CN105315957B - The bulb lamp organosilicon bonding glue composition that a kind of no spray is formed - Google Patents
The bulb lamp organosilicon bonding glue composition that a kind of no spray is formed Download PDFInfo
- Publication number
- CN105315957B CN105315957B CN201410851047.9A CN201410851047A CN105315957B CN 105315957 B CN105315957 B CN 105315957B CN 201410851047 A CN201410851047 A CN 201410851047A CN 105315957 B CN105315957 B CN 105315957B
- Authority
- CN
- China
- Prior art keywords
- mass parts
- bulb lamp
- spray
- glue composition
- organosilicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to the peripheral product of LED, and in particular to the bulb lamp organosilicon bonding glue composition that a kind of no spray is formed, it contains (A), (B) two components, wherein (A) component includes the mixture of following material:The α of (A 1) 100 mass parts, ω dialkyl polydimethylsiloxanes, (A 2) 1~5 mass parts polymethyl hydrogen siloxane, (A 3) 10~30 mass of surface handles precipitated calcium carbonate, specific surface area (BET) 150 ㎡/g~380 ㎡/g surface hydrophobicity fumed silicas of (A 4) 0~20 mass parts, (B) component include the material of following part by weight:The dimethyl polysiloxane of (B 1) 100 mass parts, (B 2) 8~12 mass parts amino silane tackifier, (B 3) 0.8~1.2 mass parts tin catalyst.The excellent silicone elastomer body of the small molecule releasing that can not be gathered into liquid, high tenacity, water resistance is can obtain after present invention solidification.
Description
Technical field
The present invention relates to the peripheral product of LEDbulb lamp, and in particular to the bulb lamp organosilicon that a kind of no spray is formed
It is bonded glue composition.
Background technology
With the development in pluralism of LEDbulb lamp, use range is more and more extensive, and use environment is also more and more diversified,
To waterproof, protection against the tide, dust-proof requirement also more and more higher under many environment, needed under many outdoor or adverse circumstances to LED ball
Steep lamp and carry out hermetically sealed protection.Organosilicon material has high-low temperature resistant, weather-resistant, electric insulation, resistance to ozone, hydrophobic, difficulty
Many excellent properties such as combustion, nontoxic, are widely used in LED adhering and sealing industries.Organosilicon for LEDbulb lamp sealing glues
Connecing glue mainly has de- ethanol system organosilicon sealant, de- oxime system organosilicon sealant, separating methanol system organosilicon sealant.
This three kinds of organosilicon sealants need to add more crosslinking agent, and ethanol system can release ethanol small molecule in solidification process, take off oxime
System can release ketoxime small molecule, and methanol system can release methanol small molecule, and these small molecules are under closed environment easily in ball
Bubble lampshade inwall is gathered into droplet, final products outward appearance and illumination effect is influenceed, so as to limit making for organosilicon sealant
With.
The content of the invention
The present invention assembles drop to solve the problems, such as that existing LEDbulb lamp seals small molecular, there is provided a kind of newly fogless
The bulb lamp organosilicon bonding glue composition that shape thing is formed.
The bulb lamp organosilicon bonding glue composition that a kind of no spray is formed, containing (A), (B) two components, (A),
(B) mass ratio of component is 10:0.8~1.2, wherein,
(A) component includes the material of following part by weight:
(A-1) α of 100 mass parts, alpha, omega-dihydroxy polydimethyl siloxane,
(A-2) 1~5 mass parts polymethyl hydrogen siloxane,
(A-3) 10~30 mass of surface processing precipitated calcium carbonate,
(A-4) specific surface area (BET) 150 ㎡/g~380 ㎡ of 0~20 mass parts/g surface hydrophobicity vapor phase method titanium dioxides
Silicon,
(B) component includes the material of following part by weight:
(B-1) dimethyl polysiloxane of 100 mass parts,
(B-2) 8~12 mass parts amino silane tackifier,
(B-3) 0.8~1.2 mass parts tin catalyst.
Another preferred scheme is that the mass ratio of (A), (B) component is 10:1.
Another preferred scheme is the α, and alpha, omega-dihydroxy polydimethyl siloxane is 1500~100000mpa.s viscosity models
107 silicon rubber enclosed, and dimethyl siloxane ring body D3~D10 contents are less than 300ppm.It is highly preferred that α, alpha, omega-dihydroxy gathers
Dimethyl siloxane is 107 silicon rubber of 1500~10000mpa.s range of viscosities.
Another preferred scheme is that the range of viscosities of the polymethyl hydrogen siloxane is 110~120mpa.s, and its hydrogen content is
0.05%~0.7%wt., and dimethyl siloxane ring body D3~D10 contents are less than 300ppm.
Drop is formed to the bulb lamp cover inwall of sealing in order to lower dimethyl siloxane ring body small molecule in 107 glue materials
Contribution, employ 107 silicon rubber of 1500~10000mpa.s range of viscosities, 107 silicon rubber of this range of viscosities can be with
This target is realized well.But even compared with low viscosity α, the dimethyl siloxane ring of alpha, omega-dihydroxy polydimethyl siloxane
Body D3~D10 contents are controlled within 300ppm, and traditional polycondensation type organosilicon systems, which need to add more crosslinking agent, to be solidified,
Also more small molecule can be released in solidification process, small molecule is in sealed states and then aggregation forms droplet, therefore, the present invention
Effectively introduce methyl hydrogen siloxane and make crosslinking agent, trace hydrogen is released in solidification process, but trace hydrogen moves to bulb lamp cover
Inwall will not be agglomerated into liquid spray, and methyl hydrogen siloxane its range of viscosities that the present invention selects is 110~120mpa.s, its
Hydrogen content is 0.05%~0.7%wt., and dimethyl siloxane ring body D3~D10 contents are less than 300ppm.Thus effectively keep away
The problem of being focused into drop with small molecule of hazing is exempted from.
Another preferred scheme is that the particle size range of the precipitated calcium carbonate of the surface treatment is 0.06~0.09 μm.
Another preferred scheme is the surface hydrophobicity fumed silica, and its surface hydrophobicity inorganic agent is hexamethyl two
One or more in silazane, vinyltrimethoxy silane, stearic acid.
Another preferred scheme is, the viscosity of the dimethyl polysiloxane is 10~20mpa.s, and dimethyl siloxane ring
Body D3~D10 contents are less than 300ppm.
Another preferred scheme is, the amino silane tackifier are N, N- dimethyl-APTES
Another preferred scheme is that described tin catalyst is dibutyl tin laurate.
Tackifier are N, and N- dimethyl-APTES, such tackifier are tertiary amine, are catalyzed with tin class
Agent, which can stablize, to be coexisted, while plays a part of increasing bonding force and catalytic promoter.
The present invention, which provides one kind and is different from conventional condensation type organosilicon sealant, to be had in the curing process without can be gathered into
The bulb lamp bonded adhesives that liquid small molecule is released.In use, A, B component are most preferably with 10:1 mass ratio is well mixed, Ran Houyong
Spot gluing equipment is played glue in bulb lamp seat groove, then lampshade is enclosed in lamp socket groove, and room temperature steeps ball after placing two hours
Lamp lights aging twenty four hours, and gained sealing elastomer tool good airproof performance, toughness is high, waterproof and dampproof excellent performance, and ball steeps
Lamp inwall is formed without vaporific droplet.
Embodiment
With reference to specific embodiment, the invention will be further described, and is done pair with conventional condensation type organosilicon sealant
Than to help the present invention is more fully understood, but protection scope of the present invention is not limited in these embodiments.
The precipitated calcium carbonate being surface-treated in the embodiment of the present invention, its particle size range are 0.06~0.09 μm.
Embodiment 1
By following material mixing it is uniformly component A in a mixing bowl:
90 parts of (25 DEG C) of viscosity are the α that 1500mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm,
Alpha, omega-dihydroxy polydimethyl siloxane, 3 parts of viscosity are 110mpa.s, and hydrogen content is 0.05%~0.7%wt., and dimethyl-silicon
Oxygen alkane ring body D3~D10 contents are less than 300ppm methyl hydrogen siloxanes crosslinking agent, 20 parts of surface treatment precipitated calcium carbonates, 10 parts of tables
Specific surface area of the face through HMDS hydrophobic treatment is 150 ㎡/g fumed silicas;
By following material mixing it is uniformly B component in stirred tank:
11 parts of (25 DEG C) of viscosity are the diformazan that 10mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm
Based polysiloxane, 1 part of N, N- dimethyl-APTES, 0.2 part of tin catalyst di lauric dibutyl
Tin;
Two above component is pressed 10:1 quality is more uniform than static mixing, is injected into spot gluing equipment, then glue point
In bulb lamp seat groove, then lampshade is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours, observes
Lampshade inwall Oil Fog drop-wise condition.A part of sizing material is injected in 2mm thickness moulds again, 25 DEG C, vulcanize 7 days under 55%RH, system
Into dumb bell sample, its performance is tested by GB/528-1998 testing standards.(being shown in Table one)
Embodiment 2
By following material mixing it is uniformly component A in a mixing bowl:
95 parts of (25 DEG C) of viscosity are the α that 5000mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm,
Alpha, omega-dihydroxy polydimethyl siloxane, 3 parts of viscosity are 110mpa.s, and hydrogen content is 0.05%~0.7%wt., and dimethyl-silicon
Oxygen alkane ring body D3~D10 contents are less than 300ppm methyl hydrogen siloxanes crosslinking agent, 17 parts of surface treatment precipitated calcium carbonates, 8 parts of tables
Specific surface area of the face through HMDS hydrophobic treatment is 150 ㎡/g fumed silicas;
By following material mixing it is uniformly B component in stirred tank:
11 parts of (25 DEG C) of viscosity are the diformazan that 10mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm
Based polysiloxane, 1 part of N, N- dimethyl-APTES, 0.1 part of dibutyl tin laurate.
Two above component is pressed 10:1 quality is more uniform than static mixing, is injected into spot gluing equipment, then glue point
In bulb lamp seat groove, then lampshade is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours, observes
Lampshade inwall Oil Fog drop-wise condition.A part of sizing material is injected in 2mm thickness moulds again, 25 DEG C, vulcanize 7 days under 55%RH, system
Into dumb bell sample, its performance is tested by GB/528-1998 testing standards.(being shown in Table one)
Embodiment 3
By following material mixing it is uniformly component A in a mixing bowl:
90 parts of (25 DEG C) of viscosity are the α that 1500mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm,
Alpha, omega-dihydroxy polydimethyl siloxane, 3 parts of viscosity are the dimethyl polysiloxanes of 100mpa.s 201, and dimethyl siloxane ring
Body D3~D10 contents are less than 300ppm, 20 parts of surface treatment precipitated calcium carbonates, and 10 parts of surfaces are through the hydrophobic place of HMDS
The specific surface area of reason is 150 ㎡/g fumed silicas;
By following material mixing it is uniformly B component in stirred tank:
8 parts of (25 DEG C) of viscosity are the dimethyl that 10mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm
Polysiloxanes, 3 parts of tetraethyl orthosilicates, 1 part of N, N- dimethyl-APTES, 0.2 part of fourth of tin dilaurate two
Ji Xi.
Two above component is pressed 10:1 quality is more uniform than static mixing, is injected into spot gluing equipment, then glue point
In bulb lamp seat groove, then lampshade is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours, observes
Lampshade inwall Oil Fog drop-wise condition.A part of sizing material is injected in 2mm thickness moulds again, 25 DEG C, vulcanize 7 days under 55%RH, system
Into dumb bell sample, its performance is tested by GB/528-1998 testing standards.(being shown in Table one)
Embodiment 4
It is by certain technique that following material mixing is uniformly close for Alpha's mono-component organic silicone in planetary mixer
Sealing:
90 parts of (25 DEG C) of viscosity are the α that 1500mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm,
Alpha, omega-dihydroxy polydimethyl siloxane, 3 parts of viscosity are the dimethyl polysiloxanes of 100mpa.s 201, and dimethyl siloxane ring
Body D3~D10 contents are less than 300ppm, 20 parts of surface treatment precipitated calcium carbonates, and 10 parts of surfaces are through the hydrophobic place of HMDS
The specific surface area of reason is 150 ㎡/g fumed silicas, 4 parts of dichloromethyl triethoxysilanes, 3 parts of diethylin methyl three
Ethoxysilane;
Above Alpha's system one-component is injected into spot gluing equipment, then glue point in bulb lamp seat groove, then
Lampshade is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours, observes lampshade inwall Oil Fog drop-wise
Condition.A part of sizing material is injected in 2mm thickness moulds again, 25 DEG C, vulcanize 7 days under 55%RH, dumb bell sample is made, by GB/
528-1998 testing standards test its performance.(being shown in Table one)
Embodiment 5
It is by certain technique that following material mixing is uniformly close for de-oxime type mono-component organic silicone in planetary mixer
Sealing:
90 parts of (25 DEG C) of viscosity are the α that 1500mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm,
Alpha, omega-dihydroxy polydimethyl siloxane, 3 parts of viscosity are the dimethyl polysiloxanes of 100mpa.s 201, and dimethyl siloxane ring
Body D3~D10 contents are less than 300ppm, 20 parts of surface treatment precipitated calcium carbonates, and 10 parts of surfaces are through the hydrophobic place of HMDS
The specific surface area of reason is 150 ㎡/g fumed silicas, 4 parts of vinyl tributyl ketoximyl silanes, the second of 0.6 γ-aminopropyl three
TMOS, 0.1 part of tin catalyst dibutyl tin laurate.
Above de-oxime type one-component is injected into spot gluing equipment, then glue point in bulb lamp seat groove, then lampshade
It is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours, observe lampshade inwall Oil Fog drop-wise condition.Again
A part of sizing material is injected in 2mm thickness moulds, 25 DEG C, vulcanize 7 days under 55%RH, dumb bell sample is made, by GB/528-1998
Testing standard tests its performance.(being shown in Table one)
Table one
Embodiment 6
By following material mixing it is uniformly component A in a mixing bowl:
100 parts of (25 DEG C) of viscosity are the α that 1500mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm,
Alpha, omega-dihydroxy polydimethyl siloxane, 5 parts of viscosity are 110mpa.s, hydrogen content 0.05%wt., and dimethyl siloxane ring
Body D3~D10 contents are less than 300ppm methyl hydrogen siloxanes crosslinking agent, 30 parts of surface treatment precipitated calcium carbonates, 20 parts of surfaces six
The specific surface area of methyl disilazane hydrophobic treatment is 380 ㎡/g fumed silicas;
By following material mixing it is uniformly B component in stirred tank:
100 parts of (25 DEG C) of viscosity are the diformazan that 10mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm
Based polysiloxane, 9 parts of N, N- dimethyl-APTES, 1 part of tin catalyst dibutyl tin laurate.
Two components of above A, B are pressed 10:1 quality is more uniform than static mixing, is injected into spot gluing equipment, then glue
Point is in bulb lamp seat groove, then lampshade is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours, sees
Examine lampshade inwall Oil Fog drop-wise condition.A part of sizing material is injected in 2mm thickness moulds again, 25 DEG C, vulcanize 7 days under 55%RH,
Dumb bell sample is made, its performance is tested by GB/528-1998 testing standards.(being shown in Table two)
Embodiment 7
By following material mixing it is uniformly component A in a mixing bowl:
100 parts of (25 DEG C) of viscosity are 10000mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm's
α, alpha, omega-dihydroxy polydimethyl siloxane, 1 part of viscosity are 120mpa.s, hydrogen content 0.7%wt., and dimethyl siloxane ring
Body D3~D10 contents are less than 300ppm methyl hydrogen siloxanes crosslinking agent, 10 parts of surface treatment precipitated calcium carbonates, 10 parts of surfaces six
The specific surface area of methyl disilazane hydrophobic treatment is 150 ㎡/g fumed silicas;
By following material mixing it is uniformly B component in stirred tank:
100 parts of (25 DEG C) of viscosity are the diformazan that 20mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm
Based polysiloxane, 12 parts of N, N- dimethyl-APTES, 1.2 parts of tin catalyst di lauric dibutyls
Tin;
Two components of above A, B are pressed 10:0.8 quality is more uniform than static mixing, is injected into spot gluing equipment, then
Glue point is in bulb lamp seat groove, then lampshade is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours,
Observe lampshade inwall Oil Fog drop-wise condition.A part of sizing material is injected in 2mm thickness moulds again, 25 DEG C, vulcanize 7 under 55%RH
My god, dumb bell sample is made, its performance is tested by GB/528-1998 testing standards.(being shown in Table two)
Embodiment 8
By following material mixing it is uniformly component A in a mixing bowl:
100 parts of (25 DEG C) of viscosity are the α that 8000mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm,
Alpha, omega-dihydroxy polydimethyl siloxane, 3 parts of viscosity are 115mpa.s, hydrogen content 0.5%wt., and dimethyl siloxane ring body
D3~D10 contents are less than 300ppm methyl hydrogen siloxanes crosslinking agent, 20 parts of surface treatment precipitated calcium carbonates, and 15 parts of surfaces are through pregnancy
The specific surface area of base disilazane hydrophobic treatment is 250 ㎡/g fumed silicas;
By following material mixing it is uniformly B component in stirred tank:
100 parts of (25 DEG C) of viscosity are the diformazan that 15mpa.s and dimethyl siloxane ring body D3~D10 contents are less than 300ppm
Based polysiloxane, 8 parts of N, N- dimethyl-APTES, 0.8 part of tin catalyst di lauric dibutyl
Tin;
Two components of above A, B are pressed 10:1.2 quality is more uniform than static mixing, is injected into spot gluing equipment, then
Glue point is in bulb lamp seat groove, then lampshade is enclosed in lamp socket groove, 25 DEG C, lower 2 hours of 55%RH, lights aging 24 hours,
Observe lampshade inwall Oil Fog drop-wise condition.A part of sizing material is injected in 2mm thickness moulds again, 25 DEG C, vulcanize 7 under 55%RH
My god, dumb bell sample is made, its performance is tested by GB/528-1998 testing standards.(being shown in Table two)
Table two
Above-described embodiment is the preferable embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, other any Spirit Essences without departing from the present invention with made under principle change, modification, replacement, combine, simplification,
Equivalent substitute mode is should be, is included within protection scope of the present invention.
Claims (7)
1. the bulb lamp organosilicon bonding glue composition that a kind of no spray is formed, contains (A), (B) two components, (A), (B)
The mass ratio of component is 10:1, it is characterized in that,
(A) component includes the material of following part by weight:
(A-1) α of 100 mass parts, alpha, omega-dihydroxy polydimethyl siloxane,
(A-2) 1~5 mass parts polymethyl hydrogen siloxane,
(A-3) 10~30 mass of surface processing precipitated calcium carbonate,
(A-4) specific surface area (BET) 150 ㎡/g~380 ㎡/g surface hydrophobicity fumed silicas of 0~20 mass parts,
(B) component includes the material of following part by weight:
(B-1) dimethyl polysiloxane of 100 mass parts,
(B-2) 8~12 mass parts amino silane tackifier,
(B-3) 0.8~1.2 mass parts tin catalyst;
The α, alpha, omega-dihydroxy polydimethyl siloxane are 107 silicon rubber of 1500~100000mPa s range of viscosities, and
Dimethyl siloxane ring body D3~D10 contents are less than 300ppm;
The range of viscosities of the polymethyl hydrogen siloxane is 110~120mPa s, and its hydrogen content is 0.05%~0.7%
Wt., and dimethyl siloxane ring body D3~D10 contents are less than 300ppm.
2. glue composition is bonded without the bulb lamp organosilicon that spray is formed according to claim 1, it is characterized in that, the α,
Alpha, omega-dihydroxy polydimethyl siloxane is 107 silicon rubber of 1500~10000mPa s range of viscosities.
3. the bulb lamp organosilicon bonding glue composition that no spray according to claim 1 or claim 2 is formed, it is characterized in that, institute
The particle size range for stating the precipitated calcium carbonate of surface treatment is 0.06~0.09 μm.
4. the bulb lamp organosilicon bonding glue composition that no spray according to claim 1 or claim 2 is formed, it is characterized in that, institute
State surface hydrophobicity fumed silica, its surface hydrophobicity inorganic agent be HMDS, vinyltrimethoxy silane,
One or more in stearic acid.
5. the bulb lamp organosilicon bonding glue composition that no spray according to claim 1 or claim 2 is formed, it is characterized in that, institute
The viscosity for stating dimethyl polysiloxane is 10~20mPa s, and dimethyl siloxane ring body D3~D10 contents are less than
300ppm。
6. glue composition is bonded without the bulb lamp organosilicon that spray is formed according to claims 1 or 2, it is characterized in that,
The amino silane tackifier are N, N- dimethyl-APTES.
7. the bulb lamp organosilicon bonding glue composition that no spray according to claim 1 or claim 2 is formed, it is characterized in that, institute
The tin catalyst stated is dibutyl tin laurate.