CN105254237A - 蒸压加气混凝土用界面砂浆 - Google Patents
蒸压加气混凝土用界面砂浆 Download PDFInfo
- Publication number
- CN105254237A CN105254237A CN201510615335.9A CN201510615335A CN105254237A CN 105254237 A CN105254237 A CN 105254237A CN 201510615335 A CN201510615335 A CN 201510615335A CN 105254237 A CN105254237 A CN 105254237A
- Authority
- CN
- China
- Prior art keywords
- powder
- agent
- steam
- boundary mortar
- pressing aero
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种蒸压加气混凝土用界面砂浆,按质量百分比计由以下组分组成:水泥38%;矿粉7%;黄砂28.8~40.3%;尾矿砂13.5~25.0%;外加剂1.2%。所述的外加剂为改性剂和稠化剂,所述的改性剂为纤维素醚、引气剂、减水剂的一种或多种混合物,本发明有效利用了大量尾矿砂以及经过选矿或冶炼后排出的残余物和工业废料形成的矿粉不仅大大降低了成本,而且实现了绿色无污染的成分配比,减少了天然黄沙的使用量同时通过纤维素醚、引气剂、减水剂的一种或多种混合物增加界面砂浆粘结性能和含气量。
Description
技术领域
本发明涉一种界面砂浆,具体地指一种蒸压加气混凝土用界面砂浆。
背景技术
界面砂浆又称界面剂,它是由水泥、石英砂、聚合物胶结料配以多种添加剂经机械混合均匀而成。主要用于处理墙体与保温层的连接部位和用以改善基层或保温层表面粘结性能。亦被称为聚合物界面砂浆。作为一种新型的建筑材料蒸压加气混凝土其由于具有良好的保温性能、隔音性能、抗渗性能以及耐火性能得到了广泛应用,由于蒸压加气混凝土在制造过程中引入空气而形成大量微小、封闭而稳定气泡,现有界面剂已无法与其匹配,必须找到气泡直径更小,气泡密度更大的界面剂才能确保粘结性能。另外对于绿色制造过程中尾矿砂以及经过选矿或冶炼后排出的残余物和工业废料形成的矿粉利用问题一直是本领域技术人员研究的对象。
发明内容
本发明提供了一种不仅充分利用矿粉、尾矿砂,且形成大量密集稳定、微小气泡,增加粘结性能的蒸压加气混凝土用界面砂浆。
一种蒸压加气混凝土用界面砂浆,按质量百分比计由以下组分组成:
所述的外加剂为改性剂和稠化剂,所述的改性剂为纤维素醚、引气剂、减水剂的一种或多种混合物。该种蒸压加气混凝土用界面砂浆有效利用了大量尾矿砂以及经过选矿或冶炼后排出的残余物和工业废料形成的矿粉不仅大大降低了成本,而且实现了绿色无污染的成分配比,减少了天然黄沙的使用量同时通过纤维素醚、引气剂、减水剂的一种或多种混合物增加界面砂浆粘结性能。所述尾矿砂为铁尾矿砂。
所述的外加剂为纤维素醚、引气剂、减水剂、稠化剂,其中各成分重量百分比3∶2∶9∶80。
所述的稠化剂为海泡石粉末、蒙脱石粉末、膨润土粉末的混合物,其中各成分重量百分比3∶2∶4。海泡石粉末是一种具层链状结构的含水富镁硅酸盐黏土矿物。斜方晶系或单斜晶系,一般呈块状、土状或纤维状集合体。海泡石是一种纤维状的含水硅酸镁,通常呈白、浅灰、浅黄等颜色,不透明也没有光泽。它们有的形状像土块,有的成一个奇怪皮壳状或结核状。在电子显微镜下可以看到它们是由无数细丝聚在一起排成片状。蒙脱石是由颗粒极细的含水铝硅酸盐构成的层状矿物,蒙脱石亚族属于蒙皂石族矿物之一是重要的黏土矿物,一般为块状或土状。分子式(Al,Mg)2[Si4O10](OH)2·nH2O,中间为铝氧八面体,上下为硅氧四面体所组成的三层片状结构的黏土矿物,在晶体构造层间含水及一些交换阳离子,有较高的离子交换容量,具有较高的吸水膨胀能力。膨润土粉末具有很好的吸水膨胀性能以及分散和悬浮及造浆性能极大的提高了稠化剂的增稠性。海泡石粉末、蒙脱石粉末、膨润土粉末相互结合利用海泡石遇到水时会吸收很多水从而变得柔软起来,而一旦干燥就又变硬了,在柔软状态下吸附大量水分在蒙脱石粉末、膨润土粉末作用下形成良好的增稠性提高蒸压加气混凝土用界面砂浆的稠度和粘性。
所述引气剂为皂荚粉末、红海榄支柱根粉末、秋茄支柱根粉末、十二烷基二甲基胺氧化物按照重量百分比15∶2∶2∶1混合构成。皂荚也称为皂角,皂角中含有一种辛辣刺鼻的提取物,主要成分为三萜皂苷。它具有良好的引起性能,三萜皂苷由单糖基、苷基和苷元素组成。苷元素有两个相联接的苷元组成,一般情况下一个苷元可以连接3个或3个以上的单糖,形成一个较大的五环三萜空间结构。单糖基中的单糖具有很多羟基能与水分子形成氢键,因而具有较强的亲水性,而苷元基中的苷元具有亲油性是憎水基。三萜皂苷属非离子型表面活性剂。当三萜皂苷溶于水后,大分子被吸附在气液界面上,形成两种基团的定向排列,从而降低了气泡界面的张力,使新界面的产生变得容易,若用机械方法搅拌溶液,就会产生气泡。且由于三萜皂分子结构较大,形成的分子膜较厚,气泡壁的弹性和强度较高,气泡能保持相对稳定。红海榄支柱根主要生长在海边,其具有发达的通气组织和致密的分子结构可以帮助皂荚粉末形成致密的气泡。秋茄支柱根这种植物是红树林中是福建常见种类,也是最能够耐寒的种类,向北可以分布到邻省浙江,除在福建外在海南、广西、广东、台湾、香港的海湾都有分布。在从外滩到内滩的区域里都有分布,多生长在河流入海口海湾较平坦的泥滩上其具有发达的通气组织和致密的分子结构可以帮助皂荚粉末形成致密的气泡。
本发明有效利用了大量尾矿砂以及经过选矿或冶炼后排出的残余物和工业废料形成的矿粉不仅大大降低了成本,而且实现了绿色无污染的成分配比,减少了天然黄沙的使用量同时通过纤维素醚、引气剂、减水剂的一种或多种混合物增加界面砂浆粘结性能和含气量。
具体实施方式
一种蒸压加气混凝土用界面砂浆,按质量百分比计由以下组分组成:
外加剂为改性剂和稠化剂,改性剂为纤维素醚、引气剂、减水剂的一种或多种混合物。
作为优选结构外加剂为纤维素醚、引气剂、减水剂、稠化剂,其中各成分重量百分比3∶2∶9∶80。稠化剂为海泡石粉末、蒙脱石粉末、膨润土粉末的混合物,其中各成分重量百分比3∶2∶4。引气剂为皂荚粉末、红海榄支柱根粉末、秋茄支柱根粉末、十二烷基二甲基胺氧化物按照重量百分比15∶2∶2∶1混合构成。尾矿砂为铁尾矿砂。
为了验证本发明蒸压加气混凝土用界面砂浆的特性,采用上述材料成分根据下表做如下实施方式,表中材料均安重量百分比计:
根据上述界面砂浆的成分配比本发明的界面砂浆各项技术指标优良,不仅大量利用了矿粉和尾矿砂等传统的废弃物实现二次利用,并且达到了蒸压加气混凝土所需要的粘合牢度和收缩性能,特别是添加了本发明引气剂可以显著提高收缩性能,而添加了本发明稠化剂显著提高了粘结强度。
Claims (5)
1.一种蒸压加气混凝土用界面砂浆,其特征在于按质量百分比计由以下组分组成:
所述的外加剂为改性剂和稠化剂,所述的改性剂为纤维素醚、引气剂、减水剂的一种或多种混合物。
2.根据权利要求1所述的蒸压加气混凝土用界面砂浆,其特征在于:所述的外加剂为纤维素醚、引气剂、减水剂、稠化剂,其中各成分重量百分比3∶2∶9∶80。
3.根据权利要求1所述的蒸压加气混凝土用界面砂浆,其特征在于:所述的稠化剂为海泡石粉末、蒙脱石粉末、膨润土粉末的混合物,其中各成分重量百分比3∶2∶4。
4.根据权利要求1所述的蒸压加气混凝土用界面砂浆,其特征在于:所述引气剂为皂荚粉末、红海榄支柱根粉末、秋茄支柱根粉末、十二烷基二甲基胺氧化物按照重量百分比15∶2∶2∶1混合构成。
5.根据权利要求1所述的蒸压加气混凝土用界面砂浆,其特征在于:所述尾矿砂为铁尾矿砂。