CN105330224A - 沥青混凝土 - Google Patents

沥青混凝土 Download PDF

Info

Publication number
CN105330224A
CN105330224A CN201510928468.1A CN201510928468A CN105330224A CN 105330224 A CN105330224 A CN 105330224A CN 201510928468 A CN201510928468 A CN 201510928468A CN 105330224 A CN105330224 A CN 105330224A
Authority
CN
China
Prior art keywords
parts
epoxy resin
coupling agent
bituminous concrete
mineral aggregate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510928468.1A
Other languages
English (en)
Inventor
许雷明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU WANSHENG CONCRETE Co Ltd
Original Assignee
SUZHOU WANSHENG CONCRETE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU WANSHENG CONCRETE Co Ltd filed Critical SUZHOU WANSHENG CONCRETE Co Ltd
Priority to CN201510928468.1A priority Critical patent/CN105330224A/zh
Publication of CN105330224A publication Critical patent/CN105330224A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种沥青混凝土，是由下述质量份数的成分制备而成的：废旧沥青料10~15份、矿料100~120份、环氧树脂0.5~3.0份、水泥10~30份、硫化钠0.5~2份、<b>活性炭</b>0.5~10份、磁铁矿0.5~5份和偶联剂0.02~0.1份。本发明具有路用性能优良、制备工艺简单、环保性能优越、原料无毒无害的特点。

Description

沥青混凝土
技术领域
本发明涉及道路工程材料领域，特别是涉及一种沥青混凝土。
背景技术
沥青路面具有良好的力学强度、耐磨耗、行车舒适、振动小、噪音低、施工简便等优点。随着公路工程建设的大规模铺开，沥青路面在高等级道路中所占比例越来越大，传统的沥青混凝土路面经常会出现裂缝现象，同时汽车数量的不断攀升，汽车尾气对环境造成的污染成为重要的社会问题，需大力治理。
发明内容
本发明主要解决的技术问题是提供一种沥青混凝土，具有路用性能优良、制备工艺简单、环保性能优越、原料无毒无害的特点。
为解决上述技术问题，本发明采用的一个技术方案是：
提供一种沥青混凝土，是由下述质量份数的成分制备而成的：废旧沥青料10~15份、矿料100~120份、环氧树脂0.5~3.0份、水泥10~30份、硫化钠0.5~2份、活性炭0.5~10份、磁铁矿0.5~5份和偶联剂0.02~0.1份。
在本发明一个较佳实施例中，所述环氧树脂为二酚基丙烷型环氧树脂。
在本发明一个较佳实施例中，所述矿料的粒径为15mm~30mm。
在本发明一个较佳实施例中，所述偶联剂为多元醇酯偶联剂。
在本发明一个较佳实施例中，是由下述质量份数的成分制备而成的：废旧沥青料10份、矿料120份、环氧树脂2.0份、水泥15份、硫化钠1.5份、活性炭3.5份、磁铁矿2.5份和偶联剂0.05份。
在本发明一个较佳实施例中，是由下述质量份数的成分制备而成的：废旧沥青料15份、矿料110份、环氧树脂1.5份、水泥25份、硫化钠1.0份、活性炭4.5份、磁铁矿1.5份和偶联剂0.08份。
本发明的有益效果是：本发明一种沥青混凝土，该配方制得的混凝土具有优良的环保性能，路用性能优良、制备工艺简单、原料无毒无害。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1：一种沥青混凝土，是由下述质量份数的成分制备而成的：废旧沥青料10份、矿料120份、环氧树脂2.0份、水泥15份、硫化钠1.5份、活性炭3.5份、磁铁矿2.5份和偶联剂0.05份。
所述环氧树脂为二酚基丙烷型环氧树脂，所述矿料的粒径为15mm~30mm，所述偶联剂为多元醇酯偶联剂。
实施例2：一种沥青混凝土，是由下述质量份数的成分制备而成的：废旧沥青料15份、矿料110份、环氧树脂1.5份、水泥25份、硫化钠1.0份、活性炭4.5份、磁铁矿1.5份和偶联剂0.08份。
其余成分同实施例1。
实施例3：一种沥青混凝土，是由下述质量份数的成分制备而成的：废旧沥青料12份、矿料100份、环氧树脂1.5份、水泥20份、硫化钠1.5份、活性炭3.8份、磁铁矿4.5份和偶联剂0.08份。
其余成分同实施例1。
上述实施例1~3中的沥青混凝土，按照各配比将成分混合后进入球磨机中研磨至产品要求的细度即可。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (6)

1.一种沥青混凝土，其特征在于，是由下述质量份数的成分制备而成的：废旧沥青料10~15份、矿料100~120份、环氧树脂0.5~3.0份、水泥10~30份、硫化钠0.5~2份、活性炭0.5~10份、磁铁矿0.5~5份和偶联剂0.02~0.1份。
2.根据权利要求1所述的沥青混凝土，其特征在于，所述环氧树脂为二酚基丙烷型环氧树脂。
3.根据权利要求1所述的沥青混凝土，其特征在于，所述矿料的粒径为15mm~30mm。
4.根据权利要求1所述的沥青混凝土，其特征在于，所述偶联剂为多元醇酯偶联剂。
5.根据权利要求1所述的沥青混凝土，其特征在于，是由下述质量份数的成分制备而成的：废旧沥青料10份、矿料120份、环氧树脂2.0份、水泥15份、硫化钠1.5份、活性炭3.5份、磁铁矿2.5份和偶联剂0.05份。
6.根据权利要求1所述的沥青混凝土，其特征在于，是由下述质量份数的成分制备而成的：废旧沥青料15份、矿料110份、环氧树脂1.5份、水泥25份、硫化钠1.0份、活性炭4.5份、磁铁矿1.5份和偶联剂0.08份。
CN201510928468.1A 2015-12-15 2015-12-15 沥青混凝土 Pending CN105330224A (zh)