CN105274279B - A method of thickening converter terminal slag - Google Patents
A method of thickening converter terminal slag Download PDFInfo
- Publication number
- CN105274279B CN105274279B CN201510786906.5A CN201510786906A CN105274279B CN 105274279 B CN105274279 B CN 105274279B CN 201510786906 A CN201510786906 A CN 201510786906A CN 105274279 B CN105274279 B CN 105274279B
- Authority
- CN
- China
- Prior art keywords
- steel
- slag
- added
- carbon content
- bottom blowing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (3)