CN105330877A - Preparation process of cellulose packaging film - Google Patents
Preparation process of cellulose packaging film Download PDFInfo
- Publication number
- CN105330877A CN105330877A CN201510820031.6A CN201510820031A CN105330877A CN 105330877 A CN105330877 A CN 105330877A CN 201510820031 A CN201510820031 A CN 201510820031A CN 105330877 A CN105330877 A CN 105330877A
- Authority
- CN
- China
- Prior art keywords
- cellulose
- packaging film
- packing film
- mierocrystalline cellulose
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a preparation process of a cellulose packaging film. The packaging film is mainly made from cellulose which can be completely biodegraded and is non-toxic. The degradable cellulose packaging film replaces a synthesized plastic film, recovery and treatment procedures are simplified, and the cellulose packaging film contributes to environmental protection. According to the preparation process of the cellulose packaging film, the processing steps are simple, and the prepared cellulose packaging film has high mechanical strength and is easy to degrade.
Description
Technical field
The present invention relates to a kind of packing film preparation technology, particularly relate to a kind of Mierocrystalline cellulose packing film preparation technology.
Background technology
Cellulose resource is enriched, and is environment-friendly material, and cellulose and its derivates has quite long history as masking starting material, has been widely used in the fields such as plastics, weaving, papermaking, food, daily use chemicals, medicine, building and biology.Play a part very important in film producing industry.Particularly recent years, various high-performance, functional fiber element film emerges in an endless stream, and is a focus in Cellulose Science research.Modal cellulose and its derivates film has the ester class film of the cruel class film of Mierocrystalline cellulose, Mierocrystalline cellulose acids film and ether of cellulose.
Summary of the invention
The invention provides a kind of Mierocrystalline cellulose packing film preparation technology, it is characterized in that, described processing step is:
(1) preparation of ionic liquid: n-propylcarbinyl chloride and N-Methylimidazole are mixed with the ratio of 2:1 row, put into ultrasonic wave afterwards to vibrate 15-20min, after completing, its temperature is risen to 90-95 DEG C and is aided with stirring and condensing reflux by heating in water bath, until no longer dropping liquid, reaction completes, for subsequent use;
(2) ionic liquid pin slurries and step (1) prepared is according to the ratio row mixing of 2:3, swelling at 70-80 DEG C after mixing, afterwards temperature is risen to 90-95 DEG C, obtain cellulose gel, by cellulose gel striking film forming on a glass, put into precipitation bath to be separated, obtain cellulose membrane packing film.
Preferably, the frequency control of the middle sonic oscillation of described step (1) is at 100-120Hz.
Preferably, in described step (2), swelling time controls at 8-10h.
Beneficial effect: the invention provides a kind of Mierocrystalline cellulose packing film preparation technology; the main raw material of this packing film is Mierocrystalline cellulose; Mierocrystalline cellulose fully biodegradable, nontoxic; synthetic plastic film is replaced to use with Mierocrystalline cellulose degradable film for package; simplify recovery and handling procedure, for contribution has been made in environment protection.Mierocrystalline cellulose packing film preparation technology provided by the invention, its processing step is simple, and the Mierocrystalline cellulose packing film physical strength simultaneously produced is high, easily degrade.
Embodiment
The technique means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with embodiment, setting forth the present invention further.
The invention provides a kind of Mierocrystalline cellulose packing film preparation technology, it is characterized in that, described processing step is:
(1) preparation of ionic liquid: n-propylcarbinyl chloride and N-Methylimidazole are mixed with the ratio of 2:1 row, put into ultrasonic wave afterwards to vibrate 15min, after completing, its temperature is risen to 90 DEG C and is aided with stirring and condensing reflux by heating in water bath, until no longer dropping liquid, reaction completes, for subsequent use;
(2) ionic liquid pin slurries and step (1) prepared is according to the ratio row mixing of 2:3, swelling at 70 DEG C after mixing, afterwards temperature is risen to 90 DEG C, obtain cellulose gel, by cellulose gel striking film forming on a glass, put into precipitation bath to be separated, obtain cellulose membrane packing film.
Preferably, the frequency control of the middle sonic oscillation of described step (1) is at 100Hz.
Preferably, in described step (2), swelling time controls at 8h.
The invention provides a kind of Mierocrystalline cellulose packing film preparation technology; the main raw material of this packing film is Mierocrystalline cellulose, Mierocrystalline cellulose fully biodegradable, nontoxic, replaces synthetic plastic film to use with Mierocrystalline cellulose degradable film for package; simplify recovery and handling procedure, for contribution has been made in environment protection.Mierocrystalline cellulose packing film preparation technology provided by the invention, its processing step is simple, and the Mierocrystalline cellulose packing film physical strength simultaneously produced is high, easily degrade.
As known by the technical knowledge, the present invention can be realized by other the embodiment not departing from its spirit or essential feature.Therefore, above-mentioned disclosed embodiment, with regard to each side, all just illustrates, is not only.Within the scope of the present invention all or be all included in the invention being equal to the change in scope of the present invention.
Claims (3)
1. a Mierocrystalline cellulose packing film preparation technology, is characterized in that, described processing step is:
(1) preparation of ionic liquid: n-propylcarbinyl chloride and N-Methylimidazole are mixed with the ratio of 2:1 row, put into ultrasonic wave afterwards to vibrate 15-20min, after completing, its temperature is risen to 90-95 DEG C and is aided with stirring and condensing reflux by heating in water bath, until no longer dropping liquid, reaction completes, for subsequent use;
(2) ionic liquid pin slurries and step (1) prepared is according to the ratio row mixing of 2:3, swelling at 70-80 DEG C after mixing, afterwards temperature is risen to 90-95 DEG C, obtain cellulose gel, by cellulose gel striking film forming on a glass, put into precipitation bath to be separated, obtain cellulose membrane packing film.
2. a kind of Mierocrystalline cellulose packing film preparation technology according to claim 1, is characterized in that, in described step (1), the frequency control of sonic oscillation is at 100-120Hz.
3. a kind of Mierocrystalline cellulose packing film preparation technology according to claim 1, is characterized in that, in described step (2), swelling time controls at 8-10h.