CN1052850C - Multipurpose steel and plastic composite material support

Info

Publication number: CN1052850C
Application number: CN96114172A
Authority: CN
Inventors: 张志孝
Original assignee: Individual
Current assignee: Individual
Priority date: 1996-12-30
Filing date: 1996-12-30
Publication date: 2000-05-31
Anticipated expiration: 2016-12-30
Also published as: CN1157385A

Abstract

The present invention relates to a multipurpose steel-plastic composite material supporter which is a double-layer pipe material whose the inner part is made of steel and the outer part is made of plastic, wherein the inner layer of the pipe material is a thin-wall metal pipe, and the outer layer is a regenerated plastic pipe. The regenerated plastic pipe is composed of waste plastic by adding a plasticizer, a light stabilizing agent, a thermal stabilizing agent, an oxidation inhibitor, a flame retardant, a lubricator, etc., and the regenerated plastic pipe is shaped out of the steel pipe together with the additives by heating extrusion in one time. The composite material supporter has the advantages of sufficient obdurability, convenient assembly and disassembly, difficult corrosion, long service life and low cost. Thereby, the composite material supporter can be used for planting vegetables, cultivating aquatic products and livestock, culturing seedlings and flowers, cultivating fruit trees, etc., and can be used as the supporter for yurts, trailer coach for tour, etc.

Description

Multipurpose steel and plastic composite material support

The present invention relates to a kind of multipurpose steel and plastic composite material support, can be used for growing vegetables, aquatic products livestock-raising, the support in fruit growing and yurt, travel activity room etc. of growing flower of growing seedlings, belong to technical field of structural materials.

Along with the raising of people's living standard, vegetables have been requisite food in people's daily life, and in particularly northerly winter, the plantation of vegetables is particularly important.Therefore utilize the technical development of crops such as plastic greenhouse cultivation vegetables very fast in recent years.At present, the skeleton of plastic tunnel mostly adopts bamboo to make, and bamboo wood will rise about 1 year after being exposed to the sun summer and split and lose ability to bear, thereby service life is short, will change in 2～3 years.And assembly and disassembly is time-consuming takes a lot of work, and bamboo wood will transport from south, increases cost.In addition can also be with reinforcing bar as big-canopy framework, though this greenhouse bracket intensity of reinforcement fabrication of using is good, cost height, cost per mu are more than ten thousand yuan, the peasant is difficult to accept.And metallic framework can't dismantle, and easy-to-rust causes certain difficulty for the reasonable utilization in soil.For this reason, the inventor once invented a kind of compound support frame material, and number of patent application is 95107473.3.This support replaces existing metal or bamboo support, has advantages such as cost is low, intensity is high, long service life.But this compound rest is a solid member, and the support dead weight is big, and complex manufacturing, and curing period is long, and long-distance transport is inconvenient.

The objective of the invention is to design a kind of multipurpose steel and plastic composite material support, utilize waste plastics recycling after, add additive, outside thin metallic tubd, once be squeezed into steel and plastic composite material support.The timbering material that steel is moulded outward in this not only has enough intensity, and saves material, and turns waste into wealth.

The multipurpose steel and plastic composite material support of the present invention's design is double-deck tubing, and nexine is a thin-wall metal pipe, and skin is the regenerated plastics pipe, and the proportioning of regenerated plastics pipe is:

Regenerated plastics: 80～95%

Plasticizer: 0.5～1.5%

Light stabilizer: 0.1～0.8%

Heat stabilizer: 0.1～0.8%

Antioxidant: 0.1～0.8%

Fire retardant: 1～15%

Lubricant: 0.1～0.8%.

Skill is in the preparation of double-deck tubing:

(1) with waste plastics masterbatch regeneration processing, oven dry;

(2) masterbatch after will drying adds in the injection machine, adds above-mentioned various additive simultaneously according to the above ratio;

(3) book wall steel pipe enters from compression sleeve one end of cover molding machine, the regenerated plastics master batch adds compression sleeve from charging aperture, along with steel pipe is pushed ahead, plastic master batch is filled in around the steel pipe, and be extruded the outer field heater element of sleeve and be heated under 120～260 ℃ and dissolve, arrive the mould outlet place and be squeezed into double-deck tubing, the tubing that stretches out mould promptly becomes composite material bracket after cooling.Also can be with the pressing method moulding of other multiple routines.

The composite material bracket of the present invention's design is a raw material with the waste or used plastics, pushes with thin metallic tubd and forms the support that interior steel is moulded outward, turns waste into wealth, for vast farmers provides a kind of economical and practical means of production.This holder combination convenient disassembly, not perishable, the intensity height, be convenient to keeping service life about 10 years, and low price, cost per mu thereby have very considerable social benefit and economic benefit about 4000 yuan.

Composite material bracket of the present invention, wherein used regenerated plastics can be thermoplastics, as polyvinyl chloride, polyethylene, polypropylene, polystyrene, ABS etc.Also can be thermoplastic engineering plastic, as polyamide, Merlon, polyformaldehyde etc.Wherein used additive, all be various commercial additives commonly used in the prior art, as plasticizer can be diisooctyl phthalate (DIDP), phthalic acid two (2-ethyl ester) (DOP) etc., light stabilizer can be 2-hydroxyl-4-methoxy benzophenone, 2-(the 3-tert-butyl group-2-hydroxy-5-methyl base phenyl)-5-chlorobenzotriazole etc., heat stabilizer can be a phosphorous acid 4,4-diisopropyl fork bis-phenol (10-16) carbon Arrcostab or stearoyl benzoyl methane etc., antioxidant can be 1,1,3-three (second-methyl-4-hydroxyl-5-tert-butyl-phenyl) butane or four (β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester etc., fire retardant can be a brominated Polystyrene (BPS) etc., and lubricant can be that the oligomer ester (name of product is LC-2) of aliphatic polyacid and polyalcohol or fatty acid emperor and monohydric alcohol are compound lubrication prescription (name of product is LC-1) of main body etc.

The cross section of composite material bracket can be circular, oval, square or rectangle.The thickness proportion of outer regenerated plastics layer and inner layer metal layer is 2～10: 1.When the support cross section was circle, diameter of section was 20～200mm.

Description of drawings:

Fig. 1 is the structural representation of the composite material bracket that designs of the present invention, among the figure, and the 1st, metal level, the 2nd, regenerated plastics layer.

Fig. 2 is the used compression sleeve structural representation of extrusion modling.Among Fig. 2, the 3rd, composite material bracket, the 4th, mould, the 5th, the masterbatch import, the 6th, heating muff, the 7th, book wall steel pipe, the 8th, heater element, the 9th, the regenerated plastics layer, the 10th, cooling water, steel pipe is along the diagram arrow direction.

Be that peace of the present invention is executed example below:

Embodiment 1: after 90% polyvinyl chloride waste plastics recycling processing, add plasticizer 1%, light stabilizer 0.5%, heat stabilizer 0.5%, antioxidant 0.5%, fire retardant 7% and lubricant 0.5%, after mixing thoroughly together, add in the cover molding machine, be that the metal tube of 0.5mm once pushes through compression sleeve and wall thickness under 150 ℃, the external diameter of the double-deck tubing of formation is 35mm, and the compression strength of tubing is 50MPa, bending strength is 45MPa, and tensile strength is 35MPa.

Embodiment 2: after 85% polyethylene waste plastics recycling processing, add plasticizer 1.5%, light stabilizer 0.7%, heat stabilizer 0.6%, antioxidant 0.7%, fire retardant 10.5% and lubricant 0.5%, after mixing thoroughly together, add in the cover molding machine, be that the metal tube of 1mm once pushes through compression sleeve and wall thickness under 180 ℃, the external diameter of the double-deck tubing of formation is 35mm, and the compression strength of tubing is 50MPa, bending strength is 45MPa, and tensile strength is 35MPa.

Embodiment 3: after 85% polyamide waste plastics recycling processing, add plasticizer 1.5%, light stabilizer 0.7%, heat stabilizer 0.6%, antioxidant 0.7%, fire retardant 10.5% and lubricant 0.5%, after mixing thoroughly together, add in the cover molding machine, be that the metal tube of 1mm once pushes through compression sleeve and wall thickness under 200 ℃, the external diameter of the double-deck tubing of formation is 35mm, and the compression strength of tubing is 55MPa, bending strength is 40MPa, and tensile strength is 36MPa.

Claims

1. multipurpose steel and plastic composite material support, this support is double-deck tubing, and internal layer is a thin-wall metal pipe, it is characterized in that, and skin is the regenerated plastics pipe; The proportioning of described regenerated plastics layer is: regenerated plastics: 80～95% plasticizer: 0.5～1.5% light stabilizer: 0.1～0.8% heat stabilizer: 0.1～0.8% antioxidant: 0.1～0.8% fire retardant: 1～15% lubricant: 0.1～0.8%

2. compound support frame material as claimed in claim 1 is characterized in that the cross section of wherein said double-deck tubing is circular, oval, square or rectangle.

3. compound support frame material as claimed in claim 1 is characterized in that the thickness proportion of wherein said outer regenerated plastics layer and inner layer metal layer is 2～10: 1.

4. compound support frame material as claimed in claim 1 is characterized in that wherein said regenerated plastics are polyvinyl chloride or polyethylene.

5. compound support frame material as claimed in claim 1, the caliber that it is characterized in that wherein said double-deck tubing is 20～200mm.