CN105295462A - High-temperature-resistant anti-corrosive coating and preparation method - Google Patents
High-temperature-resistant anti-corrosive coating and preparation method Download PDFInfo
- Publication number
- CN105295462A CN105295462A CN201510759564.8A CN201510759564A CN105295462A CN 105295462 A CN105295462 A CN 105295462A CN 201510759564 A CN201510759564 A CN 201510759564A CN 105295462 A CN105295462 A CN 105295462A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- resistant
- rotating speed
- subsequent use
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Provided are a high-temperature-resistant anti-corrosive coating and a preparation method. The high-temperature-resistant anti-corrosive coating comprises, by weight parts, 812 parts of potassium silicate solution, 32 parts of lithium hydroxide solution, 337 parts of CH3Si (OCH3), 68 parts of water, 139 parts of wollastonite, 37 parts of boron nitride, 41 parts of fine grain aluminum oxide, 35 parts of superfine zinc oxide and 38 parts of titanium oxide. The high-temperature-resistant anti-corrosive coating can be used for base layer painting of automobiles, aerospace, toys and outdoor sports equipment. The high-temperature-resistant anti-corrosive coating has the advantages of being convenient to transport and construct and non-toxic, having no foreign smell and being free of pollution and has the advantages of being high in coating hardness and resistant to friction, impact, high temperature, corrosion, aging, weather, radiation, salt fog and water.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of protective system, can be used for the fire-resistant anticorrosion paint of basic unit's brushings such as automobile, space flight, toy, outdoor activity equipment, there is transport, easy construction, nontoxic, free from extraneous odour, the advantage such as pollution-free, and there is the features such as coating hardness is high, friction resistant, shock resistance, fire resistant anticorrosive, resistance to deterioration is good, weather-proof, radioprotective, salt spray resistance, water resisting property are good.
Background technology
Protective system, is generally divided into conventional protective system and heavy-duty coating, is requisite a kind of coating in paint.Conventional protective system is under general condition, plays etch-proof effect to metal etc., the life-span that protection non-ferrous metal uses; Heavy-duty coating refers to relatively conventional protective system, can apply in relatively harsh corrosive environment, and has a class protective system that can reach the protection period longer than conventional protective system.The antiseptic principle of general protective system is chemistry, physics and electrochemistry direction; below detailed explanation: one, the rot-resistant principles of chemistry: the rot-resistant principles of chemistry are exactly neutralize harmful acid-base material for neutral innoxious substance, protect the material in corrosion protection coating not to be subject to the infringement of corrosives.Often add some amphoteric substances, such as aluminium hydroxide, hydrated barta and zinc oxide etc. in rust proof paint, these materials are easy to and soda acid nuisance generation chemical action, and realize preservative effect.Two, rot-resistant physical principle: rot-resistant physical principle is exactly protected material and extraneous corrosives are kept apart with corrosion protection coating.The physical principle of rust proof paint is exactly use membrane-forming agent to obtain fine and close corrosion protection coating, isolates the injury of preservative activity to protected material, such as, just can form lead soap after leaded coating and oil plant reaction, ensure the compactness of corrosion protection coating.Three, rot-resistant electrochemical action: rot-resistant electrochemical action refers to adds some special materials in rust proof paint, anticorrosion ion is formed by reacting during rust proof paint like this at moisture and oxygen, make the metallic surface passivation such as iron and steel, thus stop the stripping of metal ion, arrive rot-resistant object, modal in this particular matter is exactly chromic salt.Fire-resistant anticorrosion paint is the aqueous inorganic paint adopting special high-temperature solution and inorganic polymer to process, the Heat and corrosion resistant coating of coating spontaneous curing, coating filmogen: make interpenetrating net polymer based on inorganic polymer as filmogen.Fire-resistant anticorrosion paint can protect the effects such as matrix is anticorrosion, anti-oxidant, closed, wear-resistant protection in hot environment, and coating stability is high, can react in high temperature environments with other bioactive molecules, long service life.Fire-resistant anticorrosion paint brushing is on high-temperature furnace body metal; can resistance to anticorrosion, the resistibility that improves acid-fast alkali-proof of available protecting high-temperature furnace body metal in thermal-flame environment; protection metal is not by effects such as anti-oxidant, closed protectives; overcome common protective system extremely inadaptable under the high temperature conditions; heatproof is inadequate, easily produces the defects such as peeling, crowfoot cracks, variable color.
Summary of the invention
The object of the present invention is to provide a kind of protective system, can be used for the fire-resistant anticorrosion paint of basic unit's brushings such as automobile, space flight, toy, outdoor activity equipment, there is transport, easy construction, nontoxic, free from extraneous odour, the advantage such as pollution-free, and there is the features such as coating hardness is high, friction resistant, shock resistance, fire resistant anticorrosive, resistance to deterioration is good, weather-proof, radioprotective, salt spray resistance, water resisting property are good.
Present invention employs such technical scheme: the material in described fire-resistant anticorrosion paint and weight proportion respectively: potassium silicate solution 812 parts, lithium hydroxide aqueous solution 32 parts, CH
3si (OCH
3)
337 parts, 68 parts, water, wollastonite 139 parts, boron nitride 37 parts, fine-grained alumina 41 parts, super fine zinc oxide 35 parts, titanium oxide 38 parts.
The present invention is specifically related to a kind of protective system, can be used for the fire-resistant anticorrosion paint of basic unit's brushings such as automobile, space flight, toy, outdoor activity equipment.
This product has transport, easy construction, nontoxic, free from extraneous odour, the advantage such as pollution-free, and has the features such as coating hardness is high, friction resistant, shock resistance, fire resistant anticorrosive, resistance to deterioration is good, weather-proof, radioprotective, salt spray resistance, water resisting property are good.
Embodiment
Present invention employs such technical scheme: in described fire-resistant anticorrosion paint, material and weight proportion are respectively: potassium silicate solution 812 parts, lithium hydroxide aqueous solution 32 parts, CH
3si (OCH
3)
337 parts, 68 parts, water, wollastonite 139 parts, boron nitride 37 parts, fine-grained alumina 41 parts, super fine zinc oxide 35 parts, titanium oxide 38 parts.
Its preparation method is following steps:
Step one), in reaction vessel, add potassium silicate solution, rotating speed is adjusted to 1500r/min, forms whirlpool, and solution is heated to 35 DEG C, it is for subsequent use slowly to add lithium hydroxide aqueous solution in stirring;
Step 2), by step one) heating material to 70 DEG C that obtains, keep rotating speed, for subsequent use after making it fully react 1h;
Step 3) by step 2) institute obtains in material stirring and slowly adds CH
3si (OCH
3)
3, for subsequent use after making its complete hydrolysis;
Step 4) by step 3) institute obtains in material stirring and slowly adds water, rotating speed is adjusted to 1600r/min, keeps temperature, whirlpool, continues 2h, for subsequent use after obtaining colourless transparent solution;
Step 5) by step 4) institute obtains in material stirring and adds wollastonite, boron nitride, fine-grained alumina, super fine zinc oxide, titanium oxide, rotating speed is adjusted to 1000r/min, after fully stirring 40min, and filling finished product.
Claims (2)
1. a fire-resistant anticorrosion paint, is characterized in that, material and weight proportion respectively: potassium silicate solution 812 parts, lithium hydroxide aqueous solution 32 parts, CH
3si (OCH
3)
337 parts, 68 parts, water, wollastonite 139 parts, boron nitride 37 parts, fine-grained alumina 41 parts, super fine zinc oxide 35 parts, titanium oxide 38 parts.
2. according to fire-resistant anticorrosion paint according to claim 1, it is characterized in that, its preparation method, preparation method is following steps: step one), in reaction vessel, add potassium silicate solution, rotating speed is adjusted to 1500r/min, form whirlpool, and solution is heated to 35 DEG C, it is for subsequent use slowly to add lithium hydroxide aqueous solution in stirring;
Step 2), by step one) heating material to 70 DEG C that obtains, keep rotating speed, for subsequent use after making it fully react 1h;
Step 3) by step 2) institute obtains in material stirring and slowly adds CH
3si (OCH
3)
3, for subsequent use after making its complete hydrolysis;
Step 4) by step 3) institute obtains in material stirring and slowly adds water, rotating speed is adjusted to 1600r/min, keeps temperature, whirlpool, continues 2h, for subsequent use after obtaining colourless transparent solution;
Step 5) by step 4) institute obtains in material stirring and adds wollastonite, boron nitride, fine-grained alumina, super fine zinc oxide, titanium oxide, rotating speed is adjusted to 1000r/min, after fully stirring 40min, and filling finished product.