CN105297523A - Printing paper capable of being dissolved in water - Google Patents
Printing paper capable of being dissolved in water Download PDFInfo
- Publication number
- CN105297523A CN105297523A CN201510721076.8A CN201510721076A CN105297523A CN 105297523 A CN105297523 A CN 105297523A CN 201510721076 A CN201510721076 A CN 201510721076A CN 105297523 A CN105297523 A CN 105297523A
- Authority
- CN
- China
- Prior art keywords
- water
- printing paper
- printing
- bearing bed
- printed layers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Printing paper capable of being dissolved in water comprises a bearing layer and a printing layer. The printing layer is formed by printing printing ink on the bearing layer. The bearing layer is prepared from, by weight, 26% of wood fibers, 24% of outer bentonite, 30% of polyvinyl akohol, 17.5% of latex, 2% of metal powder and 0.5% of carbon dust. The printing paper is low in investment, fewer in procedure, simple in structure, good in decoration effect and convenient to use, the printing ink process is adopted as a foundation, and other several additional processes are combined.
Description
Technical field
The present invention relates to a kind of paper, particularly relate to a kind of water-soluble printing paper.
Background technology
At present, to metal, (material surface such as steel & aluminum section steel >, engineering plastics carries out the raw material of application or duplicating and method mainly contains: the duplicating of paint spraying, copy film, negative film duplicating, the duplicating of heat copying film etc. both at home and abroad.The various materials adopting above raw material and method to produce, all also exist certain limitation, as: weatherability, corrosion resistance, ABRASION RESISTANCE, pencil hardness etc. are not up to standard, also personnel health, natural environment have an impact, the scope of application is limited, can not reach ideal effect, limit industrialization process.So how to provide a kind of equipment investment less demanding, production process is few, and structure is simple, the water-soluble transfer-printing paper that raw material are nontoxic, just the problem to be solved in the present invention.
Summary of the invention
The equipment investment that the invention solves existing water copy film is large, production process is many, complex structure, raw material have the deficiency of certain influence to human body and environment, provide a kind of raw material for steel, aluminium, the duplicating processing of plastic or other material surface, and duplicating machining need be invested little, operation is few, structure is simple, the water-soluble transfer-printing paper that raw material are nontoxic.
Its concrete technical scheme is: a kind of water-soluble printing paper, comprises bearing bed and printed layers, and described printed layers is that ink is printed on bearing bed; Described bearing bed is by weight percentage: 26% wood fibre, 24% outer bentonite, 30% polyvinyl alcohol, 17.5% latex, 2% metal dust, 0.5% carbon dust.
Described wood fibre is the skeleton as supporting other additives.Described bentonite is the moisture clay pit based on montmorillonite, have bloating tendency, absorption can be equivalent to the water of own vol 8 to 20 times and be expanded to 30 times, can disperse in soliquid in aqueous medium, adding bang profit soil and make bearing bed just thoroughly dispersion in the short time in water.Described polyvinyl alcohol is water-soluble but be dissolved in organic solvent hardly, and it has film forming, can promote the tensile strength of described bearing bed; Described latex as adhesive, its excellent adsorption; Described metal dust can strengthen the efficiency that machine is dried greatly, and having no requirement to the kind of metal dust, can be the powder of the single metals such as aluminium powder, also can use the powder of alloying metal.As preferably, described printed layers is that fluorocarbon oil ink print forms.Fluorocarbon oil ink has good weatherability, advantage not easy to fade.As preferably, described bearing bed is dried by machine ovens and is formed.Owing to containing metal dust in bearing bed, greatly can improve the efficiency that machine is dried, machine drying technology is achieved, and the investment of machine ovens is far smaller than traditional steam drying box, and security and the feature of environmental protection also be better than steam drying box.As preferably, described printed layers be Shan ink print on bearing bed after form through being dried by machine ovens.Bearing bed just can print after drying via machine, after printed layers is foretold in printing, then enters machine drying in oven printed layers.
As preferably, described metal dust is iron powder.
As preferably, described carbon dust is tiny, the uniform high-quality carbon dust of particle.
The invention provides a kind of investment little, operation is few, structure is simple, the water-soluble transfer-printing paper that raw material are nontoxic, fundamentally solve the domestic and international series of problems that the raw material of application or duplicating and method exist to section bar tables such as metal (steel, aluminium) and engineering plastics at present, fully meet people to Surface of profile application or duplicate raw-material each side requirement.
Detailed description of the invention
A kind of water-soluble transfer-printing paper, comprise bearing bed and by the printed layers of ink printing on bearing bed, first bearing bed raw material is configured in production process, will by weight percentage: 26% wood fibre, 24% outer bentonite, 30% polyvinyl alcohol, 17.5% latex, 2% metal dust, the raw material preparation mixing of 0.5% carbon dust, after again the water being equivalent to above-mentioned raw materials weight one times being added, mixing and stirring, bearing bed slurry, then by bearing bed slurry uniform application on the support of surfacing, then send into microwave oven to dry, after oven dry, the bearing bed of drying is peeled off from support, then printed layers is formed with pattern required on fluorocarbon oil ink print, finally the product finished printing is sent into microwave oven again to dry, through finished product inspection, cutting packaging is the water-soluble transfer-printing paper of finished product.In use, first by activator i.e. organic solvent composition even application on object, be in the water of 50 DEG C water-soluble transfer-printing paper being floated over temperature, then the object being coated with activator is pressed on the water-soluble transfer-printing paper floated on the surface at once, submerged together with water-soluble transfer-printing paper, under the effect of hydraulic pressure, the bearing bed of water-soluble transfer-printing paper was dissolved in water greatly in two minutes, printed layers is then under the acting in conjunction of activator and hydraulic pressure, be attached to object table and, this completes transfer printing.
Claims (2)
1. a water-soluble printing paper, is characterized in that: comprise bearing bed and printed layers, and described printed layers is that ink is printed on bearing bed; Described bearing bed is by weight percentage: 26% wood fibre, 24% outer bentonite, 30% polyvinyl alcohol, 17.5% latex, 2% metal dust, 0.5% carbon dust.
2. a kind of water-soluble printing paper according to claim 1, its spy is being: its printed layers be ink printing after bearing bed, by machine dry form.