silver nanowire, still standing is carried out, and supernatant liquid is removed; and secondly, the first step is repeated three to five times, and the purified silver nanowire is obtained. By means of the method, the purity of the nanowire can be greatly improved. When the transmittance of the purified nanowire is 99.1%, the surface resistance is as low as 130 ohm. The needed raw materials are all common reagents, so that the operation method is simple and convenient. The purification method for the silver nanowire is simple, economical and easy to operate.
Description
Technical field
The present invention relates to a kind of method of purification of nano silver wire.
Background technology
Printing opacity conductor can be used for the fields such as various FPD, touch-screen, thin-film solar cells, Organic Light Emitting Diode (OLED), sensor and antistatic coating, obtains increasing concern in recent years.Transparent conductor line is verified performance more better than ITO.Owing to having low cost and high-flexibility, nano silver wire is the optimal selection doing transparent conductor.
Polyxol method has been developed to the method that is the most successfully synthesized Ag nano wire.But due to formation and the growth of the core of isomery, the product obtained by polyxol method must contain nano particle impurity.These nano particle impurity greatly reduce electrical conductivity and transparent nanometer line network.Therefore, the product needed after synthesis purifies.Traditional purification process is generally circular centrifugal and decant, and its shortcoming is very consuming time, and adopts the method exchanging filtration, purification nano wire, need the control being subject to many conditions, such as tunica fibrosa nanowire size, the size of core, and the impact of flow velocity and pressure.
Summary of the invention
The object of this invention is to provide a kind of method of purification of nano silver wire, this method of purification step is simple, with low cost, and after purification, the purity of nano wire is higher.
In order to achieve the above object, the invention provides a kind of method of purification of nano silver wire, it is characterized in that, comprising:
The first step: be dispersed in by nano silver wire in polyvinylpyrrolidone (PVP) aqueous solution and obtain nano silver wire dispersion liquid, add another kind of solvent, nano silver wire is reunited, leaves standstill, and removes supernatant liquid;
Second step: repeat first step 3-5 time, obtains the nano silver wire after purifying.
Preferably, the mass fraction < 2% of described polyvinylpyrrolidone (PVP) aqueous solution.
Preferably, described another kind of solvent is weak polar solvent.
Preferably, described another kind of solvent is acetone, and its volume is 2-5 times of nano silver wire dispersion liquid.
Preferably, the w/v of described nano silver wire and polyvinylpyrrolidone (PVP) aqueous solution is 10-20mg: 20mL.
Preferably, the average diameter of described nano silver wire is 20 nanometers, and average length is 60 microns.
Preferably, described nano silver wire is the nano silver wire adopting polyxol method synthesis.
Preferably, the described time left standstill is 5-15min.
Compared with prior art, the invention has the beneficial effects as follows:
1, this invention exploits the method for selective precipitation purification Ag nano wire, this purification method is simple, with low cost.After purification, the purity of nano wire greatly improves, and the performance of the original nano wire of Performance Ratio of the Ag nano wire after purifying is significantly improved, and the nano wire of purifying is when transmitance is 99.1%, and face resistance is low to moderate 130 ohm, and the lower transmitance of identical faces resistance improves 4%.
2, the raw material that the present invention is all is common agents, and get final product purifying nano silver wire with simple experimental procedure and device, the nano silver wire purity after purification is significantly improved, and its nano silver wire of not purifying as transparent conductor Performance Ratio also improves accordingly.The advantages such as this purification process has environmental friendliness, required raw material are easy to get, cheap, operating process is easy.
Accompanying drawing explanation
Fig. 1 is that the nano silver wire SEM prepared in the present invention schemes and grain size distribution.
Fig. 2 is SEM and the dark field optical microscope figure of nano silver wire purification front and back in the present invention.Wherein, A is the SEM figure before purification, B is that the SEM after purifying schemes, and C is the dark field optical microscope figure before purifying, D is the dark field optical microscope figure after purification.
Fig. 3 is the transmitance-face resistance curve of front and back nano silver wire as transparency electrode of purifying in the present invention.
Detailed description of the invention
Below in conjunction with specific embodiment, set forth the present invention further.Should be understood that these embodiments are only not used in for illustration of invention to limit the scope of the invention.In addition should be understood that those skilled in the art can make various changes or modifications the present invention, and these equivalent form of values fall within the application's appended claims limited range equally after the content of having read the present invention's instruction.
Embodiment 1
Conventional polyol method is adopted to obtain nano silver wire (Sun, Y.G.; Xia, Y.N.Adv.Mater.2002,14,833-837; Bergin, S.M.; Chen, Y.H.; Rathmell, A.R.; Charbonneau, P.; Li, Z.Y.; Wiley, B.J.Nanoscale2012,4,1996-2004.).Fig. 1 is the information of obtained nano silver wire, and as can be seen from the figure, the diameter of obtained nano wire is about 20nm, and diameter is evenly distributed.
Embodiment 2
A kind of method of purification of nano silver wire, concrete steps are: be 20 nanometers by the average diameter of being synthesized by polyxol method, average length is that to be dispersed in 10mL mass fraction be obtain nano silver wire dispersion liquid in polyvinylpyrrolidone (PVP) aqueous solution of 0.5% to the nano silver wire 0.02g of 60 microns, add acetone, its volume is 4 times of nano silver wire dispersion liquid, nano silver wire is reunited, leaves standstill 10min, remove supernatant liquid.Repeat above-mentioned steps 3 times, obtain the nano silver wire after purifying.Fig. 2 is the comparison diagram after purification 4 times, can see that the purity of nanowire is significantly improved.
Embodiment 3
On a glass substrate nano wire is made uniform film by Meyerrod method, test its light transmittance and face hinders.Fig. 3 shows, the nano wire after purification shows more excellent performance.
Claims (7)
1. a method of purification for nano silver wire, is characterized in that, comprising:
The first step: be dispersed in by nano silver wire in aqueous povidone solution and obtain nano silver wire dispersion liquid, adds another kind of solvent, and nano silver wire is reunited, and leaves standstill, and removes supernatant liquid;
Second step: repeat first step 3-5 time, obtains the nano silver wire after purifying.
2. the method for purification of nano silver wire as claimed in claim 1, is characterized in that, the mass fraction < 2% of described aqueous povidone solution.
3. the method for purification of nano silver wire as claimed in claim 1, it is characterized in that, described another kind of solvent is acetone, and its volume is 2-5 times of nano silver wire dispersion liquid.
4. the method for purification of nano silver wire as claimed in claim 1, it is characterized in that, described nano silver wire and the w/v of aqueous povidone solution are 10-20mg: 20mL.
5. the method for purification of nano silver wire as claimed in claim 1, it is characterized in that, the average diameter of described nano silver wire is 20 nanometers, and average length is 60 microns.
6. the method for purification of nano silver wire as claimed in claim 1, is characterized in that, described nano silver wire is the nano silver wire adopting polyxol method synthesis.
7. the method for purification of nano silver wire as claimed in claim 1, is characterized in that, the described time left standstill is 5-15min.