CN105326606A - Multifunctional nursing mat - Google Patents
Multifunctional nursing mat Download PDFInfo
- Publication number
- CN105326606A CN105326606A CN201510681850.7A CN201510681850A CN105326606A CN 105326606 A CN105326606 A CN 105326606A CN 201510681850 A CN201510681850 A CN 201510681850A CN 105326606 A CN105326606 A CN 105326606A
- Authority
- CN
- China
- Prior art keywords
- absorbed layer
- parts
- pad
- leakage layers
- application
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a multifunctional nursing mat. The multifunctional nursing mat comprises a waist protecting pad, an absorbing layer and a leakage-proof layer, wherein the waist protecting pad arc-shaped in surface is arranged in the middle of the absorbing layer and is provided with two electric massage heads and spherical magnet therapy stones, the absorbing layer with the surface being in stereoscopic diamond reticulate pattern arrangement is arranged on the leakage-proof layer, the waist protecting pad, the absorbing layer and the leakage-proof layer are connected adhesively sequentially, and the leakage-proof layer is a high-density polyethylene layer. The multifunctional nursing mat is convenient to use, comfortable, reliable and good in water absorption effect and has a healthcare function.
Description
Technical field
The present invention relates to a kind of function nursing pad.
Background technology
Nursing pad is not diaper, it is a kind of disposable sanitary articles be made up of materials such as PE film, non-woven fabrics, Time of Fluff Slurry, macromolecules, uses when being mainly used in hospital surgical, gynecologial examination, puerpera's nursing, child's nurse, paralytic's gatism, gynecologic menstrual.Nursing pad is according to the difference of purposes, and the title of crying is also different.The nursing pad used for infant is known as urine pad.Nursing pad for puerpera's nursing is known as puerperium pad, puerpera pad.The nursing pad used for gynecologic menstrual is known as little mattress in menstrual period.
According to different use crowds, nursing pad can be divided into Baby Care pad, puerpera nursing pad, adult nursing pad.Baby Care pad is mainly used in neonate, plays isolation urine effect, and to ensure that cotton-padded mattress below or mattress are not soaked by urine, therefore Baby Care pad is also referred to as is urine pad.Preferably change immediately when Baby Care pad has wet, ensure that the hip of baby are dry and comfortable.Puerpera nursing pad main women essential product in puerperal, is also referred to as puerperium pad.Harsh complete primary school child, first half of the month has a large amount of lochia and flows out every day, and general sanitary towel can not meet, and at this time needs special puerpera nursing pad.Puerpera nursing pad service time is generally use when whole puerperal hemorrhage and lochia are discharged the very first time in puerperal.The personage that adult nursing pad is mainly used in Post operation personage and paralyzed persons and can't take care of oneself.That adult nursing pad is changed is convenient, can ensure can not be dirty bedding below tall building.
Current existing nursing pad structure is simple, and function singleness, comfort is lower.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of easy to use, reliably comfortable, has health care, the function nursing pad that soaking effect is good.
For solving the problem, the present invention adopts following technical scheme:
A kind of function nursing pad, comprise Waist protection pad, absorbed layer and application of anti-leakage layers, described Waist protection pad is located in the middle part of absorbed layer, described absorbed layer is located in application of anti-leakage layers, described Waist protection pad, absorbed layer and application of anti-leakage layers successively adhesion are connected, described Waist protection pad is provided with massage head and magnetotherapy stone, described massage head is electric massage head, described massage head is provided with two, the setting spherical in shape of described magnetotherapy stone, described Waist protection pad surface camber is arranged, described application of anti-leakage layers is high-density polyethylene layer, described absorbed layer surface spatially rhombus reticulate pattern is arranged, described absorbed layer is made up of following raw material by mass fraction proportioning: Musa basjoo Sieb. Et Zucc. head 3-5 part, Herba Euphorbiae supinae 2-4 part, Uroctea compatilis Koch. 5-8 part, grass Radix Clematidis 1-2 part, Rhizoma Polygoni Paleachi 4-5 part, shark's fin wood 2-3 part, Cera Chinensis 5-8 part, Radix Lysidices rhodostegiae 4-7 part, organic phosphate starch 23-25 part, heparin 15-20 part, sodium acrylate 8-10 part and hydroxypropylation cellulose 30-35 part.
Further, described magnetotherapy stone is provided with more than one piece.
Further, described application of anti-leakage layers thickness is 4-5mm.
Further, described absorber thickness is 1.2-1.3mm.
Further, described application of anti-leakage layers area is greater than absorbed layer.
Another technical problem that the present invention will solve is for providing a kind of manufacture method of absorbed layer of function nursing pad.
For solving the problem, the present invention adopts following technical scheme: comprise the following steps:
1) Musa basjoo Sieb. Et Zucc. head 3-5 part, Herba Euphorbiae supinae 2-4 part, Uroctea compatilis Koch. 5-8 part, careless Radix Clematidis 1-2 part, Rhizoma Polygoni Paleachi 4-5 part, shark's fin wood 2-3 part, Cera Chinensis 5-8 part, Radix Lysidices rhodostegiae 4-7 part are put in baking box, keep 75-80 DEG C of bake 5-10 minute, for subsequent use;
2) step 1) gained raw material is dropped in grinder, grind to form 30-40 order granule, for subsequent use;
3) organic phosphate starch 23-25 part, heparin 15-20 part, sodium acrylate 8-10 part and hydroxypropylation cellulose 30-35 part are put in reactor, keep 45-60 DEG C, rotating speed 200r/min to react 6-10 minute, obtain cotton-shaped mixed material, for subsequent use;
4) step 2 gained drug particles is mixed with the cotton-shaped raw material of step 3) gained, by non-woven fabrics sealed envelope, uses press surface pressure to be made three-dimensional rhombus reticulate pattern.
Beneficial effect of the present invention is: the Waist protection pad of setting can keep user to lie in nursing pad can keep comfortable; massage head and magnetotherapy stone have good health-care effect; the Musa basjoo Sieb. Et Zucc. head added in absorbed layer, Herba Euphorbiae supinae, Uroctea compatilis Koch., careless Radix Clematidis, Rhizoma Polygoni Paleachi, shark's fin wood, Cera Chinensis and Radix Lysidices rhodostegiae have good hemostatic function; remain on when using as operation pad; can play a protective role, organic phosphate starch, heparin, sodium acrylate and hydroxypropylation cellulose have good soaking effect.
Accompanying drawing explanation
Fig. 1 is the overall structure schematic diagram of a kind of function nursing pad of the present invention.
Detailed description of the invention
Embodiment one:
As shown in Figure 1, a kind of function nursing pad, comprise Waist protection pad 1, absorbed layer 2 and application of anti-leakage layers 3, described Waist protection pad 1 is located in the middle part of absorbed layer 2, described absorbed layer 2 is located in application of anti-leakage layers 3, described Waist protection pad 1, absorbed layer 2 is connected with application of anti-leakage layers 3 successively adhesion, described Waist protection pad 1 is provided with massage head 4 and magnetotherapy stone 5, described massage head 4 is electric massage head, described massage head 4 is provided with two, the setting spherical in shape of described magnetotherapy stone 5, the surperficial camber of described Waist protection pad 1 is arranged, described application of anti-leakage layers 3 is high-density polyethylene layer, described absorbed layer 2 surface spatially rhombus reticulate pattern is arranged, described absorbed layer 2 is made up of following raw material by mass fraction proportioning: 3 parts, Musa basjoo Sieb. Et Zucc. head, Herba Euphorbiae supinae 2 parts, Uroctea compatilis Koch. 5 parts, grass Radix Clematidis 1 part, Rhizoma Polygoni Paleachi 4 parts, 2 parts, shark's fin wood, Cera Chinensis 5 parts, Radix Lysidices rhodostegiae 4 parts, organic phosphate starch 23 parts, heparin 15 parts, sodium acrylate 8 parts and hydroxypropylation cellulose 30 parts.
Described magnetotherapy stone 5 is provided with more than one piece.
Described application of anti-leakage layers 3 thickness is 4-5mm.
Described absorbed layer 2 thickness is 1.2-1.3mm.
Described application of anti-leakage layers 3 area is greater than absorbed layer 2.
A manufacture method for the absorbed layer 2 of function nursing pad, comprises the following steps:
1) 3 parts, Musa basjoo Sieb. Et Zucc. head, Herba Euphorbiae supinae 2 parts, Uroctea compatilis Koch. 5 parts, careless Radix Clematidis 1 part, Rhizoma Polygoni Paleachi 4 parts, 2 parts, shark's fin wood, Cera Chinensis 5 parts, Radix Lysidices rhodostegiae 4 parts are put in baking box, keep 75-80 DEG C of bake 5-10 minute, for subsequent use;
2) step 1) gained raw material is dropped in grinder, grind to form 30-40 order granule, for subsequent use;
3) organic phosphate starch 23 parts, heparin 15 parts, sodium acrylate 8 parts and hydroxypropylation cellulose 30 parts are put in reactor, keep 45-60 DEG C, rotating speed 200r/min to react 6-10 minute, obtain cotton-shaped mixed material, for subsequent use;
4) step 2 gained drug particles is mixed with the cotton-shaped raw material of step 3) gained, by non-woven fabrics sealed envelope, uses press surface pressure to be made three-dimensional rhombus reticulate pattern.
Embodiment two:
As shown in Figure 1, a kind of function nursing pad, comprise Waist protection pad 1, absorbed layer 2 and application of anti-leakage layers 3, described Waist protection pad 1 is located in the middle part of absorbed layer 2, described absorbed layer 2 is located in application of anti-leakage layers 3, described Waist protection pad 1, absorbed layer 2 is connected with application of anti-leakage layers 3 successively adhesion, described Waist protection pad 1 is provided with massage head 4 and magnetotherapy stone 5, described massage head 4 is electric massage head, described massage head 4 is provided with two, the setting spherical in shape of described magnetotherapy stone 5, the surperficial camber of described Waist protection pad 1 is arranged, described application of anti-leakage layers 3 is high-density polyethylene layer, described absorbed layer 2 surface spatially rhombus reticulate pattern is arranged, described absorbed layer 2 is made up of following raw material by mass fraction proportioning: 4 parts, Musa basjoo Sieb. Et Zucc. head, Herba Euphorbiae supinae 3 parts, Uroctea compatilis Koch. 6.5 parts, grass Radix Clematidis 1.5 parts, Rhizoma Polygoni Paleachi 4.5 parts, 2.5 parts, shark's fin wood, Cera Chinensis 6.5 parts, Radix Lysidices rhodostegiae 5.5 parts, organic phosphate starch 24 parts, heparin 17.5 parts, sodium acrylate 9 parts and hydroxypropylation cellulose 32.5 parts.
Described magnetotherapy stone 5 is provided with more than one piece.
Described application of anti-leakage layers 3 thickness is 4-5mm.
Described absorbed layer 2 thickness is 1.2-1.3mm.
Described application of anti-leakage layers 3 area is greater than absorbed layer 2.
A manufacture method for the absorbed layer 2 of function nursing pad, comprises the following steps:
1) 4 parts, Musa basjoo Sieb. Et Zucc. head, Herba Euphorbiae supinae 3 parts, Uroctea compatilis Koch. 6.5 parts, careless Radix Clematidis 1.5 parts, Rhizoma Polygoni Paleachi 4.5 parts, 2.5 parts, shark's fin wood, Cera Chinensis 6.5 parts, Radix Lysidices rhodostegiae 5.5 parts are put in baking box, keep 75-80 DEG C of bake 5-10 minute, for subsequent use;
2) step 1) gained raw material is dropped in grinder, grind to form 30-40 order granule, for subsequent use;
3) organic phosphate starch 24 parts, heparin 17.5 parts, sodium acrylate 9 parts and hydroxypropylation cellulose 32.5 parts are put in reactor, keep 45-60 DEG C, rotating speed 200r/min to react 6-10 minute, obtain cotton-shaped mixed material, for subsequent use;
4) step 2 gained drug particles is mixed with the cotton-shaped raw material of step 3) gained, by non-woven fabrics sealed envelope, uses press surface pressure to be made three-dimensional rhombus reticulate pattern.
Embodiment three:
As shown in Figure 1, a kind of function nursing pad, comprise Waist protection pad 1, absorbed layer 2 and application of anti-leakage layers 3, described Waist protection pad 1 is located in the middle part of absorbed layer 2, described absorbed layer 2 is located in application of anti-leakage layers 3, described Waist protection pad 1, absorbed layer 2 is connected with application of anti-leakage layers 3 successively adhesion, described Waist protection pad 1 is provided with massage head 4 and magnetotherapy stone 5, described massage head 4 is electric massage head, described massage head 4 is provided with two, the setting spherical in shape of described magnetotherapy stone 5, the surperficial camber of described Waist protection pad 1 is arranged, described application of anti-leakage layers 3 is high-density polyethylene layer, described absorbed layer 2 surface spatially rhombus reticulate pattern is arranged, described absorbed layer 2 is made up of following raw material by mass fraction proportioning: 5 parts, Musa basjoo Sieb. Et Zucc. head, Herba Euphorbiae supinae 4 parts, Uroctea compatilis Koch. 8 parts, grass Radix Clematidis 2 parts, Rhizoma Polygoni Paleachi 5 parts, 3 parts, shark's fin wood, Cera Chinensis 8 parts, Radix Lysidices rhodostegiae 7 parts, organic phosphate starch 25 parts, heparin 20 parts, sodium acrylate 10 parts and hydroxypropylation cellulose 35 parts.
Described magnetotherapy stone 5 is provided with more than one piece.
Described application of anti-leakage layers 3 thickness is 4-5mm.
Described absorbed layer 2 thickness is 1.2-1.3mm.
Described application of anti-leakage layers 3 area is greater than absorbed layer 2.
A manufacture method for the absorbed layer 2 of function nursing pad, comprises the following steps:
1) 5 parts, Musa basjoo Sieb. Et Zucc. head, Herba Euphorbiae supinae 4 parts, Uroctea compatilis Koch. 8 parts, careless Radix Clematidis 2 parts, Rhizoma Polygoni Paleachi 5 parts, 3 parts, shark's fin wood, Cera Chinensis 8 parts, Radix Lysidices rhodostegiae 7 parts are put in baking box, keep 75-80 DEG C of bake 5-10 minute, for subsequent use;
2) step 1) gained raw material is dropped in grinder, grind to form 30-40 order granule, for subsequent use;
3) organic phosphate starch 25 parts, heparin 20 parts, sodium acrylate 10 parts and hydroxypropylation cellulose 35 parts are put in reactor, keep 45-60 DEG C, rotating speed 200r/min to react 6-10 minute, obtain cotton-shaped mixed material, for subsequent use;
4) step 2 gained drug particles is mixed with the cotton-shaped raw material of step 3) gained, by non-woven fabrics sealed envelope, uses press surface pressure to be made three-dimensional rhombus reticulate pattern.
Beneficial effect of the present invention is: the Waist protection pad of setting can keep user to lie in nursing pad can keep comfortable; massage head and magnetotherapy stone have good health-care effect; the Musa basjoo Sieb. Et Zucc. head added in absorbed layer, Herba Euphorbiae supinae, Uroctea compatilis Koch., careless Radix Clematidis, Rhizoma Polygoni Paleachi, shark's fin wood, Cera Chinensis and Radix Lysidices rhodostegiae have good hemostatic function; remain on when using as operation pad; can play a protective role, organic phosphate starch, heparin, sodium acrylate and hydroxypropylation cellulose have good soaking effect.
The above, be only the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, and any change of expecting without creative work or replacement, all should be encompassed within protection scope of the present invention.
Claims (6)
1. a function nursing pad, it is characterized in that: comprise Waist protection pad, absorbed layer and application of anti-leakage layers, described Waist protection pad is located in the middle part of absorbed layer, described absorbed layer is located in application of anti-leakage layers, described Waist protection pad, absorbed layer and application of anti-leakage layers successively adhesion are connected, described Waist protection pad is provided with massage head and magnetotherapy stone, described massage head is electric massage head, described massage head is provided with two, the setting spherical in shape of described magnetotherapy stone, described Waist protection pad surface camber is arranged, described application of anti-leakage layers is high-density polyethylene layer, described absorbed layer surface spatially rhombus reticulate pattern is arranged, described absorbed layer is made up of following raw material by mass fraction proportioning: Musa basjoo Sieb. Et Zucc. head 3-5 part, Herba Euphorbiae supinae 2-4 part, Uroctea compatilis Koch. 5-8 part, grass Radix Clematidis 1-2 part, Rhizoma Polygoni Paleachi 4-5 part, shark's fin wood 2-3 part, Cera Chinensis 5-8 part, Radix Lysidices rhodostegiae 4-7 part, organic phosphate starch 23-25 part, heparin 15-20 part, sodium acrylate 8-10 part and hydroxypropylation cellulose 30-35 part.
2. function nursing pad as claimed in claim 1, is characterized in that: described magnetotherapy stone is provided with more than one piece.
3. function nursing pad as claimed in claim 2, is characterized in that: described application of anti-leakage layers thickness is 4-5mm.
4. function nursing pad as claimed in claim 3, is characterized in that: described absorber thickness is 1.2-1.3mm.
5. function nursing pad as claimed in claim 4, is characterized in that: described application of anti-leakage layers area is greater than absorbed layer.
6. a manufacture method for the absorbed layer of function nursing pad, is characterized in that: comprise the following steps:
1) Musa basjoo Sieb. Et Zucc. head 3-5 part, Herba Euphorbiae supinae 2-4 part, Uroctea compatilis Koch. 5-8 part, careless Radix Clematidis 1-2 part, Rhizoma Polygoni Paleachi 4-5 part, shark's fin wood 2-3 part, Cera Chinensis 5-8 part, Radix Lysidices rhodostegiae 4-7 part are put in baking box, keep 75-80 DEG C of bake 5-10 minute, for subsequent use;
2) step 1) gained raw material is dropped in grinder, grind to form 30-40 order granule, for subsequent use;
3) organic phosphate starch 23-25 part, heparin 15-20 part, sodium acrylate 8-10 part and hydroxypropylation cellulose 30-35 part are put in reactor, keep 45-60 DEG C, rotating speed 200r/min to react 6-10 minute, obtain cotton-shaped mixed material, for subsequent use;
4) step 2 gained drug particles is mixed with the cotton-shaped raw material of step 3) gained, by non-woven fabrics sealed envelope, uses press surface pressure to be made three-dimensional rhombus reticulate pattern.