CN105269899B - A kind of beverage machine cushion pad and the method for preparing the beverage machine cushion pad - Google Patents
A kind of beverage machine cushion pad and the method for preparing the beverage machine cushion pad Download PDFInfo
- Publication number
- CN105269899B CN105269899B CN201410788489.3A CN201410788489A CN105269899B CN 105269899 B CN105269899 B CN 105269899B CN 201410788489 A CN201410788489 A CN 201410788489A CN 105269899 B CN105269899 B CN 105269899B
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- cushion pad
- beverage machine
- ptfe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of beverage machine cushion pad and its method for preparing the beverage machine cushion pad, rubber earring moulding cushion described in the beverage machine cushion pad is made up of yielding rubber, the yielding rubber includes ethylene propylene diene rubber, polytetrafluoroethylene PTFE powder, zinc oxide, stearic acid, carbon black, age resistor and vulcanizing agent；The PTFE superficial layers are made up of polytetrafluoroethylene PTFE sheet material；The glue layer includes a primer and a face glue.The ageing resistace of beverage machine cushion pad provided by the invention uses more than 10 years under environment between 45 DEG C~100 DEG C, and normal temperature can reach the shock requirement of resistance to more than 100,000 times.In addition, surface is without significant change and can absorb a large amount of sound waves reduction noises, its low-temperature impact resistance is superior.
Description
Technical field
The present invention relates to a kind of cushion pad, specifically, is related to a kind of beverage machine cushion pad and prepares beverage machine buffering
The method of pad.
Background technology
At present, drinks machine is increasingly adopted and liked by people due to its great ease of use.From
Dynamic beverage machine has a variety of advantages, such as, beverage can be deposited individually, it is not necessary to which beverage can just be obtained by opening door, especially suitable
Close children to use, also there is the advantages of energy-conservation, safe in addition, meet the demand of modern people.But liked in people's selection
Beverage when skidding off beverage machine, can always send very big noise, when opening (tank), also frequently overflow carbonic acid foam or
Person sprays foam, in addition, unstable due to movement locus when going out tank, situations such as also resulting in card tank occurs.Therefore, it is badly in need of one
Kind can solve the problem that above mentioned problem and suitable for the beverage machine cushion pad under deepfreeze environment.
The content of the invention
In place of solving above-mentioned the deficiencies in the prior art, it is an object of the invention to provide a kind of beverage machine cushion pad,
The defects of to overcome in the prior art.
To achieve these goals, the invention provides a kind of beverage machine cushion pad, the beverage machine cushion pad to include rubber
Glue buffers pedestal layer, polytetrafluoroethylene PTFE superficial layer and in the rubber buffer pedestal layer and the polytetrafluoroethylene (PTFE)
The glue layer bonded between PTFE superficial layers；Wherein, the rubber earring moulding cushion is made up of yielding rubber, the yielding rubber
It is described including ethylene propylene diene rubber, polypropylene, polytetrafluorethylepowder powder, zinc oxide, stearic acid, carbon black, age resistor and vulcanizing agent
The thickness of rubber buffer pedestal layer is 3~6mm；The polytetrafluoroethylene PTFE superficial layer is by polytetrafluoroethylene PTFE sheet material system
Into the thickness of the polytetrafluoroethylene PTFE superficial layer is 0.2~0.5mm；The glue layer includes a primer and a face glue.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the yielding rubber includes 50~70 weights
Measure part ethylene propylene diene rubber, 20~30 parts by weight of polypropylene, 5~10 parts by weight polytetrafluoroethylene PTFE powder, 3~15 parts by weight
Zinc oxide, 1~5 parts by weight stearic acid, 50~90 parts by weight of carbon black per, 4~10 parts by weight age resistor and the vulcanization of 2~5 parts by weight
Agent.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the carbon black is 30~50 parts by weight
Carbon black N220 and 20~40 parts by weight carbon black N330.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the age resistor is 2~5 parts by weight
The 2 of CPPD N cyclohexyl N' phenyl p phenylene diamine and 2~5 parts by weight, 2,4- trimethyl -1,2- EEDQ polymer.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the vulcanizing agent is 2~5 parts by weight
Sulphur and 0.2~0.5 parts by weight cumyl peroxide (DCP).
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the primer is model Kai Muluoke
CH205 adhesive, the face glue are model Kai Muluoke CH238 adhesive.
It is a further object of the invention to provide a kind of method for preparing the beverage machine cushion pad, its methods described
Comprise the following steps：(1) by twin-screw extruder by yielding rubber melting, the film of rubber buffer pedestal layer is generated；Or
Yielding rubber is extruded by double screw extruder, generates the particle of rubber buffer pedestal layer；Wherein：The yielding rubber bag
Include ethylene propylene diene rubber, polypropylene, polytetrafluorethylepowder powder, zinc oxide, stearic acid, carbon black, age resistor and vulcanizing agent；(2) will
The PTFE surfaces layer surface of polytetrafluoroethylene (PTFE) first coats a primer, is coated with a face glue, then will coat the polytetrafluoroethyl-ne of glue
Alkene PTFE superficial layers are punched into the exterior surface dimension of the cushion pad pedestal；And (3) are delayed using sulfuration process shaped beverage machine
Punching pad：Polytetrafluoroethylene PTFE superficial layer after punching is put into sulfurizing mould die cavity, the rubber being then placed in step (1) delays
The film of pedestal layer is rushed, carries out vulcanizing treatment, beverage machine cushion pad is made；Or buffered using Shooting Technique shaped beverage machine
Pad：PTFE superficial layers after punching are put into molding mold cavity, then by the micelle of the rubber buffer pedestal layer in step (1)
As raw material, injection molding is carried out, beverage machine cushion pad is made.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that in step (1), double roller glue furnacing temperature
For 90~110 DEG C, twin-screw takes out a temperature as 150~170 DEG C.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that in step (3), curing temperature 160
~180 DEG C, injection temperature is 160~190 DEG C.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that in step (3), cure time 200
~350 seconds.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that in step (3), injection time 20
~40 seconds.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the yielding rubber includes 50~70 weights
Measure part ethylene propylene diene rubber, 20~30 parts by weight of polypropylene, 5~10 parts by weight polytetrafluoroethylene PTFE powder, 3~15 parts by weight
Zinc oxide, 1~5 parts by weight stearic acid, 50~90 parts by weight of carbon black per, 4~10 parts by weight age resistor and the vulcanization of 2~5 parts by weight
Agent.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the carbon black is 30~50 parts by weight
Carbon black N220 and 20~40 parts by weight carbon black N330.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the age resistor is 2~5 parts by weight
The 2 of CPPD N cyclohexyl N' phenyl p phenylene diamine and 2~5 parts by weight, 2,4- trimethyl -1,2- EEDQ polymer.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the vulcanizing agent is 2~5 parts by weight
Sulphur and 0.2-0.5 parts by weight cumyl peroxides (vulcanizing agent DCP).
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the primer is model Kai Muluoke
CH205 adhesive, the face glue are model Kai Muluoke CH238 adhesive.
Further explanation as the beverage machine cushion pad of the present invention, it is preferable that the work temperature of the beverage machine cushion pad
Spend for 0~15 DEG C.
As can be seen here, drinks machine cushion pad provided by the invention is used by polytetrafluoroethylene PTFE sheet material by surface
As superficial layer, its surface scrolls coefficient of friction is almost nil, and the canned article such as pop can and beverage bottle is easy to by design route
Operation, while polytetrafluoroethylene PTFE has extremely excellent ageing resistace, can make for a long time between -186 DEG C~250 DEG C
With；In addition, can reach amplitude using elastomeric material and change rapidly as cushion, so as to suppress the generation of carbonic acid foam,
And a large amount of sound waves can be absorbed and reduce noise, its low-temperature impact resistance is superior, and the shock that normal temperature can reach resistance to more than 100,000 times will
Ask；The age resistor added in yielding rubber, it may be such that it has very strong ageing resistace, can be in -45 DEG C~100 DEG C of environment
It is lower using 10 years with upper surface without significant change.
Brief description of the drawings
Fig. 1 is the structural representation of the beverage machine cushion pad of the present invention.
Description of reference numerals is as follows：
In rubber buffer pedestal layer 1, PTFE superficial layers 2, glue layer 3.
Embodiment
In order that auditor can further appreciate that structure, feature and the other purposes of the present invention, in conjunction with appended preferable
Embodiment be accompanied by accompanying drawing describe in detail it is as follows, this accompanying drawing embodiment described is merely to illustrate technical scheme, and
The non-limiting present invention.
Embodiment 1
First, by double rod rubber mixing machines, by 60 parts by weight ethylene propylene diene rubbers, 30 parts by weight of polypropylene, 5 parts by weight poly- four
PVF PTFE powder, 3 part by weight of zinc oxide, 2 parts by weight stearic acid, 30 parts by weight are purchased in the carbon black of Zi Gong carbon black plant
It is (anti-old that N220,20 parts by weight purchase the carbon black N330 in Zi Gong carbon black plant, 2 parts by weight CPPD N cyclohexyl N' phenyl p phenylene diamines
Agent 4010), trimethyl -1, the 2- EEDQ polymer (anti-aging agent RD) of 2 parts by weight 2,2,4-, 2 parts by weight sulphur and 0.2 weight
The yielding rubber of cumyl peroxide (vulcanizing agent DCP) composition of part carries out refining glue processing at a temperature of 100 DEG C, as sulphur
Chemical industry skill is shaped to the film of the thick rubber buffer pedestal layers of 5mm.Finally, by polytetrafluoroethylene PTFE superficial layer thick 0.2mm
Surface first coat the adhesive by the standby model Kai Muluoke CH205 of U.S.'s LORD company systems as primer, re-coating type
Number for Kai Muluoke CH238 adhesive be used as face glue, then by coating glue polytetrafluoroethylene PTFE superficial layer be punched into
The exterior surface dimension of the cushion pad pedestal, is put into sulfurizing mould die cavity, is then placed in the film of rubber buffer pedestal layer,
Vulcanize 200 seconds at a temperature of 180 DEG C, the beverage machine cushion pad of structure as shown in Figure 1 is made.
Ageing resistace test is carried out using obtained beverage machine cushion pad, experiment shows, the beverage machine cushion pad resists
Ageing properties use more than 10 years in the environment of -45 DEG C~100 DEG C, and normal temperature can reach the shock requirement of resistance to more than 100,000 times.
In addition, surface is without significant change and can absorb a large amount of sound waves reduction noises, its low-temperature impact resistance is superior.
Embodiment 2
First, by double rod rubber mixing machines, by 70 parts by weight ethylene propylene diene rubbers, 20 parts by weight of polypropylene, 6 parts by weight PTFE
Powder, 5 part by weight of zinc oxide, 5 parts by weight stearic acid, 40 parts by weight purchase the carbon black N220 in Zi Gong carbon black plant, 30 parts by weight
Buying in the carbon black N330,3 parts by weight CPPD N cyclohexyl N' phenyl p phenylene diamines (antioxidant 4010), 5 weights of Zi Gong carbon black plant
Measure the peroxidating of trimethyl -1, the 2- EEDQ polymer (anti-aging agent RD) of part 2,2,4-, 3 parts by weight sulphur and 0.5 parts by weight
The yielding rubber of diisopropylbenzene (DIPB) (vulcanizing agent DCP) composition carries out refining glue processing at a temperature of 110 DEG C, is shaped to as sulfuration process
The film of rubber buffer pedestal layer thick 3mm.
Finally, the inner surface of PTFE superficial layers thick 0.5mm is first coated and opened by the standby model of U.S.'s LORD company systems
Then Mu Luoke CH205 adhesive will as primer, re-coating model Kai Muluoke CH238 adhesive as face glue
The polytetrafluoroethylene PTFE superficial layer of coating glue is punched into the exterior surface dimension of the cushion pad pedestal, is put into sulfurizing mould type
Chamber, the film of rubber buffer pedestal layer is then placed in, vulcanized 300 seconds at a temperature of 160 DEG C, structure as shown in Figure 1 is made
Beverage machine cushion pad.
Ageing resistace test is carried out using obtained beverage machine cushion pad, experiment shows：The beverage machine cushion pad resists
Ageing properties use more than 10 years in the environment of -45 DEG C~100 DEG C, and normal temperature can reach the shock requirement of resistance to more than 100,000 times.
In addition, surface is without significant change and can absorb a large amount of sound waves reduction noises, its low-temperature impact resistance is superior.
Embodiment 3
First, by double rod rubber mixing machines, by 50 parts by weight ethylene propylene diene rubbers, 25 parts by weight of polypropylene, 10 parts by weight
PTFE powder, 15 part by weight of zinc oxide, 1 parts by weight stearic acid, 50 parts by weight purchase the carbon black N220 in Zi Gong carbon black plant, 40 weights
Measure part buying in the carbon black N330 of Zi Gong carbon black plant, 5 parts by weight CPPD N cyclohexyl N' phenyl p phenylene diamines (antioxidant 4010),
The peroxide of trimethyl -1, the 2- EEDQ polymer (anti-aging agent RD) of 3 parts by weight 2,2,4-, 5 parts by weight sulphur and 0.2 parts by weight
The yielding rubber for changing diisopropylbenzene (DIPB) (vulcanizing agent DCP) composition carries out refining glue processing at a temperature of 90 DEG C, is molded as sulfuration process
For the film of rubber buffer pedestal layer thick 6mm.
Then, the inner surface of PTFE superficial layers thick 0.4mm is first coated and opened by the standby model of U.S.'s LORD company systems
Then Mu Luoke CH205 adhesive will as primer, re-coating model Kai Muluoke CH238 adhesive as face glue
The polytetrafluoroethylene PTFE superficial layer of coating glue is punched into the exterior surface dimension of the cushion pad pedestal, is put into sulfurizing mould type
Chamber, the film for the rubber buffer pedestal layer being finally putting into, vulcanize 250 seconds at a temperature of 170 DEG C, structure as shown in Figure 1 is made
Beverage machine cushion pad.
Ageing resistace test is carried out using obtained beverage machine cushion pad, experiment shows：The beverage machine cushion pad resists
Ageing properties use more than 10 years in the environment of -45 DEG C~100 DEG C, and normal temperature can reach the shock requirement of resistance to more than 100,000 times.
In addition, surface is without significant change and can absorb a large amount of sound waves reduction noises, its low-temperature impact resistance is superior.
Embodiment 4
First, by double screw extruder, by 55 parts by weight ethylene propylene diene rubbers, 25 parts by weight of polypropylene, 8 parts by weight
PTFE powder, 10 part by weight of zinc oxide, 3 parts by weight stearic acid, 45 parts by weight purchase the carbon black N220 in Zi Gong carbon black plant, 25 weights
Amount part purchases the carbon black N330 in Zi Gong carbon black plant, 4 parts by weight CPPD N cyclohexyl N' phenyl p phenylene diamines (antioxidant 4010), 2
Parts by weight 2,2, the peroxide of 4- trimethyl -1,2- EEDQ polymer (anti-aging agent RD), 4 parts by weight sulphur and 0.2 parts by weight
The yielding rubber of change diisopropylbenzene (DIPB) (vulcanizing agent DCP) composition twin-screw at a temperature of 150 DEG C takes out grain, as rubber buffer pedestal layer
Micelle.
Finally, the inner surface of 0.45mmPTFE superficial layers is first coated by the standby model Kai Muluo of U.S.'s LORD company systems
Gram CH205 adhesive is used as face glue as primer, re-coating model Kai Muluoke CH238 adhesive, then will coat
The polytetrafluoroethylene PTFE superficial layer of glue is punched into the exterior surface dimension of the cushion pad pedestal, is put into molding mold cavity,
By rubber granule injection molding at a temperature of 190 DEG C, 20 seconds injection times, the beverage machine cushion pad of obtained structure as shown in Figure 1.
Ageing resistace test is carried out using obtained beverage machine cushion pad, experiment shows：The beverage machine cushion pad resists
Ageing properties use more than 10 years in the environment of -45 DEG C~100 DEG C, and normal temperature can reach the shock requirement of resistance to more than 100,000 times.
In addition, surface is without significant change and can absorb a large amount of sound waves reduction noises, its low-temperature impact resistance is superior.
Embodiment 5
First, by double screw extruder, by 65 parts by weight ethylene propylene diene rubbers, 28 parts by weight of polypropylene, 7 parts by weight
PTFE powder, 12 part by weight of zinc oxide, 4 parts by weight stearic acid, 35 parts by weight purchase the carbon black N220 in Zi Gong carbon black plant, 35 weights
Measure part buying in the carbon black N330 of Zi Gong carbon black plant, 2 parts by weight CPPD N cyclohexyl N' phenyl p phenylene diamines (antioxidant 4010),
The peroxide of trimethyl -1, the 2- EEDQ polymer (anti-aging agent RD) of 5 parts by weight 2,2,4-, 5 parts by weight sulphur and 0.3 parts by weight
Change diisopropylbenzene (DIPB) (vulcanizing agent DCP) composition yielding rubber, twin-screw takes out grain at a temperature of 170 DEG C, as rubber buffer pedestal layer
Micelle.
Finally, the inner surface of PTFE superficial layers thick 0.5mm is first coated and opened by the standby model of U.S.'s LORD company systems
Then Mu Luoke CH205 adhesive will as primer, re-coating model Kai Muluoke CH238 adhesive as face glue
The polytetrafluoroethylene PTFE superficial layer of coating glue is punched into the exterior surface dimension of the cushion pad pedestal, is put into injection mold type
Chamber, the micelle for the rubber buffer pedestal layer being then placed in step (1), the injection molding at a temperature of 160 DEG C, injection time 40
Second, the beverage machine cushion pad of obtained structure as shown in Figure 1.
Ageing resistace test is carried out using obtained beverage machine cushion pad, experiment shows：The beverage machine cushion pad resists
Ageing properties use more than 10 years in the environment of -45 DEG C~100 DEG C, and normal temperature can reach the shock requirement of resistance to more than 100,000 times.
In addition, surface is without significant change and can absorb a large amount of sound waves reduction noises, its low-temperature impact resistance is superior.
Embodiment 6
First, by double screw extruder, by 70 parts by weight ethylene propylene diene rubbers, 22 parts by weight of polypropylene, 9 parts by weight
PTFE powder, 8 part by weight of zinc oxide, 4 parts by weight stearic acid, 35 parts by weight purchase the carbon black N220 in Zi Gong carbon black plant, 30 weights
Amount part purchases the carbon black N330 in Zi Gong carbon black plant, 3 parts by weight CPPD N cyclohexyl N' phenyl p phenylene diamines (antioxidant 4010), 4
Parts by weight 2,2, the peroxide of 4- trimethyl -1,2- EEDQ polymer (anti-aging agent RD), 5 parts by weight sulphur and 0.5 parts by weight
The yielding rubber of change diisopropylbenzene (DIPB) (vulcanizing agent DCP) composition twin-screw at a temperature of 160 DEG C takes out grain, as rubber buffer pedestal layer
Micelle.
Finally, the inner surface of PTFE superficial layers thick 0.4mm is first coated and opened by the standby model of U.S.'s LORD company systems
Then Mu Luoke CH205 adhesive will as primer, re-coating model Kai Muluoke CH238 adhesive as face glue
The polytetrafluoroethylene PTFE superficial layer of coating glue is punched into the exterior surface dimension of the cushion pad pedestal, is put into injection mold type
Chamber, then by the micelle of rubber buffer pedestal layer, the injection molding at a temperature of 175 DEG C, 30 seconds injection times, such as Fig. 1 is made
The beverage machine cushion pad of shown structure.
Ageing resistace test is carried out using obtained beverage machine cushion pad, experiment shows：The beverage machine cushion pad resists
Ageing properties use more than 10 years in the environment of -45 DEG C~100 DEG C, and normal temperature can reach the shock requirement of resistance to more than 100,000 times.
In addition, surface is without significant change and can absorb a large amount of sound waves reduction noises, its low-temperature impact resistance is superior.
It is to be understood that foregoing invention content and embodiment are intended to prove technical scheme provided by the present invention
Practical application, it should not be construed as limiting the scope of the present invention.Those skilled in the art are in spirit and principles of the present invention
It is interior, when can various modifications may be made, equivalent substitution or improvement.Protection scope of the present invention is defined by appended claims.
Claims (6)
1. a kind of beverage machine cushion pad, it is characterised in that the beverage machine cushion pad includes rubber buffer pedestal layer (1), poly- four
PVF PTFE superficial layers (2) and the glue layer bonded between rubber buffer pedestal layer (1) and PTFE superficial layers (2)
(3)；Wherein,
Rubber buffer pedestal layer (1) is made up of yielding rubber, the yielding rubber include 50~70 parts by weight ethylene propylene diene rubbers,
20~30 parts by weight of polypropylene, 5~10 parts by weight polytetrafluoroethylene PTFE powder, 3~15 part by weight of zinc oxide, 1~5 parts by weight
Stearic acid, 50~90 parts by weight of carbon black per, 4~10 parts by weight age resistor and 2~5 parts by weight vulcanizing agents, the carbon black be 30~
The carbon black N220 of the 50 parts by weight and carbon black N330 of 20~40 parts by weight；The age resistor for 2~5 parts by weight N- cyclohexyl-
The 2,2,4 trimethyl 1,2 dihydroquinoline polymer of N'- diphenyl-para-phenylene diamines and 2~5 parts by weight；The vulcanizing agent is 2~5
The sulphur of parts by weight and 0.2~0.5 parts by weight cumyl peroxide DCP, the thickness of rubber buffer pedestal layer (1) for 3~
6mm；
Polytetrafluoroethylene PTFE superficial layer (2) is made up of polytetrafluoroethylene PTFE sheet material, and the thickness of PTFE superficial layers (2) is 0.2
~0.5mm；
Glue layer (3) includes a primer and a face glue.
2. beverage machine cushion pad as claimed in claim 1, it is characterised in that the primer is model Kai Muluoke CH205's
Adhesive, the face glue are model Kai Muluoke CH238 adhesive.
A kind of 3. method for preparing the beverage machine cushion pad as described in claim 1~2 is any, it is characterised in that methods described
Comprise the following steps：
1) it is 90~110 DEG C by yielding rubber melting, double roller glue furnacing temperature by twin-screw extruder, rubber buffer pedestal layer is made
(1) film；Or extruded yielding rubber by double screw extruder, twin-screw takes out a temperature as 150~170 DEG C, raw
Into the particle of rubber buffer pedestal layer (1)；Wherein：The yielding rubber includes 50~70 parts by weight ethylene propylene diene rubbers, 20
~30 parts by weight of polypropylene, 5~10 parts by weight polytetrafluoroethylene PTFE powder, 3~15 part by weight of zinc oxide, 1~5 parts by weight are hard
Resin acid, 50~90 parts by weight of carbon black per, 4~10 parts by weight age resistor and 2~5 parts by weight vulcanizing agents；Wherein, the carbon black is
The carbon black N220 of 30~50 parts by weight and carbon black N330 of 20~40 parts by weight；The age resistor is the N- hexamethylenes of 2~5 parts by weight
The 2,2,4 trimethyl 1,2 dihydroquinoline polymer of base-N'- diphenyl-para-phenylene diamines and 2~5 parts by weight；The vulcanizing agent is 2
The sulphur and 0.2-0.5 parts by weight cumyl peroxides of~5 parts by weight；
2) PTFE superficial layers (2) surface of polytetrafluoroethylene (PTFE) is first coated into a primer, is coated with a face glue, then will coat glue
Polytetrafluoroethylene PTFE superficial layer be punched into the exterior surface dimension of the cushion pad pedestal；And
3) sulfuration process shaped beverage machine cushion pad is used：PTFE superficial layers after punching are put into sulfurizing mould die cavity, then
The film for the rubber buffer pedestal layer being put into step 1), vulcanizing treatment is carried out, curing temperature is 160~180 DEG C, and beverage is made
Machine cushion pad；Or using Shooting Technique shaped beverage machine cushion pad：PTFE superficial layers after punching are put into injection mold type
Chamber, then using the micelle of the rubber buffer pedestal layer in step 1) as raw material, carrying out injection molding, injection temperature is 160~
190 DEG C, beverage machine cushion pad is made.
4. method as claimed in claim 3, it is characterised in that in step 3), cure time is 200~300 seconds；In step
3) in, injection time is 20~40 seconds.
5. method as claimed in claim 3, it is characterised in that the primer be model Kai Muluoke CH205 adhesive, institute
State the adhesive that face glue is model Kai Muluoke CH238.
6. method as claimed in claim 3, it is characterised in that the operating temperature of the beverage machine cushion pad is 0~15 DEG C.