CN105314906A - Multi-component potassium magnesium phosphate cement - Google Patents

Multi-component potassium magnesium phosphate cement Download PDF

Info

Publication number
CN105314906A
CN105314906A CN201510858301.2A CN201510858301A CN105314906A CN 105314906 A CN105314906 A CN 105314906A CN 201510858301 A CN201510858301 A CN 201510858301A CN 105314906 A CN105314906 A CN 105314906A
Authority
CN
China
Prior art keywords
glass fibre
potassium magnesium
magnesium phosphate
polycomponent
phosphate cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510858301.2A
Other languages
Chinese (zh)
Inventor
李乾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510858301.2A priority Critical patent/CN105314906A/en
Publication of CN105314906A publication Critical patent/CN105314906A/en
Pending legal-status Critical Current

Abstract

The invention discloses multi-component potassium magnesium phosphate cement, belonging to the field of cement. The multi-component potassium magnesium phosphate cement comprises the following components in percentage by weight: 34%-40% of KH2PO4, 43%-49% of MgO, 7.2%-8.8% of Al(H2PO4)3, 3.3%-4.9% of glass fiber, 1%-1.8% of sodium carboxymethylcellulose, 0.4%-1.2% of a phosphomonoester coupling agent, 0.4%-0.8% of sodium tripolyphosphate and 0.9%-1.3% of ethylene diamine tetra(methylene phosphonic acid) sodium. The multi-component potassium magnesium phosphate cement has the characteristics that a pore structure is relatively perfect, and the crack formation is reduced after the solidification.

Description

A kind of polycomponent potassium magnesium phosphate cement
Technical field
The present invention relates to a kind of cement, particularly a kind of polycomponent potassium magnesium phosphate cement.
Background technology
Potassium magnesium phosphate cement is by dead roasting magnesium oxide and soluble phosphate, chemical additive and mineral admixture according to a certain percentage, is changed that to generate with phosphoric acid salt be the inorganic coagulation material cohering phase in acid condition by soda acid chemical reaction and physical action.Such material, at normal temperatures by chemical bonds, has possessed the principal feature of silicates gelling material and stupalith, namely low-temperature curing, high early strong, high volume stability, cohesiveness are strong, hardenite partial neutral and good weather resistance etc.
But the thermal expansivity of prior art potassium magnesium phosphate cement is higher, hydration heat amount is large simultaneously, easily can form crack after theing cement solidifies.
Summary of the invention
Goal of the invention of the present invention is: for above-mentioned Problems existing, provides one to have and comparatively improves pore structure, reduces a kind of polycomponent potassium magnesium phosphate cement of cracking initiation after solidification.
The technical solution used in the present invention is as follows:
A kind of polycomponent potassium magnesium phosphate cement of the present invention, comprises 34% ~ 40%KH 2pO 4, 43% ~ 49%MgO, 7.2% ~ 8.8%Al(H 2pO 4) 3, 3.3% ~ 4.9% glass fibre, 1% ~ 1.8% Xylo-Mucine, 0.4% ~ 1.2% phosphate monoester coupling agent, 0.4% ~ 0.8% tripoly phosphate sodium STPP and 0.9% ~ 1.3% ethylene diamine tetra methylene phosphonic acid sodium.
Owing to have employed technique scheme, in potassium magnesium phosphate cement, add the intensity that aluminium dihydrogen phosphate can increase cement, increase water tolerance, reduce the thermal expansivity of cement, reduce the shrinkage of cement; Glass fibre can increase the toughness of cement, reduces the generation in gap; The hydrophobic side of phosphate monoester coupling agent can produce bonding action with matrix, improves interfacial combined function, the toughness reduction aspect of cement is served to the effect of buffering; Add tripoly phosphate sodium STPP, diamines tetramethylene phosphonic acid potassium and ethylene diamine tetra methylene phosphonic acid sodium can reduce hydrated cementitious system initial temperature and control the pH value of potassium magnesium phosphate hydrated cementitious system liquid phase, the time of coagulation of potassium magnesium phosphate cement slurry is obviously extended, total hydration heat amount reduces, thus ensure that crystal aquation product production is intact, crack and defect few, hardenite pore structure also improves.
A kind of polycomponent potassium magnesium phosphate cement of the present invention, comprises 37%KH 2pO 4, 46%MgO, 9%Al(H 2pO 4) 3, 4.1% glass fibre, 1.4% Xylo-Mucine, 0.8% phosphate monoester coupling agent, 0.6% tripoly phosphate sodium STPP and 1.1% ethylene diamine tetra methylene phosphonic acid sodium.
Owing to have employed technique scheme, in potassium magnesium phosphate cement water, Components of Acid-Base ratio answers the ultimate compression strength of slide and early water stability to have remarkably influenced on cement, aforementioned proportion is best Components of Acid-Base ratio, effectively can delay the early hydration speed of response of cement slurry, hydrated product crystal accumulation is tight, defect is few, and hardening of cement body has more perfect pore structure.
A kind of polycomponent potassium magnesium phosphate cement of the present invention, the particle diameter of described magnesium oxide particle is 86 μm, and the specific surface area of described magnesium oxide particle is 1737cm 2/ g.
Owing to have employed technique scheme, the operable time of construction and good degree of mobilization can be ensured, meanwhile, the less shrinkage improving cement of particle diameter, thus make cement produce microdilatancy, reduce thermal expansivity.But particle diameter is too small, can improve hydration temperature, therefore, this size is optimum value.
A kind of polycomponent potassium magnesium phosphate cement of the present invention, the particle diameter of described biphosphate k particle is 130 μm, and the specific surface area of described potassium primary phosphate is 2110cm 2/ g.
Owing to have employed technique scheme, the operable time of construction and good degree of mobilization can be ensured, meanwhile, the less shrinkage improving cement of particle diameter, thus make cement produce microdilatancy, reduce thermal expansivity.But particle diameter is too small, can improve hydration temperature, therefore, this size is optimum value.
A kind of polycomponent potassium magnesium phosphate cement of the present invention, the particle diameter of described biphosphate aluminum particulate is 90 μm, and the specific surface area of described aluminium dihydrogen phosphate is 2320cm 2/ g.
Owing to have employed technique scheme, the operable time of construction and good degree of mobilization can be ensured, meanwhile, the less shrinkage improving cement of particle diameter, thus make cement produce microdilatancy, reduce thermal expansivity.But particle diameter is too small, can improve hydration temperature, therefore, this size is optimum value.
A kind of polycomponent potassium magnesium phosphate cement of the present invention, described glass fibre is nano-TiO 2/ micron composite glass fiber, described Nano/micron TiO 2glass fibre is laminate structure, comprises TiO 2at the porous coating that fiberglass surfacing is formed, described TiO 2the particle diameter of particle is 43nm.
Owing to have employed technique scheme, nano titanium oxide and glass fibre are carried out compound, improves the interface interaction between two-phase, significantly can increase the wear resistance of glass fibre.
A kind of polycomponent potassium magnesium phosphate cement of the present invention, described nano-TiO 2/ micron composite glass fiber is prepared from by following steps:
Step one: get 1 part of butyl (tetra) titanate and be dissolved in appropriate dehydrated alcohol, according to dehydrated alcohol: methyl ethyl diketone volume ratio 1:0.2 adds methyl ethyl diketone in solution, stirs 15min according to the speed of 2000r/min;
Step 2: add appropriate amount of deionized water until precipitate completely in solution, then the nitric acid adding that in solution appropriate concentration is 30%, until sediment completely dissolve, obtain Sol A liquid;
Step 3: according to butyl (tetra) titanate: glass fibre mol ratio 1.2:1 takes glass fibre, glass fibre is dissolved in appropriate dehydrated alcohol and is made into glass fibre solution, glass fibre solution is added dropwise in Sol A liquid according to the speed of 20/, heating reflux reaction while dropping;
Step 4: drip completely at glass fibre solution, after continuing heating reflux reaction 2h, leaves standstill and naturally cools to normal temperature, obtain Powdered precipitation;
Step 5: filter, use appropriate dehydrated alcohol successively, deionized water and absolute ethanol washing powder, dry under the condition of 70 DEG C, obtain nano-TiO 2/ micron composite glass fiber.
Owing to have employed technique scheme, the conjugated fibre of synthesis, titanium dioxide and glass fibre not easily depart from.
In sum, owing to have employed technique scheme, the invention has the beneficial effects as follows:
1, obviously extend the time of coagulation of slurry, total hydration heat amount reduces, thus ensures that crystal aquation product production is intact, crack and defect few, hardenite pore structure also improves.
2, effectively delay the early hydration speed of response of cement slurry, hydrated product crystal accumulation is tight, defect is few, and hardening of cement body has more perfect pore structure.
3, improve the shrinkage of cement, thus make cement produce microdilatancy, reduce thermal expansivity, improve the interface interaction between two-phase, significantly can increase wear resistance.
Accompanying drawing explanation
Fig. 1 is that simple glass fiber SEM schemes;
Fig. 2 is nano-TiO 2/ micron composite glass fiber SEM schemes.
Embodiment
Below in conjunction with accompanying drawing, the present invention is described in detail.
In order to make the object of invention, technical scheme and advantage clearly understand, below in conjunction with drawings and Examples, the present invention is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the present invention, be not intended to limit the present invention.
Embodiment 1
A kind of polycomponent potassium magnesium phosphate cement, comprises 34%KH 2pO 4, 49%MgO, 7.2%Al(H 2pO 4) 3, 4.9% glass fibre, 1% Xylo-Mucine, 1.2% phosphate monoester coupling agent, 0.4% tripoly phosphate sodium STPP and 1.3% ethylene diamine tetra methylene phosphonic acid sodium.
Embodiment 2
A kind of polycomponent potassium magnesium phosphate cement, comprises 40%KH 2pO 4, 43%MgO, 8.8%Al(H 2pO 4) 3, 3.3% glass fibre, 1.8% Xylo-Mucine, 0.4% phosphate monoester coupling agent, 0.8% tripoly phosphate sodium STPP and 0.9% ethylene diamine tetra methylene phosphonic acid sodium.
The particle diameter of magnesium oxide particle is 86 μm, and the specific surface area of described magnesium oxide particle is 1737cm 2/ g.
The particle diameter of biphosphate k particle is 130 μm, and the specific surface area of described potassium primary phosphate is 2110cm 2/ g.
The particle diameter of biphosphate aluminum particulate is 90 μm, and the specific surface area of described aluminium dihydrogen phosphate is 2320cm 2/ g.
Embodiment 3
A kind of polycomponent potassium magnesium phosphate cement, comprises 37%KH 2pO 4, 46%MgO, 9%Al(H 2pO 4) 3, 4.1% glass fibre, 1.4% Xylo-Mucine, 0.8% phosphate monoester coupling agent, 0.6% tripoly phosphate sodium STPP and 1.1% ethylene diamine tetra methylene phosphonic acid sodium.
The particle diameter of magnesium oxide particle is 86 μm, and the specific surface area of described magnesium oxide particle is 1737cm 2/ g.
The particle diameter of biphosphate k particle is 130 μm, and the specific surface area of described potassium primary phosphate is 2110cm 2/ g.
The particle diameter of biphosphate aluminum particulate is 90 μm, and the specific surface area of described aluminium dihydrogen phosphate is 2320cm 2/ g.
Glass fibre is nano-TiO 2/ micron composite glass fiber, Nano/micron TiO 2glass fibre is laminate structure, comprises TiO 2at the porous coating that fiberglass surfacing is formed, TiO 2the particle diameter of particle is 43nm.
Embodiment 4
Nano-TiO 2/ micron composite glass fiber is prepared from by following steps:
Step one: get 1 part of butyl (tetra) titanate and be dissolved in appropriate dehydrated alcohol, according to dehydrated alcohol: methyl ethyl diketone volume ratio 1:0.2 adds methyl ethyl diketone in solution, stirs 15min according to the speed of 2000r/min;
Step 2: add appropriate amount of deionized water until precipitate completely in solution, then the nitric acid adding that in solution appropriate concentration is 30%, until sediment completely dissolve, obtain Sol A liquid;
Step 3: according to butyl (tetra) titanate: glass fibre mol ratio 1.2:1 takes glass fibre, glass fibre is dissolved in appropriate dehydrated alcohol and is made into glass fibre solution, glass fibre solution is added dropwise in Sol A liquid according to the speed of 20/, heating reflux reaction while dropping;
Step 4: drip completely at glass fibre solution, after continuing heating reflux reaction 2h, leaves standstill and naturally cools to normal temperature, obtain Powdered precipitation;
Step 5: filter, use appropriate dehydrated alcohol successively, deionized water and absolute ethanol washing powder, dry under the condition of 70 DEG C, obtain nano-TiO 2/ micron composite glass fiber.
As shown in Figure 1 to Figure 2, bare glass fibre is bar-shaped, and diameter 10 ~ 20 μm, surface is more smooth.Nano-TiO 2the uniform TiO2 coating layer of/micron composite glass fiber surface coverage, defines Nano/micron composite particles, TiO 2the particle diameter of particle is at 43nm, and coating layer is vesicular structure.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any amendments done within the spirit and principles in the present invention, equivalent replacement and improvement etc., all should be included within protection scope of the present invention.

Claims (7)

1. a polycomponent potassium magnesium phosphate cement, is characterized in that: comprise 34% ~ 40%KH 2pO 4, 43% ~ 49%MgO, 7.2% ~ 8.8%Al(H 2pO 4) 3, 3.3% ~ 4.9% glass fibre, 1% ~ 1.8% Xylo-Mucine, 0.4% ~ 1.2% phosphate monoester coupling agent, 0.4% ~ 0.8% tripoly phosphate sodium STPP and 0.9% ~ 1.3% ethylene diamine tetra methylene phosphonic acid sodium.
2. a kind of polycomponent potassium magnesium phosphate cement as claimed in claim 1, is characterized in that: comprise 37%KH 2pO 4, 46%MgO, 9%Al(H 2pO 4) 3, 4.1% glass fibre, 1.4% Xylo-Mucine, 0.8% phosphate monoester coupling agent, 0.6% tripoly phosphate sodium STPP and 1.1% ethylene diamine tetra methylene phosphonic acid sodium.
3. a kind of polycomponent potassium magnesium phosphate cement as claimed in claim 1 or 2, it is characterized in that: the particle diameter of described magnesium oxide particle is 86 μm, the specific surface area of described magnesium oxide particle is 1737cm 2/ g.
4. a kind of polycomponent potassium magnesium phosphate cement as claimed in claim 3, it is characterized in that: the particle diameter of described biphosphate k particle is 130 μm, the specific surface area of described potassium primary phosphate is 2110cm 2/ g.
5. a kind of polycomponent potassium magnesium phosphate cement as claimed in claim 4, it is characterized in that: the particle diameter of described biphosphate aluminum particulate is 90 μm, the specific surface area of described aluminium dihydrogen phosphate is 2320cm 2/ g.
6. a kind of polycomponent potassium magnesium phosphate cement as described in claim 4 or 5, is characterized in that: described glass fibre is nano-TiO 2/ micron composite glass fiber, described Nano/micron TiO 2glass fibre is laminate structure, comprises TiO 2at the porous coating that fiberglass surfacing is formed, described TiO 2the particle diameter of particle is 43nm.
7. a kind of polycomponent potassium magnesium phosphate cement as claimed in claim 6, is characterized in that, described nano-TiO 2/ micron composite glass fiber is prepared from by following steps:
Step one: get 1 part of butyl (tetra) titanate and be dissolved in appropriate dehydrated alcohol, according to dehydrated alcohol: methyl ethyl diketone volume ratio 1:0.2 adds methyl ethyl diketone in solution, stirs 15min according to the speed of 2000r/min;
Step 2: add appropriate amount of deionized water until precipitate completely in solution, then the nitric acid adding that in solution appropriate concentration is 30%, until sediment completely dissolve, obtain Sol A liquid;
Step 3: according to butyl (tetra) titanate: glass fibre mol ratio 1.2:1 takes glass fibre, glass fibre is dissolved in appropriate dehydrated alcohol and is made into glass fibre solution, glass fibre solution is added dropwise in Sol A liquid according to the speed of 20/, heating reflux reaction while dropping;
Step 4: drip completely at glass fibre solution, after continuing heating reflux reaction 2h, leaves standstill and naturally cools to normal temperature, obtain Powdered precipitation;
Step 5: filter, use appropriate dehydrated alcohol successively, deionized water and absolute ethanol washing powder, dry under the condition of 70 DEG C, obtain nano-TiO 2/ micron composite glass fiber.
CN201510858301.2A 2015-11-30 2015-11-30 Multi-component potassium magnesium phosphate cement Pending CN105314906A (en)